CN102786317B - 一种利用花岗岩粉为原料的再生发泡材料 - Google Patents

一种利用花岗岩粉为原料的再生发泡材料 Download PDF

Info

Publication number
CN102786317B
CN102786317B CN201210286373.0A CN201210286373A CN102786317B CN 102786317 B CN102786317 B CN 102786317B CN 201210286373 A CN201210286373 A CN 201210286373A CN 102786317 B CN102786317 B CN 102786317B
Authority
CN
China
Prior art keywords
powder
granite
composition
percent
fluxing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210286373.0A
Other languages
English (en)
Other versions
CN102786317A (zh
Inventor
李传强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo Strong Vibration Technology Co ltd
Original Assignee
NINGBO ZHENQIANG BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO ZHENQIANG BUILDING MATERIAL CO Ltd filed Critical NINGBO ZHENQIANG BUILDING MATERIAL CO Ltd
Priority to CN201210286373.0A priority Critical patent/CN102786317B/zh
Publication of CN102786317A publication Critical patent/CN102786317A/zh
Application granted granted Critical
Publication of CN102786317B publication Critical patent/CN102786317B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用花岗岩粉为原料的再生发泡材料,所述再生发泡材料的配方组成为:花岗岩石粉70%~90%,助熔填料6%~25%,成孔料1%~5%,聚合料1%~5%。本再生发泡材料的制作方法,依次包括以下步骤:将上述粉料的颗粒细度控制在100目以上,并搅拌混合均匀,再将混合料压成所需颗粒状材料,然后将颗粒状材料堆放成型,并送入高温炉加温,冷却取出即为成品。本发明的优点在于,可充分消化花岗岩粉废料,可以解决花岗岩加工基地长期存在的环境严重污染问题,达到环保要求。本产品物理性能稳定,轻质,保温,抗压,抗折,可用于建筑墙体或外墙装饰,达到建筑减重和节能的目标,还有本产品还具有防火、防水、隔音的性能,可用于防火材料,墙体分隔材料。

Description

一种利用花岗岩粉为原料的再生发泡材料
技术领域
本发明涉及一种利用花岗岩粉废料为原料的再生发泡材料。
背景技术
花岗岩是一种岩浆在地表以下凝结形成的火成岩,主要成分是长石和石英。因为花岗岩是深成岩,常能形成发育良好、肉眼可辨的矿物颗粒,因而得名。花岗岩不易风化,颜色美观,外观色泽可保持百年以上,由于其硬度高、耐磨损,除了用作高级建筑装饰工程、大厅地面外,还是露天雕刻的首选之材。花岗岩的天然形成需要经过上百年甚至上千前,由于人类不断的开采,天然花岗石的储量正在不断地减少,而在花岗岩的加工过程中会产生许多花岗岩的废料和花岗岩粉,这些废料和花岗岩粉不加以利用的话,就会产生严重污染,破坏环境,制约经济的发展。传统的消化花岗岩粉的方法采用低温、混粘的工艺制作再生材料,其产品的密度大,达到2.5吨/m3,传热快,且在制作过程中需要添加化学粘剂。
还有一种申请号为200710142893.3名称为《利用花岗岩粉废料制人造复合板》的中国发明专利申请公开了一种新型的人造复合板,由花岗岩废料制成。配方包括树脂、固化剂、促进剂、花岗岩粉、碎石颗粒等等。该人造复合板,样式多,且长度可以做到足够大,从而可以应用于各种场所。但由于所述人造复合板的配方中使用了易燃或有毒的化学制剂,对人体会造成伤害,且密度大,份量重,运输和安装均不方便,又不易保温,而且也不可重复利用。因此,该复合板的结构还需作进一步改进。
发明内容
本发明所要解决的技术问题是针对上述现有技术现状而提供一种保温、防火、重量轻且环保的利用花岗岩粉为原料的再生发泡材料。
本发明解决上述技术问题所采用的技术方案为:本利用花岗岩粉为原料的再生发泡材料,其特征在于:本再生发泡材料的配方组成为:花岗岩粉为70%~90%,助熔填料为6%~25%,成孔料为1%~5%,聚合料为1%~5%,上述的百分比为质量百分比。
作为改进,所述助熔填料可选择为滑石粉、硅微粉、硅灰石料、云母粉、双飞粉中的任意二种与长石粉相组合的组合物。
作为改进,所述组合物的组份比可优选为:A∶B∶C=5∶1.5∶1.5,其中A表示长石粉,B为滑石粉、硅微粉、硅灰石料、云母粉、双飞粉中的一种,C为滑石粉、硅微粉、硅灰石料、云母粉、双飞粉中的一种,且B和C为不相同的二种材料。
作为改进,所述成孔料可优选为硅藻土,钛白粉,碳化硅,碳酸钙,碳酸钡中的任意二种组合物。
再改进,所述组合物的组份比可选择为1∶1。
作为改进,所述聚合料可选择为粘土、膨润土、硼砂的组合物。
再改进,所述组合物的组份比可优选为粘土∶膨润土∶硼砂=1∶1∶1。
与现有技术相比,本发明的优点在于:本发明的再生发泡材料具有以下产品特性:
(1)所有原料为无机材料,无化学污染。
(2)高温烧成,耐高温1100度以上,耐火A级。
(3)蜂窝状闭孔结构,不透气,不透水,导热慢。防水,隔音,保温。
(4)密度范围0.3吨/m3~1.2吨/m3,抗压抗折,物理性良好。
(5)可重复利用,废弃料重新配料后依然可以烧成。
根据上述特征,本发明产品的优点在于,可充分消化花岗岩粉废料,可以解决花岗岩加工基地长期存在的环境严重污染问题,达到环保要求。本产品物理性能稳定,轻质,保温,抗压,抗折,可用于建筑墙体或外墙装饰,达到建筑减重和节能的目标。还有本产品还具有防火、防水、隔音的性能,可用于防火材料,墙体分隔材料。
具体实施方式
以下结合实施例对本发明作进一步详细描述,以下所指的百分比均为质量百分比;
实施例一,本实施例的利用花岗岩粉为原料的再生发泡材料的配方组成为花岗岩粉70%,助熔填料22%,成孔料3%,聚合料5%。所述助熔填料为长石粉料,滑石粉,硅微粉组合物,其比例为5∶1.5∶1.5,所述成孔料为硅藻土,碳化硅组合物,其比例为1∶1,所述聚合料为粘土,膨润土,硼砂组合物,其比例为1∶1∶1。
根据上述配方,再生发泡材料的制作方法,依次包括以下步骤:
一、经过粉碎、筛选将花岗岩粉、助熔填料、成孔料、聚合料粉末的颗粒细度控制为100目以上;
二、将花岗岩粉、助熔填料、成孔料、聚合料粉末搅拌混合均匀制成混合料,再将混合料通过模压或滚压制成所需的颗粒状材料;
三、将颗料状材料放入所需形状的模体中,堆放成型;
四、然后将堆放成型的材料同模体一起放入高温炉中缓慢加热,直到高温炉的温度达到1100~1400度,并在温度为1100~1400度的高温炉中进行加温50~70分钟,优选为60分钟,加温完成后从高温炉中取出,自然冷却11~13小时后从模体中取出,即为再生发泡材料成品。
实施例二,本实施例的利用花岗岩粉为原料的再生发泡材料的配方为:花岗岩粉76%,助熔填料18%,成孔料3%,聚合料3%。所述助熔填料为长石粉料,硅灰石料,云母粉组合物,其比例为5∶1.5∶1.5,所述成孔料为硅藻土,碳酸钡组合物,其比例为1∶1,所述聚合料为粘土,膨润土,硼砂组合物,其比例为1∶1∶1。
根据上述配方,再生发泡材料的制作方法,依次包括以下步骤:
一、经过粉碎、筛选将花岗岩粉、助熔填料、成孔料、聚合料粉末的颗粒细度控制为100目以上;
二、将花岗岩粉、助熔填料、成孔料、聚合料粉末搅拌混合均匀制成混合料,再将混合料通过模压或滚压制成所需的颗粒状材料;
三、将颗料状材料放入所需形状的模体中,堆放成型;
四、然后将堆放成型的材料同模体一起放入高温炉中缓慢加热,直到高温炉的温度达到1100~1400度,并在温度为1100~1400度的高温炉中进行加温50~70分钟,优选为60分钟,加温完成后从高温炉中取出,自然冷却11~13小时后从模体中取出,即为再生发泡材料成品。
实施例三,本实施例的利用花岗岩粉为原料的再生发泡材料的配方为:花岗岩粉75%,助熔填料15%,成孔料4%,聚合料6%。所述助熔填料为长石粉料,云母粉,双飞粉组合物,其比例依次为5∶1.5∶1.5,所述成孔料为钛白粉,碳化硅组合物,其比例为1∶1,所述聚合料为粘土,膨润土,硼砂组合物,其比例为1∶1∶1。
根据上述配方,再生发泡材料的制作方法,依次包括以下步骤:
一、经过粉碎、筛选将花岗岩粉、助熔填料、成孔料、聚合料粉末的颗粒细度控制为100目以上;
二、将花岗岩粉、助熔填料、成孔料、聚合料粉末搅拌混合均匀制成混合料,再将混合料通过模压或滚压制成所需的颗粒状材料;
三、将颗料状材料放入所需形状的模体中,堆放成型;
四、然后将堆放成型的材料同模体一起放入高温炉中加热,直到高温炉的温度达到1100~1400度,并在温度为1100~1400度的高温炉中进行加温50~70分钟,优选为60分钟,加温完成后从高温炉中取出,自然冷却11~13小时后从模体中取出,即为再生发泡材料成品。该再生发泡材料可加工成外墙保温砖或保温板,也可作为室内分隔的墙砖等。

Claims (1)

1.一种利用花岗岩粉为原料的再生发泡材料,其特征在于:该再生发泡材料的配方组成为:花岗岩粉为70%~90%,助熔填料为6%~25%,成孔料为1%~5%,聚合料为1%~5%,上述的百分比为质量百分比;
所述助熔填料为滑石粉、硅微粉、硅灰石料、云母粉、双飞粉中的任意二种与长石粉相组合的组合物;助熔填料组合物的组份比为:A∶B∶C=5∶1.5∶1.5,其中A表示长石粉,B为滑石粉、硅微粉、硅灰石料、云母粉、双飞粉中的一种,C为滑石粉、硅微粉、硅灰石料、云母粉、双飞粉中的一种,且B和C为不相同的二种材料;所述成孔料为硅藻土,钛白粉,碳化硅,碳酸钙,碳酸钡中的任意二种组合物;成孔料组合物的组份比为1∶1;所述聚合料为粘土、膨润土、硼砂的组合物;聚合料组合物的组份比为粘土∶膨润土∶硼砂=1∶1∶1。
CN201210286373.0A 2012-08-13 2012-08-13 一种利用花岗岩粉为原料的再生发泡材料 Expired - Fee Related CN102786317B (zh)