CN102453403A - Mastic chlorinated rubber corrosion-resistant paint - Google Patents
Mastic chlorinated rubber corrosion-resistant paint Download PDFInfo
- Publication number
- CN102453403A CN102453403A CN2010105113385A CN201010511338A CN102453403A CN 102453403 A CN102453403 A CN 102453403A CN 2010105113385 A CN2010105113385 A CN 2010105113385A CN 201010511338 A CN201010511338 A CN 201010511338A CN 102453403 A CN102453403 A CN 102453403A
- Authority
- CN
- China
- Prior art keywords
- chlorinated rubber
- corrosion
- percent
- paint
- mastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses mastic chlorinated rubber corrosion-resistant paint, which comprises liquid chlorinated rubber, plasticizer modified resin, chlorinated paraffin wax, corrosion-resistant pigments, fillers, and additives. The mass percentage of the components is as follows: 10-30 percent of liquid chlorinated rubber, 20-40 percent of plasticizer modified resin, 5-10 percent of chlorinated paraffin wax, 10-15 percent of corrosion-resistant pigments, 15-25 percent of fillers and 2-4 percent of additives. The mastic chlorinated rubber corrosion-resistant paint has good resistance against acid and salt corrosion and atmospheric corrosion and an excellent coating performance, and can be widely applied to corrosion-resistant works, such as power plants, chemical plants, bridges, engineering machinery, iron towers, port facilities, ships, containers and the like.
Description
Technical field
The present invention relates to a kind of chemistry painting industry, be specifically related to a kind of thick chlorinated rubber anticorrosive paint.
Background technology
Antifouling paste is to be used in body surface can be used for protecting interior of articles not receive one type of paint of corrosive, can under harsh conditions, use, and have weather resistance, weather resistance preferably.The kind of antifouling paint mainly contains epoxy series antifouling paste, urethane series antifouling paste, oleic series antifouling paste, chlorinated rubber anticorrosive paint etc.; That chlorinated rubber anticorrosive paint has is acidproof preferably, brine corrosion performance and atmospheric corrosion resistance; But common chlorinated rubber anticorrosive paint snappiness and poor adhesive force, brushing property are good inadequately.
Summary of the invention
Goal of the invention: the objective of the invention is provides a kind of thick chlorinated rubber anticorrosive paint of brushing excellent performance for solving the deficiency of prior art.
The technical scheme that the present invention adopts: a kind of thick chlorinated rubber anticorrosive paint, comprise chlorinated rubber liquid, plasticity modified resin, clorafin, anti-corrosion paint, filler, auxiliary agent, the mass percent of each component is:
Chlorinated rubber liquid 10%-30%
Plasticity modified resin 20%-40%
Clorafin 5%-10%
Anti-corrosion paint 10%-15%
Filler 15%-25%
Auxiliary agent 2%-4%
Described chlorinated rubber liquid is formulated by chlorinated rubber, complexing stablizer, clorafin and solvent.
As preferably, described anti-corrosion paint is an aluminium powder.
As preferably, described filler is a mica powder.
As preferably, described auxiliary agent is an organobentonite.
Beneficial effect: the present invention has increased build through adding the thickening auxiliary agent, its brushing excellent performance, and no sag, its work efficiency is 2-3 a times that conventional oil lacquerer is imitated.That the present invention simultaneously also has is acidproof preferably, brine corrosion performance and atmospheric corrosion resistance, can be widely used in the antiseptic project of power plant, chemical plant, bridge, engineering machinery, iron tower, terminal facilities, boats and ships and freight container etc.
Embodiment:
Elaborate in the face of embodiments of the invention down.
Embodiment 1
A kind of thick chlorinated rubber anticorrosive paint, staple is: chlorinated rubber liquid, plasticity modified resin, clorafin, anti-corrosion paint, filler, auxiliary agent, anti-corrosion paint wherein are aluminium powder, and filler is a mica powder, and auxiliary agent is an organobentonite.20kg chlorinated rubber liquid, plasticity modified resin 30kg, clorafin 10kg are mixed fully dispersing and dissolving of back; Add 10kg aluminium powder, 25kg mica powder, 2kg organobentonite again; Mixture was boiled 2 hours, and temperature is 100 ℃, after cooling, makes the thick chlorinated rubber anticorrosive paint.
Embodiment 2
A kind of thick chlorinated rubber anticorrosive paint, staple is: chlorinated rubber liquid, plasticity modified resin, clorafin, anti-corrosion paint, filler, auxiliary agent, anti-corrosion paint wherein are aluminium powder, and filler is a mica powder, and auxiliary agent is an organobentonite.25kg chlorinated rubber liquid, plasticity modified resin 35kg, clorafin 5kg are mixed fully dispersing and dissolving of back; Add 15kg aluminium powder, 16kg mica powder, 4kg organobentonite again; Mixture was boiled 2 hours, and temperature is 100 ℃, after cooling, makes the thick chlorinated rubber anticorrosive paint.
Embodiment 3
A kind of thick chlorinated rubber anticorrosive paint, staple is: chlorinated rubber liquid, plasticity modified resin, clorafin, anti-corrosion paint, filler, auxiliary agent, anti-corrosion paint wherein are aluminium powder, and filler is a mica powder, and auxiliary agent is an organobentonite.15kg chlorinated rubber liquid, plasticity modified resin 40kg, clorafin 10kg are mixed fully dispersing and dissolving of back; Add 10kg aluminium powder, 22kg mica powder, 3kg organobentonite again; Mixture was boiled 2 hours, and temperature is 100 ℃, after cooling, makes the thick chlorinated rubber anticorrosive paint.
Claims (5)
1. a thick chlorinated rubber anticorrosive paint comprises chlorinated rubber liquid, plasticity modified resin, clorafin, anti-corrosion paint, filler, organobentonite, and it is characterized in that: the mass percent of each component is:
Chlorinated rubber liquid 10%-30%
Plasticity modified resin 20%-40%
Clorafin 5%-10%
Anti-corrosion paint 10%-15%
Filler 15%-25%
Auxiliary agent 2%-4%
2. thick chlorinated rubber anticorrosive paint according to claim 1 is characterized in that: described chlorinated rubber liquid is formulated by chlorinated rubber, complexing stablizer, clorafin and solvent.
3. thick chlorinated rubber anticorrosive paint according to claim 1 is characterized in that: described anti-corrosion paint is an aluminium powder.
4. thick chlorinated rubber anticorrosive paint according to claim 1 is characterized in that: described filler is a mica powder.
5. thick chlorinated rubber anticorrosive paint according to claim 1 is characterized in that: described auxiliary agent is an organobentonite.