CN102952488B - 一种环氧大豆油改性的滤清器用粘合剂胶片 - Google Patents
一种环氧大豆油改性的滤清器用粘合剂胶片 Download PDFInfo
- Publication number
- CN102952488B CN102952488B CN2012104165108A CN201210416510A CN102952488B CN 102952488 B CN102952488 B CN 102952488B CN 2012104165108 A CN2012104165108 A CN 2012104165108A CN 201210416510 A CN201210416510 A CN 201210416510A CN 102952488 B CN102952488 B CN 102952488B
- Authority
- CN
- China
- Prior art keywords
- adhesive film
- soybean oil
- epoxy soybean
- filter
- modification
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种环氧大豆油改性的滤清器用粘合剂胶片，其是由氯丁橡胶CR121、苯乙烯、2.4.6-三（二甲胺基甲基）苯酚、聚乙烯醇、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇、改性碳酸钙粉、改性树木灰烬等原料制得。对碳酸钙以及树木灰烬的改性可以增加本发明的强度和韧性，制得的本发明耐温性能好、剪切强度高的同时具有优良的电绝缘性以及耐老化性，而且该粘合剂胶片固化后表面平整、韧性好、抗震效果好。
Description
技术领域
本发明涉及滤清器设备领域，确切地说是一种环氧大豆油改性的滤清器用粘合剂胶片。
背景技术
对于滤清器而言，其使用的粘合剂以环氧树脂为主要原料，该类型的粘合剂为液态粘合剂，使用前必须充分搅拌，再采用浸渍法、喷涂法、刷涂法、辊涂法、转移法等方法进行操作，因此工艺上较为复杂，易出现粘合剂分布不均匀以及造成浪费等现象；而且，粘合剂固化后很脆，不耐冲击，在后续加工、运输和安装过程中很容易损坏，致使滤清器使用寿命短。
另外，随着橡胶工业的飞速发展，橡胶复合材料得到广泛的应用，在橡胶与金属复合制品中，胶粘剂的质量是复合制品品质的关键，随着复合制品种类的增多及应用领域的拓展，对粘合剂技术的要求越来越苛刻。传统的氯化橡胶法、异氰酸酯法等技术已不能满足新的要求，需要新的粘合剂来提高橡胶复合制品的品质。
传统的橡胶粘结剂已不能满足新的要求，急需性能更好的的橡胶粘合剂来提高滤清器的品质。
发明内容
本发明的目的在于提供一种具有较高的胶结强度和韧性的环氧大豆油改性的滤清器用粘合剂胶片。
上述目的通过以下方案实现：
一种环氧大豆油改性的滤清器用粘合剂胶片，其特征在于：其是由下述重量份的原料制得：氯丁橡胶CR121 135-145、苯乙烯15-20、2.4.6-三（二甲胺基甲基）苯酚1-2、聚乙烯醇8-12、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷2-3、聚异丁烯2-3、聚四氢呋喃醚二醇2-3、聚乙烯醇缩甲醛5-8、异氰酸酯胶5-8、环氧大豆油2-5、己二酸丙二醇聚酯3-5、甲基丙烯酸正丁酯2-3、氧化镁1-2、硫磺1-2、硬脂酸钙3-5、硅藻土5-10、改性纳米碳酸钙粉25-30、炭黑N339 15-20、N660炭黑25-30、抗氧剂1010 1-2、3-氨丙基三甲氧基硅烷2-3、交联剂 TAC 1-2、促进剂CBS 0.5-1.5、防老剂RD 1-2、促进剂TETD 1-2、防老剂TPPD 1-2、防老剂OD 1-2、二茂铁1-2、改性树木灰烬1-2；
所述的改性纳米碳酸钙粉的制备方法为：取碳酸钙粉于浓度为10-15%的双氧水溶液中浸泡2-4小时，研磨成纳米粉末即得；
所述的改性树木灰烬的制备方法为：
（1）、将树木灰烬用浓度为15-20%的氢氧化钠溶液浸泡3-5小时后，再用去离子水洗涤至中性，烘干；
（2）、再于烘干的树木灰烬中加入相当于其重量1-2%的纳米碳、1.5-2.2%的2.4.6-三（二甲胺基甲基）苯酚、2-3%的a-氰基丙烯酸酯、1-2%的交联剂 TAC、2-4%的氢氧化铝，在4000-4500转/分下搅拌30-40分钟后，烘干粉碎成超细粉末即得。
所述的一种环氧大豆油改性的滤清器用粘合剂胶片，其特征在于：制备方法为：将氯丁橡胶CR121按重量份加入到苯乙烯中，加热到100-110℃，搅拌10-15分钟，再按重量份加入2.4.6-三（二甲胺基甲基）苯酚、聚乙烯醇、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇，搅拌，反应1-2小时；再按重量份加入其余原料，混炼至所需厚度，最后剪切至所需尺寸即可。
本发明的有益效果为：对碳酸钙以及树木灰烬的改性可以增加本发明的强度和韧性，制得的本发明耐温性能好、剪切强度高的同时具有优良的电绝缘性以及耐老化性，而且该粘合剂胶片固化后表面平整、韧性好、抗震效果好。
具体实施方式
一种环氧大豆油改性的滤清器用粘合剂胶片，其是由下述重量份（kg)的原料制得：氯丁橡胶CR121 145、苯乙烯 20、2.4.6-三（二甲胺基甲基）苯酚1.3、聚乙烯醇 12、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷 3、聚异丁烯 2、聚四氢呋喃醚二醇 3、聚乙烯醇缩甲醛 8、异氰酸酯胶 6、环氧大豆油3、己二酸丙二醇聚酯5、甲基丙烯酸正丁酯 3、氧化镁 1、硫磺 2、硬脂酸钙 5、硅藻土 10、改性纳米碳酸钙粉 30、炭黑N339 20、N660炭黑 27、抗氧剂1010 2、3-氨丙基三甲氧基硅烷 3、交联剂 TAC 2、促进剂CBS 0.8、防老剂RD 1.3、促进剂TETD 1.6、防老剂TPPD 2、防老剂OD 2、二茂铁1.5、改性树木灰烬1.8；
所述的改性纳米碳酸钙粉的制备方法为：取碳酸钙粉于浓度为15%的双氧水溶液中浸泡4小时，研磨成纳米粉末即得；
所述的改性树木灰烬的制备方法为：
（1）、将树木灰烬用浓度为17%的氢氧化钠溶液浸泡4小时后，再用去离子水洗涤至中性，烘干；
（2）、再于烘干的树木灰烬中加入相当于其重量1%的纳米碳、1.7%的2.4.6-三（二甲胺基甲基）苯酚、2%的a-氰基丙烯酸酯、2%的交联剂 TAC、2%的氢氧化铝，在4500转/分下搅拌40分钟后，烘干粉碎成超细粉末即得。
所述的一种环氧大豆油改性的滤清器用粘合剂胶片，制备方法为：将氯丁橡胶CR121按重量份加入到苯乙烯中，加热到110℃，搅拌15分钟，再按重量份加入2.4.6-三（二甲胺基甲基）苯酚、聚乙烯醇、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇，搅拌，反应2小时；再按重量份加入其余原料，混炼至所需厚度，最后剪切至所需尺寸即可。
本发明环氧大豆油改性的滤清器用粘合剂胶片具有较高的剪切强度和韧性，使用后常温剪切强度可达到271- 282 公斤每平方厘米，150 ℃的剪切强度可达到106-113 公斤每平方厘米，不均匀拉伸强度可达到52-56 公斤每平方厘米。
使用时，将本发明胶片粘上滤清器滤纸与端盖，然后在加温硫化，可大大提高其韧性及端盖与滤纸的粘合强度，经久耐用。保持密封状态，不会发生灰尘从缝隙里流过。
Claims (1)
1.一种环氧大豆油改性的滤清器用粘合剂胶片，其特征在于：其是由下述重量份的原料制得：氯丁橡胶CR121 135-145、苯乙烯15-20、2，4，6-三（二甲胺基甲基）苯酚1-2、聚乙烯醇8-12、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷2-3、聚异丁烯2-3、聚四氢呋喃醚二醇2-3、聚乙烯醇缩甲醛5-8、异氰酸酯胶5-8、环氧大豆油2-5、己二酸丙二醇聚酯3-5、甲基丙烯酸正丁酯2-3、氧化镁1-2、硫磺1-2、硬脂酸钙3-5、硅藻土5-10、改性纳米碳酸钙粉25-30、炭黑N339 15-20、N660炭黑25-30、抗氧剂1010 1-2、3-氨丙基三甲氧基硅烷2-3、交联剂 TAC 1-2、促进剂CBS 0.5-1.5、防老剂RD 1-2、促进剂TETD 1-2、防老剂TPPD 1-2、防老剂OD 1-2、二茂铁1-2、改性树木灰烬1-2；
所述的改性纳米碳酸钙粉的制备方法为：取碳酸钙粉于浓度为10-15%的双氧水溶液中浸泡2-4小时，研磨成纳米粉末即得；
所述的改性树木灰烬的制备方法为：
（1）、将树木灰烬用浓度为15-20%的氢氧化钠溶液浸泡3-5小时后，再用去离子水洗涤至中性，烘干；
（2）、再于烘干的树木灰烬中加入相当于其重量1-2%的纳米碳、1.5-2.2%的2，4，6-三（二甲胺基甲基）苯酚、2-3%的α-氰基丙烯酸酯、1-2%的交联剂 TAC、2-4%的氢氧化铝，在4000-4500转/分下搅拌30-40分钟后，烘干粉碎成超细粉末即得；
所述的环氧大豆油改性的滤清器用粘合剂胶片制备方法为：将氯丁橡胶CR121按重量份加入到苯乙烯中，加热到100-110℃，搅拌10-15分钟，再按重量份加入2，4，6-三（二甲胺基甲基）苯酚、聚乙烯醇、N-2-（氨乙基）-3-氨丙基三甲氧基硅烷、聚异丁烯、聚四氢呋喃醚二醇，搅拌，反应1-2小时；再按重量份加入其余原料，混炼至所需厚度，最后剪切至所需尺寸即可。