CN102381867A - 一种废玻璃制备透水性陶瓷砖的方法 - Google Patents

一种废玻璃制备透水性陶瓷砖的方法 Download PDF

Info

Publication number
CN102381867A
CN102381867A CN2010102741927A CN201010274192A CN102381867A CN 102381867 A CN102381867 A CN 102381867A CN 2010102741927 A CN2010102741927 A CN 2010102741927A CN 201010274192 A CN201010274192 A CN 201010274192A CN 102381867 A CN102381867 A CN 102381867A
Authority
CN
China
Prior art keywords
ceramic tile
cullet
water
temperature
permeable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010102741927A
Other languages
English (en)
Inventor
秦继民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2010102741927A priority Critical patent/CN102381867A/zh
Publication of CN102381867A publication Critical patent/CN102381867A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种陶瓷砖，具体涉及一种废玻璃制备透水性陶瓷砖的方法，属建筑材料加工技术领域。该制备方法利用陶瓷废料，废玻璃和粘土作为主要原料制透水性陶瓷砖，可以使目前日益增加的工业废渣得以利用，从而相应减轻环境负荷，另一方面具有对环境的美化装饰效果，能使雨水或城市用水迅速渗透于地下，从而起到了调节城市气候，减少城市水资源无辜流失。

Description

一种废玻璃制备透水性陶瓷砖的方法
技术领域
本发明涉及一种陶瓷砖，具体涉及一种废玻璃制备透水性陶瓷砖的方法，属建筑材料加工技术领域。
背景技术
随着建筑业的发展，人民生活水平的不断提高，对于陶瓷装饰材料的需求量也越来越大。建筑陶瓷厂如雨后春笋般在各地建设，规模越上越大，产品质量由低到高，花色品种由少到多。竞争日趋激烈，各厂都在想方设法，降低成本，提高竞争力，而其中一条有效途径便是综合利用一些低品位的原料及工业废渣来充当原料制砖，目前还在研制阶段，不能满足市场的需求。
发明内容
本发明的目的是为克服上述现有技术的不足之处，提供一种废玻璃制备透水性陶瓷砖的方法，利用陶瓷废料，废玻璃和粘土作为主要原料制透水性陶瓷砖，可以使目前日益增加的工业废渣得以利用，从而相应减轻环境负荷，另一方面具有对环境的美化装饰效果，能使雨水或城市用水迅速渗透于地下，从而起到了调节城市气候，减少城市水资源无辜流失。
本发明是以如下技术方案实现的：一种废玻璃制备透水性陶瓷砖的方法，其特征是：该方法以废玻璃、陶瓷废料和粘土作为主要原料，加入适量滑石粉，经碾压、烧制得陶瓷砖，所述的陶瓷砖最佳配方(重量份)为：陶瓷废料40-50份，废玻璃15-20份，粘土25-30份，滑石粉5-10份。
所述的制备透水性陶瓷砖的方法包括如下步骤：
(1)按配方分别称量原料，进行配料，用压力机压制配好的物料，制得的瓷砖尺寸为120mm×80mm×10mm；
(2)将步骤(1)的瓷砖放人干燥箱中，在120℃干燥2h，然后放入高温箱式电阻炉中烧制，温度为1000℃-1100℃，电炉的升温速度控制为80℃/h，并在烧成温度下保温1h，待炉温降至室温后取出，即得成品。
本发明的优点是：该制备方法利用陶瓷废料，废玻璃和粘土作为主要原料制透水性陶瓷砖，可以使目前日益增加的工业废渣得以利用，从而相应减轻环境负荷，另一方面具有对环境的美化装饰效果，能使雨水或城市用水迅速渗透于地下，从而起到了调节城市气候，减少城市水资源无辜流失。
具体实施方式
实施例、
该方法以废玻璃、陶瓷废料和粘土作为主要原料，加入适量滑石粉，经碾压、烧制得陶瓷砖，所述的陶瓷砖最佳配方(重量份)为：陶瓷废料45份，废玻璃20份，粘土25份，滑石粉5份。
所述的制备透水性陶瓷砖的方法包括如下步骤：
(1)按配方分别称量原料，进行配料，用压力机压制配好的物料，制得的瓷砖尺寸为120mm×80mm×10mm；
(2)将步骤(1)的瓷砖放人干燥箱中，在120℃干燥2h，然后放入高温箱式电阻炉中烧制，温度为1000℃，电炉的升温速度控制为80℃/h，并在烧成温度下保温1h，待炉温降至室温后取出，即得成品。

Claims (2)

1.一种废玻璃制备透水性陶瓷砖的方法，其特征是：该方法以废玻璃、陶瓷废料和粘土作为主要原料，加入适量滑石粉，经碾压、烧制得陶瓷砖，所述的陶瓷砖最佳配方(重量份)为：陶瓷废料40-50份，废玻璃15-20份，粘土25-30份，滑石粉5-10份。
2.根据权利要求1所述的一种废玻璃制备透水性陶瓷砖的方法，其特征是：所述的制备陶瓷砖的方法包括如下步骤：
(1)按配方分别称量原料，进行配料，用压力机压制配好的物料，制得的瓷砖尺寸为120mm×80mm×10mm；
(2)将步骤(1)的瓷砖放人干燥箱中，在120℃干燥2h，然后放入高温箱式电阻炉中烧制，温度为1000℃-1100℃，电炉的升温速度控制为80℃/h，并在烧成温度下保温1h，待炉温降至室温后取出，即得成品。
CN2010102741927A 2010-08-31 2010-08-31 一种废玻璃制备透水性陶瓷砖的方法 Pending CN102381867A (zh)