CN102719089A - 双酚a型磷酸酯改性的尼龙合金材料 - Google Patents
双酚a型磷酸酯改性的尼龙合金材料 Download PDFInfo
- Publication number
- CN102719089A CN102719089A CN2012101988550A CN201210198855A CN102719089A CN 102719089 A CN102719089 A CN 102719089A CN 2012101988550 A CN2012101988550 A CN 2012101988550A CN 201210198855 A CN201210198855 A CN 201210198855A CN 102719089 A CN102719089 A CN 102719089A
- Authority
- CN
- China
- Prior art keywords
- bisphenol
- alloy material
- parts
- nylon alloy
- modified nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种双酚
A
型磷酸酯改性的尼龙合金材料,属于高分子材料技术领域。其是由以下重量份数的原料组成:尼龙
11
树脂
40
~
47
份;聚乙烯树脂
16
~
24
份;偶联剂
0.4
~
0.9
份;填料
15
~
21
份;磷酸酯
9
~
16
;抗氧剂
0.2
~
0.7
份;玻璃纤维
20
~
26
份;表面改性剂
0.4
~
0.7
份。优点:其拉伸强度大于
150MPa
,弯曲强度大于
220MPa,
悬臂梁缺口冲击强度大于
24kj/m
2
,
熔融指数大于
26g/10min
,阻燃达到
V-0
(
UL-94-3mm
);由于不含有卤素,因而可体现环保与安全。
Description
技术领域
本发明属于高分子材料技术领域,具体涉及一种双酚A型磷酸酯改性的尼龙合金材料。
背景技术
目前,对电子电器、家用电器、建筑材料都要求具有阻燃效果,通常的做法是向材料中添加卤素类阻燃剂,而卤素类阻燃剂燃烧时容易形成有毒烟雾,有失环保并且存在损及人体健康之虞。而磷酸酯被公认为安全且阻燃的改性材料,鉴此,利用磷酸酯对尼龙材料改性具有积极意义,下面将要介绍的技术方案便是在这种背景下产生的。
发明内容
本发明的任务在于提供一种不含有卤素而藉以体现环保安全和有助于保障理想的强度的双酚A型磷酸酯改性的尼龙合金材料。
本发明的任务是这样来完成的,一种双酚A型磷酸酯改性的尼龙合金材料,其是由以下重量份数的原料组成:
在本发明的一个实施例中,所述的尼龙11树脂为熔点在200℃的树脂。
在本发明的另一个实施例中,所述的聚乙烯树脂为中密度聚乙烯。
在本发明的又一个实施例中,所述的偶联剂为硅烷偶联剂。
在本发明的再一个实施例中,所述的填料为经过表面处理的氢氧化镁。
在本发明的还有一个实施例中,所述的磷酸酯为双酚A四苯基二磷酸酯。
在本发明的更而一个实施例中,所述的抗氧剂为2,2-亚甲基双(4-甲基-6-叔丁基酚)。
在本发明的进而一个实施例中,所述的玻璃纤维为长度3mm的无碱短切玻璃纤维。
在本发明的又更而一个实施例中,所述的表面改性剂为双硬脂酸酰胺。
本发明提供的双酚A型磷酸酯改性的尼龙合金材料的拉伸强度大于150MPa,弯曲强度大于220MPa,悬臂梁缺口冲击强度大于24kj/m2, 熔融指数大于26g/10min,阻燃达到V-0(UL-94-3mm);由于不含有卤素,因而可体现环保与安全。
具体实施方式
实施例1:
按重量份数,熔点在200℃的树脂即尼龙11树脂45份,中密度聚乙烯树脂16份,偶联剂即硅烷偶联剂0.4份,填料即经过表面处理的氢氧化镁21份,磷酸酯即双酚A四苯基二磷酸酯9份,抗氧剂即2,2-亚甲基双(4-甲基-6-叔丁基酚)0.4份,长度为3mm的无碱短切玻璃纤维20份,表面改性剂即双硬脂酸酰胺0.4份。
实施例2:
按重量份数,熔点在200℃的树脂即尼龙11树脂40份,中密度聚乙烯树脂19份,偶联剂即硅烷偶联剂0.6份,填料即经过表面处理的氢氧化镁15份,磷酸酯即双酚A四苯基二磷酸酯11份,抗氧剂即2,2-亚甲基双(4-甲基-6-叔丁基酚)0.5份,长度为3mm的无碱短切玻璃纤维22份,表面改性剂即双硬脂酸酰胺0.7份。
实施例3:
按重量份数,熔点在200℃的树脂即尼龙11树脂47份,中密度聚乙烯树脂21份,偶联剂即硅烷偶联剂0.9份,填料即经过表面处理的氢氧化镁18份,磷酸酯即双酚A四苯基二磷酸酯14份,抗氧剂即2,2-亚甲基双(4-甲基-6-叔丁基酚)0.7份,长度为3mm的无碱短切玻璃纤维36份,表面改性剂即双硬脂酸酰胺0.6份。
实施例4:
按重量份数,熔点在200℃的树脂即尼龙11树脂42份,中密度聚乙烯树脂24份,偶联剂即硅烷偶联剂0.7份,填料即经过表面处理的氢氧化镁20份,磷酸酯即双酚A四苯基二磷酸酯16份,抗氧剂即2,2-亚甲基双(4-甲基-6-叔丁基酚)0.6份,长度为3mm的无碱短切玻璃纤维24份,表面改性剂即双硬脂酸酰胺0.5份。
由上述实施例1至4得到的双酚A型磷酸酯改性的尼龙合金材料经测试具有下表所示的技术效果:
Claims (9)
1.一种双酚A型磷酸酯改性的尼龙合金材料,其特征在于其是由以下重量份数的原料组成:
尼龙11树脂 40~47份;聚乙烯树脂 16~24份;偶联剂 0.4~0.9份;填料 15~21份;磷酸酯 9~16;抗氧剂 0.2~0.7份;玻璃纤维 20~26份;表面改性剂 0.4~0.7份。
2.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的尼龙11树脂为熔点在200℃的树脂。
3.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的聚乙烯树脂为中密度聚乙烯。
4.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的偶联剂为硅烷偶联剂。
5.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的填料为经过表面处理的氢氧化镁。
6.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的磷酸酯为双酚A四苯基二磷酸酯。
7.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的抗氧剂为2,2-亚甲基双(4-甲基-6-叔丁基酚)。
8.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的玻璃纤维为长度3mm的无碱短切玻璃纤维。
9.根据权利要求1所述的双酚A型磷酸酯改性的尼龙合金材料,其特征在于所述的表面改性剂为双硬脂酸酰胺。