CN102888171B - A kind of Scratch-resistant metal anti-rust paint and preparation method thereof - Google Patents
A kind of Scratch-resistant metal anti-rust paint and preparation method thereof Download PDFInfo
- Publication number
- CN102888171B CN102888171B CN201210340776.9A CN201210340776A CN102888171B CN 102888171 B CN102888171 B CN 102888171B CN 201210340776 A CN201210340776 A CN 201210340776A CN 102888171 B CN102888171 B CN 102888171B
- Authority
- CN
- China
- Prior art keywords
- paint
- raw material
- dispersion
- nano
- transported
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of Scratch-resistant metal anti-rust paint and preparation method thereof, be made up of pulping raw material and paint raw material, the paint film that rust-inhibiting paint of the present invention is formed, have that hardness is high, damage resistant, strong adhesion, salt spray resistance, salt water resistance, acid and alkali-resistance, water-fast, oil resistant, reusable at old coating surface, paint film can not be caused to damage, superpower paint film flexibility etc.The general paint film life-span can reach 8-10.
Description
Technical field
The present invention relates to a kind of metallic anti-rust paint, specifically a kind of Scratch-resistant metal anti-rust paint.
Background technology
Various mechanical means appearance all needs coating layer of metal paint, increases attractive in appearance on the one hand, on the other hand dust-proof rust resistance and corrosion resistance; Rust-inhibiting paint of the prior art, because of containing a large amount of volatile organic solvent, produces volatile gases poisonous, harmful in a large number, polluted air and infringement human health.Ubiquity weather resistance is not good, easily comes off, inadaptable complicated, severe environment.
Summary of the invention
The invention provides a kind of Scratch-resistant metal anti-rust paint and preparation method thereof, there is good mechanical stability, snappiness and surface hardness, good weatherability.
Technical scheme of the present invention is:
A kind of Scratch-resistant metal anti-rust paint, is characterized in that being made up of the feed composition of following component weight part:
Pulping raw material:
Aluminium scrap powder 3-8, propylene glycol phenylate 1-3, tripropylene glycol methyl ether 5-10, paraffin wax emulsions 1-2, anti-sedimentation agent 3300S1-2, flow agent BYK-3001-2, polyacrylic acid sodium salt SN-50003-5, dispersion agent LBD-11-2, defoamer SPA2021-2, nano-calcium carbonate 10-15, modified Nano diatomite 5-10, modified soluble nano silicone colloidal sol 5-10;
Paint raw material:
Polyvinylpyrrolidone 10-15, epoxy emulsion 25-30, myo-Inositol hexaphosphate 20-25, sodium polymethacrylate 3-5, Wickenol 116 3-5, fatty alcohol-polyoxyethylene ether 1-2, propylene glycol 50-60,1-phenoxy group-2-propyl alcohol 10-15,2-amino-2-methyl-1-propanol 1-2, Sodium hexametaphosphate 99 1-2;
Modified Nano diatomite is prepared by the following method:
(1), diatomite add (0.8 ~ 1.2) g/L potassium permanganate solution soak 2-3 hour, pulls out, be washed to neutrality, then the sodium radio-phosphate,P-32 solution putting into 2-5% soaks, stirring reaction 3-4 hour at 60-80 DEG C;
(2) in soak solution, add the 3-4% sodium laurylsulfate, 1-2% Di(dioctylpyrophosphato) ethylene titanate, 2-3% vinyl three ('beta '-methoxy oxyethyl group) silane, the 20-25% ferrophosphorus powder that are equivalent to diatomite weight, high speed dispersion 4200-4500 rev/min, 20-30 minute;
(3) dry, pulverize, make nanometer powder;
Modified soluble nano silicone colloidal sol is prepared by the following method:
Water-soluble nanoscale silica sol adds 4-5% nano-carbon powder, 3-5% ferric oxide, is mixed and heated to 50-60 DEG C, cools after 30-40 minute.
The metallic anti-rust paint that described anti-outdoor water drenches, is characterized in that being made up of the feed composition of following component weight part:
Pulping raw material:
Aluminium scrap powder 6, propylene glycol phenylate 2, tripropylene glycol methyl ether 5, paraffin wax emulsions 2, anti-sedimentation agent 3300S1, flow agent BYK-3001, polyacrylic acid sodium salt SN-50005, dispersion agent LBD-12, defoamer SPA2021, nano-calcium carbonate 10, modified Nano diatomite 10, modified soluble nano silicone colloidal sol 10;
Paint raw material:
Polyvinylpyrrolidone 10, epoxy emulsion 25, myo-Inositol hexaphosphate 25, sodium polymethacrylate 5, Wickenol 116 3, fatty alcohol-polyoxyethylene ether 1, propylene glycol 60,1-phenoxy group-2-propyl alcohol 15,2-amino-2-methyl-1-propanol 1, Sodium hexametaphosphate 99 2.
The preparation method of the metallic anti-rust paint that described anti-outdoor water drenches, is characterized in that comprising the following steps:
(1), slurrying: pulping raw material is poured into batching kettle mixing, then mixed pulping raw material is transported in high-speed dispersing kettle and carries out stirring, disperseing 50-60 minute, rotating speed 3200-3500 rev/min, slurrying component after dispersion is transported in sand mill carries out wet type sand milling, dispersion, obtain slurry, slurry mesh-of-grind is less than or equals 40 microns;
(2) paint: add paint raw material in obtained slurry, be then transported in high-speed dispersing kettle and carry out stirring, disperseing, after dispersion, being transported in sand mill of component carries out wet type sand milling, dispersion, obtains paint vehicle; Again with 3200-3600 rev/min of high speed dispersion 40-50min;
(3) obtained paint vehicle is transported to vibrating filter to carry out filtering and screening, fineness≤40um, then the product after filtration is packed, warehouse-in.
The paint film that rust-inhibiting paint of the present invention is formed, has that hardness is high, damage resistant, strong adhesion, and salt spray resistance, salt water resistance, acid and alkali-resistance, water-fast, oil resistant are reusable at old coating surface, paint film can not be caused to damage, superpower paint film flexibility etc.The general paint film life-span can reach 8-10.
Embodiment
The metallic anti-rust paint that anti-outdoor water drenches, be made up of the feed composition of following component weight part (kilogram):
Pulping raw material:
Aluminium scrap powder 6, propylene glycol phenylate 2, tripropylene glycol methyl ether 5, paraffin wax emulsions 2, anti-sedimentation agent 3300S1, flow agent BYK-3001, polyacrylic acid sodium salt SN-50005, dispersion agent LBD-12, defoamer SPA2021, nano-calcium carbonate 10, modified Nano diatomite 10, modified soluble nano silicone colloidal sol 10;
Paint raw material:
Polyvinylpyrrolidone 10, epoxy emulsion 25, myo-Inositol hexaphosphate 25, sodium polymethacrylate 5, Wickenol 116 3, fatty alcohol-polyoxyethylene ether 1, propylene glycol 60,1-phenoxy group-2-propyl alcohol 15,2-amino-2-methyl-1-propanol 1, Sodium hexametaphosphate 99 2;
Modified Nano diatomite is prepared by the following method:
(1), diatomite adds 0.8g/L potassium permanganate solution and soaks 2 hours, pulls out, is washed to neutrality, then the sodium radio-phosphate,P-32 solution putting into 5% soaks, stirring reaction 4 hours at 60-70 DEG C;
(2) in soak solution, add 3% sodium laurylsulfate, 2% Di(dioctylpyrophosphato) ethylene titanate, 2% vinyl three ('beta '-methoxy oxyethyl group) silane, the 20% ferrophosphorus powder that are equivalent to diatomite weight, high speed dispersion 4200-4500 rev/min, 20-30 minute;
(3) dry, pulverize, make nanometer powder;
Modified soluble nano silicone colloidal sol is prepared by the following method:
Water-soluble nanoscale silica sol adds 5% nano-carbon powder, 3% ferric oxide, and mix and blend, is heated to 50-60 DEG C, cools after 30-40 minute.
The preparation method of the metallic anti-rust paint that anti-outdoor water drenches:
(1), slurrying: pulping raw material is poured into batching kettle mixing, then mixed pulping raw material is transported in high-speed dispersing kettle and carries out stirring, disperseing 50-60 minute, rotating speed 3200-3500 rev/min, slurrying component after dispersion is transported in sand mill carries out wet type sand milling, dispersion, obtain slurry, slurry mesh-of-grind is less than or equals 40 microns;
(2) paint: add paint raw material in obtained slurry, be then transported in high-speed dispersing kettle and carry out stirring, disperseing, after dispersion, being transported in sand mill of component carries out wet type sand milling, dispersion, obtains paint vehicle; Again with 3200-3600 rev/min of high speed dispersion 40-50min;
(3) obtained paint vehicle is transported to vibrating filter to carry out filtering and screening, fineness≤40um, then the product after filtration is packed, warehouse-in.
Metallic anti-rust paint performance index of the present invention:
1, paint film color and outward appearance: flat smooth, color conformance with standard model and aberration scope
2, viscosity (23 ± 1 DEG C of coating-4 viscosity meters, S): 80-120
3, fineness≤50
4, time of drying (25 DEG C): surface drying 25-30min, 48h is done solid work
5, snappiness mm≤2
6, hardness >=2H
7, high temperature resistant (130 DEG C) >=450h
8, shock-resistance 50
9, salt spray resistance (120h level) >=2
10, water tolerance (29 ± 1 DEG C of 240h): non-foaming, does not come off
11, oil resistant (90# gasoline, 56h): non-foaming, does not come off
12, alkali resistance (GB/T9755-2001): by 48 hours
13, artificial weathering ageing resistance (GB/T9755-2001): by 1000 hours.
Claims (2)
1. a Scratch-resistant metal anti-rust paint, is characterized in that being made up of the feed composition of following component weight part:
Pulping raw material:
Aluminium scrap powder 3-8, propylene glycol phenylate 1-3, tripropylene glycol methyl ether 5-10, paraffin wax emulsions 1-2, anti-sedimentation agent 3300S1-2, flow agent BYK-3001-2, polyacrylic acid sodium salt SN-50003-5, dispersion agent LBD-11-2, defoamer SPA2021-2, nano-calcium carbonate 10-15, modified Nano diatomite 5-10, modified soluble nano silicone colloidal sol 5-10;
Paint raw material:
Polyvinylpyrrolidone 10-15, epoxy emulsion 25-30, myo-Inositol hexaphosphate 20-25, sodium polymethacrylate 3-5, Wickenol 116 3-5, fatty alcohol-polyoxyethylene ether 1-2, propylene glycol 50-60,1-phenoxy group-2-propyl alcohol 10-15,2-amino-2-methyl-1-propanol 1-2, Sodium hexametaphosphate 99 1-2;
Modified Nano diatomite is prepared by the following method:
(1), diatomite add (0.8 ~ 1.2) g/L potassium permanganate solution soak 2-3 hour, pulls out, be washed to neutrality, then the sodium radio-phosphate,P-32 solution putting into 2-5% soaks, stirring reaction 3-4 hour at 60-80 DEG C;
(2) in soak solution, add the 3-4% sodium laurylsulfate, 1-2% Di(dioctylpyrophosphato) ethylene titanate, 2-3% vinyl three ('beta '-methoxy oxyethyl group) silane, the 20-25% ferrophosphorus powder that are equivalent to diatomite weight, high speed dispersion 4200-4500 rev/min, 20-30 minute;
(3) dry, pulverize, make nanometer powder;
Modified soluble nano silicone colloidal sol is prepared by the following method:
Water-soluble nanoscale silica sol adds 4-5% nano-carbon powder, 3-5% ferric oxide, is mixed and heated to 50-60 DEG C, cools after 30-40 minute;
The preparation method of this Scratch-resistant metal anti-rust paint comprises the following steps:
(1), slurrying: pulping raw material is poured into batching kettle mixing, then mixed pulping raw material is transported in high-speed dispersing kettle and carries out stirring, disperseing 50-60 minute, rotating speed 3200-3500 rev/min, slurrying component after dispersion is transported in sand mill carries out wet type sand milling, dispersion, obtain slurry, slurry mesh-of-grind is less than or equals 40 microns;
(2) paint: add paint raw material in obtained slurry, be then transported in high-speed dispersing kettle and carry out stirring, disperseing, after dispersion, being transported in sand mill of component carries out wet type sand milling, dispersion, obtains paint vehicle; Again with 3200-3600 rev/min of high speed dispersion 40-50min;
(3) obtained paint vehicle is transported to vibrating filter to carry out filtering and screening, fineness≤40um, then the product after filtration is packed, warehouse-in.
2. Scratch-resistant metal anti-rust paint according to claim 1, is characterized in that being made up of the feed composition of following component weight part:
Pulping raw material:
Aluminium scrap powder 6, propylene glycol phenylate 2, tripropylene glycol methyl ether 5, paraffin wax emulsions 2, anti-sedimentation agent 3300S1, flow agent BYK-3001, polyacrylic acid sodium salt SN-50005, dispersion agent LBD-12, defoamer SPA2021, nano-calcium carbonate 10, modified Nano diatomite 10, modified soluble nano silicone colloidal sol 10;
Paint raw material:
Polyvinylpyrrolidone 10, epoxy emulsion 25, myo-Inositol hexaphosphate 25, sodium polymethacrylate 5, Wickenol 116 3, fatty alcohol-polyoxyethylene ether 1, propylene glycol 60,1-phenoxy group-2-propyl alcohol 15,2-amino-2-methyl-1-propanol 1, Sodium hexametaphosphate 99 2.