CN102863179B - Ornamental clay statuette material - Google Patents
Ornamental clay statuette material Download PDFInfo
- Publication number
- CN102863179B CN102863179B CN 201210351755 CN201210351755A CN102863179B CN 102863179 B CN102863179 B CN 102863179B CN 201210351755 CN201210351755 CN 201210351755 CN 201210351755 A CN201210351755 A CN 201210351755A CN 102863179 B CN102863179 B CN 102863179B
- Authority
- CN
- China
- Prior art keywords
- parts
- kilogram
- ornamental
- statuette
- mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an ornamental clay statuette material which comprises the following components in parts by weight: 75-85 parts of carbon powder, 45-55 parts of water, 25-35 parts of pig blood, 190-210 parts of talcum powder, 15-25 parts of latex and 3-8 parts of sodium hydroxide. The invention has the advantages of low manufacturing cost, simple manufacturing technique and high viscosity;the method for making the clay statuette by using the ornamental clay statuette material is simple; and the finished statuette product is firm and stable, and has the advantages of long service life and elegant appearance.
Description
Technical field
The present invention relates to a kind of finishing material, relate in particular to a kind of ornamental mud carving material.
Background technology
At present, on upholstery and furniture decoration, generally use the mud carving.The common used material of mud carving is greasy filth on the market, greasy filth is a kind of made synthetic materials, it is mainly founded by materials such as waste rubber, wax, vegetables oil or machine oil, talcum powder, calcium carbonate, toner, water and forms, have viscosity strong, be difficult for dry and cracked characteristics, but temperature influence is large, and price is high, and amount is few, and complex manufacturing technology is done little draft or the less works of size so general sculptor commonly uses it.
Summary of the invention
The purpose of this invention is to provide a kind of sculpture solid, attractive in appearance, durable ornamental mud carving material of mud carving out.And this mud carving material is with low cost.
In order to realize above purpose, the present invention has adopted following technical scheme: a kind of ornamental mud carving material, be used for sticking on furniture surface, and its component and each component are by weight:
75 ~ 85 parts of carbon dusts;
45 ~ 55 parts in water;
25 ~ 35 parts of pig blood;
190 ~ 210 parts of talcum powder;
15 ~ 25 parts of white glue with vinyl;
3 ~ 8 parts in caustic soda;
Above material mixing, stirring gets final product.This mud carving material can namely be joined i.e. usefulness, and is succinct, with low cost fast.If once preparation too much has exhaustless clout, only need sealing to preserve and get final product.Quality guaranteed period generally can reach about 3 years, its long quality-guarantee period.The mud carving that other this mud carving material carves out only needs at room temperature natural cold to put about 2 days, can dry up.
The component of described ornamental mud carving material and each component are by weight:
80 parts of carbon dusts;
50 parts in water;
30 parts of pig blood;
200 parts of talcum powder;
20 parts of white glue with vinyl;
5 parts in caustic soda.
White glue with vinyl is a kind of water soluble adhesive, a kind of thermoplastic binder that under the initiator effect, made through polyreaction by Vinyl Acetate Monomer, chemical name is the Vinyl Acetate Copolymer tackiness agent, be by acetic acid and ethene synthesizing vinyl acetate, add the oyster white glop that titanium dioxide forms through letex polymerization again.White glue with vinyl is normal temperature solidified, curing is very fast, bonding strength is higher, and adhesive linkage has preferably toughness and weather resistance and difficult aging.Can make the tackiness agent of waterproof paint and timber.It is take water as dispersion agent, use safe, nontoxic, do not fire, easy to clean, ambient cure has good adhesion to timber, paper and fabric, Joint strength is high, the glue-line water white transparency after the curing, good toughness does not pollute by sticky object good emulsion stability.
Adopt above technical scheme, utilize to have added the pig blood component, make that cost of the present invention reduces, manufacture craft is simple, viscosity is strong, and simultaneously, the method that use the present invention makes the mud carving is simple, and make the finished product behind the sculpture, firm solid, long service life and elegant in appearance.
Embodiment
A kind of ornamental mud carving material is used for sticking on furniture surface, and its component and each component are by weight:
75 ~ 85 parts of carbon dusts;
45 ~ 55 parts in water;
25 ~ 35 parts of pig blood;
190 ~ 210 parts of talcum powder;
15 ~ 25 parts of white glue with vinyl;
3 ~ 8 parts in caustic soda.
The component of described ornamental mud carving material and each component are by weight:
80 parts of carbon dusts;
50 parts in water;
30 parts of pig blood;
200 parts of talcum powder;
20 parts of white glue with vinyl;
5 parts in caustic soda.
The specific embodiment of making the mud carving material of the present invention is as follows:
Embodiment 1:
A kind of component of ornamental mud carving material and each composition weight are:
0.8 kilogram of carbon dust;
0.5 kilogram in water;
0.3 kilogram of pig blood;
2 kilograms of talcum powder;
0.2 kilogram of white glue with vinyl;
0.05 kilogram in caustic soda.
The method of making the mud carving of this mud carving material is:
1) is coated in the cabinet-wood surface that needs to decorate the mud carving after getting 0.1 kilogram of carbon dust and 0.05 kilogram of mixing of water, obtains one deck carbon dust layer;
2) get 0.3 kilogram of pig blood, 0.45 kilogram in water and 0.05 kilogram of mixed fermentation of caustic soda 8 hours, in the mixture that fermentation is finished, add 2 kilograms of talcum powder, 0.2 kilogram of white glue with vinyl, 0.7 kilogram of carbon dust, mixing and stirring.
3) with step 2) in the mixture that stirs be coated in the carbon dust layer surface of step 1), wait the mixture that is coated on the carbon dust layer to do after, carve according to needed mud carving shape with graver, namely get required mud after engraving is finished and carve product.
Embodiment 2:
A kind of component of ornamental mud carving material and each composition weight are:
0.85 kilogram of carbon dust;
0.55 kilogram in water;
0.35 kilogram of pig blood;
2.1 kilograms of talcum powder;
0.25 kilogram of white glue with vinyl;
0.08 kilogram in caustic soda.
The method of making the mud carving of this mud carving material is:
1) is coated in the cabinet-wood surface that needs to decorate the mud carving after getting 0.12 kilogram of carbon dust and 0.07 kilogram of mixing of water, obtains one deck carbon dust layer;
2) get 0.35 kilogram of pig blood, 0.48 kilogram in water and 0.08 kilogram of mixed fermentation of caustic soda 8 hours, in the mixture that fermentation is finished, add 2.1 kilograms of talcum powder, 0.25 kilogram of white glue with vinyl, 0.73 kilogram of carbon dust, mixing and stirring.
3) with step 2) in the mixture that stirs be coated in the carbon dust layer surface of step 1), wait the mixture that is coated on the carbon dust layer to do after, carve according to needed mud carving shape with graver, namely get required mud after engraving is finished and carve product.
Embodiment 3:
A kind of component of ornamental mud carving material and each composition weight are:
0.75 kilogram of carbon dust;
0.45 kilogram in water;
0.25 kilogram of pig blood;
1.9 kilograms of talcum powder;
0.15 kilogram of white glue with vinyl;
0.03 kilogram in caustic soda.
The method of making the mud carving of this mud carving material is:
1) is coated in the cabinet-wood surface that needs to decorate the mud carving after getting 0.07 kilogram of carbon dust and 0.03 kilogram of mixing of water, obtains one deck carbon dust layer;
2) get 0.25 kilogram of pig blood, 0.42 kilogram in water and 0.03 kilogram of mixed fermentation of caustic soda 8 hours, in the mixture that fermentation is finished, add 1.9 kilograms of talcum powder, 0.15 kilogram of white glue with vinyl, 0.68 kilogram of carbon dust, mixing and stirring.
3) with step 2) in the mixture that stirs be coated in the carbon dust layer surface of step 1), wait the mixture that is coated on the carbon dust layer to do after, carve according to needed mud carving shape with graver, namely get required mud after engraving is finished and carve product.
Claims (2)
1. an ornamental mud carving material is used for sticking on furniture surface, and it is characterized in that: its component and each component are by weight:
75 ~ 85 parts of carbon dusts;
45 ~ 55 parts in water;
25 ~ 35 parts of pig blood;
190 ~ 210 parts of talcum powder;
15 ~ 25 parts of white glue with vinyl;
3 ~ 8 parts in caustic soda;
Above material mixing, stirring gets final product to get the mud carving material.
2. described ornamental mud carving material according to claim 1, it is characterized in that: its component and each component are by weight:
80 parts of carbon dusts;
50 parts in water;
30 parts of pig blood;
200 parts of talcum powder;
20 parts of white glue with vinyl;
5 parts in caustic soda.