CN102381869A - 整体浇注的高炉热风管道 - Google Patents
整体浇注的高炉热风管道 Download PDFInfo
- Publication number
- CN102381869A CN102381869A CN2011102068537A CN201110206853A CN102381869A CN 102381869 A CN102381869 A CN 102381869A CN 2011102068537 A CN2011102068537 A CN 2011102068537A CN 201110206853 A CN201110206853 A CN 201110206853A CN 102381869 A CN102381869 A CN 102381869A
- Authority
- CN
- China
- Prior art keywords
- granularity
- parts
- water
- aggregate
- alumina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种整体浇注的高炉热风管道,管道外层为钢壳,钢壳内设有轻质耐火材料浇注的隔热层,隔热层内设有重质耐火材料浇注的耐火层,所述轻质耐火材料由以下重量份数的原料制成:粒度为5-0mm的高铝轻质骨料50-80、粒度为120-200目的粘土粉5-10、高铝水泥5-15、水10-20,所述高铝轻质骨料的Al2O3含量在70%以上;所述重质耐火材料由以下重量份数的原料制成:粒度为10-0mm的刚玉莫来石50-80、粒度为5μm以下的α-Al2O3微粉5-20、纯铝酸钠钙水泥3-10、水3-8。本发明将耐火材料与钢壳一体化浇注,轻质耐火材料耐1000-1200℃的高温,重质耐火材料耐1300-1500℃的高温,用法兰连接安装即可,整体结构稳定,密封好,施工简单,费用低。
Description
技术领域
本发明涉及一种高炉热风管道,具体涉及一种整体浇注的高炉热风管道。
背景技术
从热风炉出来的热风,经热风总管,热风围管和风口装置送入高炉,要求风口及管道密封性好,不漏风,耐高温,隔热耐用,易卸装。目前普遍采用的方法是在金属外壳内衬纤维棉,砌耐火砖,整体结构稳定性差,密封不好,容易局部产生裂缝,施工难度大。特别是管道连接处鹅颈管、弯管等部位形状复杂,最难砌筑。
发明内容
本发明要解决的技术问题是高炉热风管道使用耐火砖砌筑,整体结构稳定性差,密封不好,提供一种整体浇注的高炉热风管道。
本发明的技术方案是:整体浇注的高炉热风管道,管道外层为钢壳,钢壳内设有轻质耐火材料浇注的隔热层,隔热层内设有重质耐火材料浇注的耐火层,
所述轻质耐火材料由以下重量份数的原料制成:
粒度为5-0 mm的高铝轻质骨料 50-80
粒度为120-200目的粘土粉 5-10
高铝水泥 5-15
水 10-20
所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下重量份数的原料制成:
粒度为10-0 mm的刚玉莫来石 50-80
粒度为5 μm以下的α-Al2O3微粉 5-20
纯铝酸钠钙水泥 3-10
水 3-8。
整体浇注的高炉热风管道,所述轻质耐火材料优选由以下重量份数的原料制成:
粒度为5-0 mm的高铝轻质骨料 60-70
粒度为120-200目的粘土粉 6-8
高铝水泥 8-12
水 12-18
所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料优选由以下重量份数的原料制成:
粒度为10-0 mm的刚玉莫来石 60-70
粒度为5 μm以下的α-Al2O3微粉 10-18
纯铝酸钠钙水泥 5-8
水 4-7。
整体浇注的高炉热风管道,所述轻质耐火材料最优由以下重量份数的原料制成:
粒度为5-0 mm的高铝轻质骨料 65
粒度为120-200目的粘土粉 7
高铝水泥 10
水 15
所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料最优由以下重量份数的原料制成:
粒度为10-0mm的刚玉莫来石 65
粒度为5 μm以下的α-Al2O3微粉 15
纯铝酸钠钙水泥 6
水 5。
本发明的有益效果是:本发明将耐火材料与钢壳一体化浇注,轻质耐火材料耐1000-1200 ℃的高温,重质耐火材料耐1300-1500 ℃的高温,用法兰连接安装即可,整体结构稳定,密封好,施工简单,费用低。
附图说明
图1是本发明示意图。
具体实施方式
实施例1
一种整体浇注的高炉热风管道,如图1所示,包括管道5,管道5外层为钢壳2,钢壳2内设有轻质耐火材料浇注的隔热层3,隔热层3内设有重质耐火材料浇注的耐火层4,钢壳内焊接有锚固钉1,锚固钉1穿过隔热层3与耐火层4相连。
所述轻质耐火材料由以下原料制成:
粒度为5-0 mm的高铝轻质骨料80 kg、粒度为120目的粘土粉10 kg、高铝水泥15 kg、水20 kg,所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下原料制成:粒度为10-0 mm的刚玉莫来石80 kg、粒度为5 μm以下的α-Al2O3微粉20 kg、纯铝酸钠钙水泥10 kg、水8 kg。
实施例2
整体浇注的高炉热风管道,结构如实施例1所示。
所述轻质耐火材料由以下原料制成:
粒度为5-0 mm的高铝轻质骨料50 kg、粒度为200目的粘土粉5 kg、高铝水泥5 kg、水10 kg,所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下原料制成:
粒度为10-0 mm的刚玉莫来石50 kg、粒度为5 μm以下的α-Al2O3微粉5 kg、纯铝酸钠钙水泥3 kg、水3 kg。
实施例3
整体浇注的高炉热风管道,结构如实施例1所示。
所述轻质耐火材料由以下原料制成:
粒度为5-0 mm的高铝轻质骨料70 kg、粒度为140目的粘土粉8 kg、高铝水泥12 kg、水18 kg,所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下原料制成:
粒度为10-0 mm的刚玉莫来石70 kg、粒度为5 μm以下的α-Al2O3微粉18 kg、纯铝酸钠钙水泥8 kg、水7 kg。
实施例4
整体浇注的高炉热风管道,结构如实施例1所示。
所述轻质耐火材料由以下原料制成:
粒度为5-0 mm的高铝轻质骨料60 kg、粒度为160目的粘土粉6 kg、高铝水泥8 kg、水12 kg,所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下原料制成:
粒度为10-0 mm的刚玉莫来石60 kg、粒度为5 μm以下的α-Al2O3微粉10 kg、纯铝酸钠钙水泥5 kg、水4 kg。
实施例5
整体浇注的高炉热风管道,结构如实施例1所示。
所述轻质耐火材料由以下原料制成:
粒度为5-0 mm的高铝轻质骨料65 kg、粒度为120-200目的粘土粉7 kg、高铝水泥10 kg、水15 kg。所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下原料制成:
粒度为10-0 mm的刚玉莫来石65 kg、粒度为5 μm以下的α-Al2O3微粉15 kg、纯铝酸钠钙水泥6 kg、水5 kg。
Claims (3)
1.整体浇注的高炉热风管道,管道外层为钢壳,钢壳内设有轻质耐火材料浇注的隔热层,隔热层内设有重质耐火材料浇注的耐火层,其特征在于:
所述轻质耐火材料由以下重量份数的原料制成:
粒度为5-0 mm的高铝轻质骨料 50-80
粒度为120-200目的粘土粉 5-10
高铝水泥 5-15
水 10-20
所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下重量份数的原料制成:
粒度为10-0 mm的刚玉莫来石 50-80
粒度为5 μm以下的α-Al2O3微粉 5-20
纯铝酸钠钙水泥 3-10
水 3-8。
2.根据权利要求1所述的整体浇注的高炉热风管道,其特征在于:
所述轻质耐火材料由以下重量份数的原料制成:
粒度为5-0 mm的高铝轻质骨料 60-70
粒度为120-200目的粘土粉 6-8
高铝水泥 8-12
水 12-18
所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下重量份数的原料制成:
粒度为10-0 mm的刚玉莫来石 60-70
粒度为5 μm以下的α-Al2O3微粉 10-18
纯铝酸钠钙水泥 5-8
水 4-7。
3.根据权利要求2所述的整体浇注的高炉热风管道,其特征在于:
所述轻质耐火材料由以下重量份数的原料制成:
粒度为5-0 mm的高铝轻质骨料 65
粒度为120-200目的粘土粉 7
高铝水泥 10
水 15
所述高铝轻质骨料的Al2O3含量在70%以上;
所述重质耐火材料由以下重量份数的原料制成:
粒度为10-0 mm的刚玉莫来石 65
粒度为5 μm以下的α-Al2O3微粉 15
纯铝酸钠钙水泥 6
水 5。