CN103013154A - 一种树脂玻纤配方及由该配方制成的花盆 - Google Patents

一种树脂玻纤配方及由该配方制成的花盆 Download PDF

Info

Publication number
CN103013154A
CN103013154A CN2012105540026A CN201210554002A CN103013154A CN 103013154 A CN103013154 A CN 103013154A CN 2012105540026 A CN2012105540026 A CN 2012105540026A CN 201210554002 A CN201210554002 A CN 201210554002A CN 103013154 A CN103013154 A CN 103013154A
Authority
CN
China
Prior art keywords
glass fiber
resin glass
fiber powder
parts
flowerpot
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012105540026A
Other languages
English (en)
Inventor
严志龙
代强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HONG BAO ENVIROMENTAL TECHNOLOGY Co Ltd
Original Assignee
HONG BAO ENVIROMENTAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HONG BAO ENVIROMENTAL TECHNOLOGY Co Ltd filed Critical HONG BAO ENVIROMENTAL TECHNOLOGY Co Ltd
Priority to CN2012105540026A priority Critical patent/CN103013154A/zh
Publication of CN103013154A publication Critical patent/CN103013154A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种树脂玻纤配方及由该配方制成的花盆，提供的配方包括如下重量份数的组份：树脂玻纤粉：80～95份；环氧树脂：5～20份；所述树脂玻纤粉含铜率为小于5%。树脂玻纤型花盆由如下重量份数的组份制成：树脂玻纤粉：80～95份；环氧树脂：5～20份；所述树脂玻纤粉含铜率为小于5%。由于树脂玻纤粉的特性，以其作为原料制得的花盆具有防水、防腐、防虫蛀、防酸碱、抗老化，重量轻（相对陶土花盆），不易破裂等特点。另外，因树脂玻纤粉中有少量的重金属含量，在重金属缓慢释放过程中，可使花卉的色泽更加艳丽，花期延长等特色。

Description

一种树脂玻纤配方及由该配方制成的花盆
技术领域
  本发明涉及工业废料的回收利用，具体地讲，涉及一种来源于工业废料的树脂玻纤配方及由该配方制成的花盆。
背景技术
  随着电子工业的蓬勃发展，废旧电子线路板、废覆铜板边角料及残次品的处理与日俱增。相应地废线路板、覆铜板分选处理在提取金属后残留的树脂玻纤粉这一工业固体废物的处理、处置也成为一大棘手难题。随意倾倒会造成二次污染，焚烧、填埋会产生高昂费用并且耗用土地资源。如何妥善处置和有效地综合利用树脂玻纤粉已成为解决环保问题面临的重要课题。
发明内容
本发明的目的在于提出一种能够回收利用工业废料中提取的树脂玻纤粉途径，进而得出了一种配方,并有该配方制得一种花盆。
本发明提供的配方，包括如下重量份数的组份：
树脂玻纤粉：80～95份
环氧树脂：5～20份
所述树脂玻纤粉含铜率为小于5%。
配方中的树脂玻纤粉的回收途径是将废电子线路板、覆铜板的边角料或残次品中的一种或几种的混合物粉碎、加热、筛选，提取金属粉后得到含铜率小于5%的树脂玻纤粉；回收提取过程最优选的结果为所述树脂玻纤粉含铜率为1.5～2.0%，含铅率为0.1～0.2%，含锌率为0.1～0.2%。在上述配方的基础上，优选方案为环氧树脂所占重量份数为12～15份，树脂玻纤粉所占重量份数为85～88份。所述环氧树脂也为来自工厂的废弃和过期并经回收的胺类、酯类、醇类、烯类、苯类等各种环氧树脂。
本发明所述的配方中，由于树脂玻纤粉具备防水、防腐、防酸碱以及隔热、阻燃等诸多特性，将其与环氧树脂配合，可直接用于橡胶、塑料行业的填充料以及防渗补漏的填充料等，并且可以配合其他原料制成各种产品，因而具有一定程度的回收价值。同时，本配方经加工后可以实现与陶瓷相似的性能，还可以被用于制作花盆、瓦片等传统工艺中使用陶瓷作为主要材料的产品，而且本配方比重较陶瓷更小，所得产品更为轻质，该配方同时满足了回收利用工业废料和制造日常生活用品两项功能，实现了树脂玻纤粉的综合利用。
本发明还提供了由上述配方制成的一种树脂玻纤型花盆，由如下重量份数的组份制成：
树脂玻纤粉：80～95份
环氧树脂：5～20份
所述树脂玻纤粉含铜率为小于5%。
优选地，所述树脂玻纤粉含铜率为1.5～2.0%，含铅率为0.1～0.2%，含锌率为0.1～0.2%。环氧树脂所占重量份数为12～15份，树脂玻纤粉所占重量份数为85～88份。
本发明提供的花盆只需将调配好的原料浇入特制的模具，然后用500吨级的油压机压制即可。
本发明所得花盆可通过在制作过程中掺入无机颜料制成不同颜色的花盆。由于树脂玻纤粉的特性，以其作为原料制得的花盆具有防水、防腐、防虫蛀、防酸碱、抗老化，重量轻（相对陶土花盆），不易破裂等特点。另外，因树脂玻纤粉中有少量的重金属含量，在重金属缓慢释放过程中，可使花卉的色泽更加艳丽，花期延长等特色。
具体实施方式
实施例1
本发明提供的配方，包括如下重量份数的组份：
树脂玻纤粉：90kg
环氧树脂：20kg
所述树脂玻纤粉含铜率为为3%。
配方中的树脂玻纤粉的回收途径是将废电子线路板、覆铜板的边角料或残次品中的一种或几种的混合物粉碎、加热、筛选，提取金属粉后得到含铜率小于5%的树脂玻纤粉。
实施例2
树脂玻纤粉：90kg
环氧树脂：20kg
所述树脂玻纤粉含铜率为1.8%，含铅率为0.15%，含锌率为0.2%。
实施例3
树脂玻纤粉：86kg
环氧树脂：14kg
所述树脂玻纤粉含铜率为1.8%，含铅率为0.15%，含锌率为0.2%。
实施例4　　　
按实施例1中配方选料制作树脂玻纤型花盆，制作时将调配好的原料浇入特制的模具，然后用500吨级的油压机压制即可。
实施例5
按实施例2中配方选料制作树脂玻纤型花盆，制作时将调配好的原料浇入特制的模具，然后用500吨级的油压机压制即可。
实施例6
按实施例3中配方选料制作树脂玻纤型花盆，制作时将调配好的原料浇入特制的模具，然后用500吨级的油压机压制即可。
根据以上说明书中的阐述，本发明所属领域的技术人员还可以对上述实施方式进行适当的变更和修改。因此，上述实施例中提到的内容并非是对本发明的限定，在不脱离本发明的发明构思的前提下，任何显而易见的替换均在本发明的保护范围之内。

Claims (6)

1. 一种树脂玻纤配方，包括如下重量份数的组份：
树脂玻纤粉：80～95份
环氧树脂：5～20份
所述树脂玻纤粉含铜率为小于5%。
2. 根据权利要求1所述的配方，其特征在于：所述树脂玻纤粉含铜率为1.5～2.0%，含铅率为0.1～0.2%，含锌率为0.1～0.2%。
3. 根据权利要求1或2所述的配方，其特征在于：环氧树脂所占重量份数为12～15份，树脂玻纤粉所占重量份数为85～88份。
4. 一种树脂玻纤型花盆，由如下重量份数的组份制成：
树脂玻纤粉：80～95份
环氧树脂：5～20份
所述树脂玻纤粉含铜率为小于5%。
5. 根据权利要求4所述的配方，其特征在于：所述树脂玻纤粉含铜率为1.5～2.0%，含铅率为0.1～0.2%，含锌率为0.1～0.2%。
6. 根据权利要求4或5所述的配方，其特征在于：环氧树脂所占重量份数为12～15份，树脂玻纤粉所占重量份数为85～88份。
CN2012105540026A 2012-12-19 2012-12-19 一种树脂玻纤配方及由该配方制成的花盆 Pending CN103013154A (zh)