CN102673202B - Mark printing manufacturing process based on transparent piece material - Google Patents
Mark printing manufacturing process based on transparent piece material Download PDFInfo
- Publication number
- CN102673202B CN102673202B CN201210186138.6A CN201210186138A CN102673202B CN 102673202 B CN102673202 B CN 102673202B CN 201210186138 A CN201210186138 A CN 201210186138A CN 102673202 B CN102673202 B CN 102673202B
- Authority
- CN
- China
- Prior art keywords
- printing
- mark
- baking
- ink
- clear sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a mark printing manufacturing process based on a transparent piece material. The mark printing manufacturing process comprises the following process steps of: (1) printing a black ink layer on the back of the transparent piece material, reserving an mark position, and scooping the mark; (2) printing two layers to five layers of transparent ink on the mark position of the transparent piece material; (3) after printing the transparent ink, roasting in a furnace to be dry; (4) printing mark background colour on the transparent ink of the mark position of the transparent piece material; (5) roasting in the furnace after printing the mark background colour; (6) utilizing a protecting film to seal the region except the mark position of the transparent piece material, and vacuum-sputtering metal aluminium; (7) printing a layer of printing ink on the surface of the metal aluminum so as to protect metal aluminum; and (8) after printing ink, roasting in the furnace to finish the printing manufacture of the stereo mark. The mark printing manufacturing process disclosed by the invention can combine a vacuum sputtering technology so as to greatly reduce the printing manufacturing cost of the mark, the printed and manufactured mark is the stereo mark, and the mark has high brightness and has three-dimensional effect viewed from the front of the transparent piece material.
Description
Technical field
The present invention relates to the technology of printing on a kind of clear sheet, particularly a kind of identification printing manufacturing process based on clear sheet.
Background technology
At present, the clear sheets such as handset touch panel, panel computer touch-screen, in process, need to (as clear sheet frame region) print one deck black ink in the subregion at the clear sheet back side, and the method for printing can adopt serigraphy; In order to show the information such as production firm (as Lenovo, SAMSUNG), on clear sheet, when process black ink, also need reserved production firm's mark (LOGO) position, and this mark (LOGO) position do not give process black ink, mark is emptied.
Hold, in the prior art, after clear sheet process black ink, its reserved mark (LOGO) position also needs printing to manufacture silver color mark, and its silver color identification printing manufacturing process flow is as follows:
(1) clear sheet mark position printing mark background color;
(2) clear sheet that is printed with mark background color is entered to bake oven roasting, its baking temperature is 50 ℃~80 ℃, and baking time is 3 hours;
(3) printing mirror silver on the background color at clear sheet mark position;
(4) after printing mirror silver, blow about 30 minutes, till drying up with cold wind;
(5) republish one deck silver lustre ink in specular silver surface, to protect mirror-like silver;
(6) place 24~48 hours, dry the printing manufacture that completes mark after silver lustre ink protective layer.
But, in the above-mentioned identification printing manufacturing process based on clear sheet, there are two defects:
One, identification printing manufacturing cost are high, in above-mentioned technological process, need to use mirror-like silver as main mark colour development material, and mirror-like silver is expensive, 5000 yuan/Kg of the about RMB of average price at present, 1 kilogram of mirror-like silver approximately can print 14000 marks, 0.35 yuan of the about RMB of average each identification printing mirror-like silver cost, and the utmost point is unfavorable for the cost control in printing manufacture;
Two, due in above-mentioned (2) step, the mirror-like silver printing on the background color at clear sheet mark position is plane layer, after mark (LOGO) printing of clear sheet has been manufactured, see this mark from the front of clear sheet, this mark (LOGO) is plane mark, only have high brightness, there is no modelling effect.
Summary of the invention
The technical problem to be solved in the present invention is for above-mentioned the deficiencies in the prior art, a kind of identification printing manufacturing process based on clear sheet is provided, this printing worker artistic skill significantly reduces the printing manufacturing cost of mark in conjunction with vacuum splashing and plating technology, and what its printing was manufactured is designated stereo identification, from the front of clear sheet, this mark not only has high brightness, also has modelling effect.
For solving the problems of the technologies described above, technical scheme of the present invention is: a kind of identification printing manufacturing process based on clear sheet, comprises following processing step:
(1) in clear sheet back up black ink layer, and reserved mark position, mark is emptied;
(2) 2 layers~5 layers transparent ink of clear sheet mark position printing, comfort camber groove state by each strokes of characters at mark position;
(3) printing transparent ink fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes, till drying;
(4) printing mark background color on the transparent ink at clear sheet mark position;
(5) printing mark background color fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes;
(6) clear sheet is identified to position region diaphragm in addition and seal, adopt metallic aluminium as material vacuum sputter mark position;
(7), after vacuum splashing and plating, republish one deck ink on metallic aluminium surface, to protect metallic aluminium;
(8) printing-ink fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes, after having toasted, completes the printing manufacture of stereo identification.
In technique scheme, clear sheet mark position is preferable over 3 layers of transparent ink of printing; The baking temperature of printing transparent ink fed to boiler baking is preferably 60 ℃, and baking time is preferably 30 minutes; The baking temperature of printing mark background color fed to boiler baking is preferably 60 ℃, and baking time is preferably 30 minutes; After vacuum splashing and plating, printing-ink enters the roasting baking temperature of bake oven and is preferably 60 ℃, and baking time is preferably 30 minutes.
The invention has the beneficial effects as follows:
One, identification printing are cheap for manufacturing cost, in identification printing manufacturing process of the present invention, adopt metallic aluminium as main mark colour development material, 100 yuan/the Kg of the about RMB of aluminium wire that vacuum splashing and plating adopts, a sputter stove can plate 600 marks, only needs 2 grams of aluminium wires, 0.00003 yuan of the about RMB of cost of average each product sputter aluminium wire, production quantity is larger, can cost saving more, profit is more considerable, thereby can significantly reduce the identification printing manufacturing cost of clear sheet;
Two,, by vacuum splashing and plating, in the color developing effect of metallic aluminium and prior art, the color developing effect of mirror-like silver is very approaching; In vacuum splashing and plating process, metallic aluminium is not oxidated, and the metallic aluminium at mark position is finally wrapped up by transparent ink, background color and black ink, thereby can avoid oxidation, and mark color stability is reliable;
Three, after clear sheet back up black ink layer, each strokes of characters of reserved mark (as Lenovo, SAMSUNG) is the state of emptying, when after 2 layers~5 layers transparent ink of mark position printing, each strokes of characters of this reserved mark is comforted camber groove state, therefore, when after jet-plating metallization aluminium, at the bottom of each deep-slotted chip breaker, will plate metallic aluminium, while now observing this mark from the front of clear sheet again, each strokes of characters of mark is all toward projection, not only brightness is high, and has very strong modelling effect.
Accompanying drawing explanation
Fig. 1 is the schematic partial cross-sectional view of utilizing the stereo identification of the printed manufacture of the present invention, wherein shows certain unicursal cross section state of this stereo identification.
In figure: 1, clear sheet; 2, black ink layer; 3,2 layers~5 layers transparent ink layer; 4, mark background color layer; 5, metallic aluminium; 6, black ink layer; S, sight line.
The specific embodiment
Stereo identification printing manufacturing process based on clear sheet, comprises following processing step:
(1) at the subregion at the clear sheet back side (as clear sheet frame region) printing one deck black ink, the method for printing can adopt serigraphy; In order to show the information such as production firm (as Lenovo, SAMSUNG), on clear sheet, when process black ink, also need reserved production firm's mark (LOGO) position, and this mark (LOGO) position do not give process black ink, mark is emptied; This step is same as the prior art;
(2) 2 layers~5 layers transparent ink of clear sheet mark position printing, are preferable over 3 layers of transparent ink of printing; When after 2 layers~5 layers transparent ink of mark position printing, each strokes of characters of this reserved mark is comforted camber groove state (please refer to Fig. 1);
(3) printing transparent ink fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes, till drying; In this step, baking temperature is preferably 60 ℃, and baking time is preferably 30 minutes;
(4) printing mark background color on the transparent ink at clear sheet mark position; In this step, mark background color is identical with prior art;
(5) printing mark background color fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes; In this step, baking temperature is preferably 60 ℃, and baking time is preferably 30 minutes;
(6) clear sheet is identified to position region diaphragm in addition and seal, adopt metallic aluminium as material vacuum sputter mark position; In this step, multi-disc clear sheet can be put into vacuum splashing and plating stove sputter together, to improve sputter efficiency;
(7), after vacuum splashing and plating, republish one deck ink on metallic aluminium surface, to protect metallic aluminium; Ink in this step is preferably black ink;
(8) printing-ink fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes, after having toasted, completes the printing manufacture of stereo identification; In this step, baking temperature is preferably 60 ℃, and baking time is preferably 30 minutes.
As shown in Figure 1, for utilizing the schematic partial cross-sectional view of stereo identification of the printed manufacture of above-mentioned processing step, it should be noted that, stereo identification is made up of multiple strokes, and explain for convenient in figure, the cross section state of certain unicursal of this stereo identification is only shown, those skilled in the art can the like to every unicursal of cube mark.In Fig. 1, be followed successively by from bottom to up clear sheet 1, black ink layer 2, transparent ink layer 3, mark background color layer 4, metallic aluminium 5 and black ink layer 6.After clear sheet back up black ink layer, each strokes of characters of reserved mark (as Lenovo, SAMSUNG) is the state of emptying, when after 2 layers~5 layers transparent ink of mark position printing, each strokes of characters of this reserved mark is comforted camber groove state, therefore, when after jet-plating metallization aluminium, at the bottom of each deep-slotted chip breaker, will plate metallic aluminium, while now observing this mark from the front of clear sheet again, each strokes of characters of mark is all toward projection (please refer to sight line S direction in Fig. 1), not only brightness is high, and has very strong modelling effect.
The above, be only preferred embodiments of the present invention, and any trickle modification, equivalent variations and modification that every foundation technical scheme of the present invention is done above embodiment, all belong in the scope of technical solution of the present invention.
Claims (6)
1. the identification printing manufacturing process based on clear sheet, is characterized in that, comprises following processing step:
(1) in clear sheet back up black ink layer, and reserved mark position, mark is emptied;
(2) 2 layers~5 layers transparent ink of clear sheet mark position printing, comfort camber groove state by each strokes of characters at mark position;
(3) printing transparent ink fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes, till drying;
(4) printing mark background color on the transparent ink at clear sheet mark position;
(5) printing mark background color fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes;
(6) clear sheet is identified to position region diaphragm in addition and seal, adopt metallic aluminium as material vacuum sputter mark position;
(7), after vacuum splashing and plating, republish one deck ink on metallic aluminium surface, to protect metallic aluminium;
(8) printing-ink fed to boiler baking, its baking temperature is 50 ℃~80 ℃, baking time is 15~50 minutes, after having toasted, completes the printing manufacture of stereo identification.
2. the identification printing manufacturing process based on clear sheet according to claim 1, is characterized in that: 3 layers of transparent ink of clear sheet mark position printing.
3. the identification printing manufacturing process based on clear sheet according to claim 1, is characterized in that: the baking temperature of printing transparent ink fed to boiler baking is 60 ℃, and baking time is 30 minutes.
4. the identification printing manufacturing process based on clear sheet according to claim 1, is characterized in that: the baking temperature of printing mark background color fed to boiler baking is 60 ℃, and baking time is 30 minutes.
5. the identification printing manufacturing process based on clear sheet according to claim 1, is characterized in that: after vacuum splashing and plating, it is 60 ℃ that printing-ink reenters the roasting baking temperature of bake oven, and baking time is 30 minutes.
6. according to the identification printing manufacturing process based on clear sheet described in claim 1 or 5, it is characterized in that: after vacuum splashing and plating, the ink of printing is black ink.