CN102775107A - 一种利用沙漠沙作为骨料的新型渗水材料及其制备方法和应用 - Google Patents

一种利用沙漠沙作为骨料的新型渗水材料及其制备方法和应用 Download PDF

Info

Publication number
CN102775107A
CN102775107A CN2012102387560A CN201210238756A CN102775107A CN 102775107 A CN102775107 A CN 102775107A CN 2012102387560 A CN2012102387560 A CN 2012102387560A CN 201210238756 A CN201210238756 A CN 201210238756A CN 102775107 A CN102775107 A CN 102775107A
Authority
CN
China
Prior art keywords
aggregate
desert sand
desert
seepage material
novel seepage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102387560A
Other languages
English (en)
Other versions
CN102775107B (zh
Inventor
郝亮
赵建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hang Jin Qi Yi Jia Environmental Management Co., Ltd.
Original Assignee
MIAO GENXI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MIAO GENXI filed Critical MIAO GENXI
Priority to CN201210238756.0A priority Critical patent/CN102775107B/zh
Publication of CN102775107A publication Critical patent/CN102775107A/zh
Application granted granted Critical
Publication of CN102775107B publication Critical patent/CN102775107B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用沙漠沙作为骨料的新型渗水材料及其制备方法和应用，其特征在于按重量份所述新型渗水材料由以下组分组成：沙漠沙70-95，水性高分子粘结剂1-10，无机粘结剂2-10，着色剂0-3。上述新型渗水材料的制备方法，是将沙漠沙、无机粘结剂、着色剂，水性高分子粘结剂搅拌均匀；注入模具中；使用加压带振动成型工艺制备透水性路面透水砖、透水板。本发明利用沙漠原沙，变废为宝；与树脂型透水砖相比，价格低廉，透水性良好；环保型粘结剂：无毒、无味、无污染；应用领域广泛：制备透水砖，铺设于人行道、公园和住宅小区等路面形成透水层，利于地下水循环。

Description

一种利用沙漠沙作为骨料的新型渗水材料及其制备方法和应用
技术领域
本发明属于建筑材料领域，尤其涉及一种利用沙漠沙作为骨料的新型渗水材料及其制备方法和应用。
背景技术
目前，由于城市生态环境发展的需要，城市地面逐渐由水泥、柏油等不透水的材料覆盖改变为透水性路面材料覆盖。传统方法采用大颗粒骨架和水泥组成或采用人工处理沙和高分子粘结剂组成。水泥透水砖要么透水率不高，要么透水性能可以，但抗压强度不高，这二方面性能难兼顾；用高分子粘结剂、人工处理沙透水砖成本高，无法大范围推广。沙漠沙是目前较难高附加值利用的一种废弃物，全世界陆地面积为1.62亿平方千米，其中三分之一为荒漠地，而且每年以6万平方千米的速度扩大；中国沙漠面积128万平方千米，占全国陆地面积的13%。防沙、治沙、用沙、变沙为宝已成为亟待解决的问题。
发明内容
本发明所要解决的技术问题是提供一种利用沙漠沙作为骨料的新型渗水材料及其制备方法和应用，此渗水材料利用沙漠原沙，成本低廉、制备工艺简单；用于透水性铺装路面，透水效果好，抗压强度高。
本发明所要解决的技术问题是通过以下技术方案来实现的：
一种利用沙漠沙作为骨料的新型渗水材料，其特征在于按重量份所述新型渗水材料由以下组分组成：沙漠沙70-95，水性高分子粘结剂1-10，无机粘结剂2-10，着色剂0-3。
所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于按重量份所述新型渗水材料由以下组分组成：沙漠沙80-90，水性高分子粘结剂3-6，无机粘结剂5-8，着色剂1-2。
所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：所述沙漠沙为库布其沙漠沙，其沙粒粒径为40-120目。
所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：所述无机粘结剂为硅酸盐水泥、水玻璃或其组合物。
所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：水性高分子粘结剂为水性环氧树脂、聚醋酸乙烯树脂、聚乙烯醇或其组合。
所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：着色剂选自中铬黄、钼铬大红类无机颜料。
所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：所述的硅酸盐水泥标号为42.5；水玻璃密度为1.36-1.50g/cm3。
上述的利用沙漠沙作为骨料的新型渗水材料的制备方法，由以下步骤组成：
（a）将沙漠沙、无机粘结剂、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入水性高分子粘结剂搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。在制备过程中，使用加压带振动成型工艺才能保证成型的透水砖体有足够的结构强度，成型激振力大于3吨。
上述的利用沙漠沙作为骨料的新型渗水材料的应用，所述新型渗水材料在制备透水性铺装材料过程中的应用。
所述新型渗水材料用于制备透水性路面透水砖、透水板。
本发明有以下有益效果：
本发明利用沙漠原沙，变废为宝；与树脂型透水砖相比，价格低廉，透水性良好；环保型粘结剂：无毒、无味、无污染；应用领域广泛：制备透水砖，铺设于人行道、公园和住宅小区等路面形成透水层，利于地下水循环。
本发明制备的新型渗水材料成型过程中的作用原理为：
首先，水泥水化与聚合物成膜同时进行，最后形成水泥浆与聚合物膜相互交织在一起的互穿网络结构，从而改善了浆体的力学性能和耐久性；其次，由于固化后树脂的微相分离，水性树脂中亲水基团倾向于分布在树脂膜的外表面，使得树脂覆膜透水砖的外表面具有亲水特性；再次，渗水产品固化成型过程中，库不其沙漠沙具有粒径，且存在一定圆球度，之间形成相互贯通的细小管状通道，当水同该通道接触时，由于该高分子树脂的亲水特性，水迅速浸润管壁，管中液面呈凹形，形成的弯曲液面产生的附加压力指向细管，促进水的通过。
具体实施方式
实施例1
准确称量原料（Kg）：库布其沙漠沙85，硅酸盐水泥5，水玻璃5，水性环氧树脂粘结剂3，聚醋酸乙烯粘结剂1，着色剂钼铬大红1。
制备方法：
（a）将沙漠沙、无机粘结剂、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入水性高分子粘结剂搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。
所述新型渗水材料用于制备透水性路面透水砖。
水性环氧树脂粘结剂，优选双酚A型环氧树脂，例如双酚A型环氧树脂E-44，E-42，E-35，E-31，E-20，E-14，E-12，E-06，E-03之一或其任意组合。
对比例1
取普通石英砂85g，硅酸盐水泥5g，水玻璃5g，水性环氧粘结剂3，聚醋酸乙烯粘结剂1，着色剂钼铬大红1，混合后通过模具成型，制备成路面砖。
对比例2
取库布其筛分沙漠沙85g，硅酸盐水泥10g，着色剂1g，混合后通过模具成型，制备成路面砖。
对比例3
取库布其筛分沙漠沙85g，硅酸盐水泥5g，水玻璃5g，市场水性环氧粘结剂4g，着色剂钼铬大红1g，混合后通过模具成型，制备成路面砖。
与普通砖相比，实施例砖的抗压强度显著提高。下表1为性能结果：
表1  实施例1与各对比例之间的路面砖性能对比
Figure BDA0000187137461
实施例2
准确称量原料（Kg）：库布其沙漠沙80，水性环氧树脂3，硅酸盐水泥2、水玻璃1，中铬黄1。
制备方法：
（a）将沙漠沙、硅酸盐水泥、水玻璃、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入水性高分子粘结剂搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。
所述新型渗水材料用于制备透水性路面透水砖。
水性环氧树脂粘结剂，优选双酚A型环氧树脂，例如双酚A型环氧树脂E-44，E-42，E-35，E-31，E-20，E-14，E-12，E-06，E-03之一或其任意组合。
实施例3
准确称量原料（Kg）：库布其沙漠沙90，水性环氧树脂3、聚醋酸乙烯树脂3，硅酸盐水泥8、钼铬大红2。
制备方法：
（a）将沙漠沙、硅酸盐水泥、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入水性环氧树脂和聚醋酸乙烯树脂搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。
所述新型渗水材料用于制备透水性路面透水砖。
水性环氧树脂粘结剂，优选双酚A型环氧树脂，例如双酚A型环氧树脂E-44，E-42，E-35，E-31，E-20，E-14，E-12，E-06，E-03之一或其任意组合。
实施例4
准确称量原料（Kg）：库布其沙漠沙70，聚醋酸乙烯树脂5，水玻璃2、钼铬大红1。
制备方法：
（a）将沙漠沙、水玻璃、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入聚醋酸乙烯树脂搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。
所述新型渗水材料用于制备透水性路面透水板。
水性环氧树脂粘结剂，优选双酚A型环氧树脂，例如双酚A型环氧树脂E-44，E-42，E-35，E-31，E-20，E-14，E-12，E-06，E-03之一或其任意组合。
实施例5
准确称量原料（Kg）：库布其沙漠沙95，聚乙烯醇10，硅酸盐水泥6、水玻璃4，钼铬大红3。
制备方法：
（a）将库布其沙漠沙、水玻璃、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入聚乙烯醇搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。
所述新型渗水材料用于制备透水性路面透水板。
水性环氧树脂粘结剂，优选双酚A型环氧树脂，例如双酚A型环氧树脂E-44，E-42，E-35，E-31，E-20，E-14，E-12，E-06，E-03之一或其任意组合。
实施例6
准确称量原料（Kg）：库布其沙漠沙95，水性环氧树脂3、聚醋酸乙烯树脂3、聚乙烯醇4，硅酸盐水泥5、水玻璃5，钼铬大红3。
制备方法：
（a）将库不其沙漠沙、水玻璃、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入聚乙烯醇搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。
所述新型渗水材料用于制备透水性路面透水板。
水性环氧树脂粘结剂，优选双酚A型环氧树脂，例如双酚A型环氧树脂E-44，E-42，E-35，E-31，E-20，E-14，E-12，E-06，E-03之一或其任意组合。

Claims (10)

1.一种利用沙漠沙作为骨料的新型渗水材料，其特征在于按重量份所述新型渗水材料由以下组分组成：沙漠沙 70-95，水性高分子粘结剂1-10，无机粘结剂 2-10，着色剂 0-3。
2.如权利要求1所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于按重量份所述新型渗水材料由以下组分组成：沙漠沙 80-90，水性高分子粘结剂 3-6，无机粘结剂 5-8，着色剂 1-2。
3.如权利要求1或2所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：所述沙漠沙为库布其沙漠沙，其沙粒粒径为40-120目。
4.如权利要求1或2所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：所述无机粘结剂为硅酸盐水泥、水玻璃或其组合物。
5.如权利要求1或2所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：水性高分子粘结剂为水性环氧树脂、聚醋酸乙烯树脂、聚乙烯醇或其组合。
6.如权利要求1或2所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：着色剂选自中铬黄、钼铬大红类无机颜料。
7.如权利要求4所述的利用沙漠沙作为骨料的新型渗水材料，其特征在于：所述的硅酸盐水泥标号为42.5；水玻璃密度为1.36-1.50g/cm3。
8.一种如权利要求1-7之一所述的利用沙漠沙作为骨料的新型渗水材料的制备方法，由以下步骤组成：
（a）将沙漠沙、无机粘结剂、着色剂，加入到水泥胶砂搅拌机中搅拌均匀；
（b）加入水性高分子粘结剂搅拌均匀；
（c）将搅拌好的上述原料注入模具中；
（d）使用加压带振动成型工艺保证新型渗水材料成型，常温养护24小时，然后脱模。
9.一种如权利要求1-8之一所述的利用沙漠沙作为骨料的新型渗水材料的应用，所述新型渗水材料在制备透水性铺装材料过程中的应用。
10.如权利要求9所述的利用沙漠沙作为骨料的新型渗水材料的应用，所述新型渗水材料用于制备透水性路面透水砖、透水板。
CN201210238756.0A 2012-07-10 2012-07-10 一种利用沙漠沙作为骨料的渗水材料及其制备方法和应用 Active CN102775107B (zh)