CN102965544A - 一种用于钢丝热镀锌的锌基合金 - Google Patents

一种用于钢丝热镀锌的锌基合金 Download PDF

Info

Publication number
CN102965544A
CN102965544A CN2012104713795A CN201210471379A CN102965544A CN 102965544 A CN102965544 A CN 102965544A CN 2012104713795 A CN2012104713795 A CN 2012104713795A CN 201210471379 A CN201210471379 A CN 201210471379A CN 102965544 A CN102965544 A CN 102965544A
Authority
CN
China
Prior art keywords
zinc
base alloy
aluminium
steel wire
zinc base
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104713795A
Other languages
English (en)
Inventor
高熠辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd
Original Assignee
WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd filed Critical WUXI CHANG'AN GENERAL METAL PRODUCT CO Ltd
Priority to CN2012104713795A priority Critical patent/CN102965544A/zh
Publication of CN102965544A publication Critical patent/CN102965544A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种用于钢丝热镀锌的锌基合金，按重量计，锌铝合金的组份及含量如下：铝4.5～5%，镁0.02～0.04%，锶0.003～0.005%，铟0.001～0.002%，余量为锌。采用本发明的锌铝合金一次镀覆合金重量可达到420～450g/m2，镀层致密、均匀，耐腐蚀性能好。

Description

一种用于钢丝热镀锌的锌基合金
技术领域
本发明属于热浸镀锌领域，具体涉及一种用于钢丝热镀锌的锌基合金。
背景技术
钢铁制品被广泛应用于国民生活的各个领域，每年因腐蚀而造成大量的废钢铁，目前，国内外为了防止钢铁缺制品的腐蚀，通常在其表面镀上一层作为牺牲阳极的锌层，在纯锌镀层中加入少量的铝可以消除锌铁界面的铁-锌合金层，使镀件更具加工性，当加入的铝达到5%时，镀层兼具纯锌及纯铝镀层的防蚀特长，然而，当铝含量超过0.03%时，钢铁表面镀不上的机率大增，导致镀层厚度太薄达到工艺要求，不得不采用“双镀法”对镀层进行加厚。
发明内容
本发明的目的解决现有热浸镀锌铝时一次镀覆量低的问题，提供一种易于镀上的锌基合金。
本发明实现上述目的所采用的技术方案如下：
一种用于钢丝热镀锌的锌基合金，按重量计，锌基合金的组份及含量如下：铝4.5～5%，镁0.02～0.04%，锶 0.003～0.005%，铟0.001～0.002%，余量为锌。
上述锌基合金的制备方法，包括以下步骤：将锌、铝、镁、锶、铟按配比量加入溶化炉中，在温度为500～550℃下熔化均匀，然后浇注成型。
有益效果：采用本发明的锌基合金一次镀覆合金重量可达到420～450g/m2。镀层致密、均匀，耐腐蚀性能好。
具体实施方式
以下结合实施例对本发明做进一步详细说明。
实施例1
将50kg铝锭、949.75kg锌锭、0.2kg镁条、0.03kg锶粒和0.02kg铟粉加入至熔化炉中，氩气气氛下，炉温升至500℃，溶化完成后，机械搅拌均匀，然后浇注成条形状。
实施例2
将45kg铝锭、954.54kg锌锭、0.4kg镁条、0.05kg锶粒和0.01kg铟粉加入至熔化炉中，氩气气氛下，炉温升至550℃，溶化完成后，机械搅拌均匀，然后浇注成条形状。
采用上述实施例1的合金对钢丝进行热浸镀，钢丝行进速度为12m/min时，一次镀覆合金重量可达420～450g/m2。而采用常规的5%铝-锌合金，在其它工艺条件均相同的情况下，一次镀覆合金重量只有150～170g/m2。
采用本发明的锌基合金热镀后的钢丝加速腐蚀试验：5%NaCl溶液、试验温度35±2℃，试验180小时未见红锈。

Claims (2)

1.一种用于钢丝热镀锌的锌基合金，其特征在于，按重量计，锌铝合金的组份及含量如下：铝4.5～5%，镁0.02～0.04%，锶 0.003～0.005%，铟0.001～0.002%，余量为锌。
2.权利要求1所述用于钢丝热镀锌的锌基合金的制备方法，包括以下步骤：将锌、铝、镁、锶、铟按配比量加入溶化炉中，在温度为500～550℃下熔化均匀，然后浇注成型。
CN2012104713795A 2012-11-20 2012-11-20 一种用于钢丝热镀锌的锌基合金 Pending CN102965544A (zh)