CN103450568B - 一种repdm/riir弹性体及其制备方法 - Google Patents
一种repdm/riir弹性体及其制备方法 Download PDFInfo
- Publication number
- CN103450568B CN103450568B CN201310398899.2A CN201310398899A CN103450568B CN 103450568 B CN103450568 B CN 103450568B CN 201310398899 A CN201310398899 A CN 201310398899A CN 103450568 B CN103450568 B CN 103450568B
- Authority
- CN
- China
- Prior art keywords
- parts
- repdm
- riir
- elastomerics
- sulfur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种REPDM/RIIR弹性体及其制备方法,涉及一种弹性体材料及其制备方法,该防水材料由以下组成物的质量份组成:100份REPDM与RIIR并用,1~2份硫黄,0.9~2份促进剂,2.5~8份硫化活性剂,0~20份炭黑。EPDM与IIR并用二者有良好的工艺相容性,可得到较好的综合性能。并用胶可以采用硫黄、过氧化物、酯类及树脂进行硫化,它们的硫化速率较接近,易形成共硫化材料。本发明完全利用REPDM、RIIR来代替EPDM、IIR,配合使用补强剂、硫化助剂降低了防水材料的成本,使防水材料易成型,改善与基体的粘合性。经试验研究制得具有耐臭氧、耐候性、耐低温、耐化学介质、耐热空气老化优秀的REPDM/RIIR防水材料。
Description
技术领域
本发明涉及一种弹性体材料及其制备方法,特别是涉及一种REPDM/RIIR弹性体及其制备方法。
背景技术
废橡胶的处理是当今社会面临的严重问题之一。为了满足不断提高的材料性能要求,橡胶逐渐朝着高强度、耐磨、稳定和耐老化的方向发展,但是废弃后的橡胶长时期不能自然降解,造成了比塑料污染(白色污染)更难处理的黑色污染,浪费了宝贵的橡胶资源。建筑物渗漏一直是我国建筑行业的难问题。目前,我国房屋渗漏率很高,主要原因是防水材料档次低、质量差。因此,在我国高性能防水材料的需求很大,但由于成本问题很难将高性能的防水材料普及到建筑行业中。因此,废橡胶经处理后的再生胶将是制备低成本高性能防水材料的理想原料。
EPDM与IIR并用二者有良好的工艺相容性,EPDM/IIR防水材料具有耐候、耐热空气老化、耐臭氧、耐化学介质、耐水、耐低温等优异的综合性能,EPDM与IIR并用还可提高防水材料的粘合性,可得到较好的综合机械性能。由于二者的价格都比较昂贵,因此REPDM/RIIR防水材料的制备,不但解决了成本高的问题,又实现了再生胶的利用。而在文献专利中关于REPDM/RIIR防水材料这方面的介绍并未见报道。
发明内容
本发明的目的在于提供一种REPDM/RIIR弹性体及其制备方法,本发明利用REPDM、RIIR来代替EPDM、IIR,配合使用补强剂、硫化助剂降低了防水材料的成本,使防水材料易成型,改善与基体的粘合性,此种弹性体可作为防水材料,其制备方法简单,成本低廉。
本发明的目的是通过以下技术方案实现的:
一种REPDM/RIIR弹性体,由以下组成物的质量份组成:100份REPDM与RIIR并用,1~2份硫黄,0.9~2份促进剂,2.5~8份硫化活性剂,0~20份炭黑。
本发明所述的一种REPDM/RIIR弹性体,其所述的炭黑可为青岛凯博特橡塑助剂有限公司所生产的中超耐磨炉黑(N220)、高耐磨炉黑(N330)或快压出炉黑(N550)。
本发明所述的一种REPDM/RIIR弹性体,其所述的硫化促进剂可为石家庄市茂丰化工有限公司生产的N-环己基-2-苯并噻唑次磺酰胺(CZ)、二甲基二硫代氨基甲酸锌(BZ)、二丁基二硫代氨基甲酸锌(PZ)、二硫化四甲基秋兰姆(TMTD)、硫醇基苯并噻唑(M)或二硫化苯并噻唑(DM)单独使用,或者这几种促进剂两种或这两种以上的组合使用。
本发明所述的一种REPDM/RIIR弹性体,其所述的硫化活性剂为沈阳三威兴旺化工有限公司生产的硬脂酸、葫芦岛锌业股份有限公司生产的氧化锌两者结合使用。
一种REPDM/RIIR弹性体,其制备步骤:
a.先将REPDM与RIIR在开炼机上薄通数次使之混合均匀,然后依次加入氧化锌、硬脂酸,混炼均匀后加入炭黑,混合均匀后加入促进剂,最后加入硫化剂;之后将混炼胶打包10次,混合均匀下片,停放24小时待用;
b.将停放24小时的胶片返炼重新下片,留以待用;
c.将步骤b中的返炼胶放到平板硫化机上进行硫化,温度控制在160℃,硫化时用橡胶无转子硫化仪测定t10和t90,ML和MH(各实施例测试结果见表1);到达时间后,取出硫化胶,将其自然冷却,即得到REPDM/RIIR弹性体,用于测定力学性能。
实验中所用的开放式炼胶机为青岛环球机械股份有限公司生产,型号为XK-160;橡胶无转子硫化仪为台湾高铁科技股份有限公司生产,型号为GT-M2000-A;平板硫化机为青岛环球机械股份有限公司生产,型号为XLB-DQ400×400×2E;电子拉伸试验机为深圳市瑞格尔仪器有限公司生产,型号为RGL-30A;邵尔硬度计为营口市材料试验机厂生产,型号为XHS;冲片机为上海化工机械四厂生产,型号为CP-25。
本发明的优点与效果是:
1、本发明的一种REPDM/RIIR弹性体,该弹性体可用于防水工程,此防水材料具有耐臭氧、耐候性、耐低温、耐化学介质、耐热空气老化等优异性能。
2、本发明的一种REPDM/RIIR弹性体制备方法简单,该弹性体可用于防水材料,此防水材料成本低廉并且提高了防水材料和基材之间的粘合性。
具体实施方式
实施例1:
本实施例中,采用的硫化体系为硫黄、BZ、M组成,硫化活性剂为氧化锌与硬脂酸配合使用,具体配方:REPDM80份,RIIR20份,BZ1.5份,DM0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。
本实施例所述REPDM/RIIR弹性体,其制备步骤:
a.先将REPDM与RIIR在开炼机上薄通数次使之混合均匀,然后加入氧化锌、硬脂酸,混合均匀后加入促进剂,最后加入硫黄;之后将混炼胶打包10次,混合均匀下片,停放24小时待用;
b.将停放24小时的胶片返炼重新下片,留以待用;
c.将步骤b中的返炼胶放到平板硫化机上进行硫化,温度控制在160℃,硫化时用橡胶无转子硫化仪测定t10和t90,ML和MH(各实施例测试结果见表1);到达时间后,取出硫化胶,将其自然冷却,即得到REPDM/RIIR弹性体,用于测定力学性能。
本实施例所述REPDM/RIIR弹性体,性能测试分为拉伸性能测试,按GB/T528—2009进行;撕裂性能测试,按GB/T529-2008进行;邵尔硬度测试,按GB/T531.1—2008进行。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例2:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,BZ1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例3:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,PZ1.5份,DM0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例4:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,PZ1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例5:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,TMTD1.5份,DM0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例6:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,TMTD1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例7:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM100份,RIIR20份,PZ1份,TMTD0.5份,DM0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例8:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,PZ0.5份,BZ0.5,TMTD0.5份,DM0.2,M0.3份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例9:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,PZ0.5份,TMTD1份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例10:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,PZ0.5份,TMTD0.5份,BZ0.5,DM0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例11:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方REPDM80份,RIIR20份,BZ0.5份,TMTD1份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例12:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,PZ0.5份,TMTD0.5份,BZ0.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例13:
本实施例与实施例1的区别在于,改变了促进剂的种类,具体配方:REPDM80份,RIIR20份,BZ0.5份,TMTD1份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例14:
本实施例与实施例1的区别在于,混炼胶部分采用的硫化体系为硫黄、TMTD、BZ、DM组成,额外添加N330,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM80份,RIIR20份,TMTD1份,BZ0.5份,DM0.5份,氧化锌5份,硬脂酸3份,N3305份,硫黄1.5份。
本实施例所述REPDM/RIIR弹性体,其制备步骤:
a.先将REPDM与RIIR在开炼机上薄通数次,然后加入氧化锌、硬脂酸,混炼均匀后加入N330,混合均匀后加入促进剂,最后加入硫黄;之后将混炼胶打包10次,混合均匀下片,停放24小时待用;
b.将停放24小时的胶片返炼重新下片,留以待用;
c.将步骤b中的返炼胶放到平板硫化机上进行硫化,温度控制在160℃,硫化时用橡胶无转子硫化仪测定t10和t90,ML和MH(各实施例测试结果见表1);到达时间后,取出硫化胶,将其自然冷却,即得到REPDM/RIIR弹性体,用于测定力学性能。
本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例15:
本实施例与实施例1的区别在于,采用的硫化体系为硫黄、TMTD、BZ、DM组成,额外添加N330,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM80份,RIIR20份,TMTD1份,BZ0.5份,DM0.5份,氧化锌5份,硬脂酸3份,N33010份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例16:
本实施例与实施例1的区别在于,采用的硫化体系为硫黄、TMTD、BZ、DM组成,额外添加N330,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM80份,RIIR20份,TMTD1份,BZ0.5份,DM0.5份,氧化锌5份,硬脂酸3份,N33015份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例17:
本实施例与实施例1的区别在于,采用的硫化体系为硫黄、TMTD、BZ、DM组成,额外添加N330,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM80份,RIIR20份,TMTD1份,BZ0.5份,DM0.5份,氧化锌5份,硬脂酸3份,N33020份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例18:
本实施例与实施例1的区别在于,改变REPDM与RIIR质量份比例,采用的硫化体系为硫黄、TMTD、M组成,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM50份,RIIR50份,TMTD1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例19:
本实施例与实施例1的区别在于,改变REPDM与RIIR质量份比例,采用的硫化体系为硫黄、TMTD、M组成,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM60份,RIIR40份,TMTD1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例20:
本实施例与实施例1的区别在于,改变REPDM与RIIR质量份比例,采用的硫化体系为硫黄、TMTD、M组成,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM70份,RIIR30份,TMTD1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
实施例21:
本实施例与实施例1的区别在于,改变REPDM与RIIR质量份比例,采用的硫化体系为硫黄、TMTD、M组成,硫化化活性剂为硬脂酸与氧化锌并用。具体配方:REPDM90份,RIIR10份,TMTD1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。本实施例所述REPDM/RIIR弹性体,其力学性能测试结果见表2所示。
表1各实施例硫化数据
测试项目 | MH/dN·m | ML/dN·m | t10/min | t90/min |
实施例1 | 3 | 0 | 1:31 | 18:52 |
实施例2 | 3 | 0 | 1:13 | 14:50 |
实施例3 | 3 | 0 | 2:12 | 10:10 |
实施例4 | 2 | 0 | 0:51 | 15:37 |
实施例5 | 3 | 0 | 2:51 | 12:38 |
实施例6 | 3 | 0 | 0:55 | 13:56 |
实施例7 | 3 | 0 | 2:01 | 10:48 |
实施例8 | 3 | 0 | 1:21 | 10:37 |
实施例9 | 3 | 0 | 1:40 | 10:37 |
实施例10 | 3 | 0 | 1:36 | 9:56 |
实施例11 | 3 | 0 | 2:14 | 10:02 |
实施例12 | 3 | 0 | 1:09 | 10:41 |
实施例13 | 3 | 0 | 1:40 | 10:32 |
实施例14 | 2 | 0 | 2:11 | 11;45 |
实施例15 | 3 | 0 | 2:12 | 10:10 |
实施例16 | 3 | 0 | 2:05 | 9:12 |
实施例17 | 3 | 0 | 2:04 | 8:21 |
实施例18 | 2 | 0 | 2:11 | 11:45 |
实施例19 | 3 | 0 | 2:12 | 10:10 |
实施例20 | 3 | 0 | 2:05 | 9:12 |
实施例21 | 3 | 0 | 2:04 | 8:21 |
表2各实施例力学性能
测试项目 | 抗拉强度/MPa | 断裂伸长率/% | 撕裂强度/KN/m | 硬度/度 |
实施例1 | 6.1 | 357 | 22 | 62 |
实施例2 | 5.6 | 339 | 21 | 65 |
实施例3 | 6.0 | 366 | 21 | 64 |
实施例4 | 6.0 | 348 | 21 | 66 |
实施例5 | 5.6 | 363 | 21 | 61 |
实施例6 | 5.6 | 344 | 20 | 65 |
实施例7 | 6.3 | 334 | 19 | 65 |
实施例8 | 6.5 | 338 | 20 | 63 |
实施例9 | 5.8 | 317 | 24 | 66 |
实施例10 | 6.4 | 339 | 23 | 66 |
实施例11 | 7.1 | 340 | 23 | 65 |
实施例12 | 6.9 | 325 | 22 | 62 |
实施例13 | 6.1 | 326 | 25 | 62 |
实施例14 | 5.7 | 299 | 20 | 74 |
实施例15 | 6.0 | 223 | 22 | 77 |
实施例16 | 6.6 | 176 | 21 | 80 |
实施例17 | 6.5 | 157 | 23 | 83 |
实施例18 | 4.7 | 359 | 20 | 61 |
实施例19 | 5.3 | 338 | 22 | 62 |
实施例20 | 6.0 | 366 | 21 | 64 |
实施例21 | 5.9 | 237 | 24 | 67 |
Claims (6)
1.一种REPDM/RIIR弹性体,其特征在于,由以下组成物的质量份组成:REPDM80份,RIIR20份,PZ1.5份,DM0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。
2.一种REPDM/RIIR弹性体,其特征在于,由以下组成物的质量份组成:REPDM80份,RIIR20份,PZ1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。
3.一种REPDM/RIIR弹性体,其特征在于,由以下组成物的质量份组成:REPDM100份,RIIR20份,PZ1份,TMTD0.5份,DM0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。
4.一种REPDM/RIIR弹性体,其特征在于,由以下组成物的质量份组成:REPDM80份,RIIR20份,BZ0.5份,TMTD1份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。
5.一种REPDM/RIIR弹性体,其特征在于,由以下组成物的质量份组成:REPDM80份,RIIR20份,PZ0.5份,TMTD0.5份,BZ0.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。
6.一种REPDM/RIIR弹性体,其特征在于,由以下组成物的质量份组成:REPDM70份,RIIR30份,TMTD1.5份,M0.5份,氧化锌5份,硬脂酸3份,硫黄1.5份。