CN102633535B - 一种宝石花釉的制作方法 - Google Patents

一种宝石花釉的制作方法 Download PDF

Info

Publication number
CN102633535B
CN102633535B CN 201210081599 CN201210081599A CN102633535B CN 102633535 B CN102633535 B CN 102633535B CN 201210081599 CN201210081599 CN 201210081599 CN 201210081599 A CN201210081599 A CN 201210081599A CN 102633535 B CN102633535 B CN 102633535B
Authority
CN
China
Prior art keywords
glaze
parts
coat enamel
ground
cover
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201210081599
Other languages
English (en)
Other versions
CN102633535A (zh
Inventor
何昌楚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd
Original Assignee
HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd filed Critical HUNAN LILING CHUHUA CERAMIC INDUSTRIAL Co Ltd
Priority to CN 201210081599 priority Critical patent/CN102633535B/zh
Publication of CN102633535A publication Critical patent/CN102633535A/zh
Application granted granted Critical
Publication of CN102633535B publication Critical patent/CN102633535B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种铜钱花釉的制作方法，其特征是：按以下组份和重量百分比配制底釉和面釉，钾长石30～40，石英15～20，方解石12～18，熔块16～20，氧化铁红10～15，熔块35～40，方解石15～20，氧化铁10～20，氧化钛8～15，粘土6～15，氧化钴0.3～0.5；将底釉、面釉湿法球磨，过筛，调成45-50波美度的釉浆，底釉施加在泥坯上，自然干燥，用面釉浆刷在已上底釉的泥坯上，1180～1200℃温度烧制，即成宝石般的色泽，并且颜色鲜艳，质地晶莹，光泽灿烂。

Description

一种宝石花釉的制作方法
技术领域
本发明涉及陶瓷釉料的制作方法特别涉及一种宝石花釉的制作方法。
背景技术
宝石颜色鲜艳，质地晶莹，光泽灿烂，而且稀少，象征着财富，将宝石的色泽用于瓷器行业，将瓷器表面做成宝石花色泽的釉面一直比较困难。
发明内容
本发明的目的提供一种宝石花釉的制作方法，使瓷器具有了宝石般的鲜艳颜色和晶莹的质地。
本发明的宝石花釉，其特征在于：
(1)按以下组份和重量百分比配制
A、底釉
钾长石  30～40    石英    15～20
方解石  12～18    熔块    16～20
氧化铁红10～15
B、面釉
熔块    35～40    方解石  15～20
氧化铁  10～20    氧化钛  8～15
粘土    6～15     氧化钴  0.3～0.5
(2)底釉按料∶球∶水等于1∶2∶0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成45～50波美度的釉浆，施加在泥坯上，自然干燥后待用；
(3)面釉按料∶球∶水等于1∶2∶0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成35～40波美度的釉浆，用面釉浆在已上底釉的泥坯上绘成点状，1180～1200℃温度烧制成品。
根据以上技术方案提出的这种宝石花釉，颜色晶莹剔透，光泽鲜艳，使人爱不释手，可以用于各种餐具，茶具及瓷器艺术品。
具体实施方式
实施例一
(1)按以下组份和重量百分比配制
A、底釉
钾长石  35    石英    17
方解石  15    熔块    20
氧化铁红13
B、面釉
熔块    38    方解石    20
氧化铁  12    氧化钛    15
粘土    14.5  氧化钴    0.5
(2)底釉按料∶球∶水等于1∶2∶0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成50波美度的釉浆，施加在泥坯上，自然干燥后待用；
(3)面釉按料∶球∶水等于1∶2∶0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成35～40波美度的釉浆，用面釉浆在已上底釉的泥坯上绘成点状，1180～1200℃温度烧制成品。
实施例二
(1)按以下组份和重量百分比配制
A、底釉
钾长石    40    石英    16
方解石    12    熔块    17
氧化铁红  15
B、面釉
熔块      40    方解石    20
氧化铁    20    氧化钛    13.7
粘土      6     氧化钴    0.3
(2)底釉按料∶球∶水等于1∶2∶0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成45波美度的釉浆，施加在泥坯上，自然干燥后待用；
(3)面釉按料∶球∶水等于1∶2∶0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成35～40波美度的釉浆，用面釉浆在已上底釉的泥坯上绘成点状，1180～1200℃温度烧制成品。
本发明方案中的熔块为本行业通用的一种材料，来自专业生产厂家，其组成原料为：二氧化硅50％，钾长石20％，锂灰石15％，氧化锌10％，石英5％。

Claims (1)

1.一种宝石花釉的制作方法，其特征在于：
（1）按以下组份和重量百分比配制
A、底釉
钾长石    30~40        石英      15~20
方解石    12~18       熔块      16~20
氧化铁红  10~15      
其中上述熔块的组份和重量百分比如下：     
二氧化硅   50   钾长石  20 
   锂灰石     15   氧化锌  10  
石英5；
B、面釉
熔块     35~40      方解石      15~20
氧化铁   10~20      氧化钛      8~15
粘土     6~15       氧化钴     0.3~0.5
其中上述熔块的组份和重量百分比如下：     
二氧化硅   50   钾长石  20 
   锂灰石     15   氧化锌  10  
石英5；
（2）底釉按料：球：水等于1：2：0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成45~50波美度的釉浆，施加在泥坯上，自然干燥后待用；
（3）面釉按料：球：水等于1：2：0.6，湿法球磨18小时，球磨后之釉料过180目筛，调成35~40波美度的釉浆，用面釉浆在已上底釉的泥坯上绘成点状，1180~1200℃温度烧制成品。 
CN 201210081599 2012-03-26 2012-03-26 一种宝石花釉的制作方法 Expired - Fee Related CN102633535B (zh)