CN102443203A - 输送机滚筒耐酸碱的橡胶包覆层及其制备方法 - Google Patents
输送机滚筒耐酸碱的橡胶包覆层及其制备方法 Download PDFInfo
- Publication number
- CN102443203A CN102443203A CN2011102697346A CN201110269734A CN102443203A CN 102443203 A CN102443203 A CN 102443203A CN 2011102697346 A CN2011102697346 A CN 2011102697346A CN 201110269734 A CN201110269734 A CN 201110269734A CN 102443203 A CN102443203 A CN 102443203A
- Authority
- CN
- China
- Prior art keywords
- acid
- roller
- alkali
- rubber
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种输送机滚筒耐酸碱的橡胶包覆层及其制备方法。所述输送机滚筒的辊芯外包覆橡胶包覆层,所述橡胶包覆层包括以下组份及重量份:丁苯胶60、天然胶40,硫化剂2.5~5、促进剂0.5~1.4、活性剂7~12、补强剂40~60、增塑软化剂5~20、防剂4~5、专用配合剂30~40。所述制备方法包括胶料制备、辊芯处理、成型、硫化。与现有技术相比,本发明该耐酸碱橡胶包覆层通过采用新配方的材料制备,能长时间在酸碱浴液作用下保持原本物理机械性能,从而使输送机滚筒能够长时间在酸碱及化学药品环境中使用。
Description
技术领域
本发明涉及输送机技术领域,尤其涉及一种输送机滚筒耐酸碱的橡胶包覆层及其制备方法。
背景技术
现有普通滚筒橡胶包覆层不能在酸碱,盐洛液等化学品中工作,当普通滚筒橡胶包覆层在接触酸碱、盐洛液药品时造成腐蚀,引起橡胶的溶胀,发生橡胶分子断裂、解聚以及配合剂的分解、溶出等现象,致使它的机械强度、物理性能突显下降,橡胶层逐渐发粘、氧化、***、脆化、裂口等,受臭氧攻击而产生龟裂,以至腐蚀完全失去工作能力。
随着工业化生产不断发展,要求滚筒使用范围用途越来越广,对耐化学药品滚筒的要求也越发凸显,此配方研制成功,填补了这一空白,市场潜力巨大,发展前途十分广阔。
经检索发现,中国专利名称为:带式输送机橡胶滚筒及其制作方法,申请号:200710053813.7申请日:2007年1月8日,该专利公开了一种带式输送机橡胶滚筒,包括滚筒轴和滚筒钢管,在滚筒轴上过盈套装由一个以上废轮胎橡胶圈组成的外表面开成弧形的耐磨缓冲层。该发明还公开了该带式输送机橡胶滚筒的制作方法。利用废轮胎橡胶圈制造的耐磨滚筒、缓冲滚筒、梳形滚筒、锥形调心滚筒、摩擦调心滚筒和橡胶调心滚筒。在保证滚筒密封性能有的前提下,在滚筒钢管或轴上套装废轮胎橡胶圈,制造的耐磨滚筒、缓冲滚筒、梳形滚筒、锥形调心滚筒、摩擦调心滚筒和橡胶调心滚筒。
检索中还发现,中国实用新型专利:短纤维增强橡胶缓冲滚筒,申请号:200820015355.8申请日:2008年8月30日,该专利涉及一种用于带式输送机的短纤维增强橡胶缓冲滚筒,特征是在滚筒筒芯的表面整体模压硫化有短纤维增强橡胶层,短纤维增强橡胶层与滚筒筒芯为整体结构。所述的短纤维增强橡胶层为沟槽与突起相间的环形或螺旋形。
虽然以上的技术能够解决一定的问题,使滚筒在防腐蚀、防锈蚀、耐磨损、耐冲击、耐老化、抗撕裂等方面带来改善,但是这些技术仍然没有解决滚筒长时间在酸碱化学药品中同时又涉及高温、低温环境中使用的问题。
发明内容
本发明的目的在于解决现有技术中的上述不足,提供一种输送机滚筒的耐酸碱橡胶包覆层及其制备方法。该耐酸碱橡胶包覆层通过采用新配方的材料制备,能长时间在酸碱浴液作用下保持原本物理机械性能,从而使输送机滚筒能够长时间在酸碱及化学药品环境中使用。
本发明的目的是通过以下技术方案来实现的:
本发明涉及的一种输送机滚筒耐酸碱的橡胶包覆层,所述输送机滚筒的辊芯外包覆橡胶包覆层,所述橡胶包覆层包括以下组份及重量份:丁苯胶60、天然胶40,硫化剂2.5~5、促进剂0.5~1.4、活性剂7~12、补强剂40~60、增塑软化剂5~20、防剂4~5、专用配合剂30~40。
优选的,所述硫化剂为二硫代四甲基秋兰姆和/或硫黄。
优选的,所述促进剂为二硫代二苯并噻唑和N-环己基2-苯并噻唑次磺酰胺;所述活性剂为硬脂酸和氧化锌。
优选的,所述补强剂为高耐磨炭黑和/或通用炭黑。
优选的,所述增塑软化剂为邻苯二甲酸二辛丁酯。
优选的,所述防老剂为N-异丙基-N′-苯基对苯二胺、2,2,4-三甲基-1,2-二氢化喹啉以及微晶蜡或石蜡。
优选的,所述专用配合剂为硫酸钡或重晶石粉。
本发明还提供一种上述的输送机滚筒耐酸碱的橡胶包覆层的制备方法,包括以下步骤:
第一步,胶料制备:按所述的各组份及重量份备料;再分别进行丁苯胶、天然胶塑炼;将塑炼后的丁苯胶、天然胶一起投入密炼机进行混合3min,然后依次投入活性剂、防老剂和促进剂;补强剂、专用配合剂和增塑软化剂进行混炼,混炼均匀后排胶,排胶温度120℃,硫化剂和促进剂在开炼机上加入并出片,停放冷却待用;
第二步,辊芯处理:打毛刺除锈后用汽油或丙酮清洗油污;干燥后涂胶粘剂、刷胶浆,完全干燥后待用;
第三步,成型:将上述第一步中制得的冷却待用的胶料在开炼机上热炼,精炼出片;在第二步中处理好的辊芯上用机械法加压包胶成型;
第四步,硫化:采用直接蒸汽内控压力硫化罐登峰式硫化方法对第三步中在辊芯上包胶成型的胶料硫化处理,硫化温度和时间分别为:一段115℃,60min~90min;二段125℃,60min~90min;三段133℃,90min~120min;四段144℃,60min~150min;五段149~151℃,60min~150min;接着闷罐60min后出罐。
优选的,第一步中,所述丁苯胶塑炼具体为塑炼辊温20~40℃,用1mm辊距薄通10min/10kg后放厚辊距出片冷却8小时以上待用;所述天然胶塑炼具体为辊距0.5~1mm,薄通法,辊温控制在45~50℃之间,可塑度为0.35以上,放厚辊距出片停放10小时以上待用。
优选的,第三步中,所述精炼出片为分层出片,单片厚度为3~4.5mm。
与现有技术相比,本发明具有如下有益效果:
1、本发明的胶料加工过程中采用了最精湛的塑混炼工艺,严格控制和掌握开炼机和密炼机的操作过程,把握塑混炼温度和胶料可塑性以及加料顺序;严格执行粘合剂粘合工艺和胶料贴合工艺;在硫化过程中采用直接蒸汽内控压力硫化罐设备,采用科学的登峰式,从低温到高温的硫化方法,准确掌握硫化时间,根据滚筒大、小和橡胶层厚度给330min到600min不等合适的硫化时间,严密掌握和控制硫化工艺“三要素”,使生产出来的滚筒橡胶包覆层达到最佳硫化点,也是对耐酸碱滚筒的经久耐用起到重要作用。
2、本发明的滚筒橡胶包覆层能在长时间酸碱中并在寒热老化作用下保持原来的物理机械性能,并能正常使用,有效地解决了普通滚筒所不能使用的缺陷,填补了我国的冶金、矿山、码头等使用输送机上用耐酸碱滚筒的空白,同时满足了用户要求。因此本发明制造具有很高的推广应用价值。
附图说明
图1为本发明中的耐酸碱橡胶包覆层制备流程图。
具体实施方式
以下结合附图和具体实施例对本发明的技术方案作进一步的解释,但是以下的内容不用于限定本发明的保护范围。
实验例1~6
实施例1~6中的橡胶包覆层材料为以丁苯胶与天然胶并用为主体的耐酸碱胶料,包括丁苯胶,天然胶,硫化剂,促进剂,活性剂,补强剂,增塑软化剂,防老剂和专用配合剂;实施例1~6中的橡胶包覆层材料的具体组份及用量如表1所示:
表1实施例1~6的组份及用量(kg)
如图1所示,采用上述橡胶包覆层材料制备所述滚筒橡胶包覆层包括如下步骤:
A、以丁苯胶、天然胶作为主体材料制备滚筒耐酸碱橡胶包覆层胶料时,首先将材料进行预处理,生胶分别在16时开炼机上进行薄通塑炼,辊温控制在:丁苯胶20~40℃,天然胶40~45℃,辊距与塑炼时间:丁苯胶1mm,薄通法,时间10min(以10kg计)后放厚出片冷却8小时以上待用;天然胶0.5~1mm薄通,可塑度达0.35以上,放厚辊距出片停放10小时以上待用。混炼:用密炼机混炼,方法是:将已塑炼达到标准的两种生胶一起投入密炼机中进行混合3min,紧接着加入配合剂混炼。投料顺序为:活性剂、防老剂和促进剂;补强剂、专用配合剂和增塑软化剂;混炼均匀(达到给定的混炼时间)后排胶,排胶温度120℃,硫化剂和促进剂在开炼机上加入并出片,停放冷却待用。
B、在滚筒包覆橡胶层前,用打毛机处理辊芯表面锈迹和毛刺,再用汽油或丙酮清洗油污,干燥后涂胶粘剂(开姆洛克或列克纳),再涂刷一层胶浆,待完全干燥包胶成型。
C、成型时将停放待用的胶料再进行热炼,并根据滚筒不同规格要求及橡胶包覆层厚度,分层出片,单片厚度3~4.5mm为佳。紧接着在处理好的辊芯上用机械法包胶成型。包胶成型之后包纸包布,缠钢丝。
D、接下来进行滚筒在饱和蒸汽做介质的硫化罐中登峰式硫化,硫化温度和时间是:一段为115℃,60min~90min;二段为125℃,60min~90min;三段为133℃,90min~120min;四段为144℃,60min~150min;五段为149℃~151℃,60min~150min;接着闷罐60min后出罐;即可制成实施例1~6的橡胶包覆层在水、空气、稀酸、碱中工作,温度-30℃~+70℃;在水蒸汽中工作,温度120℃;在弱酸碱中工作,温度-45℃~+100℃,在这样环境范围中能正常工作的滚筒。
Claims (10)
1.一种输送机滚筒耐酸碱的橡胶包覆层,其特征在于,所述输送机滚筒的辊芯外包覆橡胶包覆层,所述橡胶包覆层包括以下组份及重量份:丁苯胶60、天然胶40,硫化剂2.5~5、促进剂0.5~1.4、活性剂7~12、补强剂40~60、增塑软化剂5~20、防剂4~5、专用配合剂30~40。
2.根据权利要求1所述的输送机滚筒耐酸碱的橡胶包覆层,其特征在于,所述硫化剂为二硫代四甲基秋兰姆和/或硫黄。
3.根据权利要求1所述的输送机滚筒耐酸碱的橡胶包覆层,其特征在于,所述促进剂为二硫代二苯并噻唑和N-环己基-2-苯并噻唑次磺酰胺;所述活性剂为硬脂酸和氧化锌。
4.根据权利要求1所述的输送机滚筒耐酸碱的橡胶包覆层,其特征在于,所述补强剂为高耐磨炭黑和/或通用炭黑。
5.根据权利要求1所述的输送机滚筒耐酸碱的橡胶包覆层,其特征在于,所述增塑软化剂为邻苯二甲酸二辛丁酯。
6.根据权利要求1所述的输送机滚筒耐酸碱的橡胶包覆层,其特征在于,所述防老剂为N-异丙基-N′-苯基对苯二胺、2,2,4-三甲基-1,2-二氢化喹啉以及微晶蜡或石蜡。
7.根据权利要求1所述的输送机滚筒耐酸碱的橡胶包覆层,其特征在于,所述专用配合剂为硫酸钡或重晶石粉。
8.一种根据权利要求1所述的输送机滚筒耐酸碱的橡胶包覆层的制备方法,其特征在于,包括以下步骤:
第一步,胶料制备:按所述的各组份及重量份备料;再分别进行丁苯胶、天然胶塑炼;将塑炼后的丁苯胶、天然胶一起投入密炼机进行混合3min,然后依次投入活性剂、防老剂和促进剂;补强剂、专用配合剂和增塑软化剂进行混炼,混炼均匀后排胶,排胶温度120℃,硫化剂和促进剂在开炼机上加入并出片,停放冷却待用;
第二步,辊芯处理:打毛刺除锈后用汽油或丙酮清洗油污;干燥后涂胶粘剂、刷胶浆,完全干燥后待用;
第三步,成型:将上述第一步中制得的冷却待用的胶料在开炼机上热炼,精炼出片;在第二步中处理好的辊芯上用机械法加压包胶成型;
第四步,硫化:采用直接蒸汽内控压力硫化罐登峰式硫化方法对第三步中在辊芯上包胶成型的胶料硫化处理,硫化温度和时间分别为:一段115℃,60min~90min;二段125℃,60min~90min;三段133℃,90min~120min;四段144℃,60min~150min;五段149~151℃,60min~150min;接着闷罐60min后出罐。
9.根据权利要求8所述的输送机滚筒耐酸碱的橡胶包覆层的制备方法,其特征在于,第一步中,所述丁苯胶塑炼具体为塑炼辊温20~40℃,用1mm辊距薄通10min/10kg后放厚辊距出片冷却8小时以上待用;所述天然胶塑炼具体为辊距0.5~1mm,薄通法,辊温控制在45~50℃之间,可塑度为0.35以上,放厚辊距出片停放10小时以上待用。
10.输送机滚筒耐酸碱的橡胶包覆层的制备方法,其特征在于,第三步中,所述精炼出片为分层出片,单片厚度为3~4.5mm。