CN102808490B - Abnormity exterior-wall heat insulation, decoration integrated link plate and preparation method thereof and process the mould of this product - Google Patents
Abnormity exterior-wall heat insulation, decoration integrated link plate and preparation method thereof and process the mould of this product Download PDFInfo
- Publication number
- CN102808490B CN102808490B CN201110144972.4A CN201110144972A CN102808490B CN 102808490 B CN102808490 B CN 102808490B CN 201110144972 A CN201110144972 A CN 201110144972A CN 102808490 B CN102808490 B CN 102808490B
- Authority
- CN
- China
- Prior art keywords
- layer
- link plate
- moderate soak
- soak layer
- steel bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of abnormity exterior-wall heat insulation, decoration integrated link plate and preparation method thereof and process the mould of this product.This integration link plate includes: moderate soak layer, and is wrapped in the structure sheaf matched with tundish temperature layer shape that moderate soak layer is peripheral；Described moderate soak layer medial surface is quadrangular frustum pyramid shaped, moderate soak layer lateral surface is parallel with medial surface and mutually the most across a certain distance, on moderate soak layer, the end, is with bottom outlet on described truncated rectangular pyramids in the same plane, moderate soak layer is gone to the bottom vertical with described truncated rectangular pyramids lower bottom hole plane, the frame that described structure sheaf is formed by fiberglass gridding cloth, it is positioned at the steel bar framework gone to the bottom at described fiberglass gridding cloth frame, and be filled in the coagulating layer that the glass chopped silk inside and outside fiberglass gridding cloth frame and steel bar framework is embedded in cement slurry and formed, described coagulating layer includes endosexine, extexine, upper bottom, lower bottom.Insulation and decoration of exterior wall are ideally combined by the present invention, achieve the economic benefit that significant technological progress is become reconciled.
Description
Technical field
The present invention relates to a kind of building element, particularly relate to a kind of abnormity exterior-wall heat insulation, decoration integrated link plate
And preparation method thereof and process this product mould.
Background technology
Currently, building energy conservation is surging forward in the world, and building energy conservation has been that building circle, the whole world is ripe through deep thinking
Consider later common choice.What first building energy conservation was referred to is the insulation problem of external wall, and this clause is
The compulsory execution clause of the Ministry of Construction, next to that the problem that link plate uses natural resources stone material in a large number.Present stage builds
Build exterior wall, insulation, the construction of decoration of exterior wall are substantially implemented step by step, thus reach firm, energy-conservation,
Attractive in appearance allow people pleasing building with art perfect adaptation.Just at present insulation below, the showing of decoration of exterior wall
Shape makees an analysis: first, the decoration of exterior wall of present stage generally can be divided into: swabbing, tiling and link plate
Three kinds of methods.The weak point that these three mode exists is respectively: swabbing exists fugitive color and easily corrodes
Problem, there is the insecure unsafe problems causing coming off of laminating in tiling, link plate then exists color and kind
The problem that class is dull, seam is many, efficiency of construction is low, on link plate, seam is many mainly by the material of stone material self
Property determine, the stone material specification of natural recovery can not be very big, cause the back of the body installed to hang steelframe intensive,
It is unfavorable for the decoration of skyscraper.These weak points not only bring the rising of building cost, also bring construction
The problem of inefficiency.Wherein there are two distinct issues to be: first, are stone used in the mode of link plate
Material is the limited resources in natural environment, a large amount of lithotomes use and put forward the recycling economy of wound at present, fill
The guiding theory of point Appropriate application natural resources is opposing and speed；Secondly, the problem of exterior-wall heat insulation, at present
The external wall outer insulation sheet material used in industry mainly has: EPS sheet and XPS plate, but both sheet material is all easy
Catch fire and easily drip molten material.Analyzing this several years skyscraper big fire accidents, ninety percent is to send out construction period according to statistics
Raw, closely related with XPS plate with external-wall heat-insulation material EPS sheet the most again.Shanghai high building 11.15 is especially big
Why injures and deaths are bigger for fire, and one of maximum reason is building thermal insulation material burning, causes big fire rapid
Spread to Zheng Dong building.Therefore, refusal polyurethane plate is directly entered site operation is wise move.Existing build
Building another distinct issues in construction is that insulation operation and external decoration operation are distinguished substantially, not only takes a lot of work, expense
Time, take material, at the construction field (site), many unsafe factors increase exposed insulation material bulk deposition without foundation
Add many idle works, if can both ideally be combined is development trend from now on.
Summary of the invention
It is an object of the invention to provide the insulation of a kind of exterior wall and the dress of exterior wall for prior art weak point
The special-shaped exterior-wall heat insulation that decorations operation is considered, decoration integrated link plate.
Second purpose of the present invention is to provide abnormity exterior-wall heat insulation, the manufacture method of decoration integrated link plate.
The 3rd purpose of the present invention is to provide abnormity exterior-wall heat insulation, decoration integrated link plate to process the mould of this product
Tool.
The present invention is by the following technical programs in realize: a kind of abnormity exterior-wall heat insulation, decoration integrated link plate,
It is characterized in that, it includes moderate soak layer, and be wrapped in moderate soak layer peripheral with tundish temperature layer shape
The structure sheaf that shape matches；Described moderate soak layer medial surface is quadrangular frustum pyramid shaped, upper and lower two ends of truncated rectangular pyramids
Hole is two similar rhombuses, and the line of centres of two bottom outlets is vertical with two bottom outlets, upper and lower two bottom outlet corresponding sides
The medial surface constituted is horn-like contraction by supreme base, bottom, and moderate soak layer lateral surface is put down with medial surface
The most across a certain distance, on moderate soak layer, the end, is with bottom outlet on described truncated rectangular pyramids in the same plane, middle for row and phase
Heat-insulation layer is gone to the bottom vertical with described truncated rectangular pyramids lower bottom hole plane, and described structure sheaf is formed by fiberglass gridding cloth
Frame, be positioned at and go to the bottom at the steel bar framework of described fiberglass gridding cloth frame and be filled in glass fibers
The coagulating layer institute that glass chopped silk inside and outside dimension grid cloth frame and steel bar framework is embedded in cement slurry
Composition, described coagulating layer includes endosexine, extexine, upper bottom, lower bottom.
Described structure sheaf is provided with ribs at truncated rectangular pyramids incline, and moderate soak layer is separated into four pieces by ribs.
On described truncated rectangular pyramids, Pedicellus et Pericarpium Trapae limit, the end and Pedicellus et Pericarpium Trapae limit are arc transition.
Described it is made up of the oblique line section tilted and circular arc line segment in horn-like its section line that is punctured into.
Described steel bar framework is by upper and lower a pair reinforcing steel bar frame matched with rhombus of going to the bottom, and between two reinforcing steel bar frames
Some dowels are formed.
Described steel bar framework lower floor steel bar welding is connected to built-in fitting, described rhombus horizontal diagonal line two lower side pre-
Embedded part is L-type angle steel, and the built-in fitting of rhombus horizontal diagonal line two upper side edge is band steel and connecting bolt.
Described heat-insulation layer is EPS molding foaming polystyrene board or XPS extruded plastic foam polystyrene board.
Described heat-insulation layer is that granular polystyrene mixes solidification layer with cement mortar.
A kind of abnormity exterior-wall heat insulation, the manufacture method of decoration integrated link plate: it is characterized in that, step is as follows:
Step one, prefabricated moderate soak layer, wherein:
When moderate soak layer is EPS molding foaming polystyrene board or XPS extruded plastic foam polystyrene board, by
Digit Control Machine Tool processes moderate soak layer by input program, cuts by truncated rectangular pyramids incline direction, and its cutting thickness is
The thickness of link plate ribs；
Moderate soak layer is granular polystyrene when mixing solidification layer with cement mortar, granular polystyrene and cement mortar
Percentage by weight is (6～8): 70；
Step 2, brushing remover inside link plate template, in link plate template, spray layer of glass short
Shredding and enhancing cement slurry, lay layer of glass grid cloth, and fiberglass gridding cloth is at the upper and lower end
The pre-allowance laid of upset is all left on limit, places the steel bar framework with built-in fitting at template position of going to the bottom,
Spray layer of glass chopped silk again and strengthen cement slurry, being wrapped in fiberglass gridding cloth and reinforcing steel bar frame
The lower reinforcing steel bar frame of frame, forms link plate endosexine；
Step 4, is placed on given position by the moderate soak layer being divided into four pieces made, reserves ribs
The space of plate, the side at moderate soak layer ribs is laid fiberglass gridding cloth, is sprayed one layer of glass fibers
Dimension chopped silk and enhancing cement slurry, to the most contour with moderate soak layer, form bottom and ribs under link plate；
Step 5, at lower bottom and moderate soak layer top layer and top layer, upper end spraying layer of glass chopped silk
And enhancing cement slurry, it is wrapped in upper reinforcing steel bar frame and the moderate soak layer upper surface of the steel bar framework of lower bottom,
Then fiberglass gridding cloth upset is laid, and shelves of not leaving a blank on link plate surface, by built-in fitting from glass
Fibrous mesh cloth is emerged in gap, and spraying layer of glass chopped silk and enhancing cement slurry form link plate
Extexine and upper bottom, then complete to make after general maintenance.
A kind of abnormity exterior-wall heat insulation, the mould processing this product of decoration integrated link plate, it is characterised in that
Die inside face is quadrangular frustum pyramid shaped, and upper and lower two bottom outlets of truncated rectangular pyramids are two similar rhombuses, two bottom outlets
The line of centres is vertical with two bottom outlets, upper and lower two bottom outlet corresponding sides constitute side by supreme base, bottom in
Horn-like contraction, upper bottom outlet two Pedicellus et Pericarpium Trapae limit arc transition, mould lateral surface parallel with medial surface and be separated by certain between
Away from, on mould on the end and described truncated rectangular pyramids bottom outlet in the same plane, mould is gone to the bottom and described truncated rectangular pyramids is gone to the bottom
Hole plane is vertical, and the periphery gone to the bottom is provided with frame, and the height of described frame is that the thickness of link plate is gone to the bottom with mould
Thickness sum.
The positive effect of the present invention is: the present invention propose special-shaped exterior-wall heat insulation, decoration integrated link plate and
Manufacture method and the mould of this product of processing, have the advantage that 1) warming plate is wrapped in coagulation structure layer
Centre, integration link plate material can complete in precast plant, and no longer there are exposed insulation material, warp in job site
The link plate fire rating detecting this structure reaches A level, keeps the safety in production secure, without potential safety hazard；2) exterior wall is protected
Temperature, architectural surface complete simultaneously, save operation and man-hour, reduction of erection time and quantities, are flying of a kind of matter
Jump；3) present invention uses specific glass fibre reinforced cement panel outsourcing insulation material, has high intensity,
Link plate size, up to more than 2.5 meters, is greatly reduced the back of the body and hangs the amount of steelframe, saved building cost；4) originally
Invention uses specific glass fibre reinforced cement panel to substitute lithotome, not only protects natural resources but also will not be right
Environment produces and pollutes, and meets current green, environmental protection, effectively utilizes the theory of natural resources.The present invention will protect
Gentle decoration of exterior wall ideally combines, and achieves the economic benefit that significant technological progress is become reconciled.
Accompanying drawing explanation
Fig. 1 is the structural representation of one embodiment of the invention.
Fig. 2 Fig. 1 embodiment A-A profile.
Fig. 3 is Fig. 1 embodiment steel bar framework schematic diagram.
Fig. 4 is Fig. 1 embodiment mould structure schematic diagram.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Fig. 1～Fig. 2 is the structural representation of one embodiment of the invention.In figure, a kind of abnormity exterior-wall heat insulation,
Decoration integrated link plate, it includes moderate soak layer 1, and be wrapped in moderate soak layer peripheral with tundish temperature
The structure sheaf 2 that layer shape matches；Described moderate soak layer 1 inner surface is quadrangular frustum pyramid shaped, the upper end of truncated rectangular pyramids
Hole 11, lower bottom hole 12 are two similar rhombuses, and the line of centres of two bottom outlets is vertical with two bottom outlets, upper bottom outlet
11, the medial surface 13 that lower bottom hole 12 corresponding sides are constituted is horn-like contraction by supreme base, bottom, described
It is made up of the oblique line section tilted and circular arc line segment in horn-like its cross section that is punctured into.Moderate soak layer 1 lateral surface
14 is parallel with medial surface and mutually the most across a certain distance, the end 18 and bottom outlet 11 on described truncated rectangular pyramids on moderate soak layer
In the same plane, moderate soak layer 1 is gone to the bottom 19 vertical with described truncated rectangular pyramids lower bottom hole 12 plane, described
Frame that structure sheaf 2 is formed by fiberglass gridding cloth 25, it is positioned at and goes to the bottom 19 at described fiberglass gridding
Steel bar framework 3 in cloth frame and being filled in inside and outside fiberglass gridding cloth 25 frame and steel bar framework 3
The coagulating layer that glass chopped silk is embedded in cement slurry is formed, described coagulating layer include endosexine 28,
Extexine 29, upper bottom 21, lower bottom 22.
The present invention takes following measure further: described structure sheaf 2 is provided with ribs 23 at truncated rectangular pyramids incline,
Moderate soak layer is separated into four pieces by ribs, and ribs can improve bulk strength and the rigidity of link plate.Described
On truncated rectangular pyramids, Pedicellus et Pericarpium Trapae limit, the end and Pedicellus et Pericarpium Trapae limit are arc transition, and arc transition can avoid stress to concentrate, and upper bottom outlet is used for pacifying
Dress cladding glass.
Described steel bar framework 3 is by the upper reinforcing steel bar frame 31 matched with rhombus of going to the bottom, lower reinforcing steel bar frame 32, and two steel
Some dowels 33 between muscle are formed, shown in Fig. 3.Described steel bar framework lower floor steel bar welding is connected to built-in fitting,
The built-in fitting of described rhombus horizontal diagonal line two lower side is L-type angle steel 34, on the upside of rhombus horizontal diagonal line two
The built-in fitting on limit is band steel 35 and connecting bolt 36, and the lifting link plate that is set to of built-in fitting provides conveniently, can
By L-type angle steel, suspension member is stood in the back of the body temporarily to hang on steelframe, fastening bolt again after being adjusted in place.
Described heat-insulation layer is EPS molding foaming polystyrene board or XPS extruded plastic foam polystyrene board, insulation
Plate may be used without granular polystyrene and mixes solidification layer with cement mortar, and granular polystyrene mixes with the weight of cement mortar
Than being (6～8): 70.
A kind of abnormity exterior-wall heat insulation, the manufacture method of decoration integrated link plate: the Pedicellus et Pericarpium Trapae of embodiment of the present invention link plate
Cornerwise a size of 2.50 meters * 2.60 meters of shape, belongs to big plate.
Making step is as follows:
Step one, prefabricated moderate soak layer, the moderate soak layer of the present embodiment is EPS molding foaming polyphenyl second
Alkene plate, is processed moderate soak layer by Digit Control Machine Tool by input program, cuts by truncated rectangular pyramids incline direction, and it is cut
Cut the thickness that thickness is link plate ribs；
Step 2, brushing remover inside link plate template, in link plate template, spray layer of glass short
Shredding and enhancing cement slurry, lay layer of glass grid cloth, and fiberglass gridding cloth is at the upper and lower end
The pre-allowance laid of upset is all left on limit, places the steel bar framework with built-in fitting at template position of going to the bottom,
Spray layer of glass chopped silk again and strengthen cement slurry, being wrapped in fiberglass gridding cloth and reinforcing steel bar frame
The lower reinforcing bar of frame, forms link plate inner surface；
Step 4, is placed on given position by the moderate soak layer being divided into four pieces made, reserves ribs
The space of plate, the side at moderate soak layer ribs is laid fiberglass gridding cloth, is sprayed one layer of glass fibers
Dimension chopped silk and enhancing cement slurry, to the most contour with moderate soak layer, form link plate and go to the bottom and ribs；
Step 5, go to the bottom and moderate soak layer top layer and top layer, the upper end spraying layer of glass chopped silk and
Strengthen cement slurry, be wrapped in upper reinforcing bar and the moderate soak layer upper surface of the steel bar framework gone to the bottom, then will
Fiberglass gridding cloth upset is laid, and shelves of not leaving a blank on link plate surface, by built-in fitting from glass fiber mesh
Lattice cloth is emerged in gap, and spraying layer of glass chopped silk and enhancing cement slurry form the lateral surface of link plate,
Complete to make after general maintenance.
A kind of abnormity exterior-wall heat insulation, the mould processing this product of decoration integrated link plate, Fig. 4 is that Fig. 1 is real
Execute example mould structure schematic diagram.In figure, mould 8 medial surface is quadrangular frustum pyramid shaped, the upper bottom outlet 81 of truncated rectangular pyramids,
Lower bottom hole 82 is two similar rhombuses, and the line of centres of two bottom outlets is vertical with two bottom outlets, upper bottom outlet 81, under
The medial surface 83 that bottom outlet 82 corresponding sides are constituted is horn-like contraction by supreme base, bottom, described in loudspeaker
Shape is punctured into its cross section and is made up of the oblique line section tilted and circular arc line segment, 81 liang of Pedicellus et Pericarpium Trapae limit arc transition of upper bottom outlet,
Mould 8 lateral surface 84 is parallel with medial surface 83 and mutually the most across a certain distance, the mould 8 upper end 85 and described four ribs
On platform, bottom outlet 81 is in the same plane, and mould 8 is gone to the bottom 86 vertical with described truncated rectangular pyramids lower bottom hole 82 plane,
Go to the bottom 86 periphery be provided with frame 87, the height of described frame be the thickness gone to the bottom of thickness and the mould of link plate it
With.Embodiment given by the present invention is abnormity link plate, therefore needs to use mould molding, and mould can use G R.G
Material makes.
Describe structure and the manufacture method of the present invention above in conjunction with drawings and Examples, be not intended that this
Bright restriction, in this area, according to real, those skilled in the art can show that needs are made adjustment, and wants in appended right
Various deformation or amendment is made all in protection domain in the range of asking.
Claims (10)
1. a special-shaped exterior-wall heat insulation, decoration integrated link plate, it is characterised in that it includes moderate soak layer, and is wrapped in the structure sheaf matched with moderate soak layer shape that moderate soak layer is peripheral；Described moderate soak layer medial surface is quadrangular frustum pyramid shaped, truncated rectangular pyramids upper, lower two bottom outlets are two similar Pedicellus et Pericarpium Trapae shapes, the line of centres of two bottom outlets is vertical with two bottom outlets, on, the medial surface that lower two bottom outlet corresponding sides are constituted is horn-like contraction by supreme base, bottom, moderate soak layer lateral surface is parallel with medial surface and mutually the most across a certain distance, on moderate soak layer, the end, is with bottom outlet on described truncated rectangular pyramids in the same plane, moderate soak layer is gone to the bottom vertical with described truncated rectangular pyramids lower bottom hole plane, the frame that described structure sheaf is formed by fiberglass gridding cloth, it is positioned at the steel bar framework gone to the bottom at described fiberglass gridding cloth frame, and be filled in the coagulating layer that the glass chopped silk inside and outside fiberglass gridding cloth frame and steel bar framework is embedded in cement slurry and formed, described coagulating layer includes endosexine, extexine, upper bottom, lower bottom.
Abnormity exterior-wall heat insulation, decoration integrated link plate the most according to claim 1, it is characterised in that described structure sheaf is provided with ribs at truncated rectangular pyramids incline, and moderate soak layer is separated into four pieces by ribs.
Abnormity exterior-wall heat insulation, decoration integrated link plate the most according to claim 1 and 2, it is characterised in that on described truncated rectangular pyramids, Pedicellus et Pericarpium Trapae limit, the end and Pedicellus et Pericarpium Trapae limit are arc transition.
Abnormity exterior-wall heat insulation, decoration integrated link plate the most according to claim 1 and 2, it is characterised in that described be made up of the oblique line section tilted and circular arc line segment in horn-like its section line that is punctured into.
Abnormity exterior-wall heat insulation, decoration integrated link plate the most according to claim 1 and 2, it is characterised in that described steel bar framework is by upper and lower a pair reinforcing steel bar frame matched with rhombus of going to the bottom, and the some dowels between two reinforcing steel bar frames are formed.
Abnormity exterior-wall heat insulation, decoration integrated link plate the most according to claim 1 and 2, it is characterized in that, described steel bar framework lower floor steel bar welding is connected to built-in fitting, the built-in fitting of described rhombus horizontal diagonal line two lower side is L-type angle steel, and the built-in fitting of rhombus horizontal diagonal line two upper side edge is band steel and connecting bolt.
Abnormity exterior-wall heat insulation, decoration integrated link plate the most according to claim 1 and 2, it is characterised in that described moderate soak layer is EPS molding foaming polystyrene board or XPS extruded plastic foam polystyrene board.
Abnormity exterior-wall heat insulation, decoration integrated link plate the most according to claim 1 and 2, it is characterised in that described moderate soak layer is that granular polystyrene mixes solidification layer with cement mortar.
Abnormity exterior-wall heat insulation, the manufacture method of decoration integrated link plate the most according to claim 1: it is characterized in that, step is as follows:
Step one, prefabricated moderate soak layer, wherein:
When moderate soak layer is EPS molding foaming polystyrene board or XPS extruded plastic foam polystyrene board, Digit Control Machine Tool processing moderate soak layer by input program, cut by truncated rectangular pyramids incline direction, its cutting thickness is the thickness of link plate ribs；
Moderate soak layer is granular polystyrene when mixing solidification layer with cement mortar, and granular polystyrene is (6～8) with the percentage by weight of cement mortar: 70；
Step 2, brushing remover inside link plate template, in link plate template, spray layer of glass chopped silk and strengthen cement slurry, lay layer of glass grid cloth, fiberglass gridding cloth all leaves the pre-allowance laid of upset on upper and lower base, places the steel bar framework with built-in fitting at template position of going to the bottom, then sprays layer of glass chopped silk and strengthen cement slurry, it is wrapped in the lower reinforcing steel bar frame of fiberglass gridding cloth and steel bar framework, forms link plate endosexine；
Step 3, the moderate soak layer being divided into four pieces made is placed on given position, reserve the space of deep floor, side at moderate soak layer ribs lays fiberglass gridding cloth, spraying layer of glass chopped silk and enhancing cement slurry, to the most contour with moderate soak layer, form bottom and ribs under link plate；
Step 4, at lower bottom and moderate soak layer top layer and top layer, upper end spraying layer of glass chopped silk and strengthen cement slurry, it is wrapped in upper reinforcing steel bar frame and the moderate soak layer upper surface of the steel bar framework of lower bottom, then fiberglass gridding cloth upset is laid, and shelves of not leaving a blank on link plate surface, built-in fitting is emerged from fiberglass gridding cloth gap, spraying layer of glass chopped silk and enhancing cement slurry form the extexine of link plate and upper bottom, then complete to make after general maintenance.
Abnormity exterior-wall heat insulation the most according to claim 1, the mould processing this product of decoration integrated link plate, it is characterized in that, die inside face is quadrangular frustum pyramid shaped, truncated rectangular pyramids upper, lower two bottom outlets are two similar Pedicellus et Pericarpium Trapae shapes, the line of centres of two bottom outlets is vertical with two bottom outlets, on, the side that lower two bottom outlet corresponding sides are constituted is horn-like contraction by supreme base, bottom, upper bottom outlet two Pedicellus et Pericarpium Trapae limit arc transition, mould lateral surface is parallel with medial surface and mutually the most across a certain distance, on mould, the end, is with bottom outlet on described truncated rectangular pyramids in the same plane, mould is gone to the bottom vertical with described truncated rectangular pyramids lower opening plane, the periphery gone to the bottom is provided with frame, the height of described frame is the thickness sum that the thickness of link plate is gone to the bottom with mould.