CN102863773A - Preparation method of polyphenylene oxide/polyamide 66 (PPO/PA66) synthetic plastic - Google Patents
Preparation method of polyphenylene oxide/polyamide 66 (PPO/PA66) synthetic plastic Download PDFInfo
- Publication number
- CN102863773A CN102863773A CN2012103264572A CN201210326457A CN102863773A CN 102863773 A CN102863773 A CN 102863773A CN 2012103264572 A CN2012103264572 A CN 2012103264572A CN 201210326457 A CN201210326457 A CN 201210326457A CN 102863773 A CN102863773 A CN 102863773A
- Authority
- CN
- China
- Prior art keywords
- ppo
- weight percentage
- synthetic plastics
- preparation
- polyphenylene oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of a polyphenylene oxide/polyamide 66 (PPO/PA66) synthetic plastic. The synthetic plastic comprises the following components by weight percent: 25-35% of PPO, 25-35% of PA66, 15-25% of carbon fiber, 8-12% of carbon black, 5-10% of a compatilizer, 5-10% of a toughening agent and 0.5-1.5% of additives.
Description
Technical field
The invention belongs to polymeric material field, refer to especially a kind of preparation method of PPO/PA66 synthetic plastics.
Background technology
PPO (polyphenylene oxide) resin and PA66 (nylon 66) resin is one of widely used engineering plastics.PPO has high heat-resisting, dimensional stabilizing, and electric insulating quality is good, but its processing fluidity is poor, not organic solvent-resistant.PA66 belongs to crystalline material, good fluidity, organic solvent-resistant, but its easy suction, poor dimensional stability.
The PPO/PA66 synthetic plastics combines the performance of PPO and PA66, with its excellent thermotolerance, and good processibility, but sprayabilities etc. are used widely.At present, most enhancement type PPO/PA66 synthetic plasticss adopt glass fibre to strengthen, and the density of material that makes is larger, and strength enhancing is inadequate, does not possess antistatic effect.
Summary of the invention
The purpose of this invention is to provide a kind of PPO/PA66 synthetic plastics, solve the not strong problem of existing PPO/PA66 synthetic plastics intensity and antistatic property.
The present invention is achieved through the following technical solutions:
A kind of preparation method of PPO/PA66 synthetic plastics may further comprise the steps:
At first, percentage composition comprises the polyphenylene oxide of following component: 25-35% by weight, the nylon 66 of 25-35%, and the carbon black of 8-12%, the compatilizer of 5-10%, the toughner of 5-10%, the auxiliary agent of 0.5-1.5% mixes, and makes mixture;
Secondly, under temperature 230-250 ℃ condition, be that the screw extrusion press skill of 25-40 go out process with length-to-diameter ratio with this mixture, obtain the PPO/PA66 synthetic plastics, to extrude in the treatment step at this, the adding weight percentage is the carbon fiber of 15-25%.
Described auxiliary agent includes oxidation inhibitor, lubricant and thermo-stabilizer; Described oxidation inhibitor: lubricant: thermo-stabilizer is 1: 2: 2.
The invention has the beneficial effects as follows:
By doping carbon fiber and carbon black, so that the intensity of PPO/PA66 synthetic plastics is improved, the synthetic materials antistatic property significantly promotes simultaneously.
Embodiment
Below describe the content of the technical program in detail by specific embodiment.
In the present invention, described polyphenylene oxide chemical name is called for short PPO for poly-2,6-dimethyl-Isosorbide-5-Nitrae-phenylate; The chemical name of described nylon 66 is called for short PA66 for poly-adipoyl diamines.
Compatilizer is selected from the PPO-g-MAH that percentage of grafting is 0.8-1.5%, the polyphenylene oxide grafted maleic anhydride, by adding compatilizer, strengthened the interface compatibility of PPO and PA66, so that the interface mixes more between carbon fiber, carbon black, PPO and the PA66, realize the even mixing of each component in the PPO/PA66 synthetic plastics.
Toughner is selected from sweeps the SEBS-g-MAH that a rate is 0.8-1.5%, and the SEBS grafted maleic anhydride has improved toughness and over-all properties by doping plasticizing agent in synthetic plastics.
The length of carbon fiber is preferably short carbon fiber without limits, and length is 5-10mm, by doping PPO/PA66 synthetic plastics, so that the mechanical property of synthetic plastics significantly improves, has higher physical strength, and antistatic effect promotes simultaneously.Carbon black selects existing carbon black can satisfy the requirement of technical scheme.Oxidation inhibitor is selected from triglycol two-3-(the 3-tertiary butyl-4 hydroxy-5-methyl base phenyl) fine, four [methyl-β-(3 of propylene, 5-di-t-butyl-4 hydroxy phenyl) propionic ester] one or more combinations in pentaerythritol ester, three (2, the 4-di-tert-butylphenol) phosphorous acid ester.
Lubricant is selected from one or both combinations in tetramethylolmethane stearate or the two stearic amides of ethyl.Thermo-stabilizer is selected from one or both combinations in zinc oxide or the zinc sulphide.
Embodiment 1
Be 25% PPO with weight percentage, weight percentage is 35% PA66, and weight percentage is 6% compatilizer, and weight percentage is that 5% toughner mixes, and stirs; Add again weight percentage and be 8% carbon black, weight percentage is that 1% auxiliary agent stirs, obtain mixture, this mixture is joined in the twin screw extruder that length-to-diameter ratio is 25-40, be that 20% carbon fiber joins in the forcing machine with weight percentage, through melt blending, extruding pelletization forms the PPO/PA66 synthetic plastics.
Embodiment 2
Be 35% PPO with weight percentage, weight percentage is 25% PA66, and weight percentage is 6% compatilizer, and weight percentage is that 5% toughner mixes, and stirs; Add again weight percentage and be 8% carbon black, weight percentage is that 1% auxiliary agent stirs, obtain mixture, this mixture is joined in the twin screw extruder that length-to-diameter ratio is 25-40, be that 20% carbon fiber joins in the forcing machine with weight percentage, through melt blending, extruding pelletization forms the PPO/PA66 synthetic plastics.
Embodiment 3
Be 30% PPO with weight percentage, weight percentage is 30% PA66, and weight percentage is 7% compatilizer, and weight percentage is that 7% toughner mixes, and stirs; Add again weight percentage and be 10% carbon black, weight percentage is that 1% auxiliary agent stirs, obtain mixture, this mixture is joined in the twin screw extruder that length-to-diameter ratio is 25-40, be that 15% carbon fiber joins in the forcing machine with weight percentage, through melt blending, extruding pelletization forms the PPO/PA66 synthetic plastics.
Embodiment 4
Be 30% PPO with weight percentage, weight percentage is 35% PA66, and weight percentage is 5% compatilizer, and weight percentage is that 5% toughner mixes, and stirs; Add again weight percentage and be 9% carbon black, weight percentage is that 1% auxiliary agent stirs, obtain mixture, this mixture is joined in the twin screw extruder that length-to-diameter ratio is 25-40, be that 15% carbon fiber joins in the forcing machine with weight percentage, through melt blending, extruding pelletization forms the PPO/PA66 synthetic plastics.
Embodiment 5
Be 35% PPO with weight percentage, weight percentage is 30% PA66, and weight percentage is 5% compatilizer, and weight percentage is that 5% toughner mixes, and stirs; Add again weight percentage and be 9% carbon black, weight percentage is that 1% auxiliary agent stirs, obtain mixture, this mixture is joined in the twin screw extruder that length-to-diameter ratio is 25-40, be that 15% carbon fiber joins in the forcing machine with weight percentage, through melt blending, extruding pelletization forms the PPO/PA66 synthetic plastics.
Claims (2)
1. the preparation method of a PPO/PA66 synthetic plastics is characterized in that: may further comprise the steps:
At first, percentage composition comprises the polyphenylene oxide of following component: 25-35% by weight, the nylon 66 of 25-35%, and the carbon black of 8-12%, the compatilizer of 5-10%, the toughner of 5-10%, the auxiliary agent of 0.5-1.5% mixes, and makes mixture;
Secondly, under temperature 230-250 ℃ condition, be that the screw extrusion press skill of 25-40 go out process with length-to-diameter ratio with this mixture, obtain the PPO/PA66 synthetic plastics, to extrude in the treatment step at this, the adding weight percentage is the carbon fiber of 15-25%.
2. the preparation method of PPO/PA66 synthetic plastics according to claim 1, it is characterized in that: described auxiliary agent includes oxidation inhibitor, lubricant and thermo-stabilizer; Described oxidation inhibitor: lubricant: thermo-stabilizer is 1: 2.2.