CN102952348A - Pvc-u抗紫外线雨水管 - Google Patents

Pvc-u抗紫外线雨水管 Download PDF

Info

Publication number
CN102952348A
CN102952348A CN2011102412144A CN201110241214A CN102952348A CN 102952348 A CN102952348 A CN 102952348A CN 2011102412144 A CN2011102412144 A CN 2011102412144A CN 201110241214 A CN201110241214 A CN 201110241214A CN 102952348 A CN102952348 A CN 102952348A
Authority
CN
China
Prior art keywords
parts
weight
tube
pvc
ultraviolet resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102412144A
Other languages
English (en)
Inventor
马利明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AKAN ENTERPRISE GROUP (SHANGHAI) Co Ltd
Original Assignee
AKAN ENTERPRISE GROUP (SHANGHAI) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AKAN ENTERPRISE GROUP (SHANGHAI) Co Ltd filed Critical AKAN ENTERPRISE GROUP (SHANGHAI) Co Ltd
Priority to CN2011102412144A priority Critical patent/CN102952348A/zh
Publication of CN102952348A publication Critical patent/CN102952348A/zh
Pending legal-status Critical Current

Abstract

本发明公开的一种PVC-U抗紫外线雨水管，其由以下重量组份的原料混合挤出而成：聚氯乙烯100份，氯化聚乙烯6-10份，硬脂酸钙1-3份，钛白粉0.1-0.5份，有机锡稳定剂0.5-1份，PE蜡0-0.5份，2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并***0.5-1.5份。本发明采用在聚氯乙烯树脂中加入抗紫外线材料，来增强管材的耐候性能，并且需要保证加入了该材料后不会对管材其他性能产生不利影响。

Description

PVC-U抗紫外线雨水管
技术领域
本发明涉及PVC-U管道，特别涉及一种PVC-U抗紫外线雨水管。
背景技术
PVC-U管道在国内应用已经有近三十年的历史，尤其在建筑排水和雨水排放***中得到了广泛应用。目前国内的雨水排放主要采用外排式，雨水管长期暴露在阳光中，管材的使用寿命在阳光照射下大大缩短，不仅增加了造价成本也增加了维修成本。
发明内容
本发明所要解决的技术问题在于针对现有PVC-U管道应用于建筑排水和雨水排放***中所存在的问题而提供一种PVC-U抗紫外线雨水管。
本发明所要解决的技术问题可以通过以下技术方案来实现：
一种PVC-U抗紫外线雨水管，由以下重量组份的原料混合挤出而成：
聚氯乙烯                                               100份，
氯化聚乙烯                                            6-10份，
硬脂酸钙                                               1-3份，
钛白粉                                             0.1-0.5份，
有机锡稳定剂                                         0.5-1份，
PE蜡                                                 0-0.5份，
2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并***  0.5-1.5份。
本发明采用在聚氯乙烯树脂中加入抗紫外线材料，来增强管材的耐候性能，并且需要保证加入了该材料后不会对管材其他性能产生不利影响。本发明采用1％的2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并***(化学分子式C20H24N3OCl)作为抗紫外剂，其熔点在150℃左右，与PVC树脂的加工温度接近，能够很好地进行混合加工，加工出来的管材性能应满足QB/T2480的要求，相关技术指标见下表：
具体实施方式
下面实施例用于说明本发明，但不限制在权利要求书中阐明的保护范围。
实施例1：D50规格雨水管
聚氯乙烯                                            100份，
氯化聚乙烯                                            6份，
硬脂酸钙                                            1.2份，
钛白粉                                             0.15份，
有机锡稳定剂TM-697                                  0.5份，
PE蜡                                                0.1份，
2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并***   0.5份。
实施例2：D110规格雨水管
聚氯乙烯                                            100份，
氯化聚乙烯                                            8份，
硬脂酸钙                                            1.5份，
钛白粉                                              0.2份，
有机锡稳定剂TM-697                                  0.5份，
PE蜡                                            0.15份，
2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并***  1份。
实施例3：D200规格雨水管
聚氯乙烯                                           100份，
氯化聚乙烯                                          10份，
硬脂酸钙                                           2.5份，
钛白粉                                            0.45份，
有机锡稳定剂TM-697                                 1.0份，
PE蜡                                              B0.5份，
2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并***  1.5份。
上述三个实施例的制备方法为：先按各自的配方进行混合，然后采用混料机进行混料，混料工艺是先高速捏合，温度控制在105-115度，然后冷混到40度左右下料，混料后由主机挤出，形成本发明的雨水管。

Claims (1)

1.一种PVC-U抗紫外线雨水管，其特征在于，由以下重量组份的原料混合挤出而成：
聚氯乙烯                                                100份，
氯化聚乙烯                                             6-10份，
硬脂酸钙                                                1-3份，
钛白粉                                              0.1-0.5份，
有机锡稳定剂                                          0.5-1份，
PE蜡                                                  0-0.5份，
2-(2’-羟基-3’，5’-二叔丁基苯基)-5-氯代苯并***  0.5-1.5份。
CN2011102412144A 2011-08-22 2011-08-22 Pvc-u抗紫外线雨水管 Pending CN102952348A (zh)