CN102806182A - 紫外光淋涂白底涂装的施工工艺 - Google Patents
紫外光淋涂白底涂装的施工工艺 Download PDFInfo
- Publication number
- CN102806182A CN102806182A CN201110146827XA CN201110146827A CN102806182A CN 102806182 A CN102806182 A CN 102806182A CN 201110146827X A CN201110146827X A CN 201110146827XA CN 201110146827 A CN201110146827 A CN 201110146827A CN 102806182 A CN102806182 A CN 102806182A
- Authority
- CN
- China
- Prior art keywords
- ultraviolet light
- showering
- construction process
- paint
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种紫外光淋涂白底涂装的施工工艺,包括以下步骤:素材处理、淋涂白底漆、红外流平、全固化和打磨做面漆。在素处理步骤之后还增加以下辊涂一道底漆和半固化步骤。本发明具有生产效率高,无浪费,固化速度快,打磨性好,耐侯性佳,表面效果好,附着力好,表面硬度佳,漆膜丰满度佳,不开裂等优点。
Description
技术领域
本发明涉及一种紫外光(UV)固化涂料,具体的说,是一种紫外光(UV)淋涂白底涂装的施工工艺,属于涂装的技术领域。
背景技术
目前紫外光(UV)固化涂料应用广泛,紫外光(UV)固化涂料在家具和卫浴的涂装工艺主要以喷涂和辊涂这两大类。
喷涂和辊涂这两类工艺的特点:表面流平好、施工方便、固化速度快等特点。
喷涂和辊涂的缺点:喷涂时浪费大、耐侯性差等,辊涂表面效果差,遮盖力差,生产麻烦等缺点。
提出亟待发明一种固化速度快,打磨性好,耐侯性佳,表面效果好,附着力好,表面硬度佳,漆膜丰满度佳,以及不开裂的施工方法。
发明内容
本发明的目的在于,提供一种紫外光(UV)淋涂白底涂装的施工工艺,以克服现有技术所存在的上述缺点和不足。
本发明所需要解决的技术问题,可以通过以下技术方案来实现:
一种紫外光淋涂白底涂装的施工工艺,其特征在于,包括以下步骤:
(a)素材处理:采用砂纸将素材打磨平整、清除毛刺;
(b)淋涂白底漆:用紫外光淋涂机淋涂白底漆,涂布量150~180g/m2;
(c)红外流平:用40℃~60℃红外线流平机过5~6min;
(d)全固化:才用紫外光干燥机进行紫外光照射,强度为300~350mj/m2,全固化时间为3至5秒;
(e)打磨做面漆。
根据本发明的一优选实施例,在所述步骤a和步骤b之间还增加以下步骤:
(a1)辊涂一道底漆:在所述素材表面用单辊一遍底漆,涂布量为10~15g/m2;
(a2)半固化:采用紫外光干燥机进行紫外光照射,强度为130~150mj/m2,半固化时间为3至5秒;
其中,步骤(a)中采用240号砂纸。
本发明的有益效果:
本发明采用上述技术方案,克服现有施工上所存在的喷涂时浪费大、耐侯性差等,辊涂表面效果差,遮盖力差,生产麻烦等缺点。
本发明的优点是生产效率高,无浪费,固化速度快,打磨性好,耐侯性佳,表面效果好,附着力好,表面硬度佳,漆膜丰满度佳,涂装后冷热循环(-20℃~50℃)五个循环后均不开裂等特点。
具体实施方式
以下结合具体实施例,对本发明作进一步说明。应理解,以下实施例仅用于说明本发明而非用于限定本发明的范围。
在本发明的上下文中,所述素材是指中密度板。
在本发明的实施例中采用的底漆、白底漆等均为市售产品,如上海富臣化工有限公司的产品底漆(型号1920)和白底漆(型号ZU24001等)。下列实施例中未注明具体条件的实验方法,通常按照常规条件,或厂商提供的条件进行。
实施例1
一种紫外光(UV)淋涂白底涂装的施工工艺,包括以下步骤:
(1)素材处理:采用240号砂纸将素材打磨平整、清除毛刺;
(2)辊涂一道底漆:在素材表面用单辊一遍底漆(上海富臣化工生产的牌号1920),涂布量10-15g\m2;
(3)半固化:采用紫外光干燥机,将能量调至130~150mj/m2,半固化时间为3至5秒;
(4)淋涂白底漆:用紫外光淋涂机淋涂白(上海富臣化工生产的牌号为ZU24001)底漆,涂布量150-180g\m2;
(5)红外流平:采用红外线流平机40℃~60℃,红外流平时间为5~6min;
(6)全固化:用紫外光干燥机,将能量调整至300~350mj/m2,全固化时间为3至5秒;
(7)打磨做面漆。
实施例2
(1)素材处理:采用240号砂纸将素材打磨平整、清除毛刺;
(2)淋涂白底漆:用紫外光淋涂机淋涂白底漆(上海富臣化工生产的牌号为ZU24001),涂布量150-180g\m2;
(5)红外流平:用40℃~60℃红外线流平机过5~6min;
(6)全固化:用紫外光干燥机,将能量调整至300~350mj/m2,全固化时间为3至5秒;
(7)打磨做面漆。
本发明的优点是生产效率高,无浪费,固化速度快,打磨性好,耐侯性佳,表面效果好,附着力好,表面硬度佳,漆膜丰满度佳,涂装后冷热循环五个循环后均不开裂(-20℃~50℃)等特点,结果参见表1。
表1本发明的检测
项目 | 硬度 | 打磨性 | 固化能量 | 涂布量 | 外观 | 附着力 |
指标 | ≥H | 良好 | 280~320mj/m2 | 120±20g/m2 | 乳白黏稠液 | 2级 |
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等同物界定。
Claims (3)
1.一种紫外光淋涂白底涂装的施工工艺,其特征在于,包括以下步骤:
(a)素材处理:采用砂纸将素材打磨平整、清除毛刺;
(b)淋涂白底漆:用紫外光淋涂机淋涂白底漆,涂布量150~180g/m2;
(c)红外流平:用40℃~60℃红外线流平机过5~6min;
(d)全固化:才用紫外光干燥机进行紫外光照射,强度为300~350mj/m2,全固化时间为3至5秒;
(e)打磨做面漆。
2.根据权利要求1所述的紫外光淋涂白底涂装的施工工艺,其特征在于,在所述步骤a和步骤b之间还增加以下步骤:
(a1)辊涂一道底漆:在所述素材表面用单辊一遍底漆,涂布量为10~15g/m2;
(a2)半固化:采用紫外光干燥机进行紫外光照射,强度为130~150mj/m2,半固化时间为3至5秒。
3.根据权利要求1所述的紫外光淋涂白底涂装的施工工艺,其特征在于,其中步骤(a)中采用240号砂纸。