CN102978636B - 一种废镁合金表面涂层的清洗方法 - Google Patents
一种废镁合金表面涂层的清洗方法 Download PDFInfo
- Publication number
- CN102978636B CN102978636B CN201210538283.6A CN201210538283A CN102978636B CN 102978636 B CN102978636 B CN 102978636B CN 201210538283 A CN201210538283 A CN 201210538283A CN 102978636 B CN102978636 B CN 102978636B
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- waste magnesium
- alloy piece
- cleaning
- waste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种废镁合金表面涂层的清洗方法,是针对废镁合金表面固着有机涂层污物的实际情况,采用氢氧化钠、氢氧化钾、十二烷基苯磺酸钠、乙醇、去离子水,制成强碱性混合溶液,在加热、搅拌、浸泡状态下,对废镁合金表面进行清洗,经洗涤、干燥,成表面洁净的镁合金块,清洁率达99.9%,可再次熔炼,制成新的零部件,既对废镁合金进行了回收利用,又减少了环境污染,是十分理想的废镁合金的清洗方法。
Description
技术领域
本发明涉及一种废镁合金表面涂层的清洗方法,属有色金属合金表面处理及应用的技术领域。
背景技术
镁合金是一种有色轻金属合金,在机械、电子、航空、航天、汽车等领域及民用产品中得到了广泛的应用,其零部件的种类也越来越多,随着时间的推移,机件的磨损、腐蚀,报废量越来越多,这些零部件都进行了表面处理工艺中的一种或几种,表面布有有机涂层,表面成分复杂,有的在使用中表面沾满了油污,还有的使用环境恶劣,磨损较大,以致造成大量的零部件报废,这些报废的零部件既占用庞大的储存空间,又会造成镁资源浪费及环境污染,这些零部件由于表面固着有机涂层,给回收利用也造成了困难。
发明内容
发明目的
本发明的目的是针对背景技术的状况,对报废镁合金零部件用碱性溶液在加热状态下进行清洗处理,以利于废镁合金进行回收熔炼,重新进行利用,减少污染,节约镁资源。
技术方案
本发明使用的化学物质材料为:废镁合金块、氢氧化钠、氢氧化钾、十二烷基苯磺酸钠、乙醇、去离子水,其准备用量如下:以克、毫升为计量单位
废镁合金块: 100g ±5g
氢氧化钠:NaOH 60g ±5g
氢氧化钾:KOH 60g ±5g
十二烷基苯磺酸钠:C18H29NaO3S 10g ±1g
乙醇:C2H5OH 250mL ±5mL
去离子水:H2O 1200mL ±50mL
清洗方法如下:
(1)精选化学物质
对清洗使用的化学物质材料要进行精选,并进行质量纯度控制;
废镁合金零件:固态固体 表面污染涂层面积 40%
氢氧化钠:固态固体 98.0%
氢氧化钾:固态固体 99.9%
十二烷基苯磺酸钠:固态固体 99.0%
乙醇:液态液体 98%
去离子水:液态液体 99.5%
(2)配制碱性混合溶液
①称取氢氧化钠45g±0.1g、氢氧化钾45g±0.1g、十二烷基苯磺酸钠6g ±0.1g,放入烧杯中;
加入去离子水300mL±1mL,搅拌10min,使其溶解;
②向烧杯中加入乙醇200mL±1mL,搅拌5min;
③向烧杯中加入去离子水200mL±1mL,继续搅拌10min,成1mol/L碱性混合溶液,酸碱度pH=14,呈强碱性;
(3)机械切割废镁合金零件
将废镁合金块置于机械切割机上,切割成块状,块状尺寸≤50mm×30mm×8mm;
(4)预清洗废镁合金块
对切割的废镁合金块置于不锈钢容器内,加入去离子水200mL,进行冲洗和搅拌洗涤,洗去表面灰尘和碎屑;
清洗后晾干;
(5)清洗废镁合金块表面涂层
废镁合金块表面涂层的清洗是在陶瓷清洗槽内进行的,是在强碱性混合溶液中浸泡、加热、搅拌状态下完成的;
①将废镁合金块100g加入陶瓷清洗槽内,然后加入碱性混合溶液500mL,碱性混合溶液要淹没废镁合金块;
②开启电加热器,加热碱性混合溶液,加热温度98℃±1℃;
③开启搅拌器,进行搅拌,搅拌频率10r/min,搅拌时间5min;
④在加热、搅拌、清洗过程中,废镁合金块表面涂层与碱性混合溶液发生化学反应,废镁合金块表面涂层脱落;
清洗后捞出废镁合金块,并晾干;
(6)洗涤废镁合金块
将清洗并晾干的废镁合金块置于不锈钢清洗槽内,加入去离子水 200mL,浸泡5min,搅拌清洗5min,清洗后捞出并晾干;
(7)真空干燥
将洗涤晾干的废镁合金块置于真空干燥箱中进行干燥,干燥温度100℃,真空度100Pa,干燥时间10 min;
干燥后随干燥箱冷却至25℃;
(8)检测、分析、表征
对清洗并干燥的废镁合金块进行检测、分析、表征;
用表面分析仪对清洗后的废镁合金块表面进行定性定量测量;
用多元素分析仪对废镁合金块表面进行化学成分分析;
用电子显微镜对清洗后的废镁合金块表面进行精细状态分析;
用荧光染料法对清洗后的废镁合金块表面进行洁净度评价;
结论:清洗后的废镁合金块表面洁净,呈银灰色,表面洁净度达99.9%。
有益效果
本发明与背景技术相比具有明显的先进性,是针对废镁合金块表面固着 有机涂层污物的实际情况,采用氢氧化钠、氢氧化钾、十二烷基苯磺酸钠、乙醇、去离子水,制成强碱性混合溶液,在加热、浸泡、搅拌状态下,对废镁合金块表面进行清洗,经洗涤、干燥,成表面洁净的镁合金块,清洗率达99.9%,清洁后的镁合金块可再次熔炼,制成新的零部件,既对废镁合金进行了回收利用,又减少了环境污染,是十分理想的废镁合金的清洗方法。
附图说明
图1为废镁合金块清洗状态图
图2为废镁合金块表面清洗前后金相组织对比图
图中所示,附图标记清单如下:
1、陶瓷清洗槽,2、电阻加热器,3、槽盖,4、显示屏,5、指示灯, 6、电源开关,7、温度调控器,8、搅拌调控器,9、搅拌器,10、碱性混合溶液,11、废镁合金块,12、酸碱度计。
具体实施方式
以下结合附图对本发明做进一步说明:
图1所示,为废镁合金块清洗状态图,各部位置要正确,按量配比,按序操作。
清洗使用的化学物质的量值是按预先设置的范围确定的,以克、毫升为计量单位。
废镁合金块的清洗是在陶瓷清洗槽内进行的,是在强碱性混合溶液浸泡、加热、搅拌状态下完成的;
陶瓷清洗槽1呈矩形,在陶瓷清洗槽1下部为电阻加热器2、上部为槽盖3,在电阻加热器2上设置显示屏4、指示灯5、电源开关6、温度调控器7、搅拌调控器8;在槽盖3上设有搅拌器9,并伸入陶瓷清洗槽1内,在槽盖3上设有酸碱度计12,并伸入陶瓷清洗槽1内;在陶瓷清洗槽内置放废镁合金块11、碱性混合溶液10,碱性混合溶液10要淹没废镁合金块11。
图2所示,为废镁合金块表面清洗前后金相组织对比图,清洗前有明显的边沿,为有机涂层填塞;清洗后边沿处呈不规则裸露,说明表面的涂层已被清洗掉。
Claims (2)
1.一种废镁合金表面涂层的清洗方法,其特征在于:使用的化学物质材料为废镁合金块、氢氧化钠、氢氧化钾、十二烷基苯磺酸钠、乙醇、去离子水,其准备用量如下:以克、毫升为计量单位
废镁合金块: 100g ±5g
氢氧化钠:NaOH 60g ±5g
氢氧化钾:KOH 60g ±5g
十二烷基苯磺酸钠:C18H29NaO3S 10g ±1g
乙醇:C2H5OH 250mL ±5mL
去离子水:H2O 1200mL ±50mL
清洗方法如下:
(1)精选化学物质
对清洗使用的化学物质材料要进行精选,并进行质量纯度控制;
废镁合金零件:固态固体 表面污染涂层面积 40%
氢氧化钠:固态固体 98.0%
氢氧化钾:固态固体 99.9%
十二烷基苯磺酸钠:固态固体 99.0%
乙醇:液态液体 98%
去离子水:液态液体 99.5%
(2)配制碱性混合溶液
①称取氢氧化钠45g±0.1g、氢氧化钾45g±0.1g、十二烷基苯磺酸钠6g±0.1g,放入烧杯中;
加入去离子水300mL±1mL,搅拌10min,使其溶解;
②向烧杯中加入乙醇200mL±1mL,搅拌5min;
③向烧杯中加入去离子水200mL±1mL,继续搅拌10min,成1mol/L碱性混合溶液,酸碱度pH=14,呈强碱性;
(3)机械切割废镁合金零件
将废镁合金块置于机械切割机上,切割成块状,块状尺寸≤50mm×30mm×8mm;
(4)预清洗废镁合金块
对切割的废镁合金块置于不锈钢容器内,加入去离子水200mL,进行冲洗和搅拌洗涤,洗去表面灰尘和碎屑;
清洗后晾干;
(5)清洗废镁合金块表面涂层
废镁合金块表面涂层的清洗是在陶瓷清洗槽内进行的,是在碱性混合溶液中浸泡、加热、搅拌状态下完成的;
①将废镁合金块100g加入陶瓷清洗槽内,然后加入碱性混合溶液500mL,碱性混合溶液要淹没废镁合金块;
②开启电加热器,加热碱性混合溶液,加热温度98℃±1℃;
③开启搅拌器,进行搅拌,搅拌频率10r/min,搅拌时间5min;
④在加热、搅拌、清洗过程中,废镁合金块表面涂层与碱性混合溶液发生化学反应,废镁合金块表面涂层脱落;
清洗后捞出废镁合金块,并晾干;
(6)洗涤废镁合金块
将清洗并晾干的废镁合金块置于不锈钢清洗槽内,加入去离子水200mL,浸泡5min,搅拌清洗5min,清洗后捞出并晾干;
(7)真空干燥
将洗涤晾干的废镁合金块置于真空干燥箱中进行干燥,干燥温度100℃,真空度100Pa,干燥时间10 min;
干燥后随干燥箱冷却至25℃;
(8)检测、分析、表征
对清洗并干燥的废镁合金块进行检测、分析、表征;
用表面分析仪对清洗后的废镁合金块表面进行定性定量测量;
用多元素分析仪对废镁合金块表面进行化学成分分析;
用电子显微镜对清洗后的废镁合金块表面进行精细状态分析;
用荧光染料法对清洗后的废镁合金块表面进行洁净度评价;
结论:清洗后的废镁合金块表面洁净,呈银灰色,表面洁净度达99.9%。
2.根据权利要求1所述的一种废镁合金表面涂层的清洗方法,其特征在于:废镁合金块的清洗是在陶瓷清洗槽内进行的,是在强碱性混合溶液浸泡、加热、搅拌状态下完成的;
陶瓷清洗槽1呈矩形,在陶瓷清洗槽(1)下部为电阻加热器(2)、上部为槽盖(3),在电阻加热器(2)上设置显示屏(4)、指示灯(5)、电源开关(6)、温度调控器(7)、搅拌调控器(8);在槽盖(3)上设有搅拌器(9),并伸入陶瓷清洗槽(1)内,在槽盖(3)上设有酸碱度计(12),并伸入陶瓷清洗槽(1)内;在陶瓷清洗槽(1)内置放废镁合金块(11)、碱性混合溶液(10),碱性混合溶液(10)要淹没废镁合金块(11)。