CN102643458A - 有抗过敏性能的混合乳胶液 - Google Patents

有抗过敏性能的混合乳胶液 Download PDF

Info

Publication number
CN102643458A
CN102643458A CN2012101457922A CN201210145792A CN102643458A CN 102643458 A CN102643458 A CN 102643458A CN 2012101457922 A CN2012101457922 A CN 2012101457922A CN 201210145792 A CN201210145792 A CN 201210145792A CN 102643458 A CN102643458 A CN 102643458A
Authority
CN
China
Prior art keywords
latex
weight part
weight
antianaphylaxis
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101457922A
Other languages
English (en)
Inventor
蔡瑞琳
蔡晓薇
刘新春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2012101457922A priority Critical patent/CN102643458A/zh
Publication of CN102643458A publication Critical patent/CN102643458A/zh
Pending legal-status Critical Current

Abstract

有抗过敏性能的混合乳胶液，包括以下各组分：重量百分比浓度为60%的天然乳胶、丁腈胶乳、去离子水、增稠剂、硫磺、ZDC促进剂、TMO助剂、防老剂D、氧化锌、氢氧化钾、酪素、羊毛脂。本发明所述的混合乳胶液中，天然乳胶的含量少，减少了乳胶手套中蛋白质的含量，因此，使用该混合乳胶液制作的乳胶手套具有一定的抗过敏性，使得乳胶手套的使用范围扩大，方便了人们的生活。由于本发明所述的混合乳胶液是在天然乳胶中添加了丁腈胶乳等添加剂，使用该混合乳胶液来制作乳胶手套，大大提高了乳胶手套的抗老化性能、耐屈挠性，增强了抗化学性能和弹性；比单纯的天然乳胶柔软性更好，有更强的防油脂等性能。

Description

有抗过敏性能的混合乳胶液
技术领域
本发明涉及有抗过敏性能的混合乳胶液。
背景技术
传统乳胶手套的生产已经有了近40年历史，由于天然乳胶中普遍存在引起人体过敏反应的水溶性蛋白质，因此，有许多人因为过敏而不能使用乳胶手套，限制了乳胶手套的使用，也对人们的生活引起诸多不便；另外，现有的乳胶手套多采用纯天然乳胶制成，采用纯天然乳胶制成的乳胶手套的抗老化性能差、耐屈挠性差，其弹性也较差。
发明内容
本发明所要解决的技术问题是提供有抗过敏性能的混合乳胶液，使用该混合乳胶液制作的乳胶手套不易引起皮肤过敏，且抗老化性能好、耐屈挠性好。
为解决上述技术问题，本发明提供了有抗过敏性能的混合乳胶液，该混合乳胶液包括以下各重量份的组分：
重量百分比浓度为60%的天然乳胶    65～115重量份
丁腈胶乳                          3～15重量份
去离子水                          5～30重量份
增稠剂                            5～40重量份
硫磺                              0.5～5重量份
ZDC促进剂                       0.5～5重量份
TMO助剂                         0.5～5重量份
防老剂D                          0.5～5重量份
氧化锌                            0.2～3重量份
氢氧化钾                          0.2～3重量份
酪素                              0.2～3重量份
羊毛脂                            0.2～3重量份。
丁腈胶乳系阴离子型高分子聚合物乳液，该胶乳分子量和粒径分布较均匀，耐油、耐溶剂、耐酸碱，可与硫磺、金属氧化物交联，其稳定性优于天然胶乳，其制品对皮肤无过敏反应，耐尖锐物刺划，定伸拉力优于天然胶乳制品。
ZDC促进剂能促进硫化作用的物质。可缩短硫化时间，降低硫化温度，减少硫化剂用量和提高橡胶的物理机械性能等。
防老剂D可用作橡胶抗氧剂、润滑剂、聚合抑制剂。
氧化锌主要起到交联促进剂作用，同时有补强作用。在乳胶硫化初期，氧化锌能加速硫化反应、在硫化后期延迟硫化反应，可提高其最低扭矩和最高扭矩。同时硫化胶的硬度也会增加，拉伸强度增大。氧化锌也可以提高耐温性能。
羊毛脂是优良的滋润性物质。
本发明所述的混合乳胶液中，天然乳胶的含量少，减少了乳胶手套中蛋白质的含量，且丁腈胶乳制品对皮肤无过敏反应，因此，使用该混合乳胶液制作的乳胶手套具有一定的抗过敏性，使得乳胶手套的使用范围扩大，方便了人们的生活。
由于本发明所述的混合乳胶液是在天然乳胶中添加了丁腈胶乳等添加剂，使用该混合乳胶液来制作乳胶手套，大大提高了乳胶手套的抗老化性能、耐屈挠性，增强了抗化学性能和弹性；比单纯的天然乳胶柔软性更好，有更强的防油脂等性能。
作为本发明的优化，所述混合乳胶液中还包括有0.1～0.5重量份色浆。
由于混合乳胶液中加有色浆，可以按照人们的喜好将乳胶手套制成多种颜色，丰富了其外观色彩，也可以帮助人们利用颜色来区分各手套的使用用途等，方便使用。
所述增稠剂为羧甲基纤维素或羟乙基纤维素。
综上所述，使用该混合乳胶液制作的乳胶手套不易引起皮肤过敏，且抗老化性能好、耐屈挠性好。
本发明所述混合乳胶液中的各个组分均为市售品。
所述混合乳胶液的配制方法为：在搅拌的状态下将65～115重量份的重量百分比浓度为60%的天然乳胶和3～15重量份的丁腈胶乳加入反应釜内，搅拌0.5～2小时后，依次缓慢加入5～30重量份去离子水、5～40重量份的增稠剂、0.5～5重量份硫磺、0.5～5重量份ZDC促进剂、0.5～5重量份TMO助剂、0.5～5重量份防老剂D、0.2～3重量份氧化锌、0.2～3重量份氢氧化钾、0.2～3重量份酪素、0.2～3重量份羊毛脂和0.1～0.5重量份色浆，在20～70℃的温度下混合搅拌0.5～8小时即可。
混合乳胶液配制好后即可用来制作乳胶手套等乳胶制品。
具体实施方式
实施例1：
有抗过敏性能的混合乳胶液，包括以下各重量份的组分：
重量百分比浓度为60%的天然乳胶    65重量份
丁腈胶乳                          3重量份
去离子水                          5重量份
羧甲基纤维素                      5重量份
硫磺                              0.5重量份
ZDC促进剂                       0.5重量份
TMO助剂                         0.5重量份
防老剂D                          0.5重量份
氧化锌                            0.2重量份
氢氧化钾                          0.2重量份
酪素                              0.2重量份
羊毛脂                            0.2重量份
红色色浆                          0.1重量份。
所述混合乳胶液的配制方法为：在搅拌的状态下将重量百分比浓度为60%的天然乳胶和丁腈胶乳加入反应釜内，搅拌0.5小时后，依次缓慢加入去离子水、羧甲基纤维素、硫磺、ZDC促进剂、TMO助剂、防老剂D、氧化锌、氢氧化钾、酪素、羊毛脂和色浆，在20℃的温度下混合搅拌0.5小时即可。
实施例2：
有抗过敏性能的混合乳胶液，包括以下各重量份的组分：
重量百分比浓度为60%的天然乳胶    115重量份
丁腈胶乳                          15重量份
去离子水                          30重量份
羧甲基纤维素                      40重量份
硫磺                              5重量份
ZDC促进剂                        5重量份
TMO助剂                         5重量份
防老剂D                          5重量份
氧化锌                            3重量份
氢氧化钾                          3重量份
酪素                              3重量份
羊毛脂                            3重量份
黄色色浆                         0.5重量份。
所述混合乳胶液的配制方法为：在搅拌的状态下将重量百分比浓度为60%的天然乳胶和丁腈胶乳加入反应釜内，搅拌2小时后，依次缓慢加入去离子水、羧甲基纤维素、硫磺、ZDC促进剂、TMO助剂、防老剂D、氧化锌、氢氧化钾、酪素、羊毛脂和色浆，在70℃的温度下混合搅拌8小时即可。
实施例3： 
有抗过敏性能的混合乳胶液，包括以下各重量份的组分：
重量百分比浓度为60%的天然乳胶    85重量份
丁腈胶乳                          9重量份
去离子水                          18重量份
羟乙基纤维素                      24重量份
硫磺                              2.8重量份
ZDC促进剂                       2.8重量份
TMO助剂                         2.8重量份
防老剂D                          2.8重量份
氧化锌                            1.6重量份
氢氧化钾                          1.6重量份
酪素                              1.6重量份
羊毛脂                            1.6重量份
蓝色色浆                          0.3重量份。
所述混合乳胶液的配制方法为：在搅拌的状态下将重量百分比浓度为60%的天然乳胶和丁腈胶乳加入反应釜内，搅拌1.2小时后，依次缓慢加入去离子水、羟乙基纤维素、硫磺、ZDC促进剂、TMO助剂、防老剂D、氧化锌、氢氧化钾、酪素、羊毛脂和色浆，在45℃的温度下混合搅拌4小时即可。
以上所述的仅是本发明的三种实施方式。应当指出，对于本领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出显而易见的若干变换或替代以及改型，这些也应视为属于本发明的保护范围。

Claims (3)

1.有抗过敏性能的混合乳胶液，包括以下各重量份的组分：
重量百分比浓度为60%的天然乳胶    65～115重量份
丁腈胶乳                                     3～15重量份
去离子水                                     5～30重量份
增稠剂                                        5～40重量份
硫磺                                           0.5～5重量份
ZDC促进剂                                 0.5～5重量份
TMO助剂                                    0.5～5重量份
防老剂D                                      0.5～5重量份
氧化锌                                         0.2～3重量份
氢氧化钾                                      0.2～3重量份
酪素                                            0.2～3重量份
羊毛脂                                         0.2～3重量份。
2.根据权利要求1所述的有抗过敏性能的混合乳胶液，其特征在于：所述混合乳胶液中还包括有0.1～0.5重量份色浆。
3.根据权利要求1或2所述的有抗过敏性能的混合乳胶液，其特征在于：所述增稠剂为羧甲基纤维素或羟乙基纤维素。
CN2012101457922A 2012-05-12 2012-05-12 有抗过敏性能的混合乳胶液 Pending CN102643458A (zh)