CN102557755A - 一种含有氧化锂的乳浊釉 - Google Patents
一种含有氧化锂的乳浊釉 Download PDFInfo
- Publication number
- CN102557755A CN102557755A CN2011104178368A CN201110417836A CN102557755A CN 102557755 A CN102557755 A CN 102557755A CN 2011104178368 A CN2011104178368 A CN 2011104178368A CN 201110417836 A CN201110417836 A CN 201110417836A CN 102557755 A CN102557755 A CN 102557755A
- Authority
- CN
- China
- Prior art keywords
- parts
- lithium oxide
- improved
- glaze
- opacified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含有氧化锂的乳浊釉,它是由下列重量份数的组分制成:锆英砂5~10份、氧化锂3~8份、硼酸5~10份、钾长石10~20份、硝酸钾2~5份、白云石4~10份、重质碳酸钙8~15份、高岭土6~15份、石英30~40份。本发明的一种含有氧化锂的乳浊釉,其配方中采用了氧化锂,可以降低烧成温度节约能源、延长炉龄;降低熔体粘度,提高高温流动性和玻化程度,提高抗污染能力,增强釉面强度和光滑平整度;降低热膨胀系数、克服釉面裂纹,提高热稳定性;提高白度、增强光泽度;提高化学稳定性和耐酸性。
Description
技术领域
本发明涉及一种乳浊釉,特别是一种含有氧化锂的乳浊釉。
背景技术
乳浊釉是常见陶瓷装饰的一种方法,被广泛应用。乳浊釉即白色不透明光泽釉,它是由于釉玻璃中存在着与基质玻璃相折射率不同、体积微小的第2相或第3相物质,当光线通过釉层时 乳浊粒子使光线产生散射作用从而造成釉层不透光的现象。
根据乳浊粒子的聚集状态 乳浊釉可分为3 类:一是基质玻璃中存在一定数量的微小晶体,称为晶相乳浊釉;二是釉熔体在冷却过程中发生液-液分相,在基质玻璃中分离出体积微小分散度较高的第2相玻璃,称为分相乳浊釉;三是在釉玻璃表面层以下存在大量微小气泡,称为气相乳浊釉,其中晶相乳浊釉又分为原始晶粒乳浊釉和析出晶粒乳浊釉2 种。前者是通过外加难熔物质实现釉的乳浊最常用的有锆浊釉;后者是在烧成过程中从釉玻璃中自发析出乳浊粒子造成乳浊。目前,乳浊釉已在陶瓷工业中广泛应用。乳浊釉能够遮盖坯体的颜色和某些缺陷,丰富陶瓷产品的釉面装饰,同时,使得大量劣质原料或工业废渣可以作为坯用原料。
这在高品位原料日益枯竭的今天,不仅降低了生产成本,使资源得到充分合理的利用,而且可增加产品的花色品种,提高产品档次,因此受到了人们的喜欢。近几年来,随着科学技术的发展,乳浊釉无论是在研究还是在应用方面,都有许多突破性进展,目前已被广泛应用于卫生瓷、建筑陶瓷和日用陶瓷的装饰,使陶瓷表面色彩斑斓、变化万千,展现个性化。
发明内容
本发明目的在于提供一种含有氧化锂的乳浊釉。
为解决上述问题,本发明所采用的技术方案是:一种含有氧化锂的乳浊釉,由下列重量份数的组分制成:锆英砂5~10份、氧化锂3~8份、硼酸5~10份、钾长石10~20份、硝酸钾2~5份、白云石4~10份、重质碳酸钙8~15份、高岭土6~15份、石英30~40份。
所述含有氧化锂的乳浊釉,由下列重量份数的组分制成:锆英砂5~8份、氧化锂3-7份、硼酸5~7份、钾长石12~18份、硝酸钾3~4份、白云石4~8份、重质碳酸钙8~12份、高岭土6~12份、石英30~35份。
本发明相对于现有技术的有益效果是:本发明的含有氧化锂的乳浊釉其配方中的氧化锂可以降低烧成温度节约能源、延长炉龄;降低熔体粘度,提高高温流动性和玻化程度,提高抗污染能力,增强釉面强度和光滑平整度;降低热膨胀系数、克服釉面裂纹,提高热稳定性;提高白度、增强光泽度;提高化学稳定性和耐酸性。
具体实施方式
下面通过实施例对本发明做进一步详细说明,这些实施例仅用来说明本发明,并不限制本发明的范围。
实施例1 采用下列配方制备本发明所述含有氧化锂的乳浊釉:以重量份数计的原料:锆英砂5份、氧化锂15份、硼酸10份、钾长石10份、硝酸钾2份、白云石4份、重质碳酸钙10份、高岭土6份、石英38份。
实施例2 采用下列配方制备本发明所述含有氧化锂的乳浊釉:以重量份数计的原料:锆英砂8份、氧化锂10份、硼酸8份、钾长石128份、硝酸钾3份、白云石10份、重质碳酸钙15份、高岭土8份、石英35份。
实施例3 采用下列配方制备本发明所述含有氧化锂的乳浊釉:以重量份数计的原料:锆英砂10份、氧化锂12份、硼酸5份、钾长石18份、硝酸钾5份、白云石8份、重质碳酸钙12份、高岭土15份、石英40份。
实施例4 采用下列配方制备本发明所述含有氧化锂的乳浊釉:以重量份数计的原料:锆英砂7份、氧化锂5份、硼酸7份、钾长石20份、硝酸钾4份、白云石6份、重质碳酸钙8份、高岭土10份、石英30份。
Claims (2)
1.一种含有氧化锂的乳浊釉,其特征在于:由下列重量份数的组分制成:锆英砂5~10份、氧化锂3~8份、硼酸5~10份、钾长石10~20份、硝酸钾2~5份、白云石4~10份、重质碳酸钙8~15份、高岭土6~15份、石英30~40份。
2.如权利要求1所述一种含有氧化锂的乳浊釉,其特征在于:由下列重量份数的组分制成:锆英砂5~8份、氧化锂3-7份、硼酸5~7份、钾长石12~18份、硝酸钾3~4份、白云石4~8份、重质碳酸钙8~12份、高岭土6~12份、石英30~35份。