CN102602181A - 洗衣机控制盘标识印刷的工艺 - Google Patents
洗衣机控制盘标识印刷的工艺 Download PDFInfo
- Publication number
- CN102602181A CN102602181A CN2012100559134A CN201210055913A CN102602181A CN 102602181 A CN102602181 A CN 102602181A CN 2012100559134 A CN2012100559134 A CN 2012100559134A CN 201210055913 A CN201210055913 A CN 201210055913A CN 102602181 A CN102602181 A CN 102602181A
- Authority
- CN
- China
- Prior art keywords
- degrees centigrade
- control panel
- printing
- ink
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种洗衣机控制盘标识印刷的工艺,涉及家用电器生产工艺。其工艺流程如下:第一步:根据图纸要求调墨;第二步:丝网多遍套色印刷;第三步:烘烤干燥;第四步:检验、包装、入库。烘烤干燥工步是采用阶梯温度、分时段、连续进行,其中:第一阶段炉温85至90摄氏度,延时5至6分钟,油墨底层逐步侵蚀到控制盘塑料中去,通过化学反应使油墨底层与塑料表面形成相互融和的侵蚀层;第二阶段炉温60至65摄氏度,延时7至8分钟,继续进行化学反应,逐步固化。第三阶段炉温30至35摄氏度,延时15至16分钟,侵蚀层进入时效阶段,避免标识印刷变形。处理后的洗衣机控制盘标识,色泽满足图纸要求,油墨附着力强,永不脱落。
Description
技术领域
本发明涉及一种家用电器生产工艺,具体涉及洗衣机控制盘标识印刷的工艺。也适用于其他电器的塑料面板标识的印刷工艺。
背景技术
洗衣机是使用广泛的家用电器,洗衣机控制盘上有精美的标识,这些标识是用丝网印制出来的。目前的工艺印刷的标识与控制盘机体结合不牢固,洗衣机使用不长时间,标识脱落,影响使用。
为了解决上述技术问题,本发明提供一种洗衣机控制盘标识印刷的工艺,丝印过的控制盘采用由高到低的阶梯温度、分时段、连续烘烤干燥,使油墨侵蚀到控制盘机体中去,油墨永不脱落。
本发明是通过如下技术发实现的:一种洗衣机控制盘标识印刷的工艺,其工艺流程如下:第一步:根据图纸要求的印刷标识颜色,调整与之相同颜色的油墨;第二步:人工丝网多遍套色印刷;第三步:烘烤干燥;第四步:检验、包装、入库;其特征在于:所述的烘烤干燥工步是采用由高到低的阶梯温度、分时段、连续进行的。
所述的烘烤干燥工步分三个阶段完成,其中:第一阶段炉温85至90摄氏度,延时5至6分钟;第二阶段炉温60至65摄氏度,延时7至8分钟;第三阶段炉温30至35摄氏度,延时15至16分钟。
本发明的积极效果是:由于采用阶梯温度、分时段、连续烘烤干燥,在高温阶段油墨底层侵蚀到控制盘机体中去,中温阶段使油墨侵蚀层固化,低温阶段为时效阶段,避免油墨侵蚀层变形。通过以上工艺印制出的标识永不脱落。
具体实施方式
一种洗衣机控制盘标识印刷的工艺,其工艺流程如下:第一步:根据图纸要求的印刷标识颜色,调整与之相同颜色的油墨。油墨的选用还要根据控制盘材料选用不同的油墨,比如:9290A控制盘印刷使用油墨为057/068/070,配方为3*2*1。2095N控制盘印刷使用油墨为057/068,配方为4*2。1787J控制盘印刷油墨为073/033/070,配方为6*2*1。
第二步:人工丝网多遍套色印刷。第三步:烘烤干燥;第四步:检验、包装、入库。其特征在于:所述的烘烤干燥工步是采用由高到低的阶梯温度、分时段、连续进行的。
所述的烘烤干燥工步分三个阶段完成,其中:第一阶段炉温85至90摄氏度,延时5至6分钟。油墨底层在高温阶段逐步侵蚀到控制盘机体表面的塑料中去,通过化学反应使油墨底层与塑料表面形成相互融和的侵蚀层,油墨永不脱落。
第二阶段炉温60至65摄氏度,延时7至8分钟。在此阶段,使油墨和塑料继续进行化学反应,侵蚀层逐步固化。
第三阶段炉温30至35摄氏度,延时15至16分钟。侵蚀层进入时效阶段,避免标识印刷变形。
通过以上烘烤干燥工步处理后的洗衣机控制盘标识,色泽满足图纸要求,油墨附着力强,永不脱落。
Claims (2)
1.一种洗衣机控制盘标识印刷的工艺,其工艺流程如下:第一步:根据图纸要求的印刷标识颜色,调整与之相同颜色的油墨;第二步:人工丝网多遍套色印刷;第三步:烘烤干燥;第四步:检验、包装、入库;其特征在于:所述的烘烤干燥工步是采用由高到低的阶梯温度、分时段、连续进行的。
2.根据权利要求1所述的洗衣机控制盘标识印刷的工艺,其特征在于:所述的烘烤干燥工步分三个阶段完成,其中:第一阶段炉温85至90摄氏度,延时5至6分钟;第二阶段炉温60至65摄氏度,延时7至8分钟;第三阶段炉温30至35摄氏度,延时15至16分钟。