CN102816393A - 一种低烟低卤阻燃型交联聚烯烃绝缘电缆料及其制备方法 - Google Patents

一种低烟低卤阻燃型交联聚烯烃绝缘电缆料及其制备方法 Download PDF

Info

Publication number
CN102816393A
CN102816393A CN 201210263665 CN201210263665A CN102816393A CN 102816393 A CN102816393 A CN 102816393A CN 201210263665 CN201210263665 CN 201210263665 CN 201210263665 A CN201210263665 A CN 201210263665A CN 102816393 A CN102816393 A CN 102816393A
Authority
CN
China
Prior art keywords
parts
low
cable material
insulated cable
smoke
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201210263665
Other languages
English (en)
Inventor
王社兵
赵家连
张正松
王社峰
王翠玲
方昔蓉
王岳嵩
程亚斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HONGBO CABLE Co Ltd
Original Assignee
ANHUI HONGBO CABLE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HONGBO CABLE Co Ltd filed Critical ANHUI HONGBO CABLE Co Ltd
Priority to CN 201210263665 priority Critical patent/CN102816393A/zh
Publication of CN102816393A publication Critical patent/CN102816393A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种低烟低卤阻燃型交联聚烯烃绝缘电缆料及其制备方法，该电缆料包括以下组分及含量：氯化聚乙烯树脂25-35份、聚烯烃弹性体POE848010-15份、三元乙丙橡胶10-20份、抗滴落剂3-8份、聚四氟乙烯5-10份、氯化石蜡3-8份、纳米陶土3-5份、半补强炭黑3-8份、硬脂酸锌3-5份、偏苯三酸三辛酯10-15份、聚酰亚胺5-8份和ECHO.A噻二唑衍生物1-3份。本发明由于采用氯化聚乙烯树脂、聚烯烃弹性体POE8480和三元乙丙橡胶高分子材料并用作为本发明的基础材料，同时增加了辅料聚四氟乙烯、纳米陶土、苯丙乳液、聚酰亚胺和ECHO.A噻二唑衍生物，解决了电缆材料不能满足在高温强腐蚀的环境下工作使用现状，具有低烟低卤阻燃型抗滴落的特性。

Description

一种低烟低卤阻燃型交联聚烯烃绝缘电缆料及其制备方法
技术领域
本发明涉及一种低烟低卤阻燃型交联聚烯烃绝缘电缆料及其制备方法，属于电缆制造领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视；电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，特别是航空导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合，越来越需要使用耐高温、耐气候的低烟低卤阻燃型交联聚烯烃绝缘电缆料。
发明内容
本发明的目的是在于克服上述已有技术的不足，提供一种低烟低卤阻燃型交联聚烯烃绝缘电缆料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
低烟低卤阻燃型交联聚烯烃绝缘电缆料，各原料组分的重量份为：
氯化聚乙烯树脂                           25-35份
聚烯烃弹性体POE 8480                           10-15份
三元乙丙橡胶                         10-20份
抗滴落剂                                 3-8份
聚四氟乙烯                               5-10份
氯化石蜡                                 3-8份
纳米陶土                                   3-5份
半补强炭黑                               3-8份
硬脂酸锌                                 3-5份
偏苯三酸三辛酯                           10-15份
聚酰亚胺                                 5-8份
ECHO.A 噻二唑衍生物                                   1-3份
低烟低卤阻燃型交联聚烯烃绝缘电缆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，将氯化聚乙烯树脂、聚烯烃弹性体POE 8480和三元乙丙橡胶混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入抗滴落剂、聚四氟乙烯、氯化石蜡、纳米陶土、半补强炭黑、硬脂酸锌、偏苯三酸三辛酯、聚酰亚胺和ECHO.A 噻二唑衍生物，常温下低速搅拌3-5分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度130-150℃，得到成品。
抗滴落剂采用  抗滴落剂 GSCFR-631。
或者采用自制的抗滴落剂，其组成原料重量份为聚四氟乙烯30-35、苯乙烯10-12、纳米碳酸钙3-5、丙烯酸8-12、丙烯酸酯10-12、丙烯酸甲酯10-12、丙烯酸丁酯10-12、叔碳酸乙烯酯8-12、丙烯酸六氟丁酯8-10、甲基丙烯酸丁酯8-10、甲基丙烯酸乙酯8-10、过氧化二苯甲酰0.3-0.5和溶剂醋酸丁酯 80-120；制备方法为在氮气保护气氛下，将反应原料加入到醋酸丁酯溶剂中，搅拌，加热到140-150℃，将引发剂加入反应釜中，搅拌，保温反应3-4小时，降温至90℃以上，过滤，得到。
本发明的优点：
本发明由于采用氯化聚乙烯树脂、聚烯烃弹性体POE 8480和三元乙丙橡胶高分子材料并用作为本发明的基础材料，同时增加了辅料聚四氟乙烯、纳米陶土、苯丙乳液、聚酰亚胺和ECHO.A 噻二唑衍生物，解决了电缆材料不能满足在高温强腐蚀的环境下工作使用现状，具有低烟低卤阻燃型抗滴落的特性。
具体实施方式
    实施例1：
  低烟低卤阻燃型交联聚烯烃绝缘电缆料，各原料组分的重量份为：
氯化聚乙烯树脂                           30份
聚烯烃弹性体POE 8480                   12份
三元乙丙橡胶                            16份
抗滴落剂                                  3份
（可用抗滴落剂 GSCFR-631）
聚四氟乙烯                               6份
氯化石蜡                                 5份
纳米陶土                                65份
半补强炭黑                               5份
硬脂酸锌                                 5份
偏苯三酸三辛酯                           12份
聚酰亚胺                                 6份
ECHO.A 噻二唑衍生物                       1份
低烟低卤阻燃型交联聚烯烃绝缘电缆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，将氯化聚乙烯树脂、聚烯烃弹性体POE 8480和三元乙丙橡胶混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入抗滴落剂、聚四氟乙烯、氯化石蜡、纳米陶土、半补强炭黑、硬脂酸锌、偏苯三酸三辛酯、聚酰亚胺和ECHO.A 噻二唑衍生物，常温下低速搅拌3-5分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度130-150℃，得到成品。
本发明的电缆料与现有的电缆料一般性能比较
项         目 单     位 现有电缆料 本发明电缆料
原始断裂强度 MPa  不小于 5.00 11.10
原始断裂伸长率 %  不小于 250 417
耐158℃×168h老化后 ---- ---- -----
K1 %   不小于 碳化 128
K2 %  不小于 碳化 97
K1 %  不小于 90 93
K2 %  不小于 60 79
绝缘电阻 欧姆·厘米≥ 1015 1017

Claims (2)

1.一种低烟低卤阻燃型交联聚烯烃绝缘电缆料，其特征在于各原料组分的重量份为：
氯化聚乙烯树脂                           25-35份
聚烯烃弹性体POE 8480                     10-15份
三元乙丙橡胶                             10-20份
抗滴落剂                                 3-8份
聚四氟乙烯                               5-10份
氯化石蜡                                 3-8份
纳米陶土                                 60-65份
半补强炭黑                               3-8份
硬脂酸锌                                 3-5份
偏苯三酸三辛酯                           10-15份
聚酰亚胺                                 5-8份
ECHO.A 噻二唑衍生物                      1-3份
一种如权利要求1所述的低烟低卤阻燃型交联聚烯烃绝缘电缆料的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份称取各原料，将氯化聚乙烯树脂、聚烯烃弹性体POE 8480和三元乙丙橡胶混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入抗滴落剂、聚四氟乙烯、氯化石蜡、纳米陶土、半补强炭黑、硬脂酸锌、偏苯三酸三辛酯、聚酰亚胺和ECHO.A 噻二唑衍生物，常温下低速搅拌3-5分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度130-150℃，得到成品。
2.根据权利要求1所述的低烟低卤阻燃型交联聚烯烃绝缘电缆料，其特征在于：所述的抗滴落剂采用  抗滴落剂 GSCFR-631。
CN 201210263665 2012-07-28 2012-07-28 一种低烟低卤阻燃型交联聚烯烃绝缘电缆料及其制备方法 Pending CN102816393A (zh)