CN102876232A - 多功能防潮涂料的配方及其制备方法 - Google Patents
多功能防潮涂料的配方及其制备方法 Download PDFInfo
- Publication number
- CN102876232A CN102876232A CN2012103329581A CN201210332958A CN102876232A CN 102876232 A CN102876232 A CN 102876232A CN 2012103329581 A CN2012103329581 A CN 2012103329581A CN 201210332958 A CN201210332958 A CN 201210332958A CN 102876232 A CN102876232 A CN 102876232A
- Authority
- CN
- China
- Prior art keywords
- preparation
- coating
- agent
- negative ion
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
多功能防潮涂料的配方及其制备方法,它涉及空气的净化及降低空气湿度的技术领域。本发明的组成和重量百分比分别为:310TS乳液20~30%、硅溶胶5~15%、水10~20%、硅藻土助滤剂10~20%、硅灰石针状粉10~20%、轻质碳酸钙5~10%、沸石5~10%、负离子素0.8~1%、润湿剂188A 0.5~2.5%、流平剂20200.5~2.5%、成膜助剂醇脂-120.5~2.5%、防冻剂乙二醇0.5~1.5%、增稠剂9350.5~2.5%、消泡剂NXZ 0.1~0.5%、分散剂80450.1~1.0%、防霉剂0.2~0.8%;本发明制备工艺为:将固料和液料按10∶7.5的比例分别搅拌均匀加入到搅拌机中,低温搅拌捏合30min,涂料成稠膏状体即可;本发明节能环保,减少能耗,低碳减排,具有良好的吸收凝结水,降低空气湿度,同时能吸收苯等有害气体;产品独特,配方新,适用于建筑物,电力设备等。
Description
技术领域:
本发明涉及空气的净化及降低空气湿度的技术领域,具体说是涉及一种多功能防潮涂料的配方及其制备方法。
背景技术:
近年来,随着居室装饰装璜的现代化,室内的空气质量往往处于被忽视的位置。室内空气污染已经成为全世界各国共同关注的问题,环境专家已把室内空气污染列入对人健康危害最大的5种因素之一。美国专家研究表明,室内空气的污染程度要比室外空气严重2-5倍,在特殊情况下可达到100倍。装空调的封闭室内空气负离子浓度仅为0-25个/cm3。而世界卫生组织对清新空气的负离子标准浓度规定为:1000-1500个/cm3。
此外,每逢秋冬季节或霉雨季节,当建筑物室内侧表面(包括屋盖、天棚、内墙、其它结构面及地面等)的温度低于室内空气的露点温度时,在其表面就容易出现水蒸气凝结而形成水珠的现象,使其表面湿度增大。在有些情况下,建筑物表面湿度过大可能引起严重的后果或造成很大的危害,因为当建筑物内产生水滴时,水滴将污染居室内侧表面及室内存放的物品等,并可能导致霉变,加速建筑材料的破坏,对建筑物的使用功能影响很大。特别是对于工业建筑物来说,不仅对厂房结构及厂房内的操作人员有较大影响,而且有可能造成生产产品的锈蚀、霉变等,并因此降低产品质量,造成不良后果。对于计算机房、精密仪器、仪表室等室内环境功能要求严格的高等级建筑物来说,如果发生水蒸气凝结下滴的现象,问题将会变得更为严重,甚至有可能导致运算失灵、测试紊乱、线路损坏等恶性事故,但是,令人遗憾的是,这类条件要求高的建筑物,当气温低、湿度大时,其内部尤其易于产生水滴。
发明内容:
本发明的目的是提供多功能防潮涂料的配方及其制备方法,它节能环保,减少能耗,低碳减排,具有良好的吸收水滴及水蒸气,降低空气湿度的作用,同时能吸收苯等有害气体。
为了解决背景技术所存在的问题,本发明的组成和重量百分比分别为:310TS乳液20~30%、硅溶胶5~15%、水10~20%、硅藻土助滤剂10~20%、硅灰石针状粉10~20%、轻质碳酸钙5~10%、沸石5~10%、负离子素0.8~1%、润湿剂188A0.5~2.5%、流平剂20200.5~2.5%、成膜助剂醇脂-120.5~2.5%、防冻剂乙二醇0.5~1.5%、增稠剂9350.5~2.5%、消泡剂NXZ0.1~0.5%、分散剂80450.1~1.0%、防霉剂0.2~0.8%。
本发明制备工艺为:将固料和液料按10∶7.5比例分别搅拌均匀加入到搅拌机中,低温搅拌捏合30min,涂料成稠膏状体即可。
所述的负离子素产生的负离子为羟基负离子,负离子素是由多种宝石,玉石,晶石经多种高科技手段加工,复合,激活而成。负离子素形成无数微小颗粒,每个微小颗粒都具有正负电极,这种电极是由于材料加工后自发极化而产生的,是永久的。由于正负电荷无对称中心,即具有偶极矩,当外界温度发生微小变化或外加压力发生微小变化,则离子间矩及键角发生变化,诱发偶极矩,导致束缚在单元体表面的自由电荷层一部分就被放出来,从而使其呈带电状态或在闭合回路中形成电流,在其周围形成电场及微电流。正是靠着单元体永久电极,电场及微电流物理作用导致了负离子涂料具有永久性,持续不断的释放负离子的功能。
所述的成膜助剂醇脂-12硅溶液在失去水分时,单体硅酸逐渐聚合成高聚硅胶,随水分的蒸发,胶体分子增大,最后形成-SIO-O-SIO-涂膜:IO-SI-OH+HO-SI-OH因NA2O在硅溶胶中的含量低,硅溶胶具有一定量成膜溶解的特性,其耐水性、耐热性能明显优于有机涂料。涂膜致密且较硬,不产生静电,空气中各种尘埃难粘附。在目前的建筑涂料中,它的抗污染能力是较强的。但硅溶胶在成膜过程中体积收缩较大,涂膜易开裂因而需与乳液配合使用。
所述的310TS乳液具有突出的水泥兼容性,良好的拉伸强度和延伸率,低的吸水率典型应用于水泥基防水涂料、单、双组份腻子和外墙外保温***。两者的特性相互补充,可以配制出性能优良的有机、无机复合涂料。
所述的硅藻土助滤剂及沸石为本发明主要填料,硅藻土助滤剂具有良好的微孔结构、吸附性能和抗压缩性能,沸石的吸水性极强,保证涂料具有较高的吸水率和吸湿性。
本发明具有以下有益效果:节能环保,减少能耗,低碳减排,具有良好的吸收水滴及水蒸气,降低空气湿度的作用,同时能吸收苯等有害气体;产品独特,配方新,适用于建筑物,电力设备等。
具体实施方式:
本具体实施方式的组成和重量百分比分别为:310TS乳液25%、硅溶胶10%、水15%、硅藻土助滤剂15%、硅灰石针状粉14%、轻质碳酸钙5%、沸石8%、负离子素0.8%、润湿剂188A1.5%、流平剂20201.5%、成膜助剂醇脂-121.5%、防冻剂乙二醇0.6%、增稠剂9350.8%、消泡剂NXZ0.1%、分散剂80450.4%、防霉剂0.8%。
本具体实施方式制备工艺为:将固料和液料按10∶7.5的比例进行均匀搅拌加入到搅拌机中,低温搅拌捏合30min,涂料成稠膏状体。
所述的负离子素产生的负离子为羟基负离子,负离子素是由多种宝石,玉石,晶石经多种高科技手段加工,复合,激活而成。负离子素形成无数微小颗粒,每个微小颗粒都具有正负电极,这种电极是由于材料加工后自发极化而产生的,是永久的。由于正负电荷无对称中心,即具有偶极矩,当外界温度发生微小变化或外加压力发生微小变化,则离子间矩及键角发生变化,诱发偶极矩,导致束缚在单元体表面的自由电荷层一部分就被放出来,从而使其呈带电状态或在闭合回路中形成电流,在其周围形成电场及微电流。正是靠着单元体永久电极,电场及微电流物理作用导致了负离子涂料具有永久性,持续不断的释放负离子的功能。
所述的成膜助剂醇脂-12硅溶液在失去水分时,单体硅酸逐渐聚合成高聚硅胶,随水分的蒸发,胶体分子增大,最后形成-SIO-O-SIO-涂膜:IO-SI-OH+HO-SI-OH因NA2O在硅溶胶中的含量低,硅溶胶具有一定量成膜溶解的特性,其耐水性、耐热性能明显优于有机涂料。涂膜致密且较硬,不产生静电,空气中各种尘埃难粘附。在目前的建筑涂料中,它的抗污染能力是较强的。但硅溶胶在成膜过程中体积收缩较大,涂膜易开裂因而需与乳液配合使用。
所述的310TS乳液具有突出的水泥兼容性,良好的拉伸强度和延伸率,低的吸水率典型应用于水泥基防水涂料、单、双组份腻子和外墙外保温***。两者的特性相互补充,可以配制出性能优良的有机、无机复合涂料。
所述的硅藻土助滤剂及沸石为本发明主要填料,硅藻土助滤剂具有良好的微孔结构、吸附性能和抗压缩性能,沸石的吸水性极强,保证涂料具有较高的吸水率和吸湿性。
本具体实施方式节能环保,减少能耗,低碳减排,具有良好的吸收水滴及水蒸气,降低空气湿度的作用,同时能吸收苯等有害气体;产品独特,配方新,适用于建筑物,电力设备等。
Claims (3)
1.多功能防潮涂料的配方及其制备方法,其特征在于310TS乳液20~30%、硅溶胶5~15%、水10~20%、硅藻土助滤剂10~20%、硅灰石针状粉10~20%、轻质碳酸钙5~10%、沸石5~10%、负离子素0.8~1%、润湿剂188A0.5~2.5%、流平剂20200.5~2.5%、成膜助剂醇脂-120.5~2.5%、防冻剂乙二醇0.5~1.5%、增稠剂9350.5~2.5%、消泡剂NXZ0.1~0.5%、分散剂80450.1~1.0%、防霉剂0.2~0.8%;本发明制备工艺为:将固料和液料按10∶7.5别搅拌均匀加入到搅拌机中,低温搅拌捏合30min,涂料成稠膏状体即可。
2.根据权利要求1所述的多功能防潮涂料的配方及其制备方法,其特征在于所述的负离子素产生的负离子为羟基负离子。
3.根据权利要求1所述的多功能防潮涂料的配方及其制备方法,其特征在于它的组成和重量百分比分别为:310TS乳液25%、硅溶胶10%、水15%、硅藻土助滤剂15%、硅灰石针状粉14%、轻质碳酸钙5%、沸石8%、负离子素0.8%、润湿剂188A1.5%、流平剂20201.5%、成膜助剂醇脂-121.5%、防冻剂乙二醇0.6%、增稠剂9350.8%、消泡剂NXZ0.1%、分散剂80450.4%、防霉剂0.8%。