CN102561372B - 深基坑井点降水的降水管封堵方法 - Google Patents
深基坑井点降水的降水管封堵方法 Download PDFInfo
- Publication number
- CN102561372B CN102561372B CN201110436183.8A CN201110436183A CN102561372B CN 102561372 B CN102561372 B CN 102561372B CN 201110436183 A CN201110436183 A CN 201110436183A CN 102561372 B CN102561372 B CN 102561372B
- Authority
- CN
- China
- Prior art keywords
- layer
- downcomer
- sand
- water glass
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明是一种深基坑井点降水的降水管封堵方法,属工民建降水封堵方法,其施工步骤是:一、过滤层的处置,二、填充砂层,三、塞棉絮层,四、浇灌水玻璃水泥砂浆层,五、抹敷堵漏王层,六、浇筑微膨胀混凝土层,七、焊封堵钢板;其中:在原降水管内腔下部设置的过滤层保持原状不变,填充砂层的高度填至降水管顶部向下1.5m深处;棉絮层的高度为0.7-1.0m,该水玻璃水泥砂浆层厚为50mm—80mm,随灌随凝,堵塞王层厚为40mm-60mm,微膨胀混凝土层一直浇筑到降水管上端管口为止,在微膨胀水泥层的上部用8-15mm厚的圆钢板将降水管上口满焊堵封;有效地解决降水管封堵产生渗漏的难题,操作简便,施工进度快,施工质量高成本低。
Description
技术领域
本发明属工民建降水封堵方法,尤其是涉及一种深基坑井点降水的封堵方法。
背景技术
在高层建筑施工时,由于地下水位较高,基坑开挖较深,一般都需要采用井点降水法施工进行降水,以便基坑开挖及基础的施工,但是在基础施工结束并撤除井点降水设备时,由于地下水水压作用,会造成降水管封堵困难,一般情况下,在降水管中填筑碎石,然后浇筑高标号混凝土直至混凝土顶板50mm以下,再采用10mm厚的钢板将降水管焊封,但因地下水压较大,停止降水后,地下水仍会大量上涌,降水管封堵部位易渗漏,不仅造成施工难度大,施工质量难以控制,而且施工后隐患多,日后地下室混凝土底板渗水,堵漏极为困难。
发明内容
本发明的目的是提供一种深基坑井点降水的降水管封堵方法,有效地解决降水管封堵产生渗漏的难题,不仅操作简便,施工进度快,而且提高施工质量,降低施工成本。
本发明的目的是这样来实现的:一种深基坑井点降水的降水管封堵方法,其施工步骤是:
一、过滤层的处置,二、填充砂层,三、塞棉絮层,四、浇灌水玻璃水泥砂浆层,五、抹敷堵漏王层,六 、浇筑微膨胀混凝土层,七、焊封堵钢板;
其中:
一、过滤层的处置:
在降水管中将排水水泵提升出来后,在原降水管内腔下部设置的过滤层保持原状不变,即在降水管的下部深埋的为防止降水井中杂质影响水泵的工作效能所设置的过滤器保持原状不变,此过滤器采用成品滤网,空隙率不小于20%。
[0005] 二、填充砂层:
在降水管内过滤层的上方填充砂层,采用中细砂,此中细砂粒度为0.25mm至0.35mm为宜,此中细砂经过20目和40目的筛子筛选,不得含有杂质,此砂层的高度填至降水管顶部向下1.5m深处;砂层应捣密实,密实度为90%即可,砂层填充要分层填充、分层捣密实,且以每次填充50cm厚的中细砂并捣实为佳。
三、塞棉絮层:
填充砂层后,立即将裹紧的棉絮卷塞入降水管中砂层的上方,该棉絮卷的直径比降水管内径大15-30mm,且该棉絮卷的直径比降水管内径大20mm为佳,该棉絮层的高度为0.7-1.0m,该棉絮层的高度尤以0.8m为佳,以起到隔水、防止地下水上涌的目的。
四、浇灌水玻璃水泥砂浆层:
降水管中塞紧棉絮层后,在棉絮层的上部立即浇灌水玻璃水泥砂浆层,该水玻璃水泥砂浆层厚为50mm— 80mm,且该水玻璃水泥砂浆层厚以60mm为佳,随灌随凝,水玻璃水泥主要材料:1)、水玻璃:市售、模数n=2.2、密度40°Be,2)、水泥:32.5号普通硅酸盐水泥,3)、砂:河砂、细度模数uf=2.4;该水玻璃水泥砂浆的配比为:水泥:砂:水:水玻璃=565Kg:1380Kg:360Kg:113L 即:1kg:2.44kg:1.57kg:200ml,水玻璃先与水拌合,再倒入到水泥和砂中拌制成砂浆,避免水玻璃直接倒入时使局部水泥砂浆产生速凝,防止搅拌不均匀。
五、抹敷堵漏王层:
在凝结的水玻璃水泥砂浆层上抹敷堵漏王层,此堵漏王层的厚度为40mm-60mm,此堵漏王层的厚度以50mm为佳。
六 、浇筑微膨胀混凝土层:
在堵漏王层凝固后,在堵漏王层上部浇筑微膨胀混凝土层,该微膨胀混凝土的配比为:(水泥+膨胀剂):砂:碎石:水:减水剂=(348Kg+36Kg):744Kg:1071Kg:178Kg:3.5Kg,即:(1Kg+0.10Kg):2.14Kg:3.08Kg:0.51Kg:0.01Kg,混凝土为32.5号普通硅酸盐水泥;边浇筑边振捣密实,按常规养护,此微膨胀混凝土层一直浇筑到降水管上端管口为止,浇筑后,混凝土膨胀与降水管牢固结合,防止混凝土松动,确保封堵质量。
七、焊封堵钢板:
待微膨胀水泥达到设计强度75%以后,在微膨胀水泥层的上部用8-15mm厚的圆钢板将降水管上口满焊堵封。
本发明所提供的一种深基坑井点降水的降水管封堵方法,操作方便,有效地解决了降水管封堵产生渗漏的难题,不仅施工进度快,而且提高施工质量,降低施工成本。
现结合附图和实施例对本发明提出的一种深基坑井点降水的降水管封堵方法作进一步说明。
附图说明
图1是本发明所提出的深基坑井点降水的降水管封堵方法实施示意图。
图1中:1、过滤层 2、填砂层 3、棉絮层 4、水玻璃水泥砂浆层 5、堵漏王层 6、微膨胀水泥层 7、圆钢板。
具体实施方式
[0015] 在南京莲花村B组团项目8#楼降水管采用本深基坑井点降水的降水管封堵方法,其施工步骤是:保留排水降水施工时埋设的过滤层1,填充砂层2,中细砂填至降水管顶部向下1.5m深处,然后用厚为0.8m的紧密棉絮层3封堵,接着依次用厚为50mm的水玻璃水泥浆层4(即封即凝)和厚度为50mm的堵漏王层5,堵漏王层5上部采用C35微膨胀混凝土层6浇筑到降水管上端管口,最后在微膨胀水泥层6上再用10mm厚的圆钢板7将降水管满焊焊封,圆钢板7的顶部浇筑混凝土并用厚为40mm细石混凝土与混凝土地板浇筑平齐,经相关工程技术人员细心认真的反复检查,未发现降水管渗漏现象,效果明显;在后续的12#、13#楼降水管封井中继续用本方法施工,并进一步验证了其防渗漏的效果,有效地解决了降水管封堵防潮防渗的技术难题,并在保证工程质量的前提下,使施工操作简便,加快了施工进度,降低了成本。
Claims (5)
1.一种深基坑井点降水的降水管封堵方法,其施工步骤是:
一、过滤层的处置,二、填充砂层,三、塞棉絮层,四、浇灌水玻璃水泥砂浆层,五、抹敷堵漏王层,六 、浇筑微膨胀混凝土层,七、焊封堵钢板;
其中:
一、过滤层的处置:
在降水管中将排水水泵提升出来后,在原降水管内腔下部设置的过滤层保持原状不变,即在降水管的下部深埋的为防止降水井中杂质影响水泵的工作效能所设置的过滤器保持原状不变,此过滤器采用成品滤网,空隙率不小于20%;
二、填充砂层:
在降水管内过滤层的上方填充砂层,采用中细砂,此中细砂粒度为0.25mm至0.35mm,此中细砂经过20目和40目的筛子筛选,不得含有杂质,此砂层的高度填至降水管顶部向下1.5m深处;砂层应捣密实,密实度为90%,砂层填充要分层填充、分层捣密实;
三、塞棉絮层:
填充砂层后,立即将裹紧的棉絮卷塞入降水管中砂层的上方,该棉絮卷的直径比降水管内径大15—30mm,该棉絮层的高度为0.7—1.0m,以起到隔水、防止地下水上涌的目的;
四、浇灌水玻璃水泥砂浆层:
降水管中塞紧棉絮层后,在棉絮层的上部立即浇灌水玻璃水泥砂浆层,该水玻璃水泥砂浆层厚为50mm— 80mm,随灌随凝,水玻璃水泥主要材料:1)、水玻璃:市售、模数n=2.2、密度40°Be,2)、水泥:32.5号普通硅酸盐水泥,3)、砂:河砂、细度模数uf=2.4;该水玻璃水泥砂浆的配比为:水泥:砂:水:水玻璃=565Kg:1380Kg:360Kg:113L 即:1kg:2.44kg:1.57kg:200ml,水玻璃先与水拌合,再倒入到水泥和砂中拌制成砂浆,避免水玻璃直接倒入时使局部水泥砂浆产生速凝,防止搅拌不均匀;
五、抹敷堵漏王层:
在凝结的水玻璃水泥砂浆层上抹敷堵漏王层,此堵漏王层的厚度为40mm-60mm;
六 、浇筑微膨胀混凝土层:
在堵漏王层凝固后,在堵漏王层上部浇筑微膨胀混凝土层,该微膨胀混凝土的配比为:(水泥+膨胀剂):砂:碎石:水:减水剂=(348Kg+36Kg):744Kg:1071Kg:178Kg:3.5Kg,即:(1Kg+0.10Kg):2.14Kg:3.08Kg:0.51Kg:0.01Kg,混凝土为32.5号普通硅酸盐水泥;边浇筑边振捣密实,按常规养护,此微膨胀混凝土层一直浇筑到降水管上端管口为止,浇筑后,混凝土膨胀与降水管牢固结合,防止混凝土松动,确保封堵质量;
七、焊封堵钢板:
待微膨胀混凝土达到设计强度75%以后,在微膨胀水泥层的上部用8-15mm厚的圆钢板将降水管上口满焊堵封。
2.根据权利要求1所述的深基坑井点降水的降水管封堵方法,其特征在于该棉絮层的直径比降水管内径大20mm、高度为0.8m。
3.根据权利要求1所述的深基坑井点降水的降水管封堵方法,其特征在于该水玻璃水泥砂浆层厚为60mm。
4.根据权利要求1所述的深基坑井点降水的降水管封堵方法,其特征在于此堵漏王层的厚度为50mm。
5.根据权利要求1所述的深基坑井点降水的降水管封堵方法,其特征在于砂层填充为每次填充50cm厚的中细砂并捣实。