CN102615747A - 一种脱模剂及其制备方法和用途 - Google Patents
一种脱模剂及其制备方法和用途 Download PDFInfo
- Publication number
- CN102615747A CN102615747A CN2011100361006A CN201110036100A CN102615747A CN 102615747 A CN102615747 A CN 102615747A CN 2011100361006 A CN2011100361006 A CN 2011100361006A CN 201110036100 A CN201110036100 A CN 201110036100A CN 102615747 A CN102615747 A CN 102615747A
- Authority
- CN
- China
- Prior art keywords
- releasing agent
- solvent
- polysiloxanes
- bond
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种脱模剂,其包含下述成分:具有硅氢键的聚硅氧烷、脱氢缩合反应催化剂和溶剂。本发明的脱模剂为半永久型脱模剂,此外还具有组成简单、低温快速固化、脱模剂转移少、积蜡少、施加方便以及成本低等优点,所述的脱模剂尤其在制造聚氨酯泡沫制品领域中取得了重大突破,制得的制品开孔均匀。本发明还提供了所述脱模剂的制造方法,以及其在制造聚氨酯泡沫制品、环氧树脂制品、玻璃纤维增强环氧树脂制品、橡胶制品、不饱和聚酯制品和其他聚氨酯类制品中的用途。
Description
技术领域
本发明涉及一种脱模剂、其制备方法和用途。具体地说,本发明涉及特别适用于聚氨酯泡沫制品的脱模剂、其制备方法和用途。
背景技术
在制造高分子材料制品时,一般采用模塑成型法:将熔体或溶液状材料注入模具,固化成型后,再从模具中取出成型制品。为了帮助从模具中取出制品,一般会在模具上预先涂敷脱模剂,从而使得制品冷却后与模具之间不形成粘结,进而保证制品的质量。常规的脱模剂以牺牲型脱模剂为主,所谓牺牲型脱模剂即单个制品在模具中成型后被消耗或以其他方式完全耗尽的脱模剂。牺牲型脱模剂必须在制造每个制品之前重新涂覆到模具表面上。遗憾的是,使用牺牲型脱模剂会产生很多问题:1)随着脱模剂的反复使用,脱模剂会积聚在模具表面上形成积垢,从而使模具的详细特征模糊,这会导致模具表面特征结构不能够被清晰的复印至高分子制品的表面上,以至破坏制品表面的完整性。2)由于积垢的存在,需要对模具进行定期的清洁,这导致人力和物力的增加,并使产能减少;另外,在清洗模具的过程中,会对模具产生不同程度的破坏,从而减少模具的使用寿命。3)由于牺牲型的脱模剂会转移到高分子材料制品的表面,所以会影响制品的后续加工。4)由于牺牲型脱模剂需要在制造每个制品之前重新施用到模具表面,这使得脱模剂的需求用量大大增加,同时也会增加挥发性有机物(VOC,例如脱模剂中的溶剂)的排放量,从而使得生产成本增加,且环保方面的压力也增加。
因此,开发一种可以重复脱模的脱模剂就能在较大程度上克服上述缺点。对于某些高分子制品,如环氧树脂制品、玻璃纤维增强型环氧树脂制品和橡胶制品等已有脱模剂能够实现多次脱模的效果。
但是,对于不同于上述高分子材料制品的聚氨酯泡沫制品,情况则不一样,因为公知的是要制得可以方便使用的用于聚氨酯泡沫制品的半永久型脱模剂的研发难度很大。
聚氨酯泡沫体系中通常含有异氰酸酯基(NCO)、聚醚多元醇或聚酯多元醇链段、发泡剂、匀泡剂、稳泡剂、催化剂等。由于NCO具有高反应活性,能与羟基、羧基、氨基等多种活性基团反应,因此对用于聚氨酯泡沫体系的半永久型脱模剂的首先要求是其不与NCO反应;其次,匀泡剂和稳泡剂是表面活性剂类材料,起到帮助获得细致均匀聚氨酯泡沫的作用,所以对脱模剂的要求是其不能改变聚氨酯泡沫体系的表面活性剂材料的组成,从而避免出现聚氨酯泡沫表面的消泡现象;还有,水以及一些低沸点溶剂是聚氨酯泡沫材料中通常采用的发泡剂,所以对所希望的半永久型脱模剂的要求是其不能改变发泡剂的组成,原因是水基脱模剂中的水由于难以在较短的时间内全部挥发干净(聚氨酯泡沫成型加工温度较低-室温~80℃),因此其会影响到发泡剂的组成。另外,不同的聚氨酯泡沫体系对脱模剂的适用时间(从涂敷脱模剂到注射聚氨酯发泡原料的时间)有不同的要求,有的时间只有短暂的十几秒左右,而有的则稍长,因此,基于聚氨酯泡沫体系固化的特殊要求,以易挥发溶剂为基础的脱模剂是必要的。
用于制造聚氨酯泡沫制品的半永久型脱模剂还需满足以下要求:
1)脱模剂具有高反应活性
一般制备聚氨酯泡沫的模具温度较低(室温~80℃),而半永久型聚氨酯脱模剂在涂敷后的固化时间要求较短。因此,低温下的快速固化是半永久型聚氨酯泡沫用脱模剂一定要解决的问题,所以该种脱模剂既不能与NCO反应,同时其自身也要具有高反应活性。
2)脱模剂涂层具有高惰性
由于聚氨酯泡沫原料中的NCO可与大部分的有机官能团反应,包括羟基、羧基、氨基等,因此脱模剂的涂层中应避免存在这些活性基团,脱模剂固化后的涂层应具有高惰性,但是这往往导致脱模剂无法在低温下快速固化。
3)脱模剂涂层具有高交联度
聚氨酯泡沫表层的开孔要均匀,不能出现严重的缺陷。而当脱模剂中还残留游离的低表面能物质时,其易被聚氨酯泡沫发泡过程中形成的泡沫通过毛细作用吸附,由此改变发泡体系原有的表面张力,从而导致聚氨酯制品表面出现结皮或塌陷。这就要求脱模剂涂层中的交联度极高,基本上没有什么残余物。
4)脱模剂的涂层具有高强度
与模具的强相互作用力是半永久型脱模剂的基本要求;另外,由于聚氨酯泡沫制品在制备过程中会形成大量的微泡,其毛细作用力很大,这就更要求脱模剂涂层具有足够的强度,以避免被破坏。
一般来说,聚氨酯泡沫制品目前所采用的脱模剂是基于溶剂型微晶态石蜡或溶剂型微晶态石蜡和有机硅的混合物。这些脱模剂基本满足聚氨酯泡沫体系固化的要求,但这些脱模剂都属于牺牲型脱模剂。
JP 2004034464公开了将聚乙烯蜡分散在有机溶剂中,用于脱聚氨酯泡沫。再例如DE102006026870.9公开了将聚乙烯蜡和微晶蜡熔融并加入烃类溶剂,用于脱聚氨酯泡沫。
另一方面,也有报道聚氨酯泡沫制品中已采用包含多组分聚硅氧烷作为脱模剂的溶剂型脱模组合物,这些脱模剂可重复多次使用。例如,US 4,761,443中公开了一种用于高弹性聚氨酯泡沫材料的脱模组合物,其包含两种羟基封端的聚二甲基硅氧烷和含氢硅油交联剂作为脱模剂,所述的脱模组合物在模具表面形成可重复使用的快速固化脱模涂层。但是,该组合物中的反应物为多组分,其需要在使用之前进行配制,并在一定的时间内使用,否则配制的混合物将发生反应。所以,该脱模剂的储存和使用不方便。
所以,若能制得组成简单、存储稳定、可方便使用的半永久型聚氨酯泡沫用脱模剂将是本领域的重要突破。另外,通常情况下,能够满足聚氨酯泡沫制品多次脱模要求的脱模剂,一般都能适用于其他高分子制品,如环氧树脂制品、玻璃纤维增强型环氧树脂制品、橡胶制品、不饱和聚酯制品和其他聚氨酯类制品等。
发明内容
本发明提供了一种脱模剂,其包含下述成分:具有硅氢键的聚硅氧烷、用于脱氢缩合反应的催化剂,以及溶剂。
本发明的脱模剂为半永久型脱模剂,即涂布一次能够实现多次脱模,重要的是,本发明的脱模剂具有组成简单、低温快速固化、脱模剂转移少、积蜡少、储存稳定、以及施用方便等优点。所述的脱模剂尤其在制造聚氨酯泡沫制品的领域中取得了重大突破,使用本发明的脱模剂时制得的聚氨酯泡沫制品开孔均匀。
本发明还提供了制备以上所述脱模剂的方法:其包括将具有硅氢键的聚硅氧烷、用于脱氢缩合反应的催化剂以及溶剂在搅拌下物理混合。
本发明还提供了以上所述的脱模剂在制造聚氨酯制品、环氧树脂制品、橡胶制品、聚酯制品等中的用途。
附图说明
图1所示为本发明中所用原料SiH-1的分子量检测结果GPC图。
具体实施方式
在本发明中,“半永久型脱模剂”的含义是指:脱模剂在单次模塑操作之后不被完全耗尽,涂布一次脱模剂,就能够实现多次脱模操作。
在本发明的脱模剂中所用的具有硅氢键的聚硅氧烷中,所述的硅氢键具有高反应活性,其在催化剂和水分子的共同作用下形成硅羟基,进而与未反应的硅氢基进行脱氢反应,形成自交联的涂层,以实现脱模剂的半永久性。由于这种能够实现自交联的具有硅氢键的聚硅氧烷的使用,可以减少或者避免常用交联剂(如烷氧基硅烷等)的使用量。
所述的具有硅氢键的聚硅氧烷的平均组成由如下通式(1)表示:
(R1R2R3SiO1/2)M·(R4R5SiO2/2)D·(R6SiO3/2)T·(SiO4/2)Q (1),
其中:
每一处的R1至R6彼此独立地选自氢和有机基,
条件是:
R1至R6中的至少一个是直接键接于硅原子上、由此形成硅氢键的氢原子,在通式(1)所构成的聚硅氧烷分子中,平均含有至少两个硅氢键,并且,不是所有的R1至R6都为氢原子,并且,
M、T、Q分别代表大于等于0且小于1的数,D代表大于0且小于1的数,并且同时满足关系式M+D+T+Q=1,和T+Q>0。
在上述通式(1)中,直接键接于硅原子上的氢原子相对于所述具有硅氢键的聚硅氧烷的质量百分比优选为0.01-1.63%,更优选地,直接键接于硅原子上的氢原子相对于所述具有硅氢键的聚硅氧烷的质量百分比为0.1-1.6%。
在上述通式(1)中,所述聚硅氧烷的重均分子量为400-500,000g/mol,更优选所述重均分子量为10,000-300,000g/mol。
在通式(1)中,“每一处”表示R1-R6中的任何一个的每一次出现都是独立的,其可以相同也可以不同。
在一个优选的实施方案中,R1至R6的有机基选自具有1至20个碳原子的直链或支链的烷基、具有2至20个碳原子的烯基、具有5至25个碳原子的环烷基、环烯基、具有6至30个碳原子的芳基、具有7至30个碳原子的芳基烷基、或它们的卤代物。
在一个优选的实施方案中,R1至R6的有机基彼此独立地选自具有1至8个碳原子的直链或支链的烷基,具有2至8个碳原子的烯基、具有5至10个碳原子的环烷基或环烯基、具有6至10个碳原子的芳基、或具有7至30个碳原子的芳基烷基。
在一个更优选的实施方案中,通式(1)中的R1至R6的有机基独立地是甲基、乙基、丙基、正丁基、异丁基、叔丁基、戊基、异戊基、新戊基、己基、异己基、庚基、异庚基、辛基、异辛基、壬基、癸基、乙烯基、烯丙基、己烯基、环戊基、环己基、环辛基、二环戊基、环戊烯基、环己烯基、苯基、甲苯基、乙苯基或者上述基团的卤代物,更优选为甲基、乙基、丙基、苯基或乙烯基,最优选为甲基、乙基、丙基或苯基。
在本发明中,“卤代物”可以为一卤代物或多卤代物,其中卤素选自氟、氯、溴或碘,优选选自氟、氯或溴。
在上述通式(1)中,M、T、Q分别代表大于等于0且小于1的数,D代表大于0且小于1的数,并且同时满足,M+D+T+Q=1,T+Q>0。在优选的实施方案中,M为0.01至0.5,D为0.1至0.8,T为0.1至0.7,Q为由0至0.5,更优选M为0.1至0.3,D为0.1至0.6,T为0.1至0.6,Q为0至0.3。
所述的具有硅氢键的聚硅氧烷的含量无特殊限制,优选为脱模剂总质量的0.1-80.0%,更优选为1.0-50.0%,最优选2.0-40.0%。
所述的具有硅氢键的聚硅氧烷可以为液体或固体,只要其能够被分散在合适的溶剂中。
所述具有硅氢键的聚硅氧烷的制备如下:将至少一种具有硅氢键的硅油、至少一种羟基硅树脂和至少一种脱氢催化剂分散在溶剂中,形成分散体,使所述分散体反应,然后除去溶剂和催化剂而得到所要求的具有硅氢键的聚硅氧烷。
其中,所述具有硅氢键的硅油包括下式(II)的直链的具有硅氢键的硅油,
其中R是甲基或氢,m>0,n≥0,每个分子中Si-H基团的数目是≥3,且直接键接于硅原子上的氢原子相对于所述具有硅氢键的聚硅氧烷的质量百分比为0.1-1.6%;
和/或包括下式(III)的环状的具有硅氢键的硅油:
其中x>0,y≥0,每个分子中Si-H基团的数目是≥3,且直接键接于硅原子上的氢原子相对于所述具有硅氢键的聚硅氧烷的质量百分比为0.1-1.6%;
所述羟基硅树脂具有下式(IV)的平均组成:
(R’1R’2R’3SiO1/2)M’·(R’4R’5SiO2/2)D’·(R’6SiO3/2)T’·(SiO4/2)Q’,(IV)
其中R’1至R’6是相同或者不同的基,并且独立地选自羟基和有机基,且至少R’1至R’6之一是羟基,
M’、D’、T’和Q’各自表示0-小于1的数,M’+D’+T’+Q’=1,且T’+Q’>0,并且羟基硅树脂的每个分子中Si-OH基团的数目是≥3;
条件是,具有硅氢键的聚硅氧烷中的Si-H基团与羟基硅树脂分子中Si-OH基团的摩尔比是1.0-100.0。
本发明所述的催化剂为Si-H和Si-OH脱氢缩合反应的常规催化剂,并无特殊限制,优选包括胺类催化剂和/或有机金属类催化剂。
其中所述胺类催化剂优选为以下的一种或多种:三亚乙基二胺、双(二甲氨基乙基醚)、二甲基环己胺、N-甲基二环己胺、五甲基二亚乙基三胺、五甲基二亚丙基三胺、四甲基乙二胺、四甲基丙二胺、四甲基己二胺、N-甲基吗啉、N-乙基吗啉、2,2-双吗啉基二乙基醚、可可吗啉、N-甲基咪唑、1,2-二甲基咪唑、1,4-二甲基哌嗪、1,8-二氮杂双环[5.4.0]十一碳-7-烯、1,1,3,3-四甲基胍、2,4,6-三(二甲氨基甲基)苯酚、1,3,5-三(二甲基胺丙基)-1,3,5-六氢化三嗪、N,N-二甲基乙醇胺、N,N-二甲基氨乙基乙二醇、三甲基羟乙基丙二胺、N-甲基-N-(N,N-二甲胺基乙基)乙醇胺、N,N-二甲基苄胺、三(二甲氨丙基)胺、三乙胺、N,N-二甲基(十六烷基)胺、乙烯基三丁酮肟基硅烷和四甲基亚胺基二丙基胺;所述有机金属类催化剂优选为以下的一种或多种:二月桂酸二丁基锡、辛酸亚锡、二(十二烷基硫)二丁基锡、二醋酸二丁基锡、异辛酸钾、醋酸钾、油酸钾、异辛酸铅、异辛酸锌、醋酸苯汞、钛酸四丁酯、钛酸四异丙酯、铂类催化剂和铑类催化剂。
本发明所述的催化剂优选地选自以下催化剂中的一种或多种:三亚乙基二胺、辛酸亚锡、1,1,3,3-四甲基胍、乙烯基三丁酮肟基硅烷、异辛酸锌、四甲基亚胺基二丙基胺、钛酸四丁酯、三乙胺和二醋酸二丁基锡。
本发明所述铂类催化剂选自二氧化铂、氯铂酸、氯铂酸与二烯烃的络合物、或双(乙酰丙酮)铂。
所述催化剂的含量无特殊限制,优选为脱模剂总质量的0.01-5.0%,更优选为0.1-2.0%,最优选为0.1-1.0%。
本发明所述的溶剂的选择原则是能将上述具有硅氢键的聚硅氧烷、催化剂等成分均匀分散、易挥发的溶剂,且该溶剂应该是对反应物惰性的。优选为以下的一种或多种溶剂:醇类、醇醚类、酮类、酯类、脂肪烃类、脂环烃类、芳香烃类和醚类。
所述醇类溶剂优选为以下的一种或多种:乙醇、异丙醇、丙二醇、丁醇、1,4-丁二醇、1,3-丁二醇和丙三醇;醇醚类溶剂优选为以下的一种或多种:乙二醇单丁醚、丙二醇单甲醚、丙二醇单丁醚;酮类溶剂优选为以下的一种或多种:丙酮、丁酮、甲基异丁基酮和环己酮;酯类溶剂优选为以下的一种或多种:醋酸甲酯、醋酸乙酯和醋酸丁酯;脂肪烃类溶剂优选为以下的一种或多种:正己烷、四氯化碳、石油醚和异构烷烃溶剂(如Isopar C、Isopar E、Isopar H);脂环烃类溶剂优选为以下的一种或多种:环戊烷和环己烷;芳香烃类溶剂优选为以下的一种或多种:甲苯和二甲苯;醚类溶剂优选为以下的一种或多种:四氢呋喃、二异丙醚和二丁醚。
所述溶剂的含量优选为脱模剂总质量的10.0-99.85%,更优选为40.0-99.0%,最优选为50.0-98.0%。
本发明的脱模剂还可包含其他添加剂,只要它们及其用量不显著地对本发明脱模剂带来不利的影响。所述的其他添加剂优选地包括下列添加剂中的一种或多种:颜料、硅烷、流平剂、抗老化剂、增粘剂和脱模剂转移指示剂等。
在本发明的脱模剂的制备方法中,将脱模剂的各组成成分,包括具有硅氢键的聚硅氧烷、用于脱氢缩合反应的催化剂以及溶剂,在搅拌下物理混合。所述的物理混合的温度只要低于所选用溶剂的沸点即可,并无特殊限制,优选在0-100℃下进行,更优选在0-70℃进行。所述的搅拌速度也无任何特殊限制,优选在10-1500rpm的搅拌转速下进行,更优选在100-1000rpm的搅拌转速下进行。反应时间无任何特殊限制,优选1-500分钟,更优选120分钟。
一个优选的制备方法是在0-100℃的温度下和10-1500rpm的搅拌转速下进行1-500min的混合。在一个更优选的实施方案中,混合的温度是0-70℃,在100-1000rpm的搅拌的转速下进行1-120min的混合。
各组分的混合顺序没有特别的限制,例如可以先将具有硅氢键的聚硅氧烷与溶剂混合,即采用溶剂稀释聚硅氧烷,然后再加入催化剂;或者可以将各组分同时混合,或者将聚硅氧烷和催化剂一同加入,再加入溶剂稀释;优选在干燥密闭的容器中进行所述的物理混合。
本发明还提供了所述的脱模剂在制造高分子制品中的用途。本发明的脱模剂优选地可用于制造聚氨酯制品、环氧树脂制品、玻璃纤维增强型环氧树脂制品、橡胶制品、饱和或者不饱和聚酯制品等。
本发明中所用的脱模剂是涂敷或喷洒在模塑成型的模具上的,所述模具一般是由金属制得,例如铝、黄铜等,也可以采用非金属材料,例如树脂材料等模具。
本发明所制得的脱模剂为半永久型脱模剂,涂敷施用一次,能实现脱模多次(5次以上),施用方便。该脱模剂的组成简单、储存稳定性非常好,并且具有低温快速固化的特点;可减少脱模剂的施用量,以及VOC的排放量;减少模具表面的积蜡,并减少模具清洗时间,提高模具的利用率和生产效率。由于脱模剂的极低的转移率,使得制品表面残留的脱模剂量极少,从而不影响模塑制品的后续加工。
根据本发明的脱模剂特别适合于聚氨酯泡沫材料、聚氨酯弹性体等具有特殊要求的高分子材料的模塑成型;当然,其更可以适用于一般其他的普通高分子制品的成型,该普通高分子制品如环氧树脂制品、玻璃纤维增强型环氧树脂制品、橡胶制品、饱和或不饱和聚酯制品等。
实施例
下面用实施例来进一步说明本发明,但本发明并不受其限制。
测试方法
在本发明中,具有硅氢键的聚硅氧烷的分子量通过尺寸排阻色谱法(SEC)分析,确切地就是采用凝胶渗透色谱GPC法进行分析,其中具体的测量条件如下:
-洗脱液: THF(四氢呋喃)
-标准物: 聚苯乙烯
-温度: 35℃(柱温和RI检测器).
其它优选参数如下:
-流速: 0.8ml/min
-检测: RI(折光指数)
-3Plgel混合的-D系列柱(Polymer laboratories,7.5*300mm)
-样品准备: 2.5mg/ml,在THF中
-注射体积: 100μl.
实施例中使用的具有硅氢键的聚硅氧烷为:
SiH-1:
((CH3)3SiO1/2)0.063((CH3)2SiO2/2)0.155(HCH3SiO2/2)0.520(CH3SiO3/2)0.262,其重均分子量为87000,硅氢键上的氢在聚硅氧烷中的含量为0.79%
SiH-2:
((CH3)3SiO1/2)0.063((CH3)2SiO2/2)0.153(HCH3SiO2/2)0.520(CH3SiO3/2)0.150(PhSiO3/2)0.114,其重均分子量为50000,硅氢键上的氢在聚硅氧烷中的含量为0.72%
SiH-3:
((CH3)3SiO1/2)0.005((CH3)2SiO2/2)0.230(HCH3SiO2/2)0.265(CH3SiO3/2)0.305(PhSiO3/2)0.195,其重均分子量为210000,硅氢键上的氢在聚硅氧烷中的含量为0.33%
SiH-4:
((CH3)3SiO1/2)0.006((CH3)2SiO2/2)0.260(HCH3SiO2/2)0.334(CH3SiO3/2)0.244(PhSiO3/2)0.156,其重均分子量为12000,硅氢键上的氢在聚硅氧烷中的含量为0.43%
SiH-5:
((CH3)3SiO1/2)0.050((CH3)2SiO2/2)0.150(HCH3SiO2/2)0.330(PhSiO3/2)0.370(SiO4/2)0.100,其重均分子量为94000,硅氢键上的氢在聚硅氧烷中的含量为0.36%
SiH-6:
((CH3)3SiO1/2)0.080((CH3)(C3H7)SiO2/2)0.350(HCH3SiO2/2)0.430(CH3SiO3/2)0.040(SiO4/2)0.100,其重均分子量为73000,硅氢键上的氢在聚硅氧烷中的含量为0.56%
SiH-7:
((CH3)3SiO1/2)0.020((CH3)2SiO2/2)0.430(HCH3SiO2/2)0.130(PhSiO3/2)0.120(SiO4/2)0.300,其重均分子量为320000,硅氢键上的氢在聚硅氧烷中的含量为0.17%
SiH-8:
((CH3)3SiO1/2)0.010((CH3)2SiO2/2)0.250(HCH3SiO2/2)0.190(CH3SiO3/2)0.050(SiO4/2)0.500,其重均分子量为18000,硅氢键上的氢在聚硅氧烷中的含量为0.30%
实施例1
半永久型脱模剂的配方见表1。
按表1中的用量将具有硅氢键的聚硅氧烷添加到装有溶剂的分散釜中,然后在100rpm的搅拌下加入催化剂,在20℃的温度下,在100rpm的转速下继续搅拌5min,得到半永久型脱模剂。
表1
实施例2
半永久型脱模剂的配方见表2。
按表2中的用量将具有硅氢键的聚硅氧烷添加到装有溶剂的分散釜中,然后在200rpm的搅拌下加入催化剂,在25℃的温度下,在200rpm的转速下继续搅拌6min,得到半永久型脱模剂。
表2
实施例3
半永久型脱模剂配方见表3。
按表3中的用量将具有硅氢键的聚硅氧烷添加到装有溶剂的分散釜中,然后在250rpm的搅拌下加入催化剂和硅烷,在30℃的温度下,在250rpm的转速下继续搅拌7min,得到半永久型脱模剂。
表3
实施例4
半永久型脱模剂的配方见表4。
按表4中的用量将具有硅氢键的聚硅氧烷添加到装有溶剂的分散釜中,然后在250rpm的搅拌下加入催化剂,在20℃的温度下,在250rpm转速下继续搅拌3min,得到半永久型脱模剂。
表4
实施例5
半永久型脱模剂的配方见表5。
按表5中的用量将具有硅氢键的聚硅氧烷、溶剂和催化剂添加到分散釜中,在20℃的温度下,在300rpm的转速下继续搅拌8min,得到半永久型脱模剂。
表5
实施例6
半永久型脱模剂的配方见表6。
按表6中的用量将具有硅氢键的聚硅氧烷添加到装有溶剂的分散釜中,然后在300rpm的搅拌下加入催化剂,在20℃的温度下,在300rpm的转速下继续搅拌1min,得到半永久型脱模剂。
表6
实施例7
半永久型脱模剂的配方见表7。
按表7中的用量将具有硅氢键的聚硅氧烷添加到装有溶剂的分散釜中,然后在300rpm的搅拌下加入催化剂,在30℃的温度下,在300rpm转速下继续搅拌1min,得到半永久型脱模剂。
表7
实施例8
半永久型脱模剂的配方见表8。
按表8中的用量将具有硅氢键的聚硅氧烷添加到装有溶剂的分散釜中,然后在300rpm的搅拌下加入催化剂,在10℃的温度下,在300rpm转速下继续搅拌5min,得到半永久型脱模剂。
表8
比较实施例1
牺牲型聚氨酯软泡脱模剂:KP-GHT(厦门凯平化工有限公司)。(希望申请人适当提供描述意见)脱模剂的有效成份为直链脂肪类石蜡型(C20H42到C36H74),有效成份含量为1.5%,百分比为重量比,溶剂为碳氢类溶剂。
效果实施例
脱模剂效果测试
将铝制模具加热到50-60℃,使用0.5mm的喷嘴,将实施例1-11和比较实施例1的脱模剂以实际量5g/m2喷射到铝制模具表面,固化1-2min后,将可泡沫化的聚氨酯体系注射到喷有脱模剂的铝制模具表面,发泡4min后,从模具中取出聚氨酯泡沫。
表12脱模效果的测量结果
实施例脱模剂 | 泡沫表面评定 | 脱模次数 |
1 | 细开孔、干燥 | 13 |
2 | 细开孔、干燥 | 20 |
3 | 细开孔、干燥 | 12 |
4 | 细开孔、干燥 | 13 |
5 | 细开孔、干燥 | 16 |
6 | 细开孔、干燥 | 12 |
7 | 细开孔、干燥 | 13 |
8 | 细开孔、干燥 | 15 |
比较实施例1 | 细开孔、干燥 | 2 |
由表12可见,采用本发明的脱模剂的配方及方法制备得到的脱模剂能实现半永久型,而不再需要每次重新涂抹脱模剂,施工方便,从而减少脱模剂的施用量以及表面积蜡。制得的制品开孔细、干燥,说明制品表面残留的脱模剂量少,脱模剂的转移率极低。
将本发明的脱模剂置于密封瓶中,在60℃的烘箱中存放2个月后,其脱模效果未见显著改变,这说明脱模剂的存贮稳定好。
将本发明的脱模剂置于敞口瓶中,在室温下存放8小时后,其脱模效果未见显著改变,可以满足脱模剂的施工要求。
Claims (27)
1.一种脱模剂,其包含下述成分:具有硅氢键的聚硅氧烷、用于脱氢缩合反应的催化剂,以及溶剂。
2.如权利要求1所述的脱模剂,其中具有硅氢键的聚硅氧烷的平均组成由如下通式(1)表示:
(R1R2R3SiO1/2)M·(R4R5SiO2/2)D·(R6SiO3/2)T·(SiO4/2)Q (1),
其中:
每一处的R1至R6彼此独立地选自氢和有机基,
条件是:
R1至R6中的至少一个是直接键接于硅原子上、由此形成硅氢键的氢原子,在通式(1)所构成的聚硅氧烷分子中,平均含有至少两个硅氢键,并且,不是所有的R1至R6都为氢原子;并且,
M、T、Q分别代表大于等于0且小于1的数,D代表大于0且小于1的数,并且同时满足关系式M+D+T+Q=1,和T+Q>0。
3.如权利要求2所述的脱模剂,其中直接键接于硅原子上的氢原子相对于所述具有硅氢键的聚硅氧烷的质量百分比为0.01-1.63%。
4.如权利要求3所述的脱模剂,其中直接键接于硅原子上的氢原子相对于所述具有硅氢键的聚硅氧烷的质量百分比为0.1-1.6%。
5.如权利要求2所述的脱模剂,所述聚硅氧烷的重均分子量为400-500,000g/mol。
6.如权利要求5所述的脱模剂,其中所述具有硅氢键的聚硅氧烷的重均分子量为10,000-300,000g/mol。
7.如权利要求2所述的脱模剂,其中所述有机基选自具有1至20个碳原子的直链或支链的烷基、具有2至20个碳原子的烯基、具有5至25个碳原子的环烷基或环烯基、具有6至30个碳原子的芳基、具有7至30个碳原子的芳基烷基、或它们的卤代物。
8.如权利要求7所述的脱模剂,其中所述有机基选自具有1至8个碳原子的直链或支链的烷基,具有2至8个碳原子的烯基、具有5至10个碳原子的环烷基或环烯基、具有6至10个碳原子的芳基、或具有7至30个碳原子的芳基烷基。
9.如权利要求1-8之一所述的脱模剂,其中所述具有硅氢键的聚硅氧烷的含量为脱模剂总质量的0.1-80.0%。
10.如权利要求9所述的脱模剂,其中所述具有硅氢键的聚硅氧烷的含量为脱模剂总质量的1.0-50.0%。
11.如权利要求1-8之一所述的脱模剂,其中所述脱氢缩合反应的催化剂为胺类催化剂和/或有机金属类催化剂。
12.如权利要求11所述的脱模剂,其中所述胺类催化剂选自以下的一种或多种:三亚乙基二胺、双(二甲氨基乙基醚)、二甲基环己胺、N-甲基二环己胺、五甲基二亚乙基三胺、五甲基二亚丙基三胺、四甲基乙二胺、四甲基丙二胺、四甲基己二胺、N-甲基吗啉、N-乙基吗啉、2,2-双吗啉基二乙基醚、可可吗啉、N-甲基咪唑、1,2-二甲基咪唑、1,4-二甲基哌嗪、1,8-二氮杂双环[5.4.0]十一碳-7-烯、1,1,3,3-四甲基胍、2,4,6-三(二甲氨基甲基)苯酚、1,3,5-三(二甲基胺丙基)-1,3,5-六氢化三嗪、N,N-二甲基乙醇胺、N,N-二甲基氨乙基乙二醇、三甲基羟乙基丙二胺、N-甲基-N-(N,N-二甲胺基乙基)乙醇胺、N,N-二甲基苄胺、三(二甲氨丙基)胺、三乙胺、N,N-二甲基(十六烷基)胺、乙烯基三丁酮肟基硅烷和四甲基亚胺基二丙基胺;所述有机金属类催化剂选自以下的一种或多种:二月桂酸二丁基锡、辛酸亚锡、二(十二烷基硫)二丁基锡、二醋酸二丁基锡、异辛酸钾、醋酸钾、油酸钾、异辛酸铅、异辛酸锌、醋酸苯汞、钛酸四丁酯、钛酸四异丙酯、以及铂类催化剂。
13.如权利要求12所述的脱模剂,其中所述铂类催化剂选自二氧化铂、氯铂酸、氯铂酸与二烯烃的络合物、或双(乙酰丙酮)铂。
14.如权利要求12所述的脱模剂,其中所述催化剂选自以下的一种或多种:三亚乙基二胺、辛酸亚锡、1,1,3,3-四甲基胍、乙烯基三丁酮肟基硅烷、异辛酸锌、四甲基亚胺基二丙基胺、钛酸四丁酯、三乙胺、二醋酸二丁基锡和双(乙酰丙酮)铂。
15.如权利要求1-8之一所述的脱模剂,其中所述催化剂的含量为脱模剂总质量的0.01-5%。
16.如权利要求15所述的脱模剂,其中所述催化剂的含量为脱模剂总质量的0.1-2.0%。
17.如权利要求1-8之一所述的脱模剂,其中所述溶剂为以下的一种或多种:醇类、醇醚类、酮类、酯类、脂肪烃类、脂环烃类、芳香烃类和醚类。
18.如权利要求17所述的脱模剂,其中所述醇类溶剂选自以下的一种或多种:乙醇、异丙醇、丙二醇、丁醇、1,4-丁二醇、1,3-丁二醇和丙三醇;所述醇醚类溶剂选自以下的一种或多种:乙二醇单丁醚、丙二醇单甲醚和丙二醇单丁醚;所述酮类溶剂选自以下的一种或多种:丙酮、丁酮、甲基异丁基酮和环己酮;所述酯类溶剂选自以下的一种或多种:醋酸甲酯、醋酸乙酯和醋酸丁酯;所述脂肪烃类溶剂为以下的一种或多种:正己烷、四氯化碳、石油醚和异构烷烃溶剂;所述脂环烃类溶剂以下的一种或多种:环戊烷和环己烷;所述芳香烃类溶剂选自以下的一种或多种:甲苯和二甲苯;所述醚类溶剂选自以下的一种或多种:四氢呋喃、二异丙醚和二丁醚。
19.如权利要求17或18所述的脱模剂,其中所述溶剂的含量为脱模剂总质量的10.0-99.85%。
20.如权利要求19所述的脱模剂,其中所述溶剂的含量为脱模剂总质量的40.0-99.0%。
21.如权利要求1-8之一所述的脱模剂,其特征在于:所述的脱模剂中还含有下列添加剂中的一种或多种:硅烷、颜料、流平剂、抗老化剂、增粘剂和脱模剂转移指示剂。
22.一种制备如权利要求1-21中任一项所述的脱模剂的方法:其包括将脱模剂的各组成成分在搅拌下物理混合,其中所述各组成成分包括具有硅氢键的聚硅氧烷、用于脱氢缩合反应的催化剂以及溶剂。
23.如权利要求22所述的方法,其中所述物理混合在0-100℃的温度下、和10-1500rpm的搅拌转速下进行1-500min。
24.如权利要求22或23的方法,其中首先将具有硅氢键的聚硅氧烷与溶剂混合,然后再与所述的催化剂混合。
25.如权利要求22或23的方法,其中在干燥密闭的容器中进行所述的物理混合。
26.权利要求23所述的方法,其中进行混合的温度是0-70℃,搅拌转速是100-1000rpm,搅拌时间是1-120min。
27.如权利要求1-21中任一项所述的脱模剂在制造聚氨酯制品、环氧树脂制品、橡胶制品和聚酯制品中用于促进高聚物材料脱模的用途。