CN102993516A - 一种高耐油氯丁橡胶密封垫及其制备方法 - Google Patents
一种高耐油氯丁橡胶密封垫及其制备方法 Download PDFInfo
- Publication number
- CN102993516A CN102993516A CN2012104306430A CN201210430643A CN102993516A CN 102993516 A CN102993516 A CN 102993516A CN 2012104306430 A CN2012104306430 A CN 2012104306430A CN 201210430643 A CN201210430643 A CN 201210430643A CN 102993516 A CN102993516 A CN 102993516A
- Authority
- CN
- China
- Prior art keywords
- parts
- chloroprene rubber
- trees ashes
- time
- sealing gasket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高耐油氯丁橡胶密封垫,其组成原料的重量份为:氯丁橡胶CR121135-145、氯醇橡胶H4520-25、SG-2型PVC树脂10-20、乙酰柠檬酸三(2-乙基已基)酯2-5、环氧四氢邻苯二甲酸二辛酯3-5、顺丁烯二酸二丁酯3-5、脂肪醇聚氧乙烯醚硫酸钠1-2、纳米陶土30-40、炭黑N22030-35、纳米碳酸钙粉30-35等。本发明氯丁橡胶密封垫具有良好的耐油和耐溶剂性能,能满足汽车发动机油底壳等处的密封要求。固化后容易剥离,可清理,不影响拆装和修复,具有可修复性。
Description
技术领域
本发明涉及一种密封垫,具体涉及一种高耐油氯丁橡胶密封垫及其制备方法。
背景技术
在汽车上需要油密封的地方很多,且条件较苛刻,耐油密封垫至少要满足两个条件:一是耐油。如耐油性不佳,长期使用势必渗油。二是封油不漏。要求密封材料同被密封件之间有适当的粘合力,而且要求密封材料本身要具有一定的强度。两者粘合力过小,封不住油,过大则使材料不易清除(聚硫胶就是一例),影响下次拆装。但随着汽车工业的发展,现有的密封垫已远不能满足要求。国产汽车存在的不同程度的漏油现象,就是与密封垫密切相关的。因此研发一种耐油密封垫已成为当务之急。
发明内容
本发明的目的是针对现有技术的不足,提供一种高耐油氯丁橡胶密封垫及其制备方法。
本发明采用的技术方案如下:
一种高耐油氯丁橡胶密封垫,其组成原料的重量份为:氯丁橡胶CR121 135-145、氯醇橡胶H45 20-25、SG-2型PVC树脂10-20、乙酰柠檬酸三(2-乙基已基)酯2-5、环氧四氢邻苯二甲酸二辛酯3-5、顺丁烯二酸二丁酯3-5、脂肪醇聚氧乙烯醚硫酸钠1-2、纳米陶土30-40、炭黑N220 30-35、纳米碳酸钙粉30-35、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯1-2、抗氧剂1035 2-3、防老剂RD 1-2、2-硫醇基苯骈咪唑1-2、促进剂Na-22 1-2、促进剂DM 3-4、硫磺3-5、氧化锌3-5、莱茵蜡3-5、润滑剂TR121 2-3、改性树木灰烬1-2。
所述的改性树木灰烬由以下方法制得:先用10-15%双氧水浸泡树木灰烬2-3h后,再用去离子水洗涤至中性,烘干;加入相当于树木灰烬重量2-3%的纳米碳、1-2%的聚异丁烯、2-3%的柠檬酸三丁酯、1-2%的二茂铁、3-5%氢氧化铝,高速4500-4800r/min搅拌20-30min,烘干粉碎成超细粉末。
高耐油氯丁橡胶密封垫的制备方法,包括以下步骤:
(1)按上述配方配比,将配好的原料送入炼胶机中进行炼胶, 炼胶温度控制在80-90℃,炼胶时间为15-20min;
(2)炼胶完成后,取出胶料铺平,在常温下放置冷却36-48h后,送入平板硫化机内进行两次硫化,第一次硫化的硫化温度控制在165-175℃,硫化时间为20-30min,第一次硫化完紧接着进行第二次硫化,第二次硫化为210-220℃,硫化时间5-6分钟;
(3)将完成硫化的制品取出,经检验合格者,修整毛边后即可成为成品。
本发明的有益效果:
本发明通过对树木灰烬进行改性,可以改善密封垫的阻燃性和耐油性,并具有成本低,效果优良的特点。本发明氯丁橡胶密封垫具有良好的耐油和耐溶剂性能,能满足汽车发动机油底壳等处的密封要求。固化后容易剥离,可清理,不影响拆装和修复,具有可修复性。本发明氯丁橡胶密封垫还具有压缩性和回弹性好,永久变形小;高温下不软化,不分解,低温下不硬化,不脆裂;抗腐蚀性能好,在酸,碱,油等介质中能长期工作,其体积和硬度变化小,且不粘附在金属表面上;摩擦系数小,耐磨性好;具有与密封面结合的柔软性;耐天候老化和臭氧老化性能好,经久耐用等优点。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例
一种高耐油氯丁橡胶密封垫,其组成原料的重量份为:氯丁橡胶CR121 138份、氯醇橡胶H45 22份、SG-2型PVC树脂15份、乙酰柠檬酸三(2-乙基已基)酯3份、环氧四氢邻苯二甲酸二辛酯4份、顺丁烯二酸二丁酯4份、脂肪醇聚氧乙烯醚硫酸钠2份、纳米陶土36份、炭黑N22032份、纳米碳酸钙粉35份、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯1.5份、抗氧剂1035 2.5份、防老剂RD 1.6份、2-硫醇基苯骈咪唑1.8份、促进剂Na-22 2份、促进剂DM 3份、硫磺4份、氧化锌4份、莱茵蜡5份、润滑剂TR121 2份、改性树木灰烬2份。
其中, 所述的改性树木灰烬由以下方法制得:先用12%双氧水浸泡树木灰烬3h后,再用去离子水洗涤至中性,烘干;加入相当于树木灰烬重量3%的纳米碳、2%的聚异丁烯、3%的柠檬酸三丁酯、2%的二茂铁、5%氢氧化铝,高速45000r/min搅拌30min,烘干粉碎成超细粉末。
高耐油氯丁橡胶密封垫的制备方法,包括以下步骤:
(1)按上述配方配比,将配好的原料送入炼胶机中进行炼胶, 炼胶温度控制在85℃,炼胶时间为20min;
(2)炼胶完成后,取出胶料铺平,在常温下放置冷却48h后,送入平板硫化机内进行两次硫化,第一次硫化的硫化温度控制在170℃,硫化时间为30min,第一次硫化完紧接着进行第二次硫化,第二次硫化为215℃,硫化时间为5分钟;
(3)将完成硫化的制品取出,经检验合格者,修整毛边后即可成为成品。
本实施例制备出来的密封垫的主要性能见下表1。
表1
将本发明的氯丁橡胶密封垫用于发动机密封部位,试验工况为3000r/min
加负荷运转,相当于汽车满载,车速90 km /h,行驶20km。实验结果为:各密封处无渗漏油现象,密封垫与被密封体呈软粘接状态,表面无渗油现象;密封垫拆检后,密封材料容易清理,不影响再装配,密封垫的外观和手感无明显的物理及化学变化。
Claims (3)
1.一种高耐油氯丁橡胶密封垫,其特征在于,其组成原料的重量份为:氯丁橡胶CR121 135-145、氯醇橡胶H45 20-25、SG-2型PVC树脂10-20、乙酰柠檬酸三(2-乙基已基)酯2-5、环氧四氢邻苯二甲酸二辛酯3-5、顺丁烯二酸二丁酯3-5、脂肪醇聚氧乙烯醚硫酸钠1-2、纳米陶土30-40、炭黑N220 30-35、纳米碳酸钙粉30-35、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯1-2、抗氧剂1035 2-3、防老剂RD 1-2、2-硫醇基苯骈咪唑1-2、促进剂Na-22 1-2、促进剂DM 3-4、硫磺3-5、氧化锌3-5、莱茵蜡3-5、润滑剂TR121 2-3、改性树木灰烬1-2。
2.根据权利要求1所述的高耐油氯丁橡胶密封垫,其特征在于,所述的改性树木灰烬由以下方法制得:先用10-15%双氧水浸泡树木灰烬2-3h后,再用去离子水洗涤至中性,烘干;加入相当于树木灰烬重量2-3%的纳米碳、1-2%的聚异丁烯、2-3%的柠檬酸三丁酯、1-2%的二茂铁、3-5%的氢氧化铝,高速4500-4800r/min搅拌20-30min,烘干粉碎成超细粉末。
3.一种如权利要求1所述的高耐油氯丁橡胶密封垫的制备方法,其特征在于包括以下步骤:
(1)按上述配方配比,将配好的原料送入炼胶机中进行炼胶, 炼胶温度控制在80-90℃,炼胶时间为15-20min;
(2)炼胶完成后,取出胶料铺平,在常温下放置冷却36-48h后,送入平板硫化机内进行两次硫化,第一次硫化的硫化温度控制在165-175℃,硫化时间为20-30min,第一次硫化完紧接着进行第二次硫化,第二次硫化为210-220℃,硫化时间为5-6分钟;
将完成硫化的制品取出,经检验合格者,修整毛边后即可成为成品。