CN102397904A - Beam aluminum profile production process - Google Patents
Beam aluminum profile production process Download PDFInfo
- Publication number
- CN102397904A CN102397904A CN2010102763837A CN201010276383A CN102397904A CN 102397904 A CN102397904 A CN 102397904A CN 2010102763837 A CN2010102763837 A CN 2010102763837A CN 201010276383 A CN201010276383 A CN 201010276383A CN 102397904 A CN102397904 A CN 102397904A
- Authority
- CN
- China
- Prior art keywords
- section bar
- production technology
- hours
- carry out
- actual effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a beam aluminum profile production process. The process comprises the following process steps: 1, heating an extrusion mold and an aluminum rod to a temperature of 480-500 DEG C, wherein the material of the aluminum rod is A6060; 2, placing the heated aluminum rod in the extrusion mold, adopting an extruder to carry out extruding and forming, wherein the extrusion speed is controlled to 20-22 m per minute; 3, cooling the extruded work piece to the room temperature, then carrying out a straightening treatment; 4, carrying out a heat preservation treatment for the straightened work piece for 3.5-4.5 hours at the temperature of 195-205 DEG C to carry out an actual effect treatment. With adopting the beam aluminum profile production process of the present invention to produce the beam aluminum profile, the produced product has characteristics of good quality, high qualification rate and low production cost, and the economic benefits of the enterprise are effectively improved.
Description
Technical field
The present invention relates to a kind of crossbeam aluminium section bar production technology, belong to shape extruding manufacture technology field.
Background technology
At present, be more and more widely in the use of commercial production and daily life medium section, particularly shape (for example aluminium section bar), for example door-window section bar, shaped material of radiator and frame section bar etc. all adopt aluminium alloy extrusions mostly.Along with the progressively increase of section bar use amount, people have higher requirement to the structure and the quality of section bar, in order to produce the section bar of different structure and different qualities, must adopt pointed production technology to produce corresponding section bar.
Summary of the invention
The purpose of this invention is to provide a kind of crossbeam aluminium section bar production technology.
For realizing above-mentioned purpose, the invention provides following technical scheme: a kind of crossbeam aluminium section bar production technology comprises following processing step:
At first, be that the aluminium bar of A6060 is heated between 480 ℃-500 ℃ with extrusion die and material;
Then, the aluminium bar after the heating is positioned in the extrusion die, adopts extruder to carry out extrusion modling, extrusion speed is controlled between the per minute 20m-22m;
Afterwards, with carrying out straightening processing behind the work-piece cools that squeezes out to the normal temperature;
The workpiece that subsequently, will pass through straightening processing is incubated 3.5 hours-4.5 hours and handles to carry out actual effect under 195 ℃-205 ℃ environment.
Said actual effect treatment temperature is 200 ℃.
The time that said actual effect is handled is 4 hours.
Adopt blower fan to force cooling during the said work-piece cools that squeezes out.
Adopt crossbeam aluminium section bar production technology of the present invention to carry out the production of crossbeam aluminium section bar, the quality better of its product, qualification rate are high, production cost is lower, effectively raise economic benefit of enterprises.
The specific embodiment
The invention discloses a kind of crossbeam aluminium section bar production technology, it specifically comprises following processing step:
At first, be that the aluminium bar of A6060 (A6060 is aluminium commonly used, and the technical staff in the industry all knows this aluminium, therefore its constituent is not given unnecessary details here) is heated between 480 ℃-500 ℃ with extrusion die and material;
Then, the aluminium bar after the heating is positioned in the extrusion die, adopts extruder to carry out extrusion modling, extruder adopts the 800T extruder, and extrusion speed is controlled between the per minute 20m-22m, adopts flow quantity control instrument to control extrusion speed;
Afterwards; With carrying out straightening processing behind the work-piece cools that squeezes out to the normal temperature; Adopt blower fan to force cooling to the mode of the workpiece blowing that squeezes out during cooling, when straightening processing, adopt seven-roll Abramsen machine to carry out tension straingtening, wherein tractive force is between 1 to 150 ton;
The workpiece that subsequently, will pass through straightening processing is incubated 3.5 hours-4.5 hours and handles to carry out actual effect under 195 ℃-205 ℃ environment.The actual effect treatment temperature is preferably 200 ℃ in the present embodiment, and the preferred time that actual effect is handled is 4 hours.After actual effect was handled, the case hardness of aluminium section bar reached webster hardness 8HW-13HW.
What should explain at last is: the above is merely the preferred embodiments of the present invention; Be not limited to the present invention; Although the present invention has been carried out detailed explanation with reference to previous embodiment; For a person skilled in the art, it still can be made amendment to the technical scheme that aforementioned each embodiment put down in writing, and perhaps part technical characterictic wherein is equal to replacement.All within spirit of the present invention and principle, any modification of being done, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (4)
1. crossbeam aluminium section bar production technology is characterized in that: comprise following processing step:
At first, be that the aluminium bar of A6060 is heated between 480 ℃-500 ℃ with extrusion die and material;
Then, the aluminium bar after the heating is positioned in the extrusion die, adopts extruder to carry out extrusion modling, extrusion speed is controlled between the per minute 20m-22m;
Afterwards, with carrying out straightening processing behind the work-piece cools that squeezes out to the normal temperature;
The workpiece that subsequently, will pass through straightening processing is incubated 3.5 hours-4.5 hours and handles to carry out actual effect under 195 ℃-205 ℃ environment.
2. crossbeam aluminium section bar production technology according to claim 1 is characterized in that: said actual effect treatment temperature is 200 ℃.
3. crossbeam aluminium section bar production technology according to claim 1 and 2 is characterized in that: the time that said actual effect is handled is 4 hours.
4. crossbeam aluminium section bar production technology according to claim 3 is characterized in that: adopt blower fan to force cooling during the said work-piece cools that squeezes out.