CN102852012A - 一种抗菌消臭的蚕丝纤维的制备方法 - Google Patents
一种抗菌消臭的蚕丝纤维的制备方法 Download PDFInfo
- Publication number
- CN102852012A CN102852012A CN201210311137XA CN201210311137A CN102852012A CN 102852012 A CN102852012 A CN 102852012A CN 201210311137X A CN201210311137X A CN 201210311137XA CN 201210311137 A CN201210311137 A CN 201210311137A CN 102852012 A CN102852012 A CN 102852012A
- Authority
- CN
- China
- Prior art keywords
- preparation
- silk fibers
- silk fiber
- antibiotic
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种抗菌消臭的蚕丝纤维的制备方法,首先将蚕丝纤维或织物先在染料溶液中浸渍,然后再在含铜(II)离子的溶液中固色,洗净干燥。采用本发明的制备方法制作的蚕丝纤维,对大肠肝菌的抗菌率达到99%,对金黄色葡萄球菌的抗菌率达到96%,对氨气、硫化氢的消臭率几乎达到100,且耐洗性非常好。
Description
技术领域
本发明涉及一种纤维的制备方法,尤其涉及一种抗菌消臭的蚕丝纤维的制备方法。
背景技术
纺织品的消臭功能是指消除环境中已经存在的臭气,抗菌防臭是指通过抑制细菌繁殖或杀死细菌而防止臭气产生。世界范围内老年人口逐年增加,其中瘫痪病人占相当比例,他们使用的纺织品如果更换不勤,会产生臭味而影响生活质量;另外,厕所内的臭昧、脚臭、香烟烟雾等也普遍引起人们的厌恶。这些场台使用的纺织品最好具有消臭和抗菌功能。
发明内容
本发明所要解决的技术问题是提供一种抗菌消臭的蚕丝纤维的制备方法,使得蚕丝纤维具有非常好的抗菌和消臭的功能,并且耐洗性良好。
为了解决上述技术问题本发明采用了如下的技术手段:
一种抗菌消臭的蚕丝纤维的制备方法,首先将蚕丝纤维或织物先在染料溶液中浸渍,然后再在含铜(II)离子的溶液中固色,洗净干燥。
采用本发明的制备方法制作的蚕丝纤维,对大肠肝菌的抗菌率达到99%,对金黄色葡萄球菌的抗菌率达到96%,对氨气、硫化氢的消臭率几乎达到100,且耐洗性非常好。
具体实施方式
为了更好地理解本发明,下面结合一个具体实施例对本发明进行进一步的说明:
一种抗菌消臭的蚕丝纤维的制备方法,首先将蚕丝纤维或织物先在染料溶液中浸渍,然后再在含铜(II)离子的溶液中固色,洗净干燥。
所述的染料溶液的制作方法为:称取一定量的染料(橙S或黑G)溶于0.5mol/L NaSO水溶液中。
一般浸渍时间可以12-14小时。
含铜(II)离子的溶液可以是硝酸铜或氯化铜的溶液,固色的时间为2-3小时,室温中固色。
采用本发明的方法制作出来的功能性蚕丝纤维对大肠杆菌的抗菌率达99%,对金黄色葡萄球菌的抗菌率达96.38.并且抗菌耐洗性良好。功能性蚕丝纤维对消除氨气的机理是由于氨气分子与铜(II)离子产生了配位,消除硫化氢的机理是由于硫化氢与铜(II)离子生成了硫化铜多晶。
Claims (4)
1.一种抗菌消臭的蚕丝纤维的制备方法,其特征在于,首先将蚕丝纤维或织物先在染料溶液中浸渍,然后再在含铜(II)离子的溶液中固色,洗净干燥。
2.根据权利要求1所述的一种抗菌消臭的蚕丝纤维的制备方法,其特征在于,所述的染料溶液的制作方法为:称取一定量的染料溶于0.5mol/L NaSO水溶液中。
3.根据权利要求1所述的一种抗菌消臭的蚕丝纤维的制备方法,其特征在于,一般浸渍时间可以12-14小时。
4.根据权利要求1所述的一种抗菌消臭的蚕丝纤维的制备方法,其特征在于,含铜(II)离子的溶液可以是硝酸铜或氯化铜的溶液,固色的时间为2-3小时,室温中固色。