CN102372429A - 光学玻璃 - Google Patents
光学玻璃 Download PDFInfo
- Publication number
- CN102372429A CN102372429A CN2011102220498A CN201110222049A CN102372429A CN 102372429 A CN102372429 A CN 102372429A CN 2011102220498 A CN2011102220498 A CN 2011102220498A CN 201110222049 A CN201110222049 A CN 201110222049A CN 102372429 A CN102372429 A CN 102372429A
- Authority
- CN
- China
- Prior art keywords
- content
- glass
- preferred
- composition
- mgo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种光学玻璃,其以氧化物基准的质量%计,含有P2O5:30~50%、BaO:18~43%、B2O3:2~12%、Al2O3:1.4~5%、Li2O:大于0且为6%以下、La2O3:大于0且为9%以下、MgO:0.1~8%、CaO:0~10%、SrO:0~15%、ZnO:0~5%、Gd2O3:0~7%、SiO2:0~3%,且具有nd:1.59~1.63、vd:63~68的光学常数。
Description
技术领域
本发明涉及低折射率/低分散、可精密模压成形、且板材成形性、预成形体用料滴(ゴブ)成形性优良的磷酸盐类光学玻璃。
背景技术
低分散玻璃是对光学元件的像差校正有用的玻璃。就以数码相机为代表的摄像镜头而言,减少镜头枚数而使光学体系小型化的要求正在提高,因而大多使用精密模压成非球面形状的玻璃模制镜头。为校正像差,越低分散越优选。
为了实现低分散化,也有向玻璃中导入氟的方法,但由于玻璃熔化时有环境负荷的氟会挥发,因此存在如下问题:需要除去装置,或者由于氟挥发引起的组成偏差导致条纹的产生、因加入氟导致极端低软化而难以进行玻璃熔融物的成形等。
考虑以上情况和制造成本,优选氧化物玻璃。因此,正在致力于作为氧化物类玻璃且期待低分散化的磷酸-钡系玻璃的研究(专利文献1~4),从镜头的小型化的观点出发,在低分散的同时期望高折射率,但是尚不存在在规定的高折射率区域(nd≥1.59)具有充分的低分散性(vd≥63)、并且熔化稳定性、模压成形性和化学耐久性均优良的玻璃。
现有技术文献
专利文献
专利文献1:日本特公昭63-20775号公报
专利文献2:日本特开2005-8518号公报
专利文献3:日本特开2007-15904号公报
专利文献4:日本特开2006-111499号公报
发明内容
本发明的目的在于提供具有折射率(nd)为1.59以上且阿贝数(vd)为63以上的光学常数、玻璃的熔化稳定性优良、具有适于精密模压成形的软化温度和适合预成形体用料滴成形性的液相粘度、并且化学耐久性优良的光学玻璃。
本发明提供一种光学玻璃,其以氧化物基准的质量%计,含有P2O5:30~50%、BaO:18~43%、B2O3:2~12%、Al2O3:1.4~5%、Li2O:大于0且为6%以下、La2O3:大于0且为9%以下、MgO:0.1~8%、CaO:0~10%、SrO:0~15%、ZnO:0~5%、Gd2O3:0~7%、SiO2:0~3%,且具有nd:1.59~1.63、vd:63~68的光学常数。另外,在没有特殊说明时,上述化学组成的数值范围的下限值表示该值以上、上限值表示该值以下。另外,大于0是指作为必需成分含有。
发明效果
本发明的磷酸盐类的光学玻璃(以下称为本玻璃),由于以P2O5、BaO、B2O3、Al2O3、Li2O、La2O3、MgO作为必需成分,因此能够得到折射率nd:1.59~1.63、阿贝数vd:63~68的光学特性。另外,本玻璃由于含有La2O3、MgO和Li2O作为必需成分,因此还能够兼顾化学耐久性(主要取决于La2O3和MgO成分)和低分散性(主要取决于Li2O成分)。
根据本玻璃,除了上述特性之外,还能使玻璃化转变点(Tg)为优选的570℃以下,因此能够以良好的生产率进行精密模压成形。另外,本玻璃的液相温度粘度(ηLT)能够为优选的6dPa·s以上,因此也能够制造精细(フアイン)料滴。
具体实施方式
本发明是基于为了得到折射率(nd)为1.59以上、阿贝数(vd)为63以上、且化学耐久性优良的光学玻璃而进行的各种研究的结果而完成的。本玻璃的各成分范围的设定理由如下。需要说明的是,本说明书中,以下如果没有特殊说明,则%指质量%。另外,化学组成以氧化物基准计。
本玻璃中,P2O5是必需成分,是形成玻璃的主要成分(玻璃形成氧化物),并且是提高玻璃的粘性的成分。本玻璃中,P2O5含量过少时,存在玻璃变得不稳定且粘性降低的可能性,因此,本玻璃中P2O5含量为30%以上。优选P2O5含量为33%以上,更优选P2O5含量为35%以上。另一方面,P2O5含量过多时,折射率下降,因此,本玻璃中P2O5含量为50%以下。优选P2O5含量为48%以下,更优选P2O5含量为46%以下。
本玻璃中,BaO是必需成分,具有提高玻璃的折射率并且提高玻璃的稳定化和化学耐久性的效果。含量过少时,化学耐久性有可能变得不充分,因此将BaO含量设定为18%以上。优选BaO含量为20%以上,更优选BaO含量为21%以上,特别优选BaO含量为25%以上。另一方面,BaO含量过多时,分散性增大,难以实现低分散化,因此将BaO含量设定为43%以下。优选BaO含量为40%以下,更优选BaO含量为38%以下,特别优选BaO含量为30%以下。
本玻璃中,B2O3是必需成分,是对于提高玻璃的熔化性、稳定性和耐久性有效的成分。为了发挥效果,将B2O3含量设定为2%以上。优选B2O3含量为2.5%以上,更优选B2O3含量为5%以上,特别优选B2O3含量为6%以上。另一方面,含量过多时,玻璃有可能变得不稳定,因此将B2O3含量设定为12%以下。优选B2O3含量为11.5%以下,更优选B2O3含量为11%以下,特别优选B2O3含量为10%以下。
本玻璃中,Al2O3是必需成分,具有提高玻璃的化学耐久性的效果。含量过少时,化学耐久性的提高效果变得不充分,因此Al2O3含量为1.4%以上。优选Al2O3含量为1.7%以上,更优选Al2O3含量为2%以上。另一方面,Al2O3含量过多时,使玻璃不稳定,失透倾向增强。因此,Al2O3含量为5%以下。优选Al2O3含量为4.5%以下,更优选Al2O3含量为4%以下。
本玻璃中,Li2O是必需成分,是使玻璃软化的成分,并且对于提高化学耐久性有效。另外,对于低分散化有效。本玻璃中,Li2O含量过少时,粘性增高,玻璃化转变温度、屈服点上升,从而模压成形温度升高。另外,不能实现充分的低分散化。而且,化学耐久性的提高效果降低。因此,Li2O含量大于0。优选Li2O含量为0.1%以上,更优选Li2O含量为0.5%以上。
另一方面,Li2O含量过多时,玻璃变得不稳定,失透倾向增强。另外,液相温度粘度降低,因此料滴预成形体的制造变得困难。另外,化学耐久性降低。因此,Li2O含量为6%以下。优选Li2O含量为5.5%以下,更优选Li2O含量为5%以下。
本玻璃中,La2O3是必需成分,具有使玻璃高折射率化的效果,并且还具有形成玻璃、使化学耐久性提高的效果。另外,由于高粘性,因而也是适合为形成精细料滴而进行粘度调节的成分。因此,La2O3含量大于0。优选La2O3含量为0.5%以上,更优选La2O3含量为1%以上。另一方面,La2O3含量过多时,除了变得高分散之外,软化温度上升而成形性降低。因此,La2O3含量为9%以下。优选La2O3含量为7%以下,更优选La2O3含量为4%以下。
本玻璃中,MgO是必需成分,是对于提高玻璃的化学耐久性以及低分散化有效的成分。另外,通过含有MgO,玻璃化转变点、屈服点的温度降低,玻璃模制成形性也提高。因此,MgO含量为0.1%以上。优选MgO含量为0.2%以上,更优选MgO含量为0.4%以上。另一方面,过量地导入MgO时,失透倾向增大,玻璃变得不稳定。因此,MgO含量为8%以下。优选MgO含量为6%以下,更优选MgO含量为5%以下。
本玻璃中,CaO虽然不是必需成分,但是对提高化学耐久性有效的成分。在含有CaO时,优选CaO含量为0.5%以上,更优选CaO含量为1%以上。另一方面,过量导入CaO时,失透倾向增大,玻璃变得不稳定。因此,即使在含有CaO时,CaO含量也为10%以下。优选CaO含量为9%以下,更优选CaO含量为7%以下。
本玻璃中,SrO虽然不是必需成分,但是对提高玻璃的化学耐久性有效的成分。在含有SrO时,优选SrO含量为0.1%以上,更优选SrO含量为0.2%以上。另一方面,过量地导入SrO时,失透倾向增大,玻璃变得不稳定。因此,即使在含有SrO时,SrO含量也为15%以下。优选SrO含量为10%以下,更优选SrO含量为7%以下。
本玻璃中,ZnO虽然不是必需成分,但是对于提高玻璃的熔化性、稳定性和耐久性有效的成分。在含有ZnO时,优选ZnO含量为0.3%以上,更优选ZnO含量为0.7%以上。另一方面,过量地导入ZnO时,失透倾向增大,玻璃变得不稳定。因此,即使在含有ZnO时,ZnO含量也为5%以下。优选ZnO含量为4%以下,更优选ZnO含量为3%以下。
本玻璃中,Gd2O3虽然不是必需成分,但是有助于高折射率化的成分。在含有Gd2O3时,优选Gd2O3含量为0.5%以上,更优选Gd2O3含量为1%以上。另一方面,过量地导入Gd2O3时,失透倾向增大,玻璃变得不稳定。因此,即使在含有Gd2O3时,Gd2O3含量也为7%以下。优选Gd2O3含量为5%以下,更优选Gd2O3含量为3%以下。
本玻璃中,SiO2虽然不是必需成分,但是对玻璃的稳定化有效的成分。在含有SiO2时,优选SiO2含量为0.1%以上,更优选SiO2含量为0.3%以上。另一方面,过量地导入SiO2时,难以得到所期望的光学常数。因此,即使在含有SiO2时,SiO2含量也为3%以下。优选SiO2含量为2.5%以下,更优选SiO2含量为2%以下。
本玻璃中,上述成分总计为95%以上时,能取得各特性的平衡,因此优选。更优选上述成分总计为98%以上,特别优选本玻璃实质上由上述成分构成。需要说明的是,在本说明书中,“实质上由上述成分构成”是指“除了不可避免的杂质外,由上述成分构成”。
本玻璃中,Na2O、K2O、Y2O3、ZrO2、Nb2O5或Ta2O5各成分均不是必需成分,但可以单独添加或添加多种。由于含量少时几乎得不到光学特性的调整效果,因此作为含量,以各自单独的含量计,优选含量为0.1%以上,更优选上述含量为1.0%以上,特别优选上述含量为2%以上。
另一方面,上述各成分中,Na2O或K2O含量过多时折射率降低。因此,以各自单独的含量计,优选设定为5.0%以下,更优选设定为4.0%以下,特别优选设定为3.0%以下。同样,Y2O3、ZrO2、Nb2O5或Ta2O5各成分的含量过多时,玻璃变得不稳定,或者由于原料较为昂贵,因此从成本方面出发优选极力地降低这些成分的含量。因此,以各自单独的含量计,优选设定为5.0%以下,更优选设定为4.0%以下,特别优选设定为3.0%以下。
另外,本玻璃中,从成形温度的观点和对环境的影响等出发,优选实质上不含PbO、TeO2、F、As2O3。在本说明书中,实质上不含成分X,是指除了作为不可避免的杂质混入的之外,不主动地添加。其标准为含量约小于0.05%。
本玻璃中,Sb2O3虽然不是必需成分,但可以作为玻璃熔融时的澄清剂添加。作为其含量,优选为1%以下,更优选为0.5%以下,特别优选为0.1%以下。本玻璃中,作为添加Sb2O3时的下限,优选为0.01%以上,更优选为0.05%以上,进一步优选0.1%以上。
作为本玻璃的光学特性,折射率(nd)为1.59以上,阿贝数(vd)为63以上。另外,优选具有nd为1.59以上且分散vd为66以上的光学常数、或者具有nd为1.62以上且分散vd为63以上的光学常数的光学玻璃。
本玻璃的玻璃化转变点(Tg)为570℃以下、屈服点(At)为610℃以下时能够以良好的生产率模压成形,因此优选。
另外,为了生产精细料滴,优选本玻璃的液相温度粘度(ηLT)为6dPa·s以上。本玻璃的液相温度粘度更优选为6.5dPa·s以上,特别优选为7dPa·s以上。另外,在具有nd为1.62以上且分散vd为63以上的光学常数的玻璃的情况下,特别优选液相温度粘度(ηLT)为12dPa·s以上。
作为本玻璃的利用粉末法测得的耐水性(Dw),优选为0.3%以下,更优选Dw为0.2%以下。特别优选Dw为0.1%以下。同样,作为利用粉末法测得的耐酸性(Da),优选为3%以下,更优选Da为2.5%以下。特别优选Da为1.5%以下。
本玻璃的制造方法没有特别限制,例如可以如下制造:称量氧化物、氢氧化物、碳酸盐、硝酸盐、磷酸盐等通常的光学玻璃中使用的原料并将其混合,放入铂坩埚、金坩埚、石英坩埚、氧化铝坩埚等通常的光学玻璃所使用的坩埚中,在约1000℃~约1250℃下熔融、澄清、搅拌2~10小时后,在比液相温度(LT)高的温度下,浇注到预热至450~550℃的模具中,然后缓冷。
通过分别使用上述原料中以碳酸盐导入的氧化物例如Na2CO3、以硝酸盐导入的氧化物NaNO3,能够抑制分批熔化时原料的溅起、抑制喷溢,因此可以考虑原料成本、制造时发泡控制的容易度来适当选择。
作为使用本玻璃的预成形体用料滴成形方法,可以列举如下方法作为一例:使熔融玻璃从喷嘴前端流出,分离出所需质量的熔融玻璃块,在氮气中使其上浮到模具上的同时接受烧制,制造整面为火修光(火づくり)面的玻璃块。但是,上述成形方法并不限于此。
另外,将本玻璃成形为光学元件的方法没有特别的限制,作为例子可以列举如下方法等:将基于本玻璃的玻璃液相温度(LT)通过预成形体用料滴成形制成的预成形体设置到表面形成有保护膜的、高精度加工成的压制模具(模具材质例如为SiC质、碳化钨超硬材料等)内,以预定的压力、时间进行压制,从而得到所期望的形状;使玻璃熔融液流出而先制成板材,然后通过加工由该板材制成适合模压成形的玻璃块,从而得到加工预成形体,然后,将加工预成形体设置到压制模具内,之后进行模压成形。但是,上述方法并不限于这些。
实施例
下面说明本发明的实施例等。例1~例17为本发明的实施例。
[化学组成和试样制作方法]
按照表1至表3所示的化学组成(质量%)称量原料。另外,以摩尔%表示的表1至3的化学组成作为参考示于表4至6。作为各玻璃的原料,在P2O5的情况下,使用H3PO4、BPO4、Ba(PO3)2,在B2O3的情况下,使用H3BO3或BPO4,在BaO的情况下,使用BaCO3、Ba(NO3)2或Ba(PO3)2,在Li2O的情况下,使用Li2CO3或LiPO3,在SiO2、MgO、La2O3、ZnO的情况下,分别使用氧化物。
将称量好的原料混合,装入内容积约300cc的铂坩埚内,在约1250℃下熔融、澄清、搅拌1~1.5小时后,在1100℃下保持1小时,浇注到预热至约450℃~约550℃的长100mm×宽50mm的长方形铸模中,然后以约0.5℃/分钟的速度缓冷,从而制成样品。
[评价方法]
折射率(nd)是对于氦d线的折射率,通过折射率计(カルニユ一光学工业公司制,商品名:KRP-2000)测定。折射率的值测定到小数点后第5位。
阿贝数(vd)通过vd=(nd-1)/(nF-nC)计算,将小数点后第2位四舍五入而记载到小数点后第1位。其中,nF、nC分别为对于氢F线和C线的折射率。
关于玻璃化转变温度(Tg)和屈服点(At),将所得的各玻璃加工成棒状,利用热分析装置(ブルカ一·エイエツクスエス公司制,商品名:TMA4000SA)通过热膨胀法、以5℃/分钟的升温速度进行测定。
液相温度(LT)是指,向铂皿中加入玻璃试样约5g,分别在870℃至940℃以每5℃为间隔保持1小时后,通过自然冷却进行冷却,然后利用显微镜观察有无结晶析出,将没有观察到结晶的最低温度设定为液相温度。
关于透射率,使用分光光度计(パ一キンエルマ一公司制,商品名:Lambda950),对双面研磨至厚度为10mm的试样以每1nm的间隔进行测定。
关于液相温度粘度(ηLT),通过旋转圆筒法测定粘度,作为液相温度(LT)下的粘度。
关于玻璃的熔化性等,在制作上述样品时通过目视进行了观察,结果确认:熔化性没有问题,所得的玻璃样品中没有气泡、条纹。
关于比重(SG),将试样的重量与压力101.325kPa(标准气压)下与其同体积的4℃的纯水的质量之比表示为SG,基于JIS Z 8807(1976)“在溶液中进行称量的测定方法”求出。
关于粉末法耐水性(Dw),将与SG相当的质量的粉末玻璃(粒度425~600μm)装入铂笼中,将其浸渍在装有80ml纯水(pH=6.5~7.5)的石英玻璃制圆底烧瓶内,在沸水浴中处理60分钟,求出其减量率(%)。
关于粉末法耐酸性(Da),与Dw的测定方法同样,向烧瓶内加入0.01mol/l硝酸水溶液并进行处理,求出其减量率(%)。
表1
组成/质量% | 例1 | 例2 | 例3 | 例4 | 例5 | 例6 | 例7 |
P2O5 | 46.1 | 41.3 | 47.9 | 46.4 | 42.4 | 45.0 | 47.1 |
BaO | 32.2 | 41.8 | 32.3 | 36.0 | 35.4 | 33.9 | 29.0 |
B2O3 | 4.5 | 6.0 | 6.9 | 6.7 | 8.1 | 8.3 | 8.7 |
Al2O3 | 3.5 | 3.2 | 1.7 | 3.3 | 4.7 | 4.8 | 2.5 |
Li2O | 4.0 | 0.7 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 |
La2O3 | 2.4 | 2.0 | 5.6 | 2.1 | 2.2 | 2.2 | 2.3 |
MgO | 5.7 | 2.0 | 1.6 | 1.6 | 1.6 | 1.6 | 1.7 |
CaO | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 2.3 | 2.4 |
SrO | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 4.4 |
ZnO | 1.6 | 3.0 | 3.2 | 3.1 | 3.2 | 1.1 | 1.1 |
Gd2O3 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 |
SiO2 | 0.0 | 0.0 | 0.0 | 0.0 | 1.6 | 0.0 | 0.0 |
组成总计 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
nd | 1.59929 | 1.60706 | 1.59343 | 1.59295 | 1.59382 | 1.59257 | 1.59111 |
vd | 66.0 | 65.1 | 65.7 | 66.1 | 65.9 | 66.4 | 66.7 |
Tg/℃ | 500 | 563 | 539 | 546 | 568 | 562 | 547 |
At/℃ | 535 | 611 | 585 | 592 | 595 | 589 | 597 |
LT/℃ | 1020 | 1000 | 1040 | 1000 | 1040 | 980 | 970 |
ηLT/dPa·s | 8.0 | 9.5 | 6.0 | 10.5 | 6.0 | 13.0 | 15.0 |
SG | 3.41 | 3.65 | 3.44 | 3.46 | 3.45 | 3.40 | 3.37 |
Dw/% | 0.04 | 0.08 | 0.05 | 0.10 | 0.10 | 0.07 | 0.04 |
Da/% | 1.00 | 1.02 | 1.01 | 1.19 | 1.18 | 1.08 | 1.08 |
表2
组成/质量% | 例8 | 例9 | 例10 | 例11 | 例12 | 例13 | 例14 |
P2O5 | 47.7 | 47.2 | 48.3 | 47.1 | 37.8 | 45.2 | 47.7 |
BaO | 28.7 | 28.7 | 26.7 | 29.8 | 36.2 | 29.7 | 28.7 |
B2O3 | 9.1 | 9.9 | 10.1 | 9.9 | 4.6 | 8.8 | 8.7 |
Al2O3 | 1.9 | 2.4 | 2.5 | 2.4 | 3.8 | 2.6 | 2.5 |
Li2O | 2.7 | 4.4 | 4.8 | 4.4 | 3.7 | 1.5 | 1.3 |
La2O3 | 2.4 | 2.6 | 2.7 | 1.6 | 1.2 | 2.4 | 2.3 |
MgO | 0.4 | 0.5 | 0.5 | 0.5 | 4.8 | 1.7 | 1.7 |
CaO | 2.5 | 2.7 | 2.8 | 2.7 | 6.6 | 2.4 | 2.1 |
SrO | 3.4 | 0.3 | 0.3 | 0.3 | 0.0 | 4.5 | 5.0 |
ZnO | 1.2 | 1.3 | 1.3 | 1.3 | 0.0 | 1.2 | 0.0 |
Gd2O3 | 0.0 | 0.0 | 0.0 | 0.0 | 1.3 | 0.0 | 0.0 |
SiO2 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 |
组成总计 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
nd | 1.59231 | 1.59312 | 1.59033 | 1.59215 | 1.62010 | 1.59117 | 1.59081 |
vd | 66.8 | 66.9 | 67.0 | 67.0 | 63.5 | 66.8 | 67.1 |
Tg/℃ | 490 | 486 | 481 | 484 | 521 | 546 | 547 |
At/℃ | 534 | 524 | 512 | 517 | 561 | 593 | 595 |
LT/℃ | 950 | 950 | 940 | 930 | 890 | 1010 | 980 |
ηLT/dPa·s | 6.0 | 6.0 | 8.0 | 7.5 | 15.0 | 9.0 | 15.0 |
SG | 3.33 | 3.27 | 3.22 | 3.27 | 3.55 | 3.34 | 3.34 |
Dw/% | 0.05 | 0.08 | 0.08 | 0.05 | 0.07 | 0.06 | 0.08 |
Da/% | 1.06 | 1.32 | 1.20 | 1.34 | 0.99 | 0.86 | 1.07 |
表3
组成/质量% | 例15 | 例16 | 例17 |
P2O5 | 46.9 | 43.5 | 40.1 |
BaO | 26.9 | 21.4 | 31.9 |
B2O3 | 8.6 | 11.1 | 2.6 |
Al2O3 | 2.5 | 3.3 | 4.6 |
Li2O | 1.2 | 3.8 | 3.8 |
La2O3 | 2.3 | 1.3 | 1.2 |
MgO | 1.7 | 3.7 | 5.4 |
CaO | 2.1 | 0.0 | 6.7 |
SrO | 7.8 | 12.0 | 0.0 |
ZnO | 0.0 | 0.0 | 2.4 |
Gd2O3 | 0.0 | 0.0 | 1.3 |
SiO2 | 0.0 | 0.0 | 0.0 |
组成总计 | 100.0 | 100.0 | 100.0 |
nd | 1.59236 | 1.59259 | 1.61826 |
vd | 66.5 | 67.0 | 63.7 |
Tg/℃ | 541 | 513 | 504 |
At/℃ | 585 | 551 | 550 |
LT/℃ | 970 | 980 | 910 |
ηLT/dPa·s | 16.0 | 15.0 | 9.5 |
SG | 3.34 | 3.29 | 3.53 |
Dw/% | 0.09 | 0.07 | 0.08 |
Da/% | 1.65 | 2.49 | 0.97 |
表4
组成/摩尔% | 例1 | 例2 | 例3 | 例4 | 例5 | 例6 | 例7 |
P2O5 | 34.6 | 36.4 | 43.0 | 40.9 | 35.9 | 38.1 | 39.2 |
BaO | 22.4 | 34.1 | 26.8 | 29.3 | 27.8 | 26.6 | 22.4 |
B2O3 | 6.8 | 10.9 | 12.6 | 12.1 | 14.0 | 14.2 | 14.7 |
Al2O3 | 3.7 | 3.9 | 2.1 | 4.0 | 5.6 | 5.7 | 2.9 |
Li2O | 14.4 | 3.1 | 3.3 | 3.2 | 3.2 | 3.2 | 3.3 |
La2O3 | 0.8 | 0.8 | 2.2 | 0.8 | 0.8 | 0.8 | 0.8 |
MgO | 15.2 | 6.2 | 5.0 | 4.8 | 4.8 | 4.9 | 5.0 |
CaO | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 4.9 | 5.0 |
SrO | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 5.0 |
ZnO | 2.1 | 4.7 | 5.0 | 4.8 | 4.8 | 1.6 | 1.7 |
Gd2O3 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 |
SiO2 | 0.0 | 0.0 | 0.0 | 0.0 | 3.2 | 0.0 | 0.0 |
组成总计 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
表5
组成/摩尔% | 例8 | 例9 | 例10 | 例11 | 例12 | 例13 | 例14 |
P2O5 | 38.5 | 36.1 | 36.4 | 36.0 | 27.3 | 36.8 | 39.4 |
BaO | 21.4 | 20.3 | 18.7 | 21.1 | 24.2 | 22.4 | 22.0 |
B2O3 | 15.0 | 15.5 | 15.6 | 15.4 | 6.8 | 14.7 | 14.8 |
Al2O3 | 2.1 | 2.6 | 2.6 | 2.5 | 3.8 | 2.9 | 2.9 |
Li2O | 10.3 | 16.0 | 17.1 | 15.9 | 12.9 | 5.7 | 5.0 |
La2O3 | 0.9 | 0.9 | 0.9 | 0.5 | 0.4 | 0.8 | 0.8 |
MgO | 1.2 | 1.2 | 1.2 | 1.2 | 12.1 | 5.0 | 5.0 |
CaO | 5.1 | 5.3 | 5.3 | 5.3 | 12.1 | 5.0 | 4.4 |
SrO | 3.8 | 0.3 | 0.4 | 0.3 | 0.0 | 5.0 | 5.7 |
ZnO | 1.7 | 1.8 | 1.8 | 1.8 | 0.0 | 1.7 | 0.0 |
Gd2O3 | 0.0 | 0.0 | 0.0 | 0.0 | 0.4 | 0.0 | 0.0 |
SiO2 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 | 0.0 |
组成总计 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 | 100.0 |
表6
组成/摩尔% | 例15 | 例16 | 例17 |
P2O5 | 38.6 | 31.4 | 28.6 |
BaO | 20.5 | 14.3 | 21.0 |
B2O3 | 14.4 | 16.4 | 3.8 |
Al2O3 | 2.9 | 3.3 | 4.5 |
Li2O | 4.9 | 13.0 | 12.8 |
La2O3 | 0.8 | 0.4 | 0.4 |
MgO | 4.9 | 9.4 | 13.5 |
CaO | 4.3 | 0.0 | 12.0 |
SrO | 8.7 | 11.8 | 0.0 |
ZnO | 0.0 | 0.0 | 3.0 |
Gd2O3 | 0.0 | 0.0 | 0.4 |
SiO2 | 0.0 | 0.0 | 0.0 |
组成总计 | 100.0 | 100.0 | 100.0 |
参照特定实施方式对本发明进行了详细的说明,但对本领域技术人员显而易见的是,在不脱离本发明的构思与范围的前提下可对本发明进行各种变更和修正。
本申请是基于2010年8月6日提交的日本专利申请2010-177395和2011年7月21日提交的日本专利申请2011-159941而提出的,上述申请的内容作为参考并入本说明书中。
产业上的可利用性
本玻璃具有折射率nd为1.59以上、分散vd为63以上的新组成。作为兼顾化学耐久性和低分散性的精密模压成形用光学玻璃有用。
Claims (5)
1.一种光学玻璃,其以氧化物基准的质量%计含有
P2O5:30~50%、
BaO:18~43%、
B2O3:2~12%、
Al2O3:1.4~5%、
Li2O:大于0且为6%以下、
La2O3:大于0且为9%以下、
MgO:0.1~8%、
CaO:0~10%、
SrO:0~15%、
ZnO:0~5%、
Gd2O3:0~7%、
SiO2:0~3%,
且具有nd:1.59~1.63、vd:63~68的光学常数。
2.如权利要求1所述的光学玻璃,其中,nd:1.59以上、vd:66以上。
3.如权利要求1所述的光学玻璃,其中,nd:1.62以上、vd:63以上。
4.如权利要求1~3中任一项所述的光学玻璃,其中,液相温度粘度ηLT为6dPa·s以上。
5.如权利要求4所述的光学玻璃,其中,液相温度粘度ηLT为12dPa·s以上。