CN102584148A - 一种抗碱性的瓷砖勾缝剂 - Google Patents
一种抗碱性的瓷砖勾缝剂 Download PDFInfo
- Publication number
- CN102584148A CN102584148A CN2012100666121A CN201210066612A CN102584148A CN 102584148 A CN102584148 A CN 102584148A CN 2012100666121 A CN2012100666121 A CN 2012100666121A CN 201210066612 A CN201210066612 A CN 201210066612A CN 102584148 A CN102584148 A CN 102584148A
- Authority
- CN
- China
- Prior art keywords
- alkali
- tile pointing
- pigment
- agent according
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种抗碱性的瓷砖勾缝剂,涉及建筑材料领域。所述勾缝剂按以下重量百分比的原料组成:水泥25%-40%;硅砂55-65%;木制纤维素0.1-0.5%;可再分散乳胶粉末5044N 3-5%;增稠剂0.2-1%;颜料0.2-1%;憎水剂0.2-1.5%;碱抑制剂0.2-1%。本发明能增强抗收缩和抗裂性,提高产品的触变性,起到一定的增稠作用。使得活性物质能遇水后适时释放,并在基材固化后形成憎水保护。与添加的国民淀粉的E100碱抑制剂同时使用,能明显抑制泛碱和变色现象。
Description
技术领域
本发明涉及建筑材料领域,特别是涉及一种抗碱性的瓷砖勾缝剂。
背景技术
瓷砖勾缝剂,是用于填充瓷砖和石材间缝隙的接缝材料,与瓷砖、石材等装饰材料相配合提供美观的饰面及保证饰面之间的粘结和防渗。其不足之处是:现有勾缝材料中的水泥在遇到雨水时,大量的Ca+、OH-通过瓷砖石材的毛细孔和缝隙渗透到表面,形成白色粉末结晶的现象,出现了严重泛碱现象,严重影响了用户的生活质量。
发明内容
本发明的目的在于提出一种抗碱性的瓷砖勾缝剂,该勾缝剂能增强抗收缩和抗裂性,提高产品的触变性,使得活性物质能遇水后适时释放,并在基材固化后形成憎水保,能明显抑制现有勾缝材料的泛碱和变色现象。
本发明的目的是通过以下技术方案实现的:
一种抗碱性的瓷砖勾缝剂,勾缝剂按以下重量百分比的原料组成:水泥25%-40%;硅砂55-65%;木制纤维素0.1-0.5%;可再分散乳胶粉末5044N 3-5%;增稠剂0.2-1%;颜料 0.2-1%;憎水剂 0.2-1.5%; 碱抑制剂0.2-1%。
所述的一种抗碱性的瓷砖勾缝剂,水泥为市售42.5级普通硅酸盐水泥。
所述的一种抗碱性的瓷砖勾缝剂,硅砂为70-150目。
所述的一种抗碱性的瓷砖勾缝剂,增稠剂为羟丙基甲基纤维素醚、羟乙基纤维素、羟乙基甲基纤维素中的一种。
所述的一种抗碱性的瓷砖勾缝剂,颜料为氧化铁类颜料。
所述的一种抗碱性的瓷砖勾缝剂,憎水剂为美国道康宁SHP 50;碱抑制剂为国民淀粉的E100。
本发明的优点与效果是:
1. 本发明添加的有效量的憎水剂与碱抑制剂,所制得的抗碱型瓷砖勾缝剂能有效抑制泛碱,同时还具有耐候持久、保水率高、收缩率小、无裂缝、耐碱耐磨、耐沾污、防水抗渗、安全环保等特点,具有良好的社会效率和经济效应。
2、本发明添加有效量的增稠剂,能增强抗收缩和抗裂性,提高产品的触变性,起到一定的增稠作用。
3.本发明中添加的憎水剂,使得活性物质能遇水后适时释放,并在基材固化后形成憎水保护。
4.本发明中添加的憎水剂,与添加的国民淀粉的E100碱抑制剂同时使用,能明显抑制泛碱和变色。
具体实施方式
本发明勾缝剂按以下重量百分比的原料组成:水泥25%-40%;硅砂55-65%;木制纤维素0.1-0.5%;可再分散乳胶粉末5044N 3-5%;增稠剂0.2-1%;颜料 0.2-1%;憎水剂 0.2-1.5%; 碱抑制剂0.2-1%。水泥为市售42.5级普通硅酸盐水泥,硅砂为70-150目,增稠剂为羟丙基甲基纤维素醚、羟乙基纤维素、羟乙基甲基纤维素中的一种,颜料为氧化铁类颜料;憎水剂为美国道康宁SHP 50;碱抑制剂为国民淀粉的E100。
按上述原料配方称量配料,按传统工艺方法,将上述各原料依次放入混合机内,经充分搅拌混合均匀后,即得到抗碱型瓷砖勾缝剂。
本发明中添加的憎水剂为硅烷基美国道康宁SHP 50粉末,使得活性物质能遇水后适时释放,并在基材固化后形成憎水保护。作为憎水添加剂,能用于水泥及矿物为原料的干粉砂浆***,阻止材料中毛细管/孔对水的吸收, 极大地降低基材的吸水率,给材料提供优秀的憎水性能。 与添加的国民淀粉的E100碱抑制剂在最佳的配比和添加量时,能明显抑制泛碱和变色。
本发明施工工艺是:
1、基层处理
在饰面粘结牢固后,清洁缝隙或对缝隙做预湿处理。
2、配置
按水与干粉10~11:50的重量比进行配料,用机械设备搅拌均匀,放置5~10分钟后再次简单搅拌。施工方法不同,加水量应适当调整。
3、施工方法
用刮板或专用工具将拌好的勾缝剂填压到砖缝中并抹平或作U型处理。待勾缝剂浆料稍干后(触摸不粘手),用微湿海绵擦拭压实,并清理表面;色彩反差较大的更需快速清理。
本发明勾缝剂使用时注意事项:
1、基材温度低于5℃或高于38℃不宜施工;雨天不宜施工。
2、用量因砖尺寸、砖缝宽度、填缝方法及砖面上填缝砂浆剩余量的多少而异。
3、切勿在雨中或雨后瓷砖仍潮湿时进行勾缝,勾缝后24h内应避免雨淋。
4、严禁私自添加砂子、水泥及其它添加剂。
5、施工工具用完后及时清洗干净。
实施例1
准确称取42.5级普通硅酸盐水泥300kg、80目硅砂600kg、木制纤维素5kg、可再分散乳胶粉末50kg、羟丙基甲基纤维素醚10万粘度4kg、铁黑粉30kg、有机硅憎水粉末SHP-50 7kg、碱抑制剂E100 ,4kg。将上述配合料放入混合机内,经充分混合搅拌均匀后,即得到抗碱型瓷砖勾缝剂。
上述实施例所制得的抗碱型瓷砖勾缝剂均能符合国家有关标准规定的各项性能指标(如下表格):
Claims (6)
1.一种抗碱性的瓷砖勾缝剂,其特征在于:所述勾缝剂按以下重量百分比原料组成:水泥25%-40%;硅砂55-65%;木制纤维素0.1-0.5%;可再分散乳胶粉末5044N 3-5%;增稠剂0.2-1%;颜料 0.2-1%;憎水剂 0.2-1.5%; 碱抑制剂0.2-1%。
2.根据权利要求1所述的一种抗碱性的瓷砖勾缝剂,其特征在于:水泥为市售42.5级普通硅酸盐水泥。
3.根据权利要求1所述的一种抗碱性的瓷砖勾缝剂,其特征在于:硅砂为70-150目。
4.根据权利要求1所述的一种抗碱性的瓷砖勾缝剂,其特征在于:增稠剂为羟丙基甲基纤维素醚、羟乙基纤维素、羟乙基甲基纤维素中的一种。
5.根据权利要求1所述的一种抗碱性的瓷砖勾缝剂,其特征在于:颜料为氧化铁类颜料。
6.根据权利要求1所述的一种抗碱性的瓷砖勾缝剂,其特征在于:憎水剂为美国道康宁SHP 50;碱抑制剂为国民淀粉的E100。