CN102390101A - Embossed test roller silica gel proofing method - Google Patents
Embossed test roller silica gel proofing method Download PDFInfo
- Publication number
- CN102390101A CN102390101A CN2011102494515A CN201110249451A CN102390101A CN 102390101 A CN102390101 A CN 102390101A CN 2011102494515 A CN2011102494515 A CN 2011102494515A CN 201110249451 A CN201110249451 A CN 201110249451A CN 102390101 A CN102390101 A CN 102390101A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- roller
- frame
- examination
- bubble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of embossed test roller proofing, in particular to an embossed test roller silica gel proofing method, which is characterized by adopting the following process steps of test roller cleaning, surrounding frame manufacture, silica gel preparation, bubble removal, molding, curing and sampling. Compared with the prior art, the method has the advantages that the energy is saved, the environment is protected, safety and nontoxicity are realized, in addition, the method is simple, the material loss is small, simultaneously, the curing effect of the prepared silica gel is good, and the sampled samples are flat and do not have bubbles.
Description
Technical field
The present invention relates to the embossing examination roller technical field of drawing a design, specifically a kind of embossing examination roller silica gel proofing method.
Background technology
It generally is to adopt PVC heating roll-in method that tradition embossing examination roller is drawn a design, and its shortcoming has the PVC heating and decomposition to go out toxic gas, and power consumption is big, and material loss is big etc., not enough energy-conserving and environment-protective.
Summary of the invention
The object of the invention is the deficiency that overcomes prior art, adopts the silica gel proofing method of energy-conserving and environment-protective, has solved the generation toxic gas that traditional proofing method brings, the problem that power consumption is big, material loss is big.
In order to achieve the above object, the present invention has designed a kind of embossing examination roller silica gel proofing method, it is characterized in that adopting following processing step:
(A) cleaning examination roller: cleaning is tried the roller roll surface, removes the dirt oil stain of roll surface;
(B) frame is enclosed in making: will try the roller location, will try the roller location, and try roller frame all around, enclosing frame is d=1～2cm with the gap of trying roller, and the height that encloses frame is a little more than the examination roller;
(C) preparation silica gel and Pai Pao: preparation demoulding silica gel, put into the vacuum machine then and vacuumize and drained bubble 2～3 minutes, thereby obtain the demoulding silica gel of liquid;
(D) moulding: between the gap of enclosing frame and examination roller, slowly topple over the demoulding silica gel liquid of the intact bubble of above-mentioned row in the frame of being shortlisted for, avoid toppling over excessive velocities and produce bubble, till covering whole examination roller;
(E) solidify: the examination roller behind the above-mentioned moulding is positioned over smooth place, and room temperature waited for quietly 1～2 hour, was not clamminess promptly to accomplish and draws a design in examination roller surface;
(F) sampling.
Demoulding silica gel in the described step (C) is formulated after adopting following raw materials by weight percent to stir:
Silicon oil 10%;
Silica gel 87～89%.
Row's bubble in the described step (C) can also adopt pressure cylinder row bubble 2～3 minutes.
The present invention compares with prior art, energy-conserving and environment-protective, safety non-toxic, and method is simple, and material loss is little; The silica gel solidification effect of preparation is good simultaneously, the smooth no bubble of taking a sample.
Description of drawings
Fig. 1 is for enclosing the structural representation of frame in the utility model step (C).
Wherein, 1 is the examination roller; 2 for enclosing frame.
The specific embodiment
Combine embodiment that the present invention is further specified at present.
Embodiment one:
Present embodiment adopts following processing step:
(A) cleaning examination roller: cleaning is tried the roller roll surface, removes the dirt oil stain of roll surface;
(B) frame is enclosed in making: will try the roller location, as shown in Figure 1 trying roller frame all around, enclosing frame 2 is d=2cm with the gap of trying roller 1, and the height that encloses frame 2 is a little more than trying roller 1;
(C) preparation silica gel and Pai Pao: preparation demoulding silica gel, put into the vacuum machine then and vacuumize and drained bubble 2 minutes, thereby obtain the demoulding silica gel of liquid;
(D) moulding: between the gap of enclosing frame 2 and examination roller 1, slowly topple over the demoulding silica gel liquid of the intact bubble of above-mentioned row in the frame 2 of being shortlisted for, avoid toppling over excessive velocities and produce bubble, till covering whole examination roller;
(E) solidify: the examination roller behind the above-mentioned moulding is positioned over smooth place, and room temperature waited for quietly 1～2 hour, was not clamminess promptly to accomplish and draws a design in examination roller surface;
(F) sampling.
Wherein, the demoulding silica gel in the step (C) is formulated after adopting following raw materials by weight percent to stir:
Curing agent 3%;
Silicon oil 10%;
Silica gel 87%.
Embodiment two:
Present embodiment adopts following processing step:
(A) cleaning examination roller: cleaning is tried the roller roll surface, removes the dirt oil stain of roll surface;
(B) frame is enclosed in making: will try the roller location, as shown in Figure 1 trying roller frame all around, enclosing frame 2 is d=1cm with the gap of trying roller 1, and the height that encloses frame 2 is a little more than trying roller 1;
(C) preparation silica gel and Pai Pao: preparation demoulding silica gel, put into pressure cylinder row bubble then 3 minutes, thereby obtain the demoulding silica gel of liquid;
(D) moulding: between the gap of enclosing frame 2 and examination roller 1, slowly topple over the demoulding silica gel liquid of the intact bubble of above-mentioned row in the frame 2 of being shortlisted for, avoid toppling over excessive velocities and produce bubble, till covering whole examination roller;
(E) solidify: the examination roller behind the above-mentioned moulding is positioned over smooth place, and room temperature waited for quietly 5～7 hours, was not clamminess promptly to accomplish and draws a design in examination roller surface;
(F) sampling.
Wherein, the demoulding silica gel in the step (C) is formulated after adopting following raw materials by weight percent to stir:
Silicon oil 10%;
Silica gel 89%.
By finding out that the preparation composition of demoulding silica gel can determine to try the speed of roller curing rate among above-mentioned two embodiment, curing agent content can be solidified more for a long time fast in the demoulding silica gel, otherwise then curing rate is slow.
Energy-conserving and environment-protective of the present invention, safety non-toxic, and method is simple, and material loss is little; The silica gel solidification effect of preparation is good simultaneously, the smooth no bubble of taking a sample.
Claims (3)
1. an embossing tries roller silica gel proofing method, it is characterized in that adopting following processing step:
(A) cleaning examination roller: cleaning is tried the roller roll surface, removes the dirt oil stain of roll surface;
(B) frame is enclosed in making: will try the roller location, and try roller frame all around, enclosing frame is d=1～2cm with the gap of trying roller, and the height that encloses frame is a little more than trying roller;
(C) preparation silica gel and Pai Pao: preparation demoulding silica gel, put into the vacuum machine then and vacuumize and drained bubble 2～3 minutes, thereby obtain the demoulding silica gel of liquid;
(D) moulding: between the gap of frame and examination roller, slowly topple over the demoulding silica gel liquid of the intact bubble of above-mentioned row in the frame of being shortlisted for, avoid toppling over excessive velocities and produce bubble, till covering whole examination roller;
(E) solidify: the examination roller behind the above-mentioned moulding is positioned over smooth place, and room temperature waited for quietly 1～7 hour, was not clamminess promptly to accomplish and draws a design in examination roller surface;
(F) sampling.
2. a kind of embossing examination roller silica gel proofing method according to claim 1, it is characterized in that: the demoulding silica gel in the described step (C) is formulated after adopting following raw materials by weight percent to stir:
Curing agent 1～3%;
Silicon oil 10%;
Silica gel 87～89%.
3. a kind of embossing examination roller silica gel proofing method according to claim 1, it is characterized in that: the row's bubble in the described step (C) can also adopt pressure cylinder row bubble 2～3 minutes.