CN102345234A - Water-proof processing technology for textile - Google Patents
Water-proof processing technology for textile Download PDFInfo
- Publication number
- CN102345234A CN102345234A CN2011101190851A CN201110119085A CN102345234A CN 102345234 A CN102345234 A CN 102345234A CN 2011101190851 A CN2011101190851 A CN 2011101190851A CN 201110119085 A CN201110119085 A CN 201110119085A CN 102345234 A CN102345234 A CN 102345234A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- waterproof
- processing method
- typing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a water-proof processing technology for textile. The technology comprises the steps of: (a) machine-printing and coating a water-proof combination agent; and (b) sizing and roasting, wherein the water-proof combination agent comprises the following materials in parts by weight: 100 parts of water-proofing agent, 15-21.5 parts of cross-linking agent, 14-20 parts of thickening agent and 870-1,300 parts of water. A rotary screen printing machine, particularly a 105-mesh circular screen blank and a No. 10 magnetic rod, are used for the machine-printing, the speed is 15-20 yards/minute, and the drying temperature is 150-170 DEG C; the sizing and roasting temperature is 150-170 DEG C, and the speed is 25-30 yards/minutes; and a sizing auxiliary agent is added. The textile processed by the technology has an effective water-proof effect and a durable processing effect and can keep the original handfeel; air permeability and moisture permeability are hardly influenced.
Description
Technical field
The present invention relates to a kind of textile water proof processing technology.
Background technology
Water with can be penetrated into fabric back after common weaving face fabric contacts and influence appearance of fabrics and comfortableness.Therefore, the waterproof fabrics demand that can be widely used in special climate, the particular surroundings such as daily life and rainy day, hot summer days, high temperature, field is more and more vigorous.When possessing water resistance, the breathable moisture permeability of lining also need be taken into account.That is to say that the rainwater that molecular diameter is bigger does not immerse lining under certain pressure, and the sweat of body can spread, and prevents that sweat from accumulating between body surface and lining with the form of the less steam of molecular diameter through fabric, thereby keep the comfort of body.
Waterproof fabrics roughly is divided three classes.One type is the high-density fabric that comes Waterproof Breathable through the space of lining itself, such as Coolmax class lining, sweat can be excreted at the microchannel of its fibrous inside, can prevent that rainwater from infiltrating simultaneously again.This type lining is grasped production technology by international major company, belongs to high-end product, and market penetration rate is low.Another kind of is to realize waterproof through microporous membrane, with the kinds of processes technology HAIR COLOR COMPOSITION is coated on fabric face, solidifies back formation film, thereby seals or reduce the function of the space realization Waterproof Breathable of fabric itself.This type of lining poisture-penetrability is relatively poor, can not satisfy basic Waterproof Breathable needs.The 3rd type is the non-porous film waterproof moisture permeating fabric; Thereby form the purpose that nonporous film reaches waterproof with HAIR COLOR COMPOSITION coating, oven dry back at fabric face, the hydrophilic radical that the macromolecule in the while waterproofing agent contains is given lining ventilation and perspiration function performance through penetration mechanism.The thickness of controlling diaphragm is quite important in the treatment process of this type lining.
Summary of the invention
The object of the present invention is to provide a kind of textile water proof processing technology, be applicable to the processing of aforementioned the 3rd type of non-porous film waterproof moisture permeating fabric.Reach the viscosity that coating and apparatus processing need through the proportioning of regulating the waterproof combination agent, control each item indexs such as temperature in the process, the speed of a motor vehicle, equipment simultaneously, guarantee that overlay film thickness is more than 10uM.This technology can solve the unmanageable problem of waterproof coating thickness in the existing textile water proof treatment technology, makes fabric obtain durable water resistance, and does not influence the breathable moisture permeability of converted goods.
For reaching above purpose, the method that the present invention adopted may further comprise the steps:
A) with rotary screen printing machines coating waterproof combination agent, this combination agent comprises waterproofing agent, crosslinking agent, thickener and water;
B) typing bakes.
The compound method of said waterproof combination agent is:
A) in waterproofing agent, progressively add earlier water and form dispersion;
B) with dispersion and the abundant mixing of crosslinking agent;
C) in dispersion, add thickener and regulate composition viscosity.
Wherein, as if being 100 parts of unit of weights with the waterproofing agent consumption, dosage of crosslinking agent is 15-21.5 part unit of weight
,The thickener consumption is 14-20 part unit of weight, and the consumption of water is 870-1300 part unit of weight, and combination agent viscosity is between the 3700-4000 centipoise.
Rotary screen printing machines is selected 105 order cylinder net embryos and No. 10 bar magnets.The speed of a motor vehicle be the 15-20 sign indicating number/minute.Machine seal comprises that drying process, purpose are to dry moist fabric after the coating waterproof combination agent, and drying temperature is 150-170 ℃.
Typing bakes in the step soaks fabric in advance in the typing auxiliary agent.The typing baking temperature is 150-170 ℃.The speed of a motor vehicle be the 25-30 sign indicating number/minute.
In a preferred embodiment of the invention, said typing auxiliary agent comprises antiseptic, and consumption is 0.5%.
In a preferred embodiment of the invention, said typing auxiliary agent comprises inhales apparent perspire agent, and consumption is 3%.
Compared with prior art the present invention has the following advantages:
1. adaptable across synthetic fiber, natural fabric and blended fabric thereof, like terylene, nylon, cotton, silk, hair etc.;
2. water resistance is lasting;
3. the breathable moisture permeability that keeps fabric;
4. can carry out single face waterproof processing or double-faced waterproofing processing according to demand.
Description of drawings
Fig. 1 is the most crucial process chart of the present invention, comprises with printing machine coating waterproof combination agent and typing baking two steps.
Fig. 2 has increased by two steps on the basis of core process: the washing after preliminary treatment before the processing and the processing, and to remove the residual chemicals of fabric face.
The specific embodiment
The object of the invention is the waterproof processing technology to optimize, and makes fabric obtain durable water resistance, and does not influence the breathable moisture permeability of fabric, keeps the feel of fabric.Below in conjunction with accompanying drawing the present invention is further described.
Specific embodiment 1
As shown in Figure 1, comprise in the present embodiment with printing machine coating waterproof combination agent and typing and bake two steps.
Prepare the waterproof combination agent earlier, composition comprises waterproofing agent, crosslinking agent, thickener and water.In waterproofing agent, progressively adding water and form dispersion, is 100 parts of unit of weights as if the consumption with waterproofing agent, and then water is 870 parts of unit of weights.With dispersion and the abundant mixing of crosslinking agent, dosage of crosslinking agent is 15 parts of unit of weights.The thickener adjusting composition viscosity that in dispersion, adds 14 parts of unit of weights reaches 4000 centipoises.
The coating apparatus of waterproof combination agent is a rotary screen printing machines, specifically selects 105 order cylinder net embryos and No. 10 bar magnets, and the speed of a motor vehicle is 20 yards/minute, and at 170 ℃ of dryings.
Afterwards, prepare style keeping liquid, comprise antiseptic and the apparent perspire agent of suction of 3% O.W.f. and 96.5% the water of typing auxiliary agent 0.5% O.W.f..Fabric bakes to reach the purpose of typing at 170 ℃ with 30 yards/minute speed of a motor vehicle after this style keeping liquid soaks.
Specific embodiment 2
As shown in Figure 2, increased by two steps in the front and back of waterproof processing: the washing after preliminary treatment before the processing and the processing, waterproof processing process comprise with printing machine and are coated with water-proofing composition and typing bakes.
Carrying out treating the converted goods preliminary treatment earlier before the WATER REPELLENT TREATMENT, it fully to be washed and dries, purpose is to remove medicaments such as dyestuff residual on the fabric, surfactant, to avoid influencing water proofing property and durability.
After the preliminary treatment, preparation waterproof combination agent.In waterproofing agent, progressively adding water and form dispersion, is 100 parts of unit of weights as if the consumption with waterproofing agent, and then water is 1300 parts of unit of weights.With dispersion and the abundant mixing of crosslinking agent, dosage of crosslinking agent is 21.5 parts of unit of weights.The thickener adjusting composition viscosity that in dispersion, adds 20 parts of unit of weights reaches 3700 centipoises.
The coating apparatus of waterproof combination agent is a rotary screen printing machines, specifically selects 105 order cylinder net embryos and No. 10 bar magnets, and the speed of a motor vehicle is 20 yards/minute, and at 170 ℃ of dryings.
Afterwards, prepare style keeping liquid, comprise antiseptic and the apparent perspire agent of suction of 3% O.W.f. and 96.5% the water of typing auxiliary agent 0.5% O.W.f..Fabric bakes to reach the purpose of typing at 170 ℃ with 30 yards/minute speed of a motor vehicle after this style keeping liquid soaks.
Fabric after the typing is dried after with cold water washing, and purpose is to remove the chemicals of remained on surface, and softening fabrics improves feel.
Specific embodiment 3
Comprise in the present embodiment with printing machine coating waterproof combination agent and typing and bake two steps.
Prepare the waterproof combination agent earlier, composition comprises waterproofing agent, crosslinking agent, thickener and water.In waterproofing agent, progressively adding water and form dispersion, is 100 parts of unit of weights as if the consumption with waterproofing agent, and then water is 870 parts of unit of weights.With dispersion and the abundant mixing of crosslinking agent, dosage of crosslinking agent is 15 parts of unit of weights.The thickener adjusting composition viscosity that in dispersion, adds 14 parts of unit of weights reaches 4000 centipoises.
The coating apparatus of waterproof combination agent is a rotary screen printing machines, specifically selects 105 order cylinder net embryos and No. 10 bar magnets, and the speed of a motor vehicle is 15 yards/minute, and at 150 ℃ of dryings.
Afterwards, prepare style keeping liquid, comprise antiseptic and the apparent perspire agent of suction of 3% O.W.f. and 96.5% the water of typing auxiliary agent 0.5% O.W.f..Fabric bakes to reach the purpose of typing at 150 ℃ with 25 yards/minute speed of a motor vehicle after this style keeping liquid soaks.
The above; It only is the specific embodiment of the present invention; But protection scope of the present invention is not limited thereto; Any those of ordinary skill in the art are in the technical scope that the present invention disclosed; Variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (9)
1. textile water proof processing method is characterized in that may further comprise the steps:
Use rotary screen printing machines coating waterproof combination agent, this combination agent comprises waterproofing agent, crosslinking agent, thickener and water, and said printing machine adopts 105 order cylinder net embryos and No. 10 bar magnets;
Typing bakes;
And the compound method of said waterproof combination agent is:
Earlier, the water formation dispersion that in the waterproofing agent of 100 parts of unit of weights, progressively adds 870-1300 part unit of weight;
Again, with the dispersion that mixes and the abundant mixing of crosslinking agent of 15-21.5 part unit of weight;
At last, the viscosity that in the mixed liquor of step b, adds the thickener adjusting waterproof combination agent of 14-20 part unit of weight.
2. waterproof processing method according to claim 1 is characterized in that: the viscosity of said combination agent is between the 3700-4000 centipoise.
3. waterproof processing method according to claim 1 is characterized in that: this method also comprises drying process when printing machine is coated with, and drying temperature is 150-170 ℃.
4. waterproof processing method according to claim 1 is characterized in that: the said printing machine speed of a motor vehicle be the 15-20 sign indicating number/minute.
5. waterproof processing method according to claim 1 is characterized in that: said typing baking temperature is 150-170 ℃.
6. waterproof processing method according to claim 1 is characterized in that: said typing bake the speed of a motor vehicle be the 25-30 sign indicating number/minute.
7. waterproof processing method according to claim 1 is characterized in that: said typing bakes in the step soaks fabric in the typing auxiliary agent in advance.
8. waterproof processing method according to claim 7 is characterized in that: said typing auxiliary agent comprises antiseptic, and consumption is 0.5%.
9. waterproof processing method according to claim 7 is characterized in that: said typing auxiliary agent comprises inhales apparent perspire agent, and consumption is 3%.