CN102899443A - 一种冶炼低磷钢水的工艺 - Google Patents
一种冶炼低磷钢水的工艺 Download PDFInfo
- Publication number
- CN102899443A CN102899443A CN2012104082571A CN201210408257A CN102899443A CN 102899443 A CN102899443 A CN 102899443A CN 2012104082571 A CN2012104082571 A CN 2012104082571A CN 201210408257 A CN201210408257 A CN 201210408257A CN 102899443 A CN102899443 A CN 102899443A
- Authority
- CN
- China
- Prior art keywords
- phosphorus
- blowing
- iron
- converter
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
C% | Si% | Mn% | P% | S% | 温度℃ | |
铁水 | 4.40 | 0.60 | 0.23 | 0.086 | 0.021 | 1347 |
双渣 | 3.0 | 0.03 | 0.14 | 0.022 | 0.020 | 1380 |
拉碳 | 0.10 | - | 0.05 | 0.005 | 0.014 | 1556 |
终点 | 0.03 | - | 0.04 | 0.004 | 0.014 | 1643 |
C% | Si% | Mn% | P% | S% | 温度℃ | |
铁水 | 4.52 | 0.43 | 0.16 | 0.074 | 0.032 | 1309 |
双渣 | 3.1 | 0.02 | 0.10 | 0.025 | 0.025 | 1380 |
拉碳 | 0.06 | - | 0.04 | 0.005 | 0.020 | 1593 |
终点 | 0.05 | - | 0.04 | 0.004 | 0.021 | 1660 |
Claims (1)