CN102476096A - 铝制品喷涂表面处理工艺 - Google Patents
铝制品喷涂表面处理工艺 Download PDFInfo
- Publication number
- CN102476096A CN102476096A CN2010105564036A CN201010556403A CN102476096A CN 102476096 A CN102476096 A CN 102476096A CN 2010105564036 A CN2010105564036 A CN 2010105564036A CN 201010556403 A CN201010556403 A CN 201010556403A CN 102476096 A CN102476096 A CN 102476096A
- Authority
- CN
- China
- Prior art keywords
- baking
- carried out
- time
- spraying
- carry out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种铝制品喷涂表面处理工艺,在铝制品上打蜡打磨、擦拭、静电除尘;在铝制品进行底层喷涂,在50~58℃下进行第一次烘烤,烘烤时间为26~30分钟;烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,然后进行第二次喷涂,在45~50℃下第二次烘烤,烘烤时间为40~44分钟;再撕胶带、除尘,接着再印刷、烘烤,收料;最后在包装。防护性好,以延长工件寿命,其次是装式性,达到美观宜人,极高的表面质量,均匀的漆膜厚度,极高的涂料传递效率,可达85%以上。
Description
技术领域
本发明涉及一种表面处理工艺,尤其涉及一种铝制品喷涂表面处理工艺。
背景技术
喷涂作业生产效率高,适用于手工作业及工业自动化生产,应用范围广主要有五金,塑胶,家私,军工,船舶等领域,是现今应用最普遍的一种涂装方式;喷涂作业需要环境要求有百万级到百级的无尘车间,喷涂设备有喷枪,喷漆室,供漆室,固化炉/烘干炉,喷涂工件输送作业设备,消雾及废水,废气处理设备等。
随着工业的发展,社会的进步,人们的质量意识不仅仅只留在产品性能方面,对于产品外观质量的要求也越来越高。涂料作为表面处理的一种方法和手段,其发展方兴未艾。喷涂大体上包括:喷(塑)粉和涂装(油漆)。
发明内容
本发明的目的是克服现有技术存在的不足,提供一种铝制品喷涂表面处理工艺,首先是防护性,以延长工件寿命,其次是装式性,达到美观宜人。极高的表面质量,均匀的漆膜厚度,极高的涂料传递效率,可达85%以上。
本发明的目的通过以下技术方案来实现:
铝制品喷涂表面处理工艺,其特征在于:具体包括以下步骤:
①表面处理:打蜡打磨、擦拭、静电除尘;
②表面喷涂:铝制品进行底层喷涂,在50~58℃下进行第一次烘烤,烘烤时间为26~30分钟;烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,然后进行第二次喷涂,在45~50℃下第二次烘烤,烘烤时间为40~44分钟;再撕胶带、除尘,接着再印刷、烘烤,收料;
③包装。
进一步地,上述的铝制品喷涂表面处理工艺,其中,步骤②的表面喷涂,铝制品进行底层喷涂,在55℃、27分钟下进行第一次烘烤,烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,进行第二次喷涂,在45℃、40分钟下进行第二次烘烤,再接着撕胶带、除尘、印刷、烘烤,收料。
本发明技术方案的实质性特点和进步主要体现在:
防护性好,以延长工件寿命,其次是装式性,达到美观宜人。极高的表面质量,均匀的漆膜厚度,极高的涂料传递效率,可达85%以上。再次是特殊用途,以达到特殊性能。如:隔音、决热、防火等。
具体实施方式
本发明提供一种铝制品喷涂表面处理工艺流程为:首先打蜡打磨、擦拭、静电除尘;表面喷涂,然后铝制品进行底层喷涂,在50~58℃下进行第一次烘烤,烘烤时间为26~30分钟;烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,然后进行第二次喷涂,在45~50℃下第二次烘烤,烘烤时间为40~44分钟;然后再撕胶带、除尘,接着再印刷、烘烤,收料;最后在包装。
实施例1
表面处理:打蜡打磨、擦拭、静电除尘;
表面喷涂:铝制品进行底层喷涂,在50℃下进行第一次烘烤,烘烤时间为30分钟;烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,然后进行第二次喷涂,在48℃下第二次烘烤,烘烤时间为42分钟;再撕胶带、除尘,接着再印刷、烘烤,收料;
包装。
实施例2
表面处理:打蜡打磨、擦拭、静电除尘;
表面喷涂:铝制品进行底层喷涂,在56℃下进行第一次烘烤,烘烤时间为28分钟;烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,然后进行第二次喷涂,在50℃下第二次烘烤,烘烤时间为40分钟;再撕胶带、除尘,接着再印刷、烘烤,收料;
包装。
静电除尘其原理是离子化空气中和塑胶产品上的电荷,是灰尘处于漂浮状态,空气的流动二带走灰尘,达到除尘和除静电。擦拭是带有化学药水的擦拭布,在作业员的受压力下,带走制品上油污和油脂。喷涂有几层组成,其中包括底漆、腻子、面漆罩光等。喷涂被压到枪头的油漆在枪针回缩时,枪与工件保持10~13CM,从抢眼中流出,在压缩空气的吹动下,把油漆吹散且吹到产品上,形成皮膜。底层漆是与被涂工件机体直接接触的最下层涂层,底漆层的作用是强化涂层与机体之间的附着力,强化涂层的防护性能。黑色金属在除装之前应磷化,有色金属涂装之前应氧化处理。腻子层是对于粗糙不平的机体,使用腻子层有很多缺点,诸如施工麻烦、降低涂层与机体的结合力等。烘烤的时间不宜太长,否则减低油漆表面硬度,增加脆性;油漆漆膜发黄。
综上所述,本发明成本低、功能卓越,使用方便,经济效益和社会效应显著。
需要强调的是:以上仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (2)
1.铝制品喷涂表面处理工艺,其特征在于包括以下步骤:
①表面处理:打蜡打磨、擦拭、静电除尘;
②表面喷涂:铝制品进行底层喷涂,在50~58℃下进行第一次烘烤,烘烤时间为26~30分钟;烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,然后进行第二次喷涂,在45~50℃下第二次烘烤,烘烤时间为40~44分钟;再撕胶带、除尘,接着再印刷、烘烤,收料;
③包装。
2.根据权利要求1所述的铝制品喷涂表面处理工艺,其特征在于:步骤②的表面喷涂,铝制品进行底层喷涂,在55℃、27分钟下进行第一次烘烤,烘烤后贴胶带,再打蜡打磨、擦拭、静电除尘,进行第二次喷涂,在45℃、40分钟下进行第二次烘烤,再接着撕胶带、除尘、印刷、烘烤,收料。