CN102417357A - 铁水包用叶蜡石-碳化硅碳砖及其制备方法 - Google Patents

铁水包用叶蜡石-碳化硅碳砖及其制备方法 Download PDF

Info

Publication number
CN102417357A
CN102417357A CN2011102069807A CN201110206980A CN102417357A CN 102417357 A CN102417357 A CN 102417357A CN 2011102069807 A CN2011102069807 A CN 2011102069807A CN 201110206980 A CN201110206980 A CN 201110206980A CN 102417357 A CN102417357 A CN 102417357A
Authority
CN
China
Prior art keywords
pyrophyllite
granularity
silit
parts
carbon brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102069807A
Other languages
English (en)
Inventor
辛英杰
张松善
钱长见
董寿勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd
Original Assignee
ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd filed Critical ZHENGZHOU JINGHUA REFRACTORY INDUSTRIAL Co Ltd
Priority to CN2011102069807A priority Critical patent/CN102417357A/zh
Publication of CN102417357A publication Critical patent/CN102417357A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铁水包用叶蜡石-碳化硅碳砖，它是由以下重量份数的原料制成：粒度为5-0mm的叶蜡石30-60、粒度为120-180目的叶蜡石粉20-30、粒度为120-320目的碳化硅10-20、-199#石墨5-15、酚醛树脂5-10。本发明以叶蜡石和碳化硅为主要原料，生产出不烧的铁水包内衬砖，耐1500℃以上的高温，具有整体性好，砖缝好，热稳定性好，抗铁水冲刷能力强，在120T以上的铁水包，使用寿命在800次以上，且由于叶蜡石价廉物美，整个产品的造价低，经济效益好，吨铁耐材消耗少。

Description

铁水包用叶蜡石-碳化硅碳砖及其制备方法
技术领域
本发明涉及一种铁水包用内衬转，具体一种涉及叶蜡石-碳化硅碳砖及其制备方法。 
背景技术
铁水包内衬砖要求较高，一般使用碳化硅碳砖，碳化硅碳砖不仅需要烧结，并且成本高。 
发明内容
本发明要解决的技术问题是碳化硅碳砖不仅需要烧结，并且成本高，提供一种叶蜡石-碳化硅碳砖及其制备方法。 
本发明的技术方案是：一种铁水包用叶蜡石-碳化硅碳砖，它是由以下重量份数的原料制成： 
粒度为5-0 mm的叶蜡石             30-60
粒度为120-180目的叶蜡石粉         20-30
粒度为120-320目的碳化硅           10-20
-199#石墨                          5-15
酚醛树脂                           5-10。
铁水包用叶蜡石-碳化硅碳砖，它优选由以下重量份数的原料制成： 
粒度为5-0 mm的叶蜡石             40-50
粒度为120-180目的叶蜡石粉         22-28
粒度为120-320目的碳化硅           12-18
-199#石墨                          8-12
酚醛树脂                           6-8。
铁水包用叶蜡石-碳化硅碳砖，它最优由以下重量份数的原料制成： 
粒度为5-0 mm的叶蜡石             45
粒度为120-180目的叶蜡石粉         25
粒度为120-320目的碳化硅           15
-199#石墨                          10
酚醛树脂                           7。
铁水包用叶蜡石-碳化硅碳砖的制备方法：将原料混合后，在230-270 ℃的条件下烘干24-28小时。 
本发明的有益效果是：本发明以叶蜡石和碳化硅为主要原料，生产出不烧的铁水包内衬砖，耐1500℃以上的高温，具有整体性好，砖缝好，热稳定性好，抗铁水冲刷能力强，在120T以上的铁水包，使用寿命在800次以上，且由于叶蜡石价廉物美，整个产品的造价低，经济效益好，吨铁耐材消耗少。 
具体实施方式
实施例1 
一种铁水包用叶蜡石-碳化硅碳砖，它是由以下原料制成：粒度为5-0 mm的叶蜡石60 kg、粒度为120目的叶蜡石粉30 kg、粒度为120目的碳化硅20 kg、-199#石墨15 kg、酚醛树脂10 kg。
铁水包用叶蜡石-碳化硅碳砖的制备方法：将原料混合后，在230 ℃的条件下烘干28小时。 
实施例2 
一种铁水包用叶蜡石-碳化硅碳砖，它是由以下原料制成：粒度为5-0 mm的叶蜡石30 kg、粒度为140目的叶蜡石粉20 kg、粒度为320目的碳化硅10 kg、-199#石墨5 kg、酚醛树脂5 kg。
铁水包用叶蜡石-碳化硅碳砖的制备方法：将原料混合后，在250 ℃的条件下烘干25小时。 
实施例3 
铁水包用叶蜡石-碳化硅碳砖，它是由以下原料制成：
粒度为5-0 mm的叶蜡石50 kg、粒度为140目的叶蜡石粉28 kg、粒度为220目的碳化硅18 kg、-199#石墨12 kg、酚醛树脂8 kg。
铁水包用叶蜡石-碳化硅碳砖的制备方法：将原料混合后，在260 ℃的条件下烘干26小时。 
实施例4 
铁水包用叶蜡石-碳化硅碳砖，它是由以下原料制成：
粒度为5-0 mm的叶蜡石40 kg、粒度为160目的叶蜡石粉22 kg、粒度为180目的碳化硅12 kg、-199#石墨8 kg、酚醛树脂6 kg。
铁水包用叶蜡石-碳化硅碳砖的制备方法：将原料混合后，在260 ℃的条件下烘干28小时。 
实施例5 
铁水包用叶蜡石-碳化硅碳砖，它是由以下重量份数的原料制成：粒度为5-0 mm的叶蜡石45 kg、粒度为120-180目的叶蜡石粉25 kg、粒度为120-320目的碳化硅15 kg、-199#石墨10 kg、酚醛树脂7 kg。
铁水包用叶蜡石-碳化硅碳砖的制备方法：将原料混合后，在230-270 ℃的条件下烘干24-28小时。 

Claims (4)

1.一种铁水包用叶蜡石-碳化硅碳砖，其特征在于，它是由以下重量份数的原料制成：
粒度为5-0 mm的叶蜡石             30-60
粒度为120-180目的叶蜡石粉         20-30
粒度为120-320目的碳化硅           10-20
-199#石墨                          5-15
酚醛树脂                           5-10。
2.根据权利要求1所述的铁水包用叶蜡石-碳化硅碳砖，其特征在于，它是由以下重量份数的原料制成：
粒度为5-0 mm的叶蜡石             40-50
粒度为120-180目的叶蜡石粉         22-28
粒度为120-320目的碳化硅           12-18
-199#石墨                          8-12
酚醛树脂                           6-8。
3.根据权利要求2所述的铁水包用叶蜡石-碳化硅碳砖，其特征在于，它是由以下重量份数的原料制成：
粒度为5-0 mm的叶蜡石             45
粒度为120-180目的叶蜡石粉         25
粒度为120-320目的碳化硅           15
-199#石墨                          10
酚醛树脂                           7。
4.如权利要求1或2或3所述的铁水包用叶蜡石-碳化硅碳砖的制备方法，其特征在于：将原料混合后，在230-270 ℃的条件下烘干24-28小时。
CN2011102069807A 2011-07-22 2011-07-22 铁水包用叶蜡石-碳化硅碳砖及其制备方法 Pending CN102417357A (zh)