CN102532438A - 水体浮油聚合物吸附剂及制备方法 - Google Patents
水体浮油聚合物吸附剂及制备方法 Download PDFInfo
- Publication number
- CN102532438A CN102532438A CN201110314890XA CN201110314890A CN102532438A CN 102532438 A CN102532438 A CN 102532438A CN 201110314890X A CN201110314890X A CN 201110314890XA CN 201110314890 A CN201110314890 A CN 201110314890A CN 102532438 A CN102532438 A CN 102532438A
- Authority
- CN
- China
- Prior art keywords
- oil slick
- water body
- octadecyl acrylate
- body oil
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种水体浮油聚合物吸附剂及制备方法。该聚合物吸附剂包含苯乙烯、丙烯酸十八酯和烯丙基环糊精三种结构单元。其合成方法为:在浓度为0.2g/mL聚乙烯醇水溶液中搅拌下加入浓度为0.5g/mL烯丙基环糊精,10-20min后再加入苯乙烯和丙烯酸十八酯。苯乙烯与丙烯酸十八酯的摩尔比为1∶1,烯丙基环糊精用量为苯乙烯与丙烯酸十八酯重量和的6-8%。最后加入偶氮二异丁腈,其用量为苯乙烯与丙烯酸十八酯重量和的2%。通氮气1小时后,升温到60℃并持续搅拌反应8-12小时。将反应器中珠状物用蒸馏水洗净,室温下真空干燥24h,则得水体浮油聚合物吸附剂。该聚合物在净化水体浮油污染中具有很好的吸附效果,可用于河流湖泊及海洋浮油污染治理。
Description
技术领域
本发明涉及一种水体浮油吸附剂及制备方法。
背景技术
随着石油天然气勘探开发和水上油运行业的快速发展,水体漏油事故增多。另外,石油燃料的广泛使用,也会造成河流湖泊水体浮油污染。本发明制备了一种水体浮油聚合物吸附剂。
发明内容
本发明的目的是:为了吸附河流、湖泊及海洋等水体表面浮油,达到净化水体效果,特提供一种水体浮油聚合物吸附剂及制备方法。
为了达到上述目的,本发明采用了以下技术方案:水体浮油聚合物吸附剂及制备方法,其特征是,该吸附剂聚合物由烯丙基环糊精、苯乙烯和丙烯酸十八酯三种单体悬浮共聚而成。
水体浮油聚合物吸附剂的制备方法,包括以下步骤:
在浓度为0.2g/mL聚乙烯醇水溶液中搅拌下加入浓度为0.5g/mL烯丙基环糊精,10-20min后再加入苯乙烯和丙烯酸十八酯。苯乙烯与丙烯酸十八酯的摩尔比为1∶1,烯丙基环糊精用量为苯乙烯与丙烯酸十八酯重量和的6-8%。最后加入偶氮二异丁腈,其用量为苯乙烯与丙烯酸十八酯重量和的2%。通氮气搅拌1小时后,升温到60℃并持续搅拌反应8-12小时。将反应器中珠状物用蒸馏水洗净,室温下真空干燥24h,则得水体浮油聚合物吸附剂。
与现有技术相比,本发明具有以下有益效果:水体浮油聚合物吸附剂的制备方法简便可行,反应条件温和。该方法制备的聚合物吸附剂由于含有环糊精单元,能够形成海绵状开放的多孔结构,多孔结构有利于油进入聚合物吸附剂里面,从而实现高吸油效率。
具体实施方式
下面通过实施例对本发明进一步说明。
实施例1水体浮油聚合物吸附剂的制备
在250mL玻璃反应容器中首先加入浓度为0.2g/mL聚乙烯醇水溶液100mL和浓度为0.5g/mL的烯丙基环糊精40mL。室温搅拌15min。再加入苯乙烯5.2g和丙烯酸十八酯16.2g。苯乙烯与丙烯酸十八酯的摩尔比为1∶1。再加入偶氮二异丁腈0.5g。通氮气搅拌1小时。加热反应到60℃,聚合反应开始,并持续12小时,得珠状物。将珠状物用蒸馏水洗净,室温下在真空烘箱中干燥24h,得水体浮油聚合物吸附剂。该水体浮油聚合物吸附剂的产率为98%。
实施例2水体浮油聚合物吸附剂的吸油效果
室温下分别取实例1所得聚合物吸附剂0.02克各浸在苯,0号柴油,90号汽油和辽河高升集输站的稀原油中,12小时后取出,沥油1分钟后称重,计算吸油率。
吸油率计算公式为:吸油后吸附剂重量/吸油前吸附剂重量。
水体浮油聚合物吸附剂吸油率如表1所示。
表1 水体浮油聚合物吸附剂吸油效果
油相名称 | 吸油率 |
苯 | 48 |
0号柴油 | 45 |
90号汽油 | 46 |
原油 | 27 |
Claims (3)
1.一种水体浮油聚合物吸附剂及制备方法。该聚合物吸附剂包含苯乙烯、丙烯酸十八酯和烯丙基环糊精三种结构单元。
2.如权利要求1所述的水体浮油聚合物吸附剂及制备方法,其特征在于:在浓度为0.2g/mL聚乙烯醇水溶液中搅拌下加入浓度为0.5g/mL烯丙基环糊精,10-20min后再加入苯乙烯和丙烯酸十八酯。苯乙烯与丙烯酸十八酯的摩尔比为1∶1,烯丙基环糊精用量为苯乙烯与丙烯酸十八酯重量和的6-8%。最后加入偶氮二异丁腈,其用量为苯乙烯与丙烯酸十八酯重量和的2%。通氮气1小时后,升温到60℃并持续搅拌反应8-12小时。将反应器中珠状物用蒸馏水洗净,室温下真空干燥24h,则得水体浮油聚合物吸附剂。
3.根据权利要求1所述的水体浮油聚合物吸附剂及制备方法,其特征是:烯丙基环糊精为烯丙基-α-环糊精或烯丙基环-β-糊精烯丙基-γ-环糊精。