Summary of the invention
The object of the present invention is to provide a kind of hot transfer wax ribbon, can well meet the requirement of market to hot transfer wax ribbon, can be transferred to completely after being heated and undertake the printing of on carrier, layer of ink has adaptability widely to carrier of undertaking the printing of, and adhesive force is good, scratch-resistant.
The technical solution used in the present invention is as follows:
A kind of hot transfer wax ribbon, be made up of the release coating above back coating, base material and base material, the ink coating above release coating, described ink coating is made up of following component by weight percentage: resin 1-10.3%, wax class 29-34%, pigment 9-10%, dispersant 0.7-0.8% and solvent 51-55%.
Described weight resin percentage composition is: vinylite 0-3%, Petropols 1-6%, acrylic resin or mylar 0-1.3%.
Described wax class weight percent is composed as follows: palm wax 16-17%, full refining wax 13-17%.
Preferably, described ink coating is composed as follows: vinylite 2.5%, Petropols 3.9%, acrylic resin 1%, palm wax 16.5%, full refining wax 13.2%, pigment 9.6%, dispersant 0.7%, solvent 52.6%, and described ink coating thickness is 2.2-2.8 μm preferably 2.5 μm.
The weight percent of described release coating consists of: mylar 2-3%, solvent 97-98%, and release coating layer thickness is 0.05-0.06 μm.
Described back coating and release coating lay respectively at the two sides of base material, and the weight percent of described back coating consists of: organosilicon 3-3.5%, solvent 96.5-97%.The thickness of described back coating can be ignored.
Described base material is polyester material, and thickness is 4.2-4.5 μm.
Dispersant major function in ink layer component is the scattering problem solving pigment, and granules of pigments is scattered in system equably.
Described hot transfer wax ribbon is conventionally prepared, and has no special requirements.
Hot transfer wax ribbon provided by the invention, ink coating can be transferred to after applicable energy level is heated undertakes the printing of (transferring rate >95%) on carrier, ink coating has adaptability widely to carrier of undertaking the printing of, and can realize high-quality transfer printing on the carriers of undertaking the printing of such as non-coated paper, coated paper, heat-transferring printing paper; Adhesive force is good, scratch-resistant, adhesion, can be applicable to various speed (2ips, 4ips, 6ips), more extensively print the heat transfer type bar code printer of energy level (the printing gear of bar code printer, generally from 0 to 30, energy level scope of the present invention can be 14-28).Ink coating and release coating have good adhesion simultaneously; Its release coating has good intermediary performance, is less than the adhesive force with ink coating with the adhesive force of base material, and transferability is fine, and transfer printing character edge is neat, has good flexibility.
The present invention, relative to prior art, has following advantage:
Hot transfer wax ribbon provided by the invention, transferring rate is high, and adhesive force is good, scratch-resistant, adhesion, can be applicable to various speed, more extensively print energy level and difference and to undertake the printing of the heat transfer type bar code printer of carrier.
Detailed description of the invention
With specific embodiment, technical scheme of the present invention is described below, but protection scope of the present invention is not limited thereto:
Embodiment 1
Base material is polyester (PET basement membrane), and thickness is 4.5 μm;
Every 100g is composed as follows for ink coating:
Dispersant |
0.8 |
Palm wax |
16.5 |
Vinylite |
2.5 |
Pigment |
9.6 |
Full refining wax |
16.8 |
Petropols |
1.2 |
Solvent |
52.6 |
Every 100g is composed as follows for release coating:
Every 100g is composed as follows for back coating:
Organosilicon |
3g |
Solvent |
97g |
Vinylite selects the VA-600 of Hunan petrochemistry company, Petropols select the A-1100 of Heng Shi company, the Carnauba-3 of Foncepi company selected by palm wax, the AP-1000 of Heng Shi company selected by full refining wax, the BeBlack6316F1 of Yong Feng company selected by pigment, dispersant selects A4300 and the 1005(A4300:1005 mass ratio=5:2 of refined rich color science and technology), solvent uses toluene.The ES-110 of SK chemical industry selected by mylar.The KR-605 of Ke Lin company selected by organosilicon.
By back coating compositing formula, make mixed solution, by coating apparatus at substrate backside coating film forming, dry under 105 DEG C of conditions.Make hybrid resin solvent by release coating formula again, be coated into by coating apparatus the film that thickness is 0.05-0.06 μm, dry under 105 DEG C of conditions.According to ink layer formula, first dispersant heating for dissolving in a solvent, other components are added again by the order of above-mentioned formula, by grinder, system is uniformly dispersed, be coated in release coating by coating machine, dry at the temperature of 105 DEG C, its thickness is 2.5 μm, forms hot transfer wax ribbon.
Embodiment 2
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.8 |
Palm wax |
16.5 |
Vinylite |
2.5 |
Pigment |
9.6 |
Full refining wax |
14.4 |
Petropols |
2.9 |
Mylar |
0.7 |
Solvent |
52.6 |
Wherein the ES-812 of SK chemical industry selected by mylar; All the other material therefors are identical with embodiment 1.By as above filling a prescription, first dispersant heating for dissolving in a solvent, add other components in the order by above-mentioned formula, by grinder, system is uniformly dispersed, is coated in release coating by coating machine, dry at the temperature of 105 DEG C, its thickness is 2.5 μm, forms hot transfer wax ribbon.
The composition of release coating, back coating and preparation method are with embodiment 1.
Embodiment 3
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.7g |
Pigment |
9.6g |
Palm wax |
16.5g |
Full refining wax |
13.2g |
Vinylite |
2.5g |
Petropols |
3.9g |
Mylar |
1.0g |
Solvent |
52.6g |
Other are with embodiment 1.
Embodiment 4
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.8g |
Pigment |
9.6g |
Palm wax |
16.5g |
Full refining wax |
14.4g |
Vinylite |
0g |
Petropols |
4.9g |
Mylar |
1.2g |
Solvent |
52.6g |
Other are with embodiment 1.
Embodiment 5
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.7g |
Pigment |
9.6g |
Palm wax |
16.5g |
Full refining wax |
13.2g |
Vinylite |
1.3g |
Petropols |
4.9g |
Mylar |
1.2g |
Solvent |
52.6g |
Other are with embodiment 1.
Embodiment 6
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.8g |
Pigment |
9.6g |
Palm wax |
16.5g |
Full refining wax |
13.2g |
Vinylite |
1.3g |
Petropols |
6.0g |
Solvent |
52.6g |
Other are with embodiment 1.
Embodiment 7
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.7g |
Pigment |
9.6g |
Palm wax |
16.5g |
Full refining wax |
14.4g |
Vinylite |
1.3g |
Petropols |
3.9g |
Mylar |
1.0g |
Solvent |
52.6g |
Other are with embodiment 1.
Embodiment 8
Base material is polyester, and thickness is 4.5 μm
Ink coating:
Dispersant |
0.7g |
Pigment |
9.6g |
Palm wax |
16.5g |
Full refining wax |
13.2g |
Vinylite |
1.3g |
Petropols |
5.5g |
Mylar |
0.6g |
Solvent |
52.6g |
Other are with embodiment 1.
Embodiment 9
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.8g |
Pigment |
9.6g |
Palm wax |
16.5g |
Full refining wax |
13.2g |
Vinylite |
2.5g |
Petropols |
4.3g |
Mylar |
0.5g |
Solvent |
52.6g |
Other are with embodiment 1.
Embodiment 10
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.7g |
Palm wax |
16.5g |
Vinylite |
1.3g |
Pigment |
9.6g |
Full refining wax |
13.2g |
Petropols |
4.9g |
Acrylic resin |
1.2g |
Solvent |
52.6g |
Wherein acrylic resin selects the 13LP of permanent stone; Other are with embodiment 1.
Embodiment 11
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.7g |
Palm wax |
16.5g |
Vinylite |
1.3g |
Pigment |
9.6g |
Full refining wax |
13.2g |
Petropols |
5.5g |
Acrylic resin |
0.6g |
Solvent |
52.6g |
Wherein acrylic resin selects the 13LP of permanent stone, and other are with embodiment 1.
Embodiment 12
Base material is polyester, and thickness is 4.5 μm
Ink coating:
Dispersant |
0.7g |
Palm wax |
16.5g |
Vinylite |
1.3g |
Pigment |
9.6g |
Full refining wax |
14.4g |
Petropols |
3.9g |
Acrylic resin |
1.0g |
Solvent |
52.6g |
Wherein acrylic resin selects the CPP of permanent stone, and other are with embodiment 1.
Embodiment 13
Base material is polyester, and thickness is 4.5 μm;
Ink coating:
Dispersant |
0.7g |
Palm wax |
16.5g |
Vinylite |
2.5g |
Pigment |
9.6g |
Full refining wax |
13.2g |
Petropols |
3.9g |
Acrylic resin |
1.0g |
Solvent |
52.6g |
Wherein acrylic resin selects the CPP of permanent stone, and other are with embodiment 1.
effect
The hot transfer wax ribbon that above-described embodiment 1-13 is manufactured observe its transferring effect, with to undertake the printing of the adhesive force of paper and the adaptability to carrier of undertaking the printing of.
Transferring effect is that the transferring rate of ink layer realizes, and is divided into three phases by following benchmark, >95% → A, 95-90% → B, <90% → C by after printing.
Adhesive force is the bistrique with loading 800 grams, rubs 50 times, observe the damaged area of transferred ink layer to paper of undertaking the printing of, with without breakage → A, damaged fewer than half → B, complete breakage → C evaluate damaged area.
The adaptability of carrier of undertaking the printing of does printing test with dissimilar paper of undertaking the printing of, and the rank of its applicability transferring rate is evaluated, >95% → A, 95-90% → B, <90% → C.
Above-described embodiment is the preferred embodiment of the present invention, but embodiments of the present invention are not restricted to the described embodiments, and the change that other any the present invention of not deviating from does all should be equivalent substitute mode, is included within protection scope of the present invention.