CN102627890A - 一种超能净化乳胶漆及其制备方法、应用和使用方法 - Google Patents
一种超能净化乳胶漆及其制备方法、应用和使用方法 Download PDFInfo
- Publication number
- CN102627890A CN102627890A CN2012100965195A CN201210096519A CN102627890A CN 102627890 A CN102627890 A CN 102627890A CN 2012100965195 A CN2012100965195 A CN 2012100965195A CN 201210096519 A CN201210096519 A CN 201210096519A CN 102627890 A CN102627890 A CN 102627890A
- Authority
- CN
- China
- Prior art keywords
- wall
- emulsion paint
- rubber
- emulsion
- metope
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种超能净化乳胶漆及其制备方法、应用和使用方法,一种超能净化乳胶漆,由包括如下重量份数的组分制成:VAE净味乳液,35~50份;环保型助剂,2~4份;水,20~22份;颜料,5~15份;填料,20~30份;天然硅藻土,10~20份。本发明中采用的VAE净味乳液为零VOC排放,低气味,零APEO,且由于添加了天然硅藻土、超细填料可以起到防水防潮的作用,高效净化空气的作用,增强抗污易洁、耐擦洗的性能。
Description
技术领域
本发明属于乳胶漆技术领域,尤其是涉及一种超能净化乳胶漆及其制备方法、应用和使用方法。
背景技术
乳胶漆又称为合成树脂乳液涂料,是有机涂料的一种,是以合成树脂乳液为基料加入颜料、填料及各种助剂配制而成的一类水性涂料。跟据生产原料的不同,乳胶漆主要有聚醋酸乙烯乳胶漆、乙丙乳胶漆、纯丙烯酸乳胶漆、苯丙乳胶漆等品种;乳胶漆具有传统油漆的基本性质,施工方便,装饰效果好,深受人们的喜爱。乳胶漆是水溶性的,在涂装的过程中,需要加水进行稀释,但是在固化后,却不易受潮和擦拭,因为整个墙面的湿度不会完全统一,那么溶解程度也不一样,等水干了以后,墙面就会花掉,影响美观。
近年来,随着社会进步和人们生活水平及认识水平的快速提高,人们的环保、健康意识日益增强,国际和国内的环保呼声也都越来越高。而墙面装修材料乳胶漆作为建筑装饰的必备材料,人们对乳胶漆的质量的要求也越来越高,更加青睐于无毒、无味、无有机挥发物(VOC)的健康型乳胶漆,世界各发达国家纷纷出台了日趋严格的限制标准,我国政府出台了越来越严格的限制标准,国家标准要求VOC小于200克/升,国家环境认证标准要求VOC小于100克/升。事实说明降低乳胶漆中VOC的含量已成为大势所趋,因为VOC是空气污染中导致人们身体受损伤的主要因素,然而水性乳胶漆中会含有VOC,这是由乳胶漆的制备方法决定的,在制备乳胶漆的过程中需要添加大量的各种含有VOC的助剂,这样在乳胶漆施工时,就会连同这些有机挥发物一起刷到了墙上,那么乳胶漆在干燥过程中和以后的使用中墙体就不断的向外挥发VOC,造成空气污染,从而对人的伤害也越大。
发明内容
本发明要解决的技术问题是提供一种采用净味环保、防水防潮、防霉抗菌、抗污易洁、耐擦洗、超低VOC排放的超能净化乳胶漆,。
为了解决上述技术问题,本发明的技术方案是:一种超能净化乳胶漆,由包括如下重量份数的组分制成:
其中:VAE净味乳液为醋酸乙烯-乙烯共聚乳液。
所述环保型助剂包括二丙二醇丁醚、二丙二醇甲醚、润湿剂和触变剂。
优选的,所述环保型助剂中二丙二醇丁醚、二丙二醇甲醚、润湿剂和触变剂的质量配比为:1∶1∶0.15∶0.2。
优选的,所述填料为重钙或滑石粉或两者的混合物。
优选的,所述填料为重钙与滑石粉的组合物,两者的质量配比为2∶1。
优选的,所述颜料为钛白粉。
本发明还提供了一种制备超能净化乳胶漆的方法,包括如下步骤:1)、将润湿剂及触变剂在搅拌状态下加入水中,搅拌均匀后加入颜料、填料和天然硅藻土,高速分散20分钟;2)、在搅拌状态下加入VAE净味乳液,再缓慢加入二丙二醇丁醚及二丙二醇甲醚,中速搅拌20分钟。
本发明同时提供了一种超能净化乳胶漆的用途,应用于建筑物内墙的混凝土或水泥沙浆墙面装饰及保护。
本发明还提供了一种超能净化乳胶漆的使用方法:
1)、理论涂布量:10平方米/升/单遍,因实际施工表面的粗糙程度和稀释比例不同,耗漆量也有所不同;
2)、重涂时间:25~30℃下,以40微米干膜计,表干时间为60分钟,然后在25℃下,六个小时后,可再重涂覆,(7天内均可再涂刷第二或三道乳胶漆);超过7天,需要视情况重涂;
3)、表面处理:涂装前,内墙墙面必须牢固、干燥、清洁和无浮灰,可根据情况采取以下不同方法处理:
A、新墙未上过涂料:
a)、保证墙体充分干燥,混凝土、抹灰墙面应有足够的养护期;
b)、墙体湿度,砖石、砂浆墙面的湿度应在10%以下;
c)、水泥墙面的碱性,混凝土或水泥沙浆墙面的碱性应保证pH值小于10;d)、除去墙体表面的灰浆渣及凸起部位;
e)、细小油脂污物及粉尘使用中性清洗剂或溶剂清洗,或用湿布擦洗,以彻底清除所有污迹;
f)、墙体表面大的裂缝及凹陷用水泥沙浆修补;细小的孔洞及裂缝如涂料不能补平,需用专用内墙腻子修补;使用修补材料后,墙体需彻底干燥并打磨平整;
B、旧墙未上过涂料:
a)、首先检查墙面状况,根据不同表面缺陷,按步骤A中提及的方法处理;
b)、清除墙面积存的浮尘;
c)、墙面滋生的霉菌或苔藓用高压水除去,并用防霉溶液处理,再用清水洗净,干燥;
C、旧墙涂刷过乳胶漆:
a)、原涂层完好附着在墙面上,由于受侵蚀产生粉化,可用高压水枪除去粉化层,干燥;
b)、旧涂膜局部出现破损时,除去破损涂膜至仍旧牢固部分的边缘,并修补平整;
c)、旧涂膜破损并有粉化现象时,应将其铲起并修补平整后,涂刷配套底漆;
d)、有纹路的旧涂膜如表面牢固可直接重涂;否则需使用喷砂方法处理
4)、施工方法:采用无气喷涂、刷涂或辊涂;
5)、施工温度和湿度,不要在气温低于5℃,相对湿度大于85%的条件下进行施工
本发明的优点及效果:本发明中采用的VAE净味乳液为零VOC排放,低气味,零APEO,且由于添加了天然硅藻土、超细填料可以起到防水防潮的作用,高效净化空气的作用,增强抗污易洁、耐擦洗的性能。
具体实施方式
为了理解本发明,下面通过具体的实施例对本发明作进一步说明。
本发明使用的VAE净味乳液采购于巴斯夫有限公司,使用的天然硅藻土采购于临江赛力特硅藻土有限公司,使用的填料均为超细填料。
实施例一
一种超能净化乳胶漆,由包括如下重量份数的组分制成:
其中:VAE净味乳液为醋酸乙烯-乙烯共聚乳液。环保型助剂中包括二丙二醇丁醚、二丙二醇甲醚、润湿剂和触变剂几种物质,其质量配比为:1∶1∶0.15∶0.2。
实施例二
一种超能净化乳胶漆,由包括如下重量份数的组分制成:
其中:VAE净味乳液为醋酸乙烯-乙烯共聚乳液。环保型助剂中包括二丙二醇丁醚、二丙二醇甲醚、润湿剂和触变剂几种物质,其质量配比为:1∶1∶0.15∶0.2。
实施例三
一种超能净化乳胶漆,由包括如下重量份数的组分制成:
其中:VAE净味乳液为醋酸乙烯-乙烯共聚乳液。环保型助剂中包括二丙二醇丁醚、二丙二醇甲醚、润湿剂和触变剂几种物质,其质量配比为:1∶1∶0.15∶0.2。
上述几种实施例提到的超能净化乳胶漆的制备方法,包括如下步骤:1)、将润湿剂及触变剂在搅拌状态下加入水中,搅拌均匀后加入颜料、填料和天然硅藻土,高速分散20分钟;2)、在搅拌状态下加入VAE净味乳液,再缓慢加入二丙二醇丁醚及二丙二醇甲醚,中速搅拌20分钟。
上述几种实施例提到的超能净化乳胶漆可应用于建筑物内墙的混凝土或水泥沙浆墙面装饰及保护。
本发明一种超能净化乳胶漆的使用方法:
1)、理论涂布量:10平方米/升/单遍,因实际施工表面的粗糙程度和稀释比例不同,耗漆量也有所不同;
2)、重涂时间:25~30℃下,以40微米干膜计,表干时间为60分钟,然后在25℃下,六个小时后,可再重涂覆,(7天内均可再涂刷第二或三道乳胶漆),
超过7天,需要视情况重涂;
3)、表面处理:涂装前,内墙墙面必须牢固、干燥、清洁和无浮灰,可根据情况采取以下不同方法处理:
A、新墙未上过涂料:
a)、保证墙体充分干燥,混凝土、抹灰墙面应有足够的养护期;
b)、墙体湿度,砖石、砂浆墙面的湿度应在10%以下;
c)、水泥墙面的碱性,混凝土或水泥沙浆墙面的碱性应保证pH值小于10;d)、除去墙体表面的灰浆渣及凸起部位;
e)、细小油脂污物及粉尘使用中性清洗剂或溶剂清洗,或用湿布擦洗,以彻底清除所有污迹;
f)、墙体表面大的裂缝及凹陷用水泥沙浆修补;细小的孔洞及裂缝如涂料不能补平,需用专用内墙腻子修补;使用修补材料后,墙体需彻底干燥并打磨平整;
B、旧墙未上过涂料:
a)、首先检查墙面状况,根据不同表面缺陷,按步骤A中提及的方法处理;
b)、清除墙面积存的浮尘;
c)、墙面滋生的霉菌或苔藓用高压水除去,并用防霉溶液处理,再用清水洗净,干燥;
C、旧墙涂刷过乳胶漆:
a)、原涂层完好附着在墙面上,由于受侵蚀产生粉化,可用高压水枪除去粉化层,干燥;
b)、旧涂膜局部出现破损时,除去破损涂膜至仍旧牢固部分的边缘,并修补平整;
c)、旧涂膜破损并有粉化现象时,应将其铲起并修补平整后,涂刷配套底漆;
d)、有纹路的旧涂膜如表面牢固可直接重涂;否则需使用喷砂方法处理
4)、施工方法:采用无气喷涂、刷涂或辊涂;
5)、施工温度和湿度,不要在气温低于5℃,相对湿度大于85%的条件下进行施工
以上对本发明的较佳实施例进行了详细说明,但所述内容仅为本发明的较佳实施例,不能被认为用于限定本发明的实施范围。凡依本发明申请范围所作的均等变化与改进等,均应仍归属于本发明的专利涵盖范围之内。
Claims (8)
2.如权利要求1所述的超能净化乳胶漆,其特征在于:所述环保型助剂中二丙二醇丁醚、二丙二醇甲醚、润湿剂和触变剂的质量配比为:1∶1∶0.15∶0.2。
3.如权利要求1所述的超能净化乳胶漆,其特征在于:所述填料为重钙或滑石粉或两者的混合物。
4.如权利要求1所述的超能净化乳胶漆,其特征在于:所述填料为重钙与滑石粉的组合物,两者的质量配比为2∶1。
5.如权利要求1所述的超能净化乳胶漆,其特征在于:所述颜料为钛白粉。
6.一种制备如权利要求1所述的超能净化乳胶漆的方法,其特征在于:包括如下步骤:1)、将润湿剂及触变剂在搅拌状态下加入水中,搅拌均匀后加入颜料、填料和天然硅藻土,高速分散20分钟;2)、在搅拌状态下加入VAE净味乳液,再缓慢加入二丙二醇丁醚及二丙二醇甲醚,中速搅拌20分钟。
7.权利要求1~6所述超能净化乳胶漆在建筑物内墙的混凝土或水泥沙浆墙面装饰及保护中的应用。
8.一种权利要求1所述的超能净化乳胶漆的使用方法,其特征在于:
1)、理论涂布量:10平方米/升/单遍;
2)、重涂时间:25~30℃下,以40微米干膜计,表干时间为60分钟,然后在25℃下,六个小时后,可再重涂覆,(7天内均可再涂刷第二或三道乳胶漆);
3)、表面处理:涂装前,内墙墙面必须牢固、干燥、清洁和无浮灰,可根据情况采取以下不同方法处理:
A、新墙未上过涂料:
a)、保证墙体充分干燥,混凝土、抹灰墙面应有足够的养护期;
b)、墙体湿度,砖石、砂浆墙面的湿度应在10%以下;
c)、水泥墙面的碱性,混凝土或水泥沙浆墙面的碱性应保证pH值小于10;
d)、除去墙体表面的灰浆渣及凸起部位;
e)、细小油脂污物及粉尘使用中性清洗剂或溶剂清洗,或用湿布擦洗,以彻底清除所有污迹;
f)、墙体表面大的裂缝及凹陷用水泥沙浆修补;细小的孔洞及裂缝如涂料不能补平,需用专用内墙腻子修补;使用修补材料后,墙体需彻底干燥并打磨平整;
B、旧墙未上过涂料:
a)、首先检查墙面状况,根据不同表面缺陷,按步骤A中提及的方法处理;
b)、清除墙面积存的浮尘;
c)、墙面滋生的霉菌或苔藓用高压水除去,并用防霉溶液处理,再用清水洗净,干燥;
C、旧墙涂刷过乳胶漆:
a)、原涂层完好附着在墙面上,由于受侵蚀产生粉化,可用高压水枪除去粉化层,干燥;
b)、旧涂膜局部出现破损时,除去破损涂膜至仍旧牢固部分的边缘,并修补平整;
c)、旧涂膜破损并有粉化现象时,应将其铲起并修补平整后,涂刷配套底漆;
d)、有纹路的旧涂膜如表面牢固可直接重涂;否则需使用喷砂方法处理
4)、施工方法:采用无气喷涂、刷涂或辊涂;
5)、施工温度和湿度,不要在气温低于5℃,相对湿度大于85%的条件下进行施工。