CN102424905A - Production method and system of aluminum alloy plates - Google Patents
Production method and system of aluminum alloy plates Download PDFInfo
- Publication number
- CN102424905A CN102424905A CN2011104208965A CN201110420896A CN102424905A CN 102424905 A CN102424905 A CN 102424905A CN 2011104208965 A CN2011104208965 A CN 2011104208965A CN 201110420896 A CN201110420896 A CN 201110420896A CN 102424905 A CN102424905 A CN 102424905A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- aluminium alloy
- alloy strips
- plate materials
- strips
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a production method of aluminum alloy plates, comprising the following steps of: decoiling aluminum alloy plates by a decoiler to obtain aluminum alloy tapes; cleaning the aluminum alloy tapes for the first time; enabling the aluminum alloy tapes to pass through an air cushion furnace at a set speed, performing continuous annealing in the air cushion furnace, wherein the temperature of a heating section of the air cushion furnace is a set annealing temperature, and the temperature of a holding section of the air cushion furnace is a set cooling temperature; cleaning the aluminum alloy tapes for the second time; performing stretch leveling on the aluminum alloy tapes by a stretcher leveler; coiling the aluminum alloy tapes by a coiler to obtain aluminum alloy coils; and cutting the aluminum alloy coils to length in a transverse cutting unit to obtain finished products of aluminum alloy plates. The production method of aluminum alloy plates reduces scratches, oil stain and aluminum ash residue on the surfaces of the aluminum alloy plates, and meets the requirements on surface quality of aluminum alloy plates for electrommunication control cabinets. The invention also provides a production system of the aluminum alloy plates.
Description
Technical field
The present invention relates to telecommunications control cabinet manufacturing technology field, more particularly, relate to a kind of working method and system of aluminum alloy plate materials.
Background technology
Along with the fast development of telecommunications industry, for electronics require increasingly highly, wherein, the specification of quality of telecommunications control cabinet with aluminum alloy plate materials increased.
Telecommunications control cabinet need spray with aluminum alloy plate materials; The wiping scuffing on the surface of aluminum alloy plate materials, greasy dirt and aluminium ash residue can influence spraying effect; Therefore telecommunications control cabinet is had relatively high expectations with the surface quality of aluminum alloy plate materials, i.e. telecommunications control cabinet must not have too much wiping scuffing, greasy dirt and aluminium ash residue with the surface of aluminum alloy plate materials.
At present, the working method of aluminum alloy plate materials mainly contains two kinds: the piece chip is produced and rolling production.
The technical process of piece chip production is:
1) shears the buttress sheet;
2) annealing;
3) aligning;
4) scale.
In the existing chip production process; Shear the duraluminum coiled material; And its buttress put together, become the annealing of buttress then, cause aluminum alloy sheet material surface to form too much wiping scratching easily like this; Finally cause the surface quality of aluminum alloy plate materials relatively poor, can not satisfy telecommunications control cabinet with the requirement of aluminum alloy plate materials to its surface quality.
The technical process that rolling is produced is:
1) coiled material cleans;
2) coiled material annealing;
3) shear scale.
Existing rolling is produced and is adopted coiled material annealing, and in the annealed process, because aluminum strip is a coiled material, the greasy dirt on aluminum strip surface is not volatile, is prone to cause greasy dirt to form oil mark so; When simultaneously coiled material cleaned, the aluminium ash residue on the coiled material was difficult for cleaning, and caused on the coiled material aluminium ash residue also more.Aforesaid method finally causes the surface quality of aluminum alloy plate materials lower, can not reach telecommunications control cabinet with the requirement of aluminum alloy plate materials to its surface quality.
In addition, in piece chip production process, the production cycle is longer, has finally reduced the production efficiency of aluminum alloy plate materials; In the rolling production process, the cooling time that needs during coiled material annealing is longer, has finally reduced the production efficiency of aluminum alloy plate materials.
In sum; How a kind of working method of aluminum alloy plate materials is provided; With wiping scuffing, greasy dirt and the aluminium ash residue that reduces aluminum alloy sheet material surface; And then the surface quality of raising aluminum alloy plate materials, satisfy telecommunications control cabinet with the requirement of aluminum alloy plate materials to its surface quality, be present those skilled in the art's problem demanding prompt solution.
Summary of the invention
In view of this; The invention provides a kind of working method of aluminum alloy plate materials; Reduced wiping scuffing, greasy dirt and the aluminium ash residue of aluminum alloy sheet material surface, and then improved the surface quality of aluminum alloy plate materials, satisfied telecommunications control cabinet with the requirement of aluminum alloy plate materials to its surface quality.
In order to achieve the above object, the present invention provides following technical scheme:
A kind of working method of aluminum alloy plate materials comprises:
1) adopts Abrollhaspel to the aluminum alloy plate materials uncoiling, obtain aluminium alloy strips;
2) said aluminium alloy strips being carried out the first time cleans;
3) said aluminium alloy strips passes through air cushion furnace with the speed of setting, and in air cushion furnace, carries out continuous annealing, the annealing temperature of the Heating Zone Temperature of said air cushion furnace for setting, the cooling temperature of the heat preservation zone temperature of said air cushion furnace for setting;
4) the said aluminium alloy strips to annealed processing carries out the cleaning second time;
5) through stretching straightener the said aluminium alloy strips through cleaning is for the second time carried out tension leveling;
6) batch said aluminium alloy strips through reeling machine, obtain the duraluminum coiled material;
7) in transverse cutting machine row, said duraluminum coiled material is carried out cutting to length, obtain the aluminum alloy plate materials finished product.
Preferably, in the working method of above-mentioned aluminum alloy plate materials, said step 2) be specially and adopt the mode of spray equipment spraying water to clean said aluminium alloy strips.
Preferably, in the working method of above-mentioned aluminum alloy plate materials, said step 4) is specially and adopts the mode that adopts brush roll to scrub after the shower nozzle spray water to clean said aluminium alloy strips earlier.
Preferably, in the working method of above-mentioned aluminum alloy plate materials, the temperature of said water is between 40-80 ℃.
Preferably, the working method of above-mentioned aluminum alloy plate materials, said step 1) and said step 2) between also comprise:
11) said aluminium alloy strips is cut edge, make the width of said aluminium alloy strips reach the size of setting;
12) some said aluminium alloy strips of annealed of treating are sewed up successively from beginning to end.
Preferably, in the working method of above-mentioned aluminum alloy plate materials, the speed of setting described in the said step 3) is according to the thickness setting of said aluminium alloy strips; Annealing temperature is according to alloy, state and the thickness setting of said aluminium alloy strips, and said cooling temperature is a normal temperature.
Based on the working method of the above-mentioned aluminum alloy plate materials that provides, the present invention also provides a kind of production system of aluminum alloy plate materials, comprising: the uncoiling aluminum alloy plate materials obtains the Abrollhaspel of aluminium alloy strips;
Clean first washing unit of said aluminium alloy strips;
To the said aluminium alloy strips annealed air cushion furnace that cleans through first washing unit;
Clean second washing unit of annealed said aluminium alloy strips;
Stretching straightener to the said aluminium alloy strips tension leveling of cleaning through second washing unit;
Said aluminium alloy strips is batched the reeling machine into the duraluminum coiled material;
Cutting to length through said reeling machine roll up the transverse cutting machine row of said duraluminum coiled material;
Be provided with transport unit between the device of said adjacent operation;
Said air cushion furnace comprises the heater block and the heat preservation component of alloy, state and thickness setting temperature according to said aluminium alloy strips.
Preferably, in the production system of above-mentioned aluminum alloy plate materials, said first washing unit is a spray equipment, is positioned at the top and the bottom of said aluminium alloy strips; Said second washing unit comprises some groups of nozzles and brush roll, is positioned at the top and the bottom of said aluminium alloy strips.
Preferably, the production system of above-mentioned aluminum alloy plate materials also comprises the bead cutter and the sewing machine of sewing up said aluminium alloy strips through side cut after of cutting through the said aluminum alloy strip edge portion of said Abrollhaspel uncoiling.
Preferably, in the production system of above-mentioned aluminum alloy plate materials, said aluminium alloy strips is the speed according to the thickness setting of said aluminium alloy strips through said air cushion furnace annealed transmission speed; The annealing temperature of said aluminium alloy strips is the temperature of alloy, state and thickness setting according to said aluminium alloy strips.
In the working method of aluminum alloy plate materials provided by the invention, aluminium alloy strips is carried out twice cleaning, reduced the greasy dirt and the aluminium ash residue on aluminium alloy strips surface effectively; In the annealed process, the warm air in the stove partly volatilizees the greasy dirt on aluminium alloy strips surface in air cushion furnace, has reduced the greasy dirt on aluminium alloy strips surface effectively; Adopt air cushion furnace that aluminium alloy strips is annealed, air cushion supports aluminium alloy strips, has avoided causing wiping to draw to aluminium alloy strips.The working method of above-mentioned aluminum alloy plate materials has reduced wiping scuffing, greasy dirt and the aluminium ash residue of aluminum alloy sheet material surface, and then has improved the surface quality of aluminum alloy plate materials, has satisfied telecommunications control cabinet with the requirement of aluminum alloy plate materials to its surface quality.
Description of drawings
In order to be illustrated more clearly in the embodiment of the invention or technical scheme of the prior art; To do to introduce simply to the accompanying drawing of required use in embodiment or the description of the Prior Art below; Obviously, the accompanying drawing in describing below only is some embodiments of the present invention, for those of ordinary skills; Under the prerequisite of not paying creative work, can also obtain other accompanying drawing according to these accompanying drawings.
The schematic flow sheet of the embodiment one of the working method of the aluminum alloy plate materials that Fig. 1 provides for the embodiment of the invention;
The schematic flow sheet of the embodiment two of the working method of the aluminum alloy plate materials that Fig. 2 provides for the embodiment of the invention;
The system chart of the production system of the aluminum alloy plate materials that Fig. 3 provides for the embodiment of the invention.
Among last Fig. 3:
Abrollhaspel 1, bead cutter 2, sewing machine 3, first washing unit 4, air cushion furnace 5, second washing unit 6, stretching straightener 7, reeling machine 8, transverse cutting machine row 9, transport unit 10.
Embodiment
The invention provides a kind of working method of aluminum alloy plate materials; Wiping scuffing, greasy dirt and the aluminium ash residue of aluminum alloy sheet material surface have been reduced; And then improved the surface quality of aluminum alloy plate materials, satisfied telecommunications control cabinet with the requirement of aluminum alloy plate materials to its surface quality.
To combine the accompanying drawing in the embodiment of the invention below, the technical scheme in the embodiment of the invention is carried out clear, intactly description, obviously, described embodiment only is the present invention's part embodiment, rather than whole embodiment.Based on the embodiment among the present invention, those of ordinary skills are not making the every other embodiment that is obtained under the creative work prerequisite, all belong to the scope of the present invention's protection.
Please refer to accompanying drawing 1-3, the schematic flow sheet of the embodiment one of the working method of the aluminum alloy plate materials that Fig. 1 provides for the embodiment of the invention; The schematic flow sheet of the embodiment two of the working method of the aluminum alloy plate materials that Fig. 2 provides for the embodiment of the invention; The system chart of the production system of the aluminum alloy plate materials that Fig. 3 provides for the embodiment of the invention.
Please refer to accompanying drawing 1, the schematic flow sheet of the embodiment one of the working method of the aluminum alloy plate materials that Fig. 1 provides for the embodiment of the invention, concrete grammar is following:
S101) adopt 1 pair of aluminum alloy plate materials uncoiling of Abrollhaspel, obtain aluminium alloy strips:
The duraluminum coiled material is become aluminium alloy strips, prepare for cleaning better;
S102) aluminium alloy strips being carried out the first time cleans:
The greasy dirt of main cleaning aluminum alloy strip surface and aluminium ash residue;
S103) aluminium alloy strips passes through air cushion furnace 5 with the speed of setting, and in air cushion furnace 5, carries out continuous annealing, the annealing temperature of the Heating Zone Temperature of air cushion furnace 5 for setting, and the cooling temperature of the heat preservation zone temperature of air cushion furnace 5 for setting:
Aluminium alloy strips passes through air cushion furnace 5 with the speed of setting; Air cushion in the air cushion furnace 5 supports aluminium alloy strips, makes aluminium alloy strips not contact with air cushion furnace 5, when air cushion supports aluminium alloy strips; It is heated; Aluminium alloy strips is heated in the heating zone of air cushion furnace 5, and temperature is an annealing temperature, and aluminium alloy strips is cooled in the heat preservation zone of air cushion furnace 5;
S104) annealed aluminium alloy treated band being carried out the second time cleans:
Clean once more, further the greasy dirt of cleaning aluminum alloy strip surface and aluminium ash residue;
S105) carry out tension leveling through 7 pairs of aluminium alloy strips of stretching straightener through cleaning for the second time;
S106) batch aluminium alloy strips through reeling machine 8, obtain the duraluminum coiled material;
S107) in transverse cutting machine row 9, the duraluminum coiled material is carried out cutting to length, obtain the aluminum alloy plate materials finished product.
In the working method of the aluminum alloy plate materials that the foregoing description provides, aluminium alloy strips is carried out twice cleaning, reduced the greasy dirt and the aluminium ash residue on aluminium alloy strips surface effectively; In the annealed process, the warm air in the stove partly volatilizees the greasy dirt on aluminium alloy strips surface in air cushion furnace 5, has reduced the greasy dirt on aluminium alloy strips surface effectively; Adopt 5 pairs of aluminium alloy strips of air cushion furnace to anneal, the air cushion in the air cushion furnace 5 supports aluminium alloy strips, has avoided causing wiping to draw to aluminium alloy strips.The working method of above-mentioned aluminum alloy plate materials has reduced wiping scuffing, greasy dirt and the aluminium ash residue of aluminum alloy sheet material surface, and then has improved the surface quality of aluminum alloy plate materials, has satisfied telecommunications control cabinet with the requirement of aluminum alloy plate materials to its surface quality.
Simultaneously, the working method of above-mentioned aluminum alloy plate materials adopts continuous annealing, can control the performance of products scope well, makes that the performance of aluminum alloy plate materials is more stable, has reduced the performance difference of aluminum alloy plate materials; In annealing process, heating and cooling are carried out simultaneously, have saved the annealed time, and aluminum alloy plate materials uncoiling, cleaning, annealing, tension leveling are accomplished on a production line, have saved the time, and then have improved the production efficiency of aluminum alloy plate materials.
Please refer to accompanying drawing 2, the schematic flow sheet of the embodiment two of the working method of the aluminum alloy plate materials that Fig. 2 provides for the embodiment of the invention, concrete grammar is following:
S201) adopt 1 pair of aluminum alloy plate materials uncoiling of Abrollhaspel, obtain aluminium alloy strips:
The duraluminum coiled material is become aluminium alloy strips, prepare for cleaning better;
S202) mode that adopts spray equipment to spray water is carried out the first time to aluminium alloy strips and is cleaned:
Spray equipment is positioned at the top and the bottom of aluminium alloy strips; Simultaneously the two sides of aluminium alloy strips is cleaned; The spray equipment spray water is cleaned, the temperature of water between 40-80 ℃, the greasy dirt of main cleaning aluminum alloy strip surface and the grey residue of aluminium; Certainly the temperature of water can also can near 40 ℃ or 80 ℃ not between 40-80 ℃;
S203) aluminium alloy strips is cut edge, makes the width of aluminium alloy strips reach the size of setting:
According to the needs of physical size, remove the limit portion of aluminium alloy strips, make the size of aluminium alloy strips reach the size of setting;
S204) some annealed aluminium alloy strips of treating are sewed up successively from beginning to end:
For the ease of continuous production, with the head and the tail stitching successively of some aluminium alloy strips along the edge;
S205) aluminium alloy strips passes through air cushion furnace 5 with the speed of setting, and in air cushion furnace 5, carries out continuous annealing, the annealing temperature of the Heating Zone Temperature of air cushion furnace 5 for setting, and the cooling temperature of the heat preservation zone temperature of air cushion furnace 5 for setting:
Aluminium alloy strips passes through air cushion furnace 5 with the speed of setting, and the speed of setting is decided according to the thickness of aluminium alloy strips, and the air cushions in the air cushion furnace 5 support aluminium alloy strips; Make aluminium alloy strips not contact, when air cushion supports aluminium alloy strips, it is heated with air cushion furnace 5; Aluminium alloy strips is heated in the heating zone of air cushion furnace 5, and temperature is an annealing temperature, and annealing temperature is confirmed according to alloy, state and the thickness of aluminium alloy strips; Aluminium alloy strips is cooled in the heat preservation zone of air cushion furnace 5, and cooling temperature is a normal temperature, and normal temperature is 20 ℃; Certainly be slightly larger than or be slightly less than 20 ℃ also passable, 20 ℃ is most preferred temperature;
S206) adopting the mode that adopts brush roll to scrub after the shower nozzle spray water that annealed aluminium alloy treated band is carried out the second time earlier cleans:
Shower nozzle and brush roll all are positioned at the end face and the bottom surface of aluminium alloy strips; Adopt the shower nozzle water spray to clean earlier; The temperature of water adopts brush roll to scrub between 40-80 ℃ then, and then washes the most greasy dirt and the aluminium ash residue on aluminium alloy strips surface; Certainly the temperature of water can also can near 40 ℃ or 80 ℃ not between 40-80 ℃;
S207) carry out tension leveling through 7 pairs of aluminium alloy strips of stretching straightener through cleaning for the second time;
S208) batch aluminium alloy strips through reeling machine 8, obtain the duraluminum coiled material;
S209) in transverse cutting machine row 9, the duraluminum coiled material is carried out cutting to length, obtain the aluminum alloy plate materials finished product.
In the working method of the aluminum alloy plate materials that provides in the foregoing description, can adopt other cleaning way cleaning aluminum alloy band, the present invention does not limit this particularly yet.
The working method of the aluminum alloy plate materials that provides based on the foregoing description, the present invention also provides a kind of production system of aluminum alloy plate materials, and it comprises: the uncoiling aluminum alloy plate materials obtains the Abrollhaspel 1 of aluminium alloy strips; First washing unit 4 of cleaning aluminum alloy band; To the aluminium alloy strips annealed air cushion furnace 5 that cleans through first washing unit 4; Clean second washing unit 6 of annealed aluminium alloy strips; Stretching straightener 7 to the aluminium alloy strips tension leveling of cleaning through second washing unit 6; Aluminium alloy strips is batched the reeling machine 8 into the duraluminum coiled material; Cutting to length through reeling machine 8 roll up the transverse cutting machine row 9 of duraluminum coiled material; Be provided with transport unit 10 between the device of adjacent operation; Air cushion furnace 5 comprises the heater block and the heat preservation component of alloy, state and thickness setting temperature according to aluminium alloy strips.
The production system of above-mentioned aluminum alloy plate materials has realized the production of the aluminum alloy plate materials that surface quality is higher through the transport unit 10 between the device of Abrollhaspel 1, first washing unit 4, air cushion furnace 5, second washing unit 6, stretching straightener 7, reeling machine 8, transverse cutting machine row 9 and adjacent operation.
In the production system of the aluminum alloy plate materials that the foregoing description provides, first washing unit 4 is a spray equipment, is positioned at the top and the bottom of aluminium alloy strips; Second washing unit 6 comprises some groups of nozzles and brush roll, is positioned at the top and the bottom of said aluminium alloy strips.First washing unit 4 and second washing unit 6 all are positioned at the top and the bottom of aluminium alloy strips, and the two sides of aluminium alloy strips is cleaned simultaneously.Preferably; The temperature of the water of hydro-peening is between 40-80 ℃; The greasy dirt of main cleaning aluminum alloy strip surface and aluminium ash residue, the temperature of water can also can near 40 ℃ or 80 ℃ not between 40-80 ℃ certainly; As long as can realize the cleaning to aluminum alloy plate materials, the present invention does not do qualification particularly to this.
Please refer to accompanying drawing 3, the production system of the aluminum alloy plate materials that the foregoing description provides also comprises the bead cutter 2 and the sewing machine 3 of sewing up aluminium alloy strips through cut edge after of cutting through the aluminum alloy strip edge portion of Abrollhaspel 1 uncoiling.According to the needs of physical size, through the limit portion of bead cutter 2 removal aluminium alloy strips; For the ease of continuous production, aluminium alloy strips is stitched together along the edge from beginning to end through sewing machine 3.
Preferably, in the production system of the aluminum alloy plate materials that the foregoing description provides, aluminium alloy strips is the speed according to the thickness setting of aluminium alloy strips through air cushion furnace annealed transfer rate; The annealing temperature of aluminium alloy strips is the temperature of alloy, state and thickness setting according to aluminium alloy strips.Set rational transmission speed, help improving the mechanical property and the production efficiency that improves aluminum alloy plate materials of aluminum alloy plate materials; The annealing temperature that the aluminum alloy plate materials of different thickness needs is different; Simultaneously; The pressure of air cushion is also confirmed according to the thickness of said aluminum alloy plate materials in the air cushion furnace 5; Select suitable cushion pressure; Avoid causing the aluminum alloy plate materials unfairness in air cushion furnace 5 because of the excessive aluminum alloy plate materials of cushion pressure trembles, also avoid because of the too small aluminum alloy plate materials of cushion pressure because of the stressed levitation position that causes inadequately is lower, cause scuffing.
To the above-mentioned explanation of the disclosed embodiments, make this area professional and technical personnel can realize or use the present invention.Multiple modification to these embodiment will be conspicuous concerning those skilled in the art, and defined General Principle can realize under the situation that does not break away from the spirit or scope of the present invention in other embodiments among this paper.Therefore, the present invention will can not be restricted to these embodiment shown in this paper, but will meet and principle disclosed herein and features of novelty the wideest corresponding to scope.
Claims (10)
1. the working method of an aluminum alloy plate materials is characterized in that, comprising:
1) adopts Abrollhaspel to the aluminum alloy plate materials uncoiling, obtain aluminium alloy strips;
2) said aluminium alloy strips being carried out the first time cleans;
3) said aluminium alloy strips passes through air cushion furnace with the speed of setting, and in air cushion furnace, carries out continuous annealing, the annealing temperature of the Heating Zone Temperature of said air cushion furnace for setting, the cooling temperature of the heat preservation zone temperature of said air cushion furnace for setting;
4) the said aluminium alloy strips to annealed processing carries out the cleaning second time;
5) through stretching straightener the said aluminium alloy strips through cleaning is for the second time carried out tension leveling;
6) batch said aluminium alloy strips through reeling machine, obtain the duraluminum coiled material;
7) in transverse cutting machine row, said duraluminum coiled material is carried out cutting to length, obtain the aluminum alloy plate materials finished product.
2. the working method of aluminum alloy plate materials according to claim 1 is characterized in that, said step 2) be specially and adopt the mode of spray equipment spraying water to clean said aluminium alloy strips.
3. the working method of aluminum alloy plate materials according to claim 1 is characterized in that, said step 4) is specially and adopts the mode that adopts brush roll to scrub after the shower nozzle spray water to clean said aluminium alloy strips earlier.
4. according to the working method of claim 2 or 3 described aluminum alloy plate materials, it is characterized in that the temperature of said water is between 40-80 ℃.
5. the working method of aluminum alloy plate materials according to claim 1 is characterized in that, said step 1) and said step 2) between also comprise:
11) said aluminium alloy strips is cut edge, make the width of said aluminium alloy strips reach the size of setting;
12) some said aluminium alloy strips of annealed of treating are sewed up successively from beginning to end.
6. the working method of aluminum alloy plate materials according to claim 1 is characterized in that, the speed of setting described in the said step 3) is according to the thickness setting of said aluminium alloy strips; Annealing temperature is according to alloy, state and the thickness setting of said aluminium alloy strips, and said cooling temperature is a normal temperature.
7. the production system of an aluminum alloy plate materials is characterized in that, comprising:
The uncoiling aluminum alloy plate materials obtains the Abrollhaspel of aluminium alloy strips;
Clean first washing unit of said aluminium alloy strips;
To the said aluminium alloy strips annealed air cushion furnace that cleans through first washing unit;
Clean second washing unit of annealed said aluminium alloy strips;
Stretching straightener to the said aluminium alloy strips tension leveling of cleaning through second washing unit;
Said aluminium alloy strips is batched the reeling machine into the duraluminum coiled material;
Cutting to length through said reeling machine roll up the transverse cutting machine row of said duraluminum coiled material;
Be provided with transport unit between the device of said adjacent operation;
Said air cushion furnace comprises the heater block and the heat preservation component of alloy, state and thickness setting temperature according to said aluminium alloy strips.
8. the production equipment of aluminum alloy plate materials according to claim 7 is characterized in that, said first washing unit is a spray equipment, is positioned at the top and the bottom of said aluminium alloy strips; Said second washing unit comprises some groups of nozzles and brush roll, is positioned at the top and the bottom of said aluminium alloy strips.
9. the production equipment of aluminum alloy plate materials according to claim 7 is characterized in that, also comprises the bead cutter and the sewing machine of sewing up said aluminium alloy strips through side cut after of cutting through the said aluminum alloy strip edge portion of said Abrollhaspel uncoiling.
10. according to the production equipment of any described aluminum alloy plate materials among the claim 7-9, it is characterized in that said aluminium alloy strips is the speed according to the thickness setting of said aluminium alloy strips through said air cushion furnace annealed transmission speed; The annealing temperature of said aluminium alloy strips is the temperature of alloy, state and thickness setting according to said aluminium alloy strips.