CN102618912A - 焊丝拉丝前的表面处理工艺方法 - Google Patents
焊丝拉丝前的表面处理工艺方法 Download PDFInfo
- Publication number
- CN102618912A CN102618912A CN2012100990479A CN201210099047A CN102618912A CN 102618912 A CN102618912 A CN 102618912A CN 2012100990479 A CN2012100990479 A CN 2012100990479A CN 201210099047 A CN201210099047 A CN 201210099047A CN 102618912 A CN102618912 A CN 102618912A
- Authority
- CN
- China
- Prior art keywords
- welding wire
- additive
- pickling
- wait
- surface treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种焊丝拉丝前的表面处理工艺方法,其工艺步骤中的去除待拉焊丝的氧化皮在剥壳机进行氧化皮物理去除;其再进行电解酸洗的工艺条件是:待拉焊丝的移动速度为0.3-0.5米/秒,待拉焊丝的表面电流密度为150-350A/d㎡;电解液温度控制在15-60℃;电解液由硫酸、盐酸、硫酸钠和添加剂组成,所述添加剂由十二烷基苯磺酸钠、烷基酚聚氧乙烯醚组成。本发明解决了焊丝拉丝前的表面处理存在着酸洗时间长、生产效率低、去除氧化皮效果不理想、环境污染等问题。
Description
技术领域
本发明涉及焊丝生产技术领域,尤其是一种焊丝拉丝前进行的连续表面处理方法。
背景技术
成卷的焊丝在机械工业的生产线中使用得非常普遍,且使用量非常大。而目前焊丝的加工多是用直径较粗的特制待拉焊丝经一系列的拉拔和其它处理工序后制成各种规格成卷的焊丝。在焊丝生产线中,在拉拔工序前对于加工焊丝的原料待拉焊丝,要求除去其表面氧化皮,油污等杂物;目前对原料粗待拉焊丝的氧化皮去除是采用化学酸洗的传统工艺,即直接用盐酸等酸类溶液进行酸洗,通过酸洗中的化学反应达到去掉氧化皮的目的,而这种酸洗是单独完成后才进入拉拨工序并不直接在整条焊丝生产线上连续进行,因此存在着酸洗时间长、生产效率低、去除氧化皮效果不理想、环境污染等问题。
发明内容
本发明所要解决的技术问题是提供一种焊丝拉丝前的表面处理工艺方法,它可以解决焊丝生产线中对原料待拉焊丝表面处理存在酸洗时间长,生产效率低,去除氧化皮效果不理想和环境污染等问题。
为了解决上述问题,本发明的技术方案是:这种焊丝拉丝前的表面处理工艺方法,其工艺步骤依次是:⑴去除待拉焊丝的氧化皮;⑵酸洗前水洗;⑶电解酸洗;⑷酸洗后水洗;⑸烘干;所述去除待拉焊丝的待拉焊丝氧化皮的步骤是在一个剥壳机进行氧化皮剥离,这种剥壳机包括有至少一组由三个轴线横向设置,相对位置呈“品”字形排列的横向槽轮构成的横向折绕轮组,和至少一组由三个轴线纵向设置,相对位置呈“品”字形排列的纵向槽轮构成的纵向折绕轮组;所述待拉焊丝在所述剥壳机中是通过绕过所述横向折绕轮组和纵向折绕轮组使其表面的氧化皮脱离;所述电解酸洗步骤是将待拉焊丝置于盛有电解液的电解槽中以待拉焊丝为阳极,以铅板为阴极进行电解酸洗,其工艺条件是:待拉焊丝的移动速度为0.3-0.5米/秒,待拉焊丝的表面电流密度为150-350A/d㎡;电解液温度控制在15-60℃;电解液由硫酸、盐酸、硫酸钠和添加剂组成,其重量比为:硫酸1%-3.8%,盐酸1-2%,硫酸钠4-5% ,添加剂0.002-0.005%,余量为水;所述添加剂由十二烷基苯磺酸钠、烷基酚聚氧乙烯醚组成,其重量比为:十二烷基苯磺酸钠50-80%,烷基酚聚氧乙烯醚5-20%。
上述的焊丝拉丝前的表面处理工艺方法更为具体的方案是:所述电解酸洗步骤的工艺条件是待拉焊丝的移动速度为0.5米/秒,待拉焊丝的表面电流密度为350A/d㎡,所述电解液的温度控制在25-35℃,所述电解液中的组份的重量比是硫酸1%、盐酸2%,硫酸钠5% ,添加剂0.005%,其添加剂的组份的重量比是十二烷基苯磺酸钠80%,烷基酚聚氧乙烯醚5%,余量为水。
由于采用上述技术方案,本发明与现有的工艺相比具有如下有益效果:
1、本发明中待拉焊丝先经剥壳机中折绕轮组折绕脱去表面的大部分氧化皮与现有酸液将氧化皮化学反应去除相比,不仅可以防止为对待拉焊丝快速去皮的强烈反应造成不带氧化皮或略带氧化皮的基体发生过腐蚀,而且更为重要的是还可以获得快速脱皮的技术效果,特别适用于加入焊丝拉丝生产线中使用;
2、由于待拉焊丝的氧化皮脱除是采用机械物理方法完成,因此,可比化学腐蚀脱皮大大减小了酸液的用量,还免除了废水的处理及其对环境带来的污染。
附图说明
图1是本 发明实施例的主视图;
图2是图1中A-A处的剖视图。
具体实施方式
下面结合附图和实施例对本发明作进一步详细说明:
实施例1,对直径为5.5毫米,ER50-6E型的待拉焊丝进行拉拔前的表面处理,其步骤是:
去除待拉焊丝的金属氧化皮:将待拉焊丝3经过剥壳机进行氧化皮剥离,剥壳机如图1和图2所示,该剥壳机有装在机壳1内的一组由三个轴线竖立设置的纵向槽轮2,这三个纵向槽轮2的相对位置呈“品”字形排列构成一组纵向折绕轮组;机壳1内,在纵向折绕轮组后安装有三个轴线水平设置的横向槽轮4,这三个横向槽轮4的相对位置呈“品”字形排列构成一组横向折绕轮组,待拉焊丝3的在剥壳机中先后绕过三个纵向槽轮2构成的纵向折绕轮组和三个横向槽轮4构成的横向折绕轮组使其表面的氧化皮的反复折弯后脱离;脱离的氧化皮从机壳1底部的出口5排出;
酸洗前水洗:将剥离氧化皮后的待拉焊丝3穿过水洗槽进行水洗;
电解酸洗:将水洗后的待拉焊丝3穿过电解槽中的电解液进行酸洗,通过导向轮将待拉焊丝3与电源阳极相连接,在电解槽中还装有连接电源阴级的铅板,待拉焊丝3的牵拉行走速度为0.3米/秒,待拉焊丝3的表面电流密度调整为150A/d㎡; 电解液温度控制在35-50℃;电解液由硫酸、盐酸、硫酸钠和添加剂组成,其重量比为:硫酸3.8%、盐酸1%,硫酸钠4% ,添加剂0.005%,余量为水;添加剂预先由十二烷基苯磺酸钠和烷基酚聚氧乙烯醚组成,其重量比为:十二烷基苯磺酸钠50%,烷基酚聚氧乙烯醚20%,余量为水。
酸洗后进入后一水洗槽再进行水洗;水洗后进入烘干箱进行烘干,然后进入拉丝机进行拉拔。在电解酸洗工序中采用阳极电解酸洗法,待拉焊丝置于盛有电解液的电解槽中并以0.3米/秒的速度移动;以移动的待拉焊丝为阳极,以铅板为阴极,以直流电源为电解电源,进行电解;电解时的工艺参数如下:电流密度150A/d㎡,电解液温度35-50℃;电解液由硫酸、盐酸、硫酸钠和添加剂组成,其重量比为:硫酸3.8%、盐酸1%,硫酸钠4% ,添加剂0.002%,余量为水;添加剂由十二烷基苯磺酸钠和烷基酚聚氧乙烯醚组成,其重量比为:十二烷基苯磺酸钠50%,烷基酚聚氧乙烯醚20%,余量为水;电解液中的添加剂既能够加速电解进程,提高电解速度,同时又是一种良好的酸雾抑制剂,能够抑制待拉焊丝与电解液反应时产生的酸雾;
酸洗后水洗:将电解酸洗后的待拉焊丝3穿过水洗槽进行水洗;
烘干:将经过酸洗后水洗的待拉焊丝3穿过烘干箱完成烘干。
实施例2:对直径为5.5毫米,ER50-6E型的待拉焊丝进行拉拔前的表面处理,其步骤是:
本实施例除下列参数外,其它部分与实施例1相同:电解酸洗步骤的工艺条件是待拉焊丝的移动速度为0.5米/秒,待拉焊丝的表面电流密度为350A/d㎡,电解液的温度控制在25-35℃,电解液中下列组份的重量比是硫酸1%、盐酸2%,硫酸钠5% ,添加剂0.005%,其添加剂的下列组份的重量比是十二烷基苯磺酸钠80%,烷基酚聚氧乙烯醚5%,余量为水。
Claims (2)
1.一种焊丝拉丝前的表面处理工艺方法,其工艺步骤依次是:⑴去除待拉焊丝的氧化皮;⑵酸洗前水洗;⑶电解酸洗;⑷酸洗后水洗;⑸烘干,其特征在于:
所述去除待拉焊丝的氧化皮的步骤是在一个剥壳机进行氧化皮剥离,这种剥壳机包括有至少一组由三个轴线横向设置,相对位置呈“品”字形排列的横向槽轮构成的横向折绕轮组,和至少一组由三个轴线纵向设置,相对位置呈“品”字形排列的纵向槽轮构成的纵向折绕轮组;所述待拉焊丝在所述剥壳机中是通过绕过所述横向折绕轮组和纵向折绕轮组使其表面的氧化皮脱离;
所述电解酸洗步骤是将待拉焊丝置于盛有电解液的电解槽中以待拉焊丝为阳极,以铅板为阴极进行电解酸洗,其工艺条件是:待拉焊丝的移动速度为0.3-0.5米/秒,待拉焊丝的表面电流密度为150-350A/d㎡;电解液温度控制在15-60℃;电解液由硫酸、盐酸、硫酸钠和添加剂组成,其重量比为:硫酸1%-3.8%,盐酸1-2%,硫酸钠4-5% ,添加剂0.002-0.005%,余量为水;所述添加剂由十二烷基苯磺酸钠、烷基酚聚氧乙烯醚组成,其重量比为:十二烷基苯磺酸钠50-80%,烷基酚聚氧乙烯醚5-20%。
2.根据权利要求1所述的焊丝拉丝前的表面处理工艺方法,其特征在于: 所述电解酸洗步骤的工艺条件是待拉焊丝的移动速度为0.5米/秒,待拉焊丝的表面电流密度为350A/d㎡,所述电解液的温度控制在25-35℃,所述电解液中的组份的重量比是硫酸1%、盐酸2%,硫酸钠5% ,添加剂0.005%,其添加剂的组份的重量比是十二烷基苯磺酸钠80%,烷基酚聚氧乙烯醚5%,余量为水。