CN102560716B - 高可纺性对位芳纶短纤维及其生产方法 - Google Patents
高可纺性对位芳纶短纤维及其生产方法 Download PDFInfo
- Publication number
- CN102560716B CN102560716B CN201010588042.3A CN201010588042A CN102560716B CN 102560716 B CN102560716 B CN 102560716B CN 201010588042 A CN201010588042 A CN 201010588042A CN 102560716 B CN102560716 B CN 102560716B
- Authority
- CN
- China
- Prior art keywords
- para
- paraphthaloyl chloride
- condensation polymerization
- curling
- staple fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实例1 | 实例2 | |
断裂强度CN/dtex | 16.5 | 17.2 |
模量CN/dtex | 650.8 | 700.6 |
卷曲数/个/25mm | 8.4 | 12.5 |
卷曲回复率(%) | 6.5 | 7 |
卷曲弹性回复率(%) | 68 | 75 |
上油率(%) | 0.5 | 0.8 |
比电阻 | 2.5*108 | 1.7*107 |
可纺性 | 好 | 好 |
Claims (2)