CN102838813A - 冰箱冰柜内胆门胆材料的制备方法 - Google Patents

冰箱冰柜内胆门胆材料的制备方法 Download PDF

Info

Publication number
CN102838813A
CN102838813A CN201210333923XA CN201210333923A CN102838813A CN 102838813 A CN102838813 A CN 102838813A CN 201210333923X A CN201210333923X A CN 201210333923XA CN 201210333923 A CN201210333923 A CN 201210333923A CN 102838813 A CN102838813 A CN 102838813A
Authority
CN
China
Prior art keywords
weight part
preparation
temperature
refrigerator
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210333923XA
Other languages
English (en)
Inventor
王光华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210333923XA priority Critical patent/CN102838813A/zh
Publication of CN102838813A publication Critical patent/CN102838813A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种冰箱冰柜内胆门胆材料的制备方法，本发明的目的是提供一种成本低、加工便利的冰箱冰柜内胆门胆材料的制备方法，本发明的技术方案要点是，选取聚苯乙烯100-110重量份，聚丙烯10-20重量份，苯乙烯–丁二烯–苯乙烯嵌段共聚物15-25重量份，稳定剂0.3-0.5重量份，抗氧剂0.7-0.9重量份，润滑剂0.075-0.09重量份，颜料0.01-0.02重量份，填充剂1-2重量份；将上述重量份的各材料放入高速搅拌机，搅拌150秒—250秒，搅拌温度为室温，再将搅拌后的材料由双杆同向平行塑料挤出机挤出，机身温度：190-220℃，机头温度：190-215℃，挤出后的材料在由水温45-60℃的水进行冷却，完成制备。本发明的生产成本较低，加工工艺简单。

Description

冰箱冰柜内胆门胆材料的制备方法
技术领域：
    本发明涉及新材料，特别是一种冰箱冰柜内胆门胆材料的制备方法。
背景技术：
目前，各种家用电器如冰箱、冰柜等使用的内胆、门胆均采用单纯的ABS、HIPS材料制作，加工工艺复杂，生产成本较高。如目前的冰箱、冰柜内胆、门胆，一般采用进口或国产ABS、HIPS材料，装配前需要加工成不同型号的冰箱、冰柜的内胆、门胆，然后固定在冰箱、冰柜内部，发泡定型。不仅成本高，而且加工难度大，产品一旦成型不易更改。另外，板边等下脚料再利用比较麻烦，ABS材质板边下脚料还存在与其它材质不容，难以回收等问题。但对于冰箱、冰柜的内胆、门胆一般不受力，不需要很高的强度。而ABS、HIPS格较高，一是增加了冰箱、冰柜内胆、门胆材料的成本，二是由于这些材料的强度较高，加工工艺复杂，增加了其制造成本。
发明内容：
本发明的目的是提供一种成本低、加工便利的冰箱冰柜内胆门胆材料的制备方法。
本发明的技术方案是，冰箱冰柜内胆门胆材料的制备方法，其特征在于：选取聚苯乙烯100-110重量份，聚丙烯10-20重量份，苯乙烯–丁二烯–苯乙烯嵌段共聚物15-25重量份，稳定剂0.3-0.5重量份，抗氧剂0.7-0.9重量份，润滑剂0.075-0.09重量份，颜料0.01-0.02重量份，填充剂1-2重量份；将上述重量份的各材料放入高速搅拌机，搅拌150秒—250秒，搅拌温度为室温，再将搅拌后的材料由双杆同向平行塑料挤出机挤出，机身温度：190-220℃，机头温度：190-215℃，挤出后的材料在由水温45-60℃的水进行冷却，完成制备。所述的稳定剂为硬脂酸锌或硬脂酸钙；所述的抗氧剂为抗氧剂ODP或抗氧剂1010；所述的润滑剂为固体石蜡或硬脂酸；所述的颜料为群青、锰紫、炭黑；所述的填充剂为轻质碳酸钙或活性碳酸钙。
本发明的生产成本较低，加工工艺简单，本发明应用于冰箱、冰柜的内胆、门胆，取代了原有冰箱、冰柜采用单纯ABS、HIPS制作冰箱、冰柜内胆、门胆等带来复杂的加工工艺，使产品内部可以具有美观、时尚、大方的特点，容易被顾客接受，能够满足客户对产品观感效果的更高要求。    
具体实施方式：
具体描述实施例，
实施例一，
选取聚苯乙烯100重量份，聚丙烯10重量份，苯乙烯–丁二烯–苯乙烯嵌段共聚物15重量份，硬脂酸锌0.3重量份，抗氧剂ODP为0.8重量份，固体石蜡0.08重量份，锰紫0.01重量份，轻质碳酸钙1重量份，将上述重量份的各材料放入高速搅拌机：搅拌150秒，搅拌温度为室温，再将搅拌后的材料由双杆同向平行塑料挤出机挤出，机身温度：190℃，机头温度：190℃，挤出后的材料在由水温45℃的水进行冷却，制得本发明。
实施例二，
选取聚苯乙烯105重量份，聚丙烯15重量份，苯乙烯–丁二烯–苯乙烯嵌段共聚物18重量份，硬脂酸钙0.5重量份, 抗氧剂1010为0.7重量份，硬脂酸 0.075重量份，群青0.015重量份，活性碳酸钙1.8重量份，将上述重量份的各材料放入高速搅拌机：搅拌180秒，搅拌温度为室温，再将搅拌后的材料由双杆同向平行塑料挤出机挤出，机身温度：200℃，机头温度：205℃，挤出后的材料在由水温50℃的水进行冷却，制得本发明。
实施例三，
选取聚苯乙烯110重量份，聚丙烯20重量份，苯乙烯–丁二烯–苯乙烯嵌段共聚物20重量份，硬脂酸锌0.45重量份,抗氧剂ODP为0.9重量份，硬脂酸0.09重量份，炭黑0.012重量份，轻质碳酸钙2重量份，将上述重量份的各材料放入高速搅拌机：搅拌200秒，搅拌温度为室温，再将搅拌后的材料由双杆同向平行塑料挤出机挤出，机身温度：210℃，机头温度：210℃，挤出后的材料在由水温60℃的水进行冷却，制得本发明。
实施例四，
选取聚苯乙烯107重量份，聚丙烯17重量份，苯乙烯–丁二烯–苯乙烯嵌段共聚物25重量份，硬脂酸钙0.35重量份，抗氧剂1010为 0.82重量份，固体石蜡0.083重量份，群青0.02重量份，活性碳酸钙2.5重量份，将上述重量份的各材料放入高速搅拌机：搅拌250秒，搅拌温度为室温，再将搅拌后的材料由双杆同向平行塑料挤出机挤出，机身温度：220℃，机头温度：215℃，挤出后的材料在由水温55℃的水进行冷却，制得本发明。
本发明的加工工艺简单，生产成本低廉，重量轻，不变形，易于安装与搬运，同时本发明具有高抗冲击强度，优良的机械性能、并具有耐腐蚀性、耐撕裂性和阻燃性，而且拉伸强度好和耐高温、耐低温等综合性能，还具备有极高流动性、高韧性的特点；本发明适用范围广泛，可使冰箱、冰柜的门胆和内胆的制造成本得以有效降低，并且还可适用于多种电器产品。

Claims (2)

1.冰箱冰柜内胆门胆材料的制备方法，其特征在于：选取聚苯乙烯100-110重量份，聚丙烯10-20重量份，苯乙烯–丁二烯–苯乙烯嵌段共聚物15-25重量份，稳定剂0.3-0.5重量份，抗氧剂0.7-0.9重量份，润滑剂0.075-0.09重量份，颜料0.01-0.02重量份，填充剂1-2重量份；将上述重量份的各材料放入高速搅拌机，搅拌150秒—250秒，搅拌温度为室温，再将搅拌后的材料由双杆同向平行塑料挤出机挤出，机身温度：190-220℃，机头温度：190-215℃，挤出后的材料在由水温45-60℃的水进行冷却，完成制备。
2.如权利要求1所述的冰箱冰柜内胆门胆材料的制备方法，其特征在于：所述的稳定剂为硬脂酸锌或硬脂酸钙；所述的抗氧剂为抗氧剂ODP或抗氧剂1010；所述的润滑剂为固体石蜡或硬脂酸；所述的颜料为群青、锰紫、炭黑；所述的填充剂为轻质碳酸钙或活性碳酸钙。
CN201210333923XA 2012-09-11 2012-09-11 冰箱冰柜内胆门胆材料的制备方法 Pending CN102838813A (zh)