CN103009015A - 双金属复合耐磨冶金轧辊的制造方法 - Google Patents

双金属复合耐磨冶金轧辊的制造方法 Download PDF

Info

Publication number
CN103009015A
CN103009015A CN2013100107146A CN201310010714A CN103009015A CN 103009015 A CN103009015 A CN 103009015A CN 2013100107146 A CN2013100107146 A CN 2013100107146A CN 201310010714 A CN201310010714 A CN 201310010714A CN 103009015 A CN103009015 A CN 103009015A
Authority
CN
China
Prior art keywords
welding
built
roller
resistant metallurgical
composite wear
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100107146A
Other languages
English (en)
Other versions
CN103009015B (zh
Inventor
赵春祥
牛茂文
李清
王树伟
安跃良
宋洪朝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HANDAN YONGGU METALLURGY SPARE PARTS CO Ltd
Original Assignee
HANDAN YONGGU METALLURGY SPARE PARTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HANDAN YONGGU METALLURGY SPARE PARTS CO Ltd filed Critical HANDAN YONGGU METALLURGY SPARE PARTS CO Ltd
Priority to CN201310010714.6A priority Critical patent/CN103009015B/zh
Publication of CN103009015A publication Critical patent/CN103009015A/zh
Application granted granted Critical
Publication of CN103009015B publication Critical patent/CN103009015B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

双金属复合耐磨冶金轧辊的制造方法,包括辊芯加工步骤、预热步骤、堆焊复合层步骤、精加工步骤和热处理步骤,其中:辊芯加工步骤为先用抗拉强度、屈服强度和抗冲击性能优良的钢材通过锻压和调质处理,制作辊芯毛坯,然后将辊芯毛坯粗加工至预留堆焊复合层尺寸;预热步骤为将辊芯预热至380C°±5C°的适焊温度。堆焊复合层步骤为将预热后的辊芯表面用埋弧焊工艺将预留的堆焊复合层用药芯焊丝堆焊填满;精加工步骤为将堆焊后的双金属复合耐磨冶金轧辊毛坯加工至设计尺寸;热处理步骤为将精加工后的双金属复合耐磨冶金轧辊进行淬火和调质处理,使其表层达到具备好的抗粘着磨损、抗磨粒磨损、红硬性、抗冷热疲劳性和抗剥落性的要求。

Description

双金属复合耐磨冶金轧辊的制造方法
技术领域
 本发明涉及一种轧辊的制作方法,尤其是一种双金属复合耐磨冶金轧辊的制造方法,用该方法制作的轧辊不但成本低,而且使用寿命长,可减少轧钢事故,降低轧制成本,属于表面硬化技术领域。
背景技术
目前,传统的冶金轧辊一般采用铸钢或60CrNiMo、65CrNiMo、60CrMnMo材质的锻钢通过调质、淬火等热处理工序来制造,材质中含有大量的贵重金属;因此,目前上述轧辊每吨在2.4万元~6万元之间,每支轧辊的重量在15~120吨之间,每支轧辊的价格在36万元~720万元之间,价格非常高,且制造工期长。由于轧钢过程中造成的轧辊磨损,轧辊在使用一个周期后,要进行缩径车修,反复几次后轧辊就要报废,一支轧辊从原始直径到报废,有效使用量约为轧辊总重量的20~25%,作为废钢处理的重量为轧辊总重量的75~80%;另外,目前的轧辊内外材质一致,由于过分强调材质的抗粘着磨损、抗磨粒磨损、红硬性、抗冷热疲劳性和抗剥落性,致使轧辊材质的韧性、屈服强度较低,加上操作失误等原因,断辊现象时有发生,断辊失效约占轧辊总用量的5~8%;资料显示,2010年我国消耗各种轧辊约450万吨,其中钢质轧辊占总消耗量的80%,钢质轧辊消耗约为360万吨,断辊直接报废为20~30万吨,正常报废约为250~270万吨,年总耗费约为270~300万吨;数量非常惊人;目前用60CrNiMo、65CrNiMo、60CrMnMo制造的冶金轧辊的过钢量低。因此,研究一种能够使轧辊芯部具备良好韧性和高屈服强度而表层具备好的抗粘着磨损、抗磨粒磨损、红硬性、抗冷热疲劳性和抗剥落性的双金属复合耐磨冶金轧辊的制造方法,是目前需要解决的技术问题。
发明内容
本发明所要解决的技术问题是提供一种能够使轧辊芯部具备良好韧性和高屈服强度而表层具备好的抗粘着磨损、抗磨粒磨损、红硬性、抗冷热疲劳性和抗剥落性的双金属复合耐磨冶金轧辊的制造方法。
本发明解决其技术问题的技术方案是:
双金属复合耐磨冶金轧辊的制造方法,包括辊芯加工步骤、预热步骤、堆焊复合层步骤、精加工步骤和热处理步骤,其中:
辊芯加工步骤为先用抗拉强度、屈服强度和抗冲击性能优良的钢材通过锻压和调质处理,制作辊芯毛坯,然后将辊芯毛坯粗加工至预留堆焊复合层尺寸;
预热步骤为将辊芯预热至380C°±5C°的适焊温度。
堆焊复合层步骤为将预热后的辊芯表面用埋弧焊工艺将预留的堆焊复合层用药芯焊丝堆焊填满;
精加工步骤为将堆焊后的双金属复合耐磨冶金轧辊毛坯加工至设计尺寸;
热处理步骤为将精加工后的双金属复合耐磨冶金轧辊进行淬火和调质处理,使其表层达到具备好的抗粘着磨损、抗磨粒磨损、红硬性、抗冷热疲劳性和抗剥落性的要求。
所述的堆焊复合层分三层焊接,第一层直接在辊芯表面堆焊,为熔合层,第二层在熔合层上堆焊,为过渡层,第三层在过渡层堆焊,为工作层;堆焊熔合层的焊丝与辊芯的材质要具有好的焊接性,堆焊过渡层的焊丝与熔合层要具有好的焊接性,堆焊工作层的焊丝与过渡层要具有好的焊接性。
辊芯的材质的化学成分的质量分数为0.3—0.45%C、0.17—0.37%Si、0.5—0.8%Mn、0.9—1.2%Cr、0.15—0.25%Mo,余量为Fe。
堆焊熔合层的焊丝的化学成分的质量分数为0.1—0.2%C、0.15—0.2%Cr、0.6—1.2%Mn、1.5—1.8%Ni、0.2—0.6%Mo、0.03—0.05%Re和0.02—0.05%N,余量为Fe。
堆焊过渡层的焊丝的化学成分的质量分数为0.15—0.2%C、0.8—1.4%Cr、1.5—1.8%Mn、1.8—2.2%Ni、0.3—0.5%Mo、0.1—0.3%V和0.03—0.05%Re,余量为Fe。
堆焊工作层的焊丝的化学成分的质量分数为0.25—0.5%C、6.5—7.5%Cr、1.5—1.8%Mn、1.8—2.2%Ni、0.8—2.0%Mo、0.5—1.5%V、0.03—0.05%Re和0.5—1.4Nb,余量为Fe。
与现有技术相比,利用本发明方法制造的冶金轧辊,不但比现有技术的冶金轧辊的过钢量提高2.5倍以上,且避免了轧钢过程中断辊事故的发生。同时又由于利用本发明方法制造的冶金轧辊,在使用一个周期后可以将约1.5—2mm的疲劳层车除,重新堆焊工作层,因此可以多次重复使用,经济效益可观。
附图说明
图1是本发明第一实施例的示意图(平辊);
图2是本发明第二实施例的示意图(二孔型辊);
图中1为辊芯的辊身、2为辊颈、3为工作层、4为过渡层、5为熔合层。
具体实施方式
双金属复合耐磨冶金轧辊的制造方法,包括辊芯加工步骤、预热步骤、堆焊复合层步骤、精加工步骤和热处理步骤,其中:
辊芯加工步骤为先用抗拉强度、屈服强度和抗冲击性能优良的钢材通过锻压和调质处理,制作辊芯毛坯,然后将辊芯毛坯粗加工至预留堆焊复合层尺寸;
预热步骤为将辊芯预热至380C°±5C°的适焊温度。
堆焊复合层步骤为将预热后的辊芯表面用埋弧焊工艺将预留的堆焊复合层用药芯焊丝堆焊填满;
精加工步骤为将堆焊后的双金属复合耐磨冶金轧辊毛坯加工至设计尺寸;
热处理步骤为将精加工后的双金属复合耐磨冶金轧辊进行淬火和调质处理,使其表层达到具备好的抗粘着磨损、抗磨粒磨损、红硬性、抗冷热疲劳性和抗剥落性的要求。
所述的堆焊复合层分三层焊接,第一层直接在辊芯表面堆焊,为熔合层(5),第二层在熔合层(5)上堆焊,为过渡层(4),第三层在过渡层(4)堆焊,为工作层(3);堆焊熔合层(5)的焊丝与辊芯的材质要具有好的焊接性,堆焊过渡层(4)的焊丝与熔合层(5)要具有好的焊接性,堆焊工作层(3)的焊丝与过渡层(4)要具有好的焊接性。
辊芯的材质的化学成分的质量分数为0.3—0.45%C、0.17—0.37%Si、0.5—0.8%Mn、0.9—1.2%Cr、0.15—0.25%Mo,余量为Fe。
堆焊熔合层的焊丝的化学成分的质量分数为0.1—0.2%C、0.15—0.2%Cr、0.6—1.2%Mn、1.5—1.8%Ni、0.2—0.6%Mo、0.03—0.05%Re和0.02—0.05%N,余量为Fe。
堆焊过渡层的焊丝的化学成分的质量分数为0.15—0.2%C、0.8—1.4%Cr、1.5—1.8%Mn、1.8—2.2%Ni、0.3—0.5%Mo、0.1—0.3%V和0.03—0.05%Re,余量为Fe。
堆焊工作层的焊丝的化学成分的质量分数为0.25—0.5%C、6.5—7.5%Cr、1.5—1.8%Mn、1.8—2.2%Ni、0.8—2.0%Mo、0.5—1.5%V、0.03—0.05%Re和0.5—1.4Nb,余量为Fe。

Claims (6)

1.双金属复合耐磨冶金轧辊的制造方法,其特征在于,包括辊芯加工步骤、预热步骤、堆焊复合层步骤、精加工步骤和热处理步骤,其中:
辊芯加工步骤为先用抗拉强度、屈服强度和抗冲击性能优良的钢材通过锻压和调质处理,制作辊芯毛坯,然后将辊芯毛坯粗加工至预留堆焊复合层尺寸;
预热步骤为将辊芯预热至380C°±5C°的适焊温度;
堆焊复合层步骤为将预热后的辊芯表面用埋弧焊工艺将预留的堆焊复合层用药芯焊丝堆焊填满;
精加工步骤为将堆焊后的双金属复合耐磨冶金轧辊毛坯加工至设计尺寸;
热处理步骤为将精加工后的双金属复合耐磨冶金轧辊进行淬火和调质处理,使其表层达到具备好的抗粘着磨损、抗磨粒磨损、红硬性、抗冷热疲劳性和抗剥落性的要求。
2.根据权利要求1所述的双金属复合耐磨冶金轧辊的制造方法,其特征在于,所述的堆焊复合层分三层焊接,第一层直接在辊芯表面堆焊,为熔合层(5),第二层在熔合层(5)上堆焊,为过渡层(4),第三层在过渡层(4)堆焊,为工作层(3);堆焊熔合层(5)的焊丝与辊芯的材质要具有好的焊接性,堆焊过渡层(4)的焊丝与熔合层(5)要具有好的焊接性,堆焊工作层(3)的焊丝与过渡层(4)要具有好的焊接性。
3.根据权利要求2所述的双金属复合耐磨冶金轧辊的制造方法,其特征在于,辊芯的材质的化学成分为质量分数:0.3—0.45%C、0.17—0.37%Si、0.5—0.8%Mn、0.9—1.2%Cr、0.15—0.25%Mo,余量为Fe。
4.根据权利要求2所述的双金属复合耐磨冶金轧辊的制造方法,其特征在于,堆焊熔合层的焊丝的化学成分的质量分数为0.1—0.2%C、0.15—0.2%Cr、0.6—1.2%Mn、1.5—1.8%Ni、0.2—0.6%Mo、0.03—0.05%Re和0.02—0.05%N,余量为Fe。
5.根据权利要求2所述的双金属复合耐磨冶金轧辊的制造方法,其特征在于,堆焊过渡层的焊丝的化学成分的质量分数为0.15—0.2%C、0.8—1.4%Cr、1.5—1.8%Mn、1.8—2.2%Ni、0.3—0.5%Mo、0.1—0.3%V和0.03—0.05%Re,余量为Fe。
6.根据权利要求2所述的双金属复合耐磨冶金轧辊的制造方法,其特征在于,堆焊工作层的焊丝的化学成分的质量分数为0.25—0.5%C、6.5—7.5%Cr、1.5—1.8%Mn、1.8—2.2%Ni、0.8—2.0%Mo、0.5—1.5%V、0.03—0.05%Re和0.5—1.4Nb,余量为Fe。
CN201310010714.6A 2013-01-13 2013-01-13 双金属复合耐磨冶金轧辊的制造方法 Active CN103009015B (zh)