CN102674774A - 一种弹性抗裂抹面砂浆及其制备工艺 - Google Patents
一种弹性抗裂抹面砂浆及其制备工艺 Download PDFInfo
- Publication number
- CN102674774A CN102674774A CN2012101661996A CN201210166199A CN102674774A CN 102674774 A CN102674774 A CN 102674774A CN 2012101661996 A CN2012101661996 A CN 2012101661996A CN 201210166199 A CN201210166199 A CN 201210166199A CN 102674774 A CN102674774 A CN 102674774A
- Authority
- CN
- China
- Prior art keywords
- cracking resistance
- plastering mortar
- parts
- cement
- elasticity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种弹性抗裂抹面砂浆及其制备工艺，属于弹性抗裂抹面砂浆及其制备工艺技术领域。包括以下质量份数的原料：水泥28-45份、建筑用砂45-60份、胶粉2-4份、聚氨酯硬质泡沫塑料粉末2-10份、抗裂纤维0.05-0.1份、纤维素醚0.2-0.5份。工艺：将水泥28-45份、建筑用砂45-60份、胶粉2-4份、聚氨酯硬质泡沫塑料粉末2-10份、抗裂纤维0.05-0.1份、纤维素醚0.2-0.5份置于混合机内混合均匀；2）、将步骤1）的混合物料加水搅拌均匀，混合物料与水的质量比为：100：（40-70），即得弹性抗裂抹面砂浆。本发明具有一定的弹性及柔韧性，能有效避免墙体开裂，能够增加施工性及湿粘性，提高施工效率。
Description
技术领域
本发明涉及一种弹性抗裂抹面砂浆及其制备工艺，属于弹性抗裂抹面砂浆及其制备工艺技术领域。
背景技术
在建筑施工中通常需要在建筑物和构件表面以及基底材料的表面刮涂抹面砂浆，以保护基层以及防止墙体开裂，而墙体一旦开裂就存在渗漏的问题。
目前硬质聚氨酯泡沫塑料作为一种保温材料在外墙保温、家电行业中得到了广泛的应用，不论是生产、建筑施工还是旧家电淘汰过程中都会产生大量的不可再生的聚氨酯泡沫塑料废料，这些废料不论是以掩埋还是焚烧的方式处理都会污染环境。
发明内容
本发明的目的在于解决上述现有技术存在的不足之处，提供一种具有一定的弹性及柔韧性，能有效避免墙体开裂，能够增加施工性及湿粘性，提高施工效率的弹性抗裂抹面砂浆及其制备工艺。
一种弹性抗裂抹面砂浆，其特殊之处在于包括以下质量份数的原料：
水泥28-45份、建筑用砂45-60份、胶粉2-4份、硬质聚氨酯泡沫塑料粉末2-10份、抗裂纤维0.05-0.1份、纤维素醚0.2-0.5份；
为了保水增稠，提高施工性，减少细部裂纹,所述原料中还包括木质纤维0.2-0.6份；
为了降低水及水泥的用量，提高强度，所述原料中还包括减水剂0.2-0.5份；
所述水泥为硅酸盐水泥、矿渣硅酸盐水泥、火山灰质硅酸盐水泥、粉煤灰质硅酸盐水泥中的任意一种，强度不低于42.5强度等级；
所述建筑用砂为目数为50-100目的河砂或者水洗砂；
所述胶粉为VAE胶粉；
所述抗裂纤维为聚丙烯纤维、聚丙烯酰胺纤维、尼龙-66中的任意一种，纤维单丝长度为2-6mm；
所述的木质纤维长度为0.5-3mm；
所述的纤维素醚为羟丙基甲基纤维素醚或甲基纤维素；
所述硬质聚氨酯泡沫塑料粉末为生产、建筑施工以及旧家电淘汰过程中产生的聚氨酯硬质泡沫废料经过粉碎后的粉末，目数为40-80目；
所述减水剂为磺酸盐减水剂、聚羧酸盐减水剂中的任意一种； 一种弹性抗裂抹面砂浆的制备工艺，其特殊之处在于包括以下步骤：
1）、将水泥28-45份、建筑用砂45-60份、胶粉2-4份、硬质聚氨酯泡沫塑料粉末2-10份、抗裂纤维0.05-0.1份、木质纤维0.2-0.6份、纤维素醚0.2-0.5份、减水剂0.2-0.5份置于混合机内混合均匀；
2）、将步骤1）的混合物料加水搅拌均匀，混合物料与水的质量比为：100：（40-70），即得弹性抗裂抹面砂浆。
本发明的一种弹性抗裂抹面砂浆及其制备工艺，在不增加胶粉含量的情况下添加粉碎后的硬质聚氨酯泡沫塑料粉末使硬化后的抹面层不仅具有一定的弹性以及柔韧性，逐层渐变柔性释放应力，有效解决了墙体开裂情况，而且本抹面砂浆与基层的粘结强度高，施工性强，具有较高的应用价值以及社会意义。
具体实施方式
以下给出本发明的具体实施方式，用来对本发明做进一步的说明。
实施例1
本实施例的一种弹性抗裂抹面砂浆，包括以下质量份数的原料：
水泥28份、建筑用砂45份、胶粉2份、硬质聚氨酯泡沫塑料粉末2份、抗裂纤维0.05份、纤维素醚0.2份；
其中，水泥为硅酸盐水泥，强度不低于42.5强度等级，建筑用砂选用目数为50目的河砂，胶粉选用VAE胶粉，硬质聚氨酯泡沫塑料粉末为生产、建筑施工以及旧家电淘汰过程中产生的硬质聚氨酯泡沫塑料废料经过粉碎后的粉末，目数为40目，抗裂纤维为聚丙烯纤维，纤维单丝长度为2-6mm，纤维素醚为羟丙基甲基纤维素醚。
本实施例的一种弹性抗裂抹面砂浆，制备工艺如下：
1、将水泥28份、河砂45份、VAE胶粉2份、硬质聚氨酯泡沫塑料粉末2份、聚丙烯纤维0.05份、羟丙基甲基纤维素醚0.2份置于混合机内混合均匀；
2、将步骤1的混合物料加水搅拌均匀，混合物料与水的质量比为：100： 40，即得弹性抗裂抹面砂浆。
施工方法：抹到墙上后放置7-14天养护，7-14天后再进行下一步施工，本实施例的弹性抗裂抹面砂浆，原强度大于0.1MPa，湿强度大于0.1MPa。
实施例2
本实施例的一种弹性抗裂抹面砂浆，包括以下质量份数的原料：
水泥45份、建筑用砂60份、胶粉4份、硬质聚氨酯泡沫塑料粉末10份、抗裂纤维0.1份、纤维素醚0.5份；
其中，水泥为矿渣硅酸盐水泥，建筑用砂为目数为50-100目的水洗砂，
，胶粉为VAE胶粉，抗裂纤维为聚丙烯酰胺纤维，纤维单丝长度为2-6mm，
纤维素醚为甲基纤维素，硬质聚氨酯泡沫塑料粉末为生产、建筑施工以及旧家电淘汰过程中产生的硬质聚氨酯泡沫废料经过粉碎后的粉末，目数为40-80目；
本实施例的一种弹性抗裂抹面砂浆，制备工艺如下：
1、将矿渣硅酸盐水泥45份、水洗砂60份、VAE胶粉4份、硬质聚氨酯泡沫塑料粉末10份、聚丙烯酰胺纤维0.1份、甲基纤维素0.5份置于混合机内混合均匀；
2、将步骤1的混合物料加水搅拌均匀，混合物料与水的质量比为：100： 70，即得弹性抗裂抹面砂浆。
实施例3
本实施例的一种弹性抗裂抹面砂浆，包括以下质量份数的原料：
水泥35份、建筑用砂57份、胶粉4份、硬质聚氨酯泡沫塑料粉末4份、抗裂纤维0.08份、纤维素醚0.4份、木质纤维0.2份、减水剂0.2份；
其中，水泥采用火山灰质硅酸盐水泥，建筑用砂采用80目的河砂，胶粉采用VAE胶粉，抗裂纤维为尼龙-66，纤维单丝长度为4mm，纤维素醚为甲基纤维素，木质纤维长度为0.5mm，减水剂为磺酸盐减水剂。
一种弹性抗裂抹面砂浆的制备工艺，包括以下步骤：
1、将火山灰质硅酸盐水泥35份、河砂57份、VAE胶粉4份、硬质聚氨酯泡沫塑料粉末4份、尼龙-66 0.08份、木质纤维0.2份、甲基纤维素0.4份、磺酸盐减水剂0.2份置于混合机内混合均匀；
2、将步骤1的混合物料加水搅拌均匀，混合物料与水的质量比为：100：50，养护14天原强度为0.23MPa，湿强度为0.21MPa，即得弹性抗裂抹面砂浆。
实施例4
本实施例的一种弹性抗裂抹面砂浆，包括以下质量份数的原料：
水泥30.5份、建筑用砂52.7份、胶粉3份、硬质聚氨酯泡沫塑料粉末6份、聚丙烯纤维0.05份、纤维素醚0.4份、木质纤维0.4份、减水剂0.3份；
其中，水泥为粉煤灰质硅酸盐水泥，强度不低于42.5强度等级，建筑用砂为目数为100目的水洗砂，胶粉为VAE胶粉，抗裂纤维为聚丙烯纤维，纤维单丝长度为6mm，木质纤维长度为1mm，纤维素醚为羟丙基甲基纤维素醚，硬质聚氨酯泡沫塑料粉末为生产、建筑施工以及旧家电淘汰过程中产生的硬质聚氨酯泡沫塑料废料经过粉碎后的粉末，目数为80目，减水剂为磺酸盐减水剂。
一种弹性抗裂抹面砂浆的制备工艺，包括以下步骤：
1、将粉煤灰质硅酸盐水泥30.5份、水洗砂52.7份、VAE胶粉3份、硬质聚氨酯泡沫塑料粉末6份、聚丙烯纤维0.05份、木质纤维0.4份、羟丙基甲基纤维素醚0.4份、磺酸盐减水剂0.3份置于混合机内混合均匀；
2、将步骤1的混合物料加水搅拌均匀，混合物料与水的质量比为：100：60，养护14天原强度为0.23MPa，湿强度为0.20MPa，即得弹性抗裂抹面砂浆。
表1：现有的抹面砂浆与上述实施例的原强度及湿强度对照表
目前，市面上现有的抹面砂浆的原强度及湿强度保持在0.1MPa，本发明的抹面砂浆的原强度与湿强度均可以达到0.2-0.23MPa之间。
本发明的一种掺杂硬质聚氨酯泡沫塑料粉末的弹性抗裂抹面砂浆，添加了由聚氨酯硬质泡沫塑料粉末，使抹面砂浆具有一定的弹性以及柔韧性，逐层渐变柔性释放应力，有效解决了墙体开裂情况，其中纤维素醚具有保水性，可以增加施工性以及湿粘性，提高施工效率。
Claims (10)
1. 一种弹性抗裂抹面砂浆，其特征在于包括以下质量份数的原料：
水泥28-45份、建筑用砂45-60份、胶粉2-4份、聚氨酯硬质泡沫塑料粉末2-10份、抗裂纤维0.05-0.1份、纤维素醚0.2-0.5份。
2.按照权利要求1所述的一种弹性抗裂抹面砂浆，其特征在于所述原料中还包括木质纤维0.2-0.6份。
3.按照权利要求1所述的一种弹性抗裂抹面砂浆，其特征在于所述原料中还包括减水剂0.2-0.5份。
4.按照权利要求1所述的一种弹性抗裂抹面砂浆，其特征在于所述水泥为硅酸盐水泥、矿渣硅酸盐水泥、火山灰质硅酸盐水泥、粉煤灰质硅酸盐水泥中的任意一种。
5.按照权利要求1所述的一种弹性抗裂抹面砂浆，其特征在于所述抗裂纤维为聚丙烯纤维、聚丙烯酰胺纤维、尼龙-66中的任意一种，纤维单丝长度为2-6mm。
6.按照权利要求1所述的一种弹性抗裂抹面砂浆，其特征在于所述聚氨酯硬质泡沫塑料粉末的目数为40-80目。
7.按照权利要求1所述的一种弹性抗裂抹面砂浆，其特征在于所述减水剂为磺酸盐减水剂、聚羧酸盐减水剂中的任意一种。
8.按照权利要求1或4-6任一权利要求所述的一种弹性抗裂抹面砂浆的制备工艺，其特征在于包括以下步骤：
1）、将水泥28-45份、建筑用砂45-60份、胶粉2-4份、聚氨酯硬质泡沫塑料粉末2-10份、抗裂纤维0.05-0.1份、纤维素醚0.2-0.5份置于混合机内混合均匀；
2）、将步骤1）的混合物料加水搅拌均匀，混合物料与水的质量比为：100：（40-70），即得弹性抗裂抹面砂浆。
9.按照权利要求8所述的一种弹性抗裂抹面砂浆的制备工艺，其特征在于
步骤1）中的原料中还包括木质纤维0.2-0.6份，减水剂0.2-0.5份。
10.按照权利要求8所述的一种弹性抗裂抹面砂浆的制备工艺，其特征在于
所述水泥为硅酸盐水泥、矿渣硅酸盐水泥、火山灰质硅酸盐水泥、粉煤灰质硅酸盐水泥中的任意一种；
所述抗裂纤维为聚丙烯纤维、聚丙烯酰胺纤维、尼龙-66中的任意一种，纤维单丝长度为2-6mm；
所述聚氨酯硬质泡沫塑料粉末的目数为40-80目；
所述减水剂为磺酸盐减水剂、聚羧酸盐减水剂中的任意一种。