CN102936856A - 一种纺织品颜料的制备方法 - Google Patents
一种纺织品颜料的制备方法 Download PDFInfo
- Publication number
- CN102936856A CN102936856A CN2012104763224A CN201210476322A CN102936856A CN 102936856 A CN102936856 A CN 102936856A CN 2012104763224 A CN2012104763224 A CN 2012104763224A CN 201210476322 A CN201210476322 A CN 201210476322A CN 102936856 A CN102936856 A CN 102936856A
- Authority
- CN
- China
- Prior art keywords
- pigment
- textiles
- preparation
- paint
- textile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纺织品颜料的制备方法，制备方式如下：将超支化分散剂与阴离子表面活性剂以2～10:1～5的比例进行复配分散制备颜料；所制备的颜料颗粒粒径为1900～2200nm；所述复配分散体系稳定性为80%～90%。采用本发明的方法制备纺织品颜料，由于采用超支化分散剂，制备工艺简单，制得的颜料成品率高，颗粒均匀，带来了更好的效果。
Description
技术领域
本发明涉及一种化学用制备颜料的方法，尤其涉及一种制备纺织品用颜料的方法。
背景技术
随刻人们生活水平的不断提高，人们对纺织品的要求也越来越高。除了纺织品本身质地，人们对纺织品的颜色要求也逐渐提高。由于纺织品质地不同，因此纺织品生产时所使用的颜料要求也不同；但是，现有的纺织品颜料由于制备方法的缺陷，在作用于纺织品上时，达不到理想效果，对产品造成一定的影响。
发明内容
本发明的主要目的在于，克服现有的纺织品颜料的制备方法在的缺陷，而提供一种制备纺织品用颜料的方法，使其加工工序少、成品率高、颜料颗粒更均匀，从而更加适于实用，且具有产业上的利用价值。
本发明的目的及解决其技术问题是采用以下技术方案来实现的：一种纺织品颜料的制备方法，制备方式如下：将超支化分散剂与阴离子表面活性剂以2～10:1～5的比例进行复配分散制备颜料。
进一步地，所制备的颜料颗粒粒径为1900～2200nm。
再进一步地，所述复配分散体系稳定性为80%～95%。
与现有技术相比，本发明的有益之处在于：这种纺织品颜料的制备方法采用超支化分散剂，制备工艺简单，制得的颜料成品率高，颗粒均匀，带来了更好的效果。
具体实施方式
为更进一步阐述本发明为达成预定发明目的所采取的技术手段及功效,对依据本发明提出的纺织品颜料的制备方法其具体实施方式、特征及其功效，详细说明如后。
一种纺织品颜料的制备方法，制备方式如下：将超支化分散剂与阴离子表面活性剂以2～10:1～5的比例进行复配分散制备颜料；所制备的颜料颗粒粒径为1900～2200nm；所述复配分散体系稳定性为80%～90%。
这种纺织品颜料的制备方法采用超支化分散剂，制备工艺简单，制得的颜料成品率高，颗粒均匀，带来了更好的效果。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明,任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内,当可利用上述揭示的技术内容做出些许更动或修饰为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (3)
1.一种纺织品颜料的制备方法，其特征是，制备方式如下：将超支化分散剂与阴离子表面活性剂以2～10:1～5的比例进行复配分散制备颜料。
2.根据权利要求1所述的纺织品颜料的制备方法，其特征是，所制备的颜料颗粒粒径为1900～2200nm。
3.根据权利要求1所述的纺织品颜料的制备方法，其特征是，所述复配分散体系稳定性为80%～95%。