CN203344422U - Stereoscopic-pattern window glass - Google Patents
Stereoscopic-pattern window glass Download PDFInfo
- Publication number
- CN203344422U CN203344422U CN 201320308815 CN201320308815U CN203344422U CN 203344422 U CN203344422 U CN 203344422U CN 201320308815 CN201320308815 CN 201320308815 CN 201320308815 U CN201320308815 U CN 201320308815U CN 203344422 U CN203344422 U CN 203344422U
- Authority
- CN
- China
- Prior art keywords
- rete
- dimensional line
- thick
- transparent color
- sight glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model discloses stereoscopic-pattern window glass. The stereoscopic-pattern window glass comprises glass, a transparent sheet bond on the glass through optical adhesive, a stereoscopic-pattern UV adhesive layer transferred onto the transparent sheet, a transparent color film layer plated on the UV adhesive layer, and an ink layer screen-printed on the transparent color film layer. Compared with the prior art, the stereoscopic-pattern window glass has the advantages as follows: a true stereoscopic-pattern visual effect can be achieved on the front surface of the window glass: the window glass cannot be damaged and depreciated.
Description
Technical field
The utility model relates to a kind of three-dimensional line sight glass.
Background technology
Along with the emergence of smart mobile phone in recent years, the large-size screen monitors touch screen more and more becomes main flow.The glass screen in mobile phone front is as with the user, contacting the closest one side, and being decorated by the brand business on the mobile phone screen glass surface more and more paid attention to.
At glass surface, being decorated is always an industry difficult problem, but mainly contains the deficiencies such as the low decorative effect of yield is few.At present the decoration of sight glass mostly adopted and directly printed in inboard or the outside of sight glass, or obtain the texture with stereoeffect in the outside of sight glass by machining or UV transfer printing.Before the printed decorative pattern gone out of a kind of mode not have third dimension, a color also relatively single; There is relief texture although rear a kind of mode can obtain, due to sight glass long-term with staff or other object contacts, friction, even adopt expensive high hardness material, also easily wear and tear and seem outmoded, and high cost.
Summary of the invention
Technical problem to be solved in the utility model is, for above-mentioned defect, provides three-dimensional line sight glass, and it has true, three-dimensional three-dimensional line visual effect, and cost is low, not easy to wear.
Explanation of nouns: the alleged three-dimensional line of the utility model refers to the solid grain formed by roller mould, includes but not limited to drawing pattern, CD line, cloudy surface, bright the lines such as lines.
Technical problem of the present utility model is solved by following technological means:
A kind of three-dimensional line sight glass comprises: glass, by optical cement, be bonded in clear sheet on glass, be transferred in the UV glue-line with three-dimensional line on described clear sheet, be plated in transparent color rete and the ink layer of silk-screen on described transparent color rete on described UV glue-line.
Preferably:
Described clear sheet is the PET sheet material.
Described transparent color rete comprise one deck or two-layer more than.
Described transparent color rete comprises (being followed successively by from the UV glue-line) from inside to outside successively: the SiO that 100～160nm is thick
2rete, the Ti that 40～60nm is thick
3o
5the SiO that rete and 30～40nm are thick
2rete.
Described transparent color rete comprises (being followed successively by from the UV glue-line) from inside to outside successively: the SiO that 60～80nm is thick
2rete, the Ti that 25～35nm is thick
3o
5the SiO that rete and 15～25nm are thick
2rete.
Described transparent color rete comprises (being followed successively by from the UV glue-line) from inside to outside successively: the Ti that 15～20nm is thick
3o
5rete, the SiO that 15～20nm is thick
2the Ti that rete and 15～20nm are thick
3o
5rete.
Described three-dimensional line is drawing pattern, CD line, cloudy surface or bright lines.
Described ink layer is black ink layer, and ink film thickness is 10～20 μ m.
Compared with prior art, at first technique scheme of the present invention forms three-dimensional line on clear sheet, and utilize vacuum coating to form transparent color rete on three-dimensional line, then utilize ink layer as substrate, finally by clear sheet, shiny surface and the sight glass laminating of the three-dimensional line of transfer printing are not integral.Because three-dimensional line is necessary being, and transparent color rete is formed on three-dimensional line, cooperation is as the substrate of visual background, thereby can obtain real three-dimensional line visual effect in the front of sight glass, but because three-dimensional line is positioned at the inboard of sight glass, with any object, do not rub, thereby can damaged, depreciation.
The accompanying drawing explanation
Fig. 1 is the structural representation of the three-dimensional line sight glass of the utility model specific embodiment;
Fig. 2 is the flow chart of the manufacture method of the utility model specific embodiment.
The specific embodiment
Below preferred embodiment the utility model is described in further detail for contrast accompanying drawing combination.
As shown in Figure 1, a kind of three-dimensional line sight glass comprises: glass, by optical cement, be bonded in clear sheet on glass, be transferred in the UV glue-line with three-dimensional line on described clear sheet, be plated in transparent color rete and the ink layer of silk-screen on described transparent color rete on described UV glue-line.Described three-dimensional line sight glass includes but not limited to the sight glass of following product: the products such as mobile phone, computer, lithographic plate computer, TV, player
As shown in Figure 2, present embodiment also provides a kind of manufacture method of three-dimensional line sight glass, and for the preparation of aforesaid three-dimensional line sight glass, this manufacture method comprises the steps: to utilize the UV transfer technique to form three-dimensional line on the surface of clear sheet; On three-dimensional line, vacuum coating forms one deck, both sides or multi-layer transparent color rete; The first ink layer of silk-screen predetermined pattern on transparent color rete, cover and need the transparent color rete retained; Clear sheet after silk-screen is placed in to decoating liquid and carries out strip, remove unwanted transparent color rete; Then according to predetermined profile, carry out die-cut to obtain the size needed; Thereby finally die-cut good clear sheet not being had to the face of three-dimensional line and sight glass is fitted and is obtained the sight glass with three-dimensional line visual effect.As a kind of preferred scheme, between strip and die-cut step, also can be formed with at clear sheet face screen printing pattern and/or second ink layer of three-dimensional line.
More in specific embodiment:
The UV transfer printing comprises the following steps: 1) die sinking (making roller mould): the three-dimensional line in the time of will making the UV transfer printing on mould (for example: vertically wire drawing lines), and locating hole when locating dowel and printing-ink; 2) transfer printing: the mode by UV glue by silk-screen prints on roller mould; 3) pressing: the PET sheet material is put on roller mould, then with the glue rod, sheet material is pressed onto on roller mould, the UV glue after pressing and PET sheet material need to be placed 3～5 minutes at the temperature of 20～25 ℃; 4) light is solid: sheet material and roller mould are put in the solid machine of light to carry out light solid, the temperature in the solid machine of light cannot surpass 50 ℃, and UV lamp energy density is 300～500mj/cm
2; 5) demoulding: the product that transfer printing is good takes out and gets final product from mould.Wherein the PET sheet material is clear sheet, but the utility model is not limited to the PET sheet material, in the situation that meet light transmittance, can adopt other transparent sheet materials.
Vacuum coating comprises: the PET sheet material is arrived in the coating machine vacuum chamber with rubberized fabric adhere, the side that the PET sheet material is printed on three-dimensional line outwardly, by vavuum pump, the air of vacuum chamber is taken away again, is made it pressure and remain on 0.002Pa between 0.006Pa, one preferably pressure value be 0.004Pa.Need to be used for the SiO of plated film
2with Ti
3o
5should be placed on the evaporation source of vacuum chamber the inside prior to the PET sheet material.Can carry out plated film afterwards, on the three-dimensional line surface of transfer printing, form transparent color rete.
The first silk-screen step: the PET sheet material after vacuum coating is carried out to serigraphy with printing ink, the preferred black ink of printing ink, what this example adopted is the IPX-971 of kingdom black ink, the three-dimensional line pattern form that the silk-screen half tone need obtain according to wish is made, printing-ink on the transparent color rete only retained at needs, positions such as form, photographic hole is printing-ink not, outside above-mentioned position, can also reserve the part position simultaneously and not do printing and make it, after following operation is processed, other pattern effect is arranged.Print thickness is at 5～10 μ m, and baking temperature is 50～80 ℃, and baking time is 10～20 minutes.
Strip: the tank rinsing 5-10 second the PET sheet material after the first silk-screen step process with the decoating liquid that strip agent: water=1:10 is housed of putting into normal temperature, the PET sheet material does not have the locational film plating layer of ink for screen printing can be dissolved to fall, then is positioned over baking in the baking oven of 50 ℃ after cleaning with clear water and within 3-5 minute, completes strip.
The second silk-screen step: the PET sheet material after strip is carried out to serigraphy to form the ink layer that transparent color rete is shielded with printing ink; the printing ink that this example adopts is identical with the first silk-screen step; half tone is also identical with the first silk-screen step; print thickness is at 10～20um; baking temperature is 50～80 ℃, and baking time is 20～30 minutes.As a kind of preferred version, the silk-screen of the enterprising mark of doing business in position, logo or other special patterns that the second silk-screen step also can be reserved in the first silk-screen step, the printing ink of its protective effect of silk-screen again after silk-screen.Certainly, as a kind of possibility, the ink layer that also silk-screen does not shield, and the next step that improves after the special pattern that only silk-screen needs.
Die-cut: the PET sheet material after silk-screen is put on stamping machine, needs before this to make corresponding mould according to the handset viewing window shape, then the PET sheet material can be punched goes out needed handset viewing window profile at suitable pressures.
Laminating: the back side of die-cut good PET handset viewing window sheet material (one side that there is no the three-dimensional line of transfer printing) and identical shaped mobile phone screen optical cement (Optically Clear Adhesive, initialism: OCA) be bonded and produce required finished product for glass.
As shown in Figure 2, the three-dimensional line sight glass that prepared by the present embodiment comprises following structure sheaf: glass 100, by optical cement, be bonded in PET200 on glass, be transferred in the UV glue-line 300 with three-dimensional line on PET, be plated in transparent color rete 400 and the ink layer 500 of silk-screen on transparent color rete on the UV glue-line; In Fig. 2, each layer all is positioned at the periphery of glass 100, and glass 100 intermediate blank parts are form.。
Transparent color rete preferably adopts silica and titanium oxide vacuum coating to form, by difference put in order, the selection of thickness silica and titanium oxide layer, coordinate black ink can form multiple different visual effect, three kinds of preferred transparent color rete schemes hereinafter be provided:
Scheme 1:
| Sequentially | Rete | Thickness (nm) | Sedimentation rate (A/S) |
| 0 | The PET sheet material | / | / |
| 1 | |
100～160 | 8 |
| 2 | Ti 3O 5 | 40～60 | 2 |
| 3 | SiO 2 | 30～40 | 8 |
Such scheme can form the three-dimensional line visual effect of highlighted, bright-coloured gold.Preferred rete scheme is: SiO
2: Ti
3o
5: SiO
2=160nm:60nm:40nm.
Scheme 2:
| Sequentially | Rete | Thickness (nm) | Sedimentation rate (A/S) |
| 0 | The PET sheet material | / | / |
| 1 | SiO 2 | 60～80 | 8 |
| 2 | Ti 3O 5 | 25～35 | 2 |
| 3 | SiO 2 | 15～25 | 8 |
Such scheme can obtain dazzles the three-dimensional line effect of beautiful royalblue.More preferably the rete scheme is: SiO
2: Ti
3o
5: SiO
2=80nm:30nm:20nm
Scheme 3:
| Sequentially | Rete | Thickness (nm) | Sedimentation rate (A/S) |
| 0 | The PET sheet material | / | / |
| 1 | Ti 3O 5 | 15～20 | 2 |
| 2 | SiO 2 | 15～20 | 8 |
| 3 | Ti 3O 5 | 15～20 | 2 |
Such scheme can obtain the three-dimensional line effect of purple.Scheme: Ti more preferably
3o
5: SiO
2: Ti
3o
5=15nm:17nm:16nm.
Above content is in conjunction with concrete preferred embodiment further detailed description of the utility model, can not assert that concrete enforcement of the present utility model is confined to these explanations.For the utility model person of ordinary skill in the field; without departing from the concept of the premise utility; can also make some being equal to substitutes or obvious modification, and performance or purposes identical, all should be considered as belonging to protection domain of the present utility model.
Claims (8)
1. a three-dimensional line sight glass, it is characterized in that, comprising: glass, by optical cement, be bonded in clear sheet on glass, be transferred in the UV glue-line with three-dimensional line on described clear sheet, be plated in transparent color rete and the ink layer of silk-screen on described transparent color rete on described UV glue-line.
2. three-dimensional line sight glass according to claim 1, it is characterized in that: described clear sheet is the PET sheet material.
3. three-dimensional line sight glass according to claim 1 is characterized in that: described transparent color rete comprise one deck or two-layer more than.
4. three-dimensional line sight glass according to claim 1, it is characterized in that: described transparent color rete comprises from inside to outside successively: the SiO that 100～160nm is thick
2rete, the Ti that 40～60nm is thick
3o
5the SiO that rete and 30～40nm are thick
2rete.
5. three-dimensional line sight glass according to claim 1, it is characterized in that: described transparent color rete comprises from inside to outside successively: the SiO that 60～80nm is thick
2rete, the Ti that 25～35nm is thick
3o
5the SiO that rete and 15～25nm are thick
2rete.
6. three-dimensional line sight glass according to claim 1, it is characterized in that: described transparent color rete comprises from inside to outside successively: the Ti that 15～20nm is thick
3o
5rete, the SiO that 15～20nm is thick
2the Ti that rete and 15～20nm are thick
3o
5rete.
7. according to the described three-dimensional line sight glass of claim 1～6 any one, it is characterized in that: described three-dimensional line is drawing pattern, CD line, cloudy surface or bright lines.
8. according to the described three-dimensional line sight glass of claim 1～6 any one, it is characterized in that: described ink layer is black ink layer, and ink film thickness is 10～20 μ m.