CN102517757A - Plain weave horizontal splayed fabric and post treatment finishing method thereof - Google Patents
Plain weave horizontal splayed fabric and post treatment finishing method thereof Download PDFInfo
- Publication number
- CN102517757A CN102517757A CN2011104493112A CN201110449311A CN102517757A CN 102517757 A CN102517757 A CN 102517757A CN 2011104493112 A CN2011104493112 A CN 2011104493112A CN 201110449311 A CN201110449311 A CN 201110449311A CN 102517757 A CN102517757 A CN 102517757A
- Authority
- CN
- China
- Prior art keywords
- plain weave
- fabric
- cloth
- sorting
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plain weave horizontal splayed fabric and a post treatment finishing method thereof. The plain weave horizontal splayed fabric is formed by interweaving warp silks with weft silks, wherein the warp silks are 5s/2 fancy cotton threads; and the weft silks are 6s/2 bamboo fiber yarns. The post treatment finishing method of the plain weave horizontal splayed fabric comprises the following steps of: a, soft finish: impregnating the fabric by using 20-30g/L padding hydrophilic softener and then tentering, wherein the temperature in the tentering process is adjusted to be 150-160DEG C and the vehicle speed is 40-50m/min and finally pre-shrinking and carrying out liquid resin impregnation treatment; b, water and oil repellent finish: treating the fabric subjected to liquid resin impregnation treatment by using 20-30g/L water and oil repellent finish agent, 40-50g/L penetrating agent and solution with the pH value being 6-6.5; and refinishing the pickup to be 70-80 percent and drying at the temperature of 110-120DEG C for 1-2 minutes. According to the plain weave horizontal splayed fabric and the post treatment finishing method thereof disclosed by the invention, the technical problems that the current fabric made of pure cotton material is easy to fluff and the softness of the fabric is easy to reduce can be solved.
Description
Technical field
The present invention relates to the horizontal herringbone cloth of plain weave that constitutes by bamboo, cotton fiber in the textile industry and cloth is carried out the post processing method for sorting.
Background technology
At present the horizontal herringbone cloth of plain weave mostly adopts cotton textiles to process, and purified cotton cloth has the good characteristic that hygroscopicity is strong, flexibility is good, but along with the increase of use, its flexibility descends gradually.
Summary of the invention
The purpose of this invention is to provide the horizontal herringbone cloth of a kind of plain weave, solve the technical problem that the cloth flexibility that adopts textile material to process at present is prone to decline and is prone to fluffing.
Another object of the present invention provides a kind ofly carries out the post processing method for sorting to above-mentioned cloth.
The horizontal herringbone cloth of plain weave is interwoven by organizine and tram, and organizine is that 5s/2 fancy cotton, parallel are 6s/2 bamboo fibre yarn.
The horizontal herringbone cloth of plain weave post processing method for sorting:
A, soft finish: use the hydrophilic softener that pads of 20-30g/L that cloth is flooded, tentering again, wherein the adjustment in the tentering process is that 150-160 degree, the speed of a motor vehicle are 40-50m/min, last preshrunk is also handled through resin;
B, water and oil repellent finish: use water-refusing oil-refusing finishing agent, the bleeding agent of 40-50g/L, the adjusting pH value of 20-30g/L the cloth of handling through resin to be handled as the solution of 6-6.5; Put pick-up rate 70%-80% again in order, oven dry, bake out temperature 110-120 degree wherein, the time is 1-2min.
The said speed of a motor vehicle is 45 m/min.
It is 6.2 that said prime number is regulated pH value.
Said bake out temperature is 115 degree.
Said drying time is 1.5min.
The invention has the beneficial effects as follows:
1, because the horizontal herringbone cloth of plain weave adopts the cotton yarn that mixes of bamboo, utilize the characteristic of antibiotic, wear-resisting, painted, the moisture absorption of bamboo fibre like this, make the horizontal herringbone cloth of processing by cotton, bamboo fibre of plain weave have good characteristic.
2, the post processing method for sorting gives the horizontal herringbone cloth of plain weave soft, smooth hand feeling, is difficult for fuzz balls, passes through preshrunk after the softness again, washing shrinkage can not only be provided, and fabric feeling is further improved.
Description of drawings
Fig. 1 is the horizontal herringbone cloth of a plain weave sectional structure sketch map among the embodiment;
Among the figure 1, organizine, 2. tram.
The specific embodiment
Please refer to Fig. 1, the horizontal herringbone cloth of the plain weave among this embodiment is interwoven by organizine 1 and tram 2, and organizine 1 is that 5s/2 fancy cotton, parallel 2 are 6s/2 bamboo fibre yarn.
The horizontal herringbone cloth of plain weave its feel before being untreated is relatively poor, in order to be that it has good hand feeling, needs to use softener to carry out soft finish,
Embodiment 1:
The post processing method for sorting:
A, soft finish: use the hydrophilic softener that pads of 20g/L that cloth is flooded, tentering again, wherein the adjustment in the tentering process is that 150 degree, the speed of a motor vehicle are 40m/min, last preshrunk is also handled through resin;
B, water and oil repellent finish: use water-refusing oil-refusing finishing agent, the 40g/L of 20g/L bleeding agent, to regulate pH value be that 6 solution is handled the cloth of handling through resin; Put pick-up rate 70% again in order, bake out temperature 110, drying time are 1min.
A, soft finish: use the hydrophilic softener that pads of 30g/L that cloth is flooded, tentering again, wherein the adjustment in the tentering process is that 160 degree, the speed of a motor vehicle are 50m/min, last preshrunk is also handled through resin;
B, water and oil repellent finish: use water-refusing oil-refusing finishing agent, the 50g/L of 30g/L bleeding agent, to regulate pH value be that 6.5 solution is handled the cloth of handling through resin; Put pick-up rate 80% again in order, bake out temperature 120 degree, drying time is 2min.
Embodiment 3
A, soft finish: use the hydrophilic softener that pads of 25g/L that cloth is flooded, tentering again, wherein the adjustment in the tentering process is that 155 degree, the speed of a motor vehicle are 45m/min, last preshrunk is also handled through resin;
B, water and oil repellent finish: use water-refusing oil-refusing finishing agent, the 45g/L of 25g/L bleeding agent, to regulate pH value be that 6.2 solution is handled the cloth of handling through resin; Put pick-up rate 75% again in order, bake out temperature 115 degree, drying time is 1.5min.
Claims (6)
1. the horizontal herringbone cloth of plain weave is interwoven by organizine and tram, it is characterized in that: organizine is that 5s/2 fancy cotton, parallel are 6s/2 bamboo fibre yarn.
2. the horizontal herringbone cloth of plain weave post processing method for sorting: it is characterized in that:
A, soft finish: use the hydrophilic softener that pads of 20-30g/L that cloth is flooded, tentering again, wherein the adjustment in the tentering process is that 150-160 degree, the speed of a motor vehicle are 40-50m/min, last preshrunk is also handled through resin;
B, water and oil repellent finish: use water-refusing oil-refusing finishing agent, the bleeding agent of 40-50g/L, the adjusting pH value of 20-30g/L the cloth of handling through resin to be handled as the solution of 6-6.5; Put pick-up rate 70%-80% again in order, oven dry, bake out temperature 110-120 degree wherein, the time is 1-2min.
3. according to the horizontal herringbone cloth of the described plain weave of claim 2 post processing method for sorting: it is characterized in that: the said speed of a motor vehicle is 45 m/min.
4. according to the horizontal herringbone cloth of the described plain weave of claim 2 post processing method for sorting: it is characterized in that: it is 6.2 that said prime number is regulated pH value.
5. according to the horizontal herringbone cloth of the described plain weave of claim 2 post processing method for sorting: it is characterized in that: said bake out temperature is 115 degree.
6. according to the horizontal herringbone cloth of the described plain weave of claim 2 post processing method for sorting: it is characterized in that: said drying time is 1.5min.