CN102322103A - Rock wool composite heat insulating board enwrapped by fibreglass gridding cloth and manufacture method thereof - Google Patents
Rock wool composite heat insulating board enwrapped by fibreglass gridding cloth and manufacture method thereof Download PDFInfo
- Publication number
- CN102322103A CN102322103A CN201110184422A CN201110184422A CN102322103A CN 102322103 A CN102322103 A CN 102322103A CN 201110184422 A CN201110184422 A CN 201110184422A CN 201110184422 A CN201110184422 A CN 201110184422A CN 102322103 A CN102322103 A CN 102322103A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- rock wool
- fiber reticular
- reticular cloth
- rubber cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a rock wool composite heat insulating board enwrapped by multiple layers of fibreglass gridding cloth and a manufacture method thereof, which are characterized in that the rock wool composite heat insulating board comprises an upper-layer fibreglass gridding cloth and a lower-layer fibreglass gridding cloth; and a layer of low-intensity heat insulating rock wool board is arranged between the two layers of fibreglass gridding cloth which is dipped with mucilage. The rock wool composite heat insulating board enwrapped by the fibreglass gridding cloth and the manufacture method have the advantages of simple structural design, fire prevention and better heat insulating effect and can be extensively applied to the external wall heat insulation of various buildings.
Description
Technical field
The present invention relates to a kind of warming plate, more specifically relate to a kind of glass fiber reticular cloth and coat the rock wool composite insulation boards, also relate to the preparation method of this warming plate simultaneously.
Background technology
The enforcement with the building energy conservation policy of coming of energy crisis has promoted the fast development of wall heat insulation material.At present; It is the Outwall thermal insulation board system of heat insulating material that the skin space enclosing structure adopts with organic foam plastics such as polystyrene foam plastics, rigid polyurethane fat vacuole foam plastics more, and still, such heat insulating material very easily burns; Fire spreading is rapid during burning; And, bring exceptional hardship to rescue work of extinguishing fire with a large amount of poison gases and flue gas generation, be prone to cause casualties and property loss.Simultaneously such heat insulating material also exist be prone to aging, poor dimensional stability, with shortcomings such as the surface material adhesion strength is low.Recently; Building fire frequently takes place; People are had higher requirement to the fireproof performance of heat insulating material, fireproof performance is good, ageing-resistant, coefficient of deformation is little because of having for inorganic heat insulation material, with surface material adhesion strength advantages of higher, caused people's extensive concern; Inorganic heat insulation material is applied in the wall heat insulation material, has popularizing application prospect widely.
The rock wool heat-preservation plate is to be primary raw material with basalt and other natural crystal etc., becomes fine through high-temperature fusion, adds an amount of cementing agent, solidifies processing and makes.The rock wool heat-preservation plate has fire-proof function, and the material combustion grade reaches the A level, also has the characteristics of light weight, insulation simultaneously, but the intensity of rock wool heat-preservation plate is low, be prone to dry linting, globality is poor, has limited its large-scale promotion application.
Summary of the invention
The objective of the invention is to overcome the deficiency of prior art, provide a kind of light weight, high-strength, insulation, fireproof glass fiber reticular cloth to coat rock wool composite insulation boards and preparation method thereof.
For realizing above-mentioned purpose; The present invention takes following technical scheme: a kind of glass fiber reticular cloth coats the rock wool composite insulation boards; It is characterized in that: it comprises the glass fiber reticular cloth of upper and lower two-layer dipping rubber cement, and one deck rock wool heat-preservation plate is set between the glass fiber reticular cloth of said two-layer dipping rubber cement.
The thickness of the glass fiber reticular cloth of said dipping rubber cement is 0.3~1.5mm.
The slurry that said glass fiber reticular cloth dipping rubber cement uses is polymer cement.
The density of said rock wool heat-preservation plate is 100~200kg/m
3, thickness is 40~120mm.
Above-mentioned glass fiber reticular cloth coats the preparation method of rock wool composite insulation boards, and it may further comprise the steps: 1) with glass fiber reticular cloth under the traction of automatic winding machine, pass through polymer cement dipping tank and drying box successively, make the glass fiber reticular cloth of dipping rubber cement continuously; 2) lay the glass fiber reticular cloth that one deck floods rubber cement at mold bottom; 3) respectively apply the one layer of polymeric rubber cement on the upper and lower surface of rock wool heat-preservation plate, and be placed on the glass fiber reticular cloth of dipping rubber cement in the mould; 4) extrusion forming behind the glass fiber reticular cloth of laying one deck dipping rubber cement on the rock wool heat-preservation plate in mould makes glass fiber reticular cloth and coats the rock wool composite insulation boards; 5) glass fiber reticular cloth is coated the rock wool composite insulation boards and from mould, eject, and place drying box dry.
The present invention is owing to take above technical scheme, and it has the following advantages: the present invention has respectively coated the glass fiber reticular cloth of one deck dipping rubber cement on the upper and lower surface of rock wool heat-preservation plate, has improved the intensity and the globality of warming plate.Structure design of the present invention is simple, and fire prevention, heat insulation and preservation effect is good, can be widely used in various skins insulations.
Description of drawings
Fig. 1 is the structural representation that glass fiber reticular cloth of the present invention coats the rock wool composite insulation boards.
Fig. 2 is the drawing in side sectional elevation that glass fiber reticular cloth of the present invention coats the rock wool composite insulation boards.
Among the figure, 1 for glass fiber reticular cloth coats the rock wool composite insulation boards, 2 glass fiber reticular cloths for the dipping rubber cement, and 3 is the rock wool heat-preservation plate.
The specific embodiment
Below in conjunction with accompanying drawing and embodiment the present invention is carried out detailed description.
As shown in Figure 1, the present invention includes the glass fiber reticular cloth 2 of upper and lower two-layer dipping rubber cement, one deck rock wool heat-preservation plate 3 is set, as middle insulation layer between the glass fiber reticular cloth 2 of two-layer dipping rubber cement.
In the foregoing description, the thickness of the glass fiber reticular cloth 2 of two-layer dipping rubber cement is 0.3~1.5mm.
In the foregoing description, the slurry that glass fiber reticular cloth dipping rubber cement uses is polymer cement.
In the foregoing description, the density of intermediate layer rock wool heat-preservation plate 3 is 100~200kg/m
3, thickness is 40~120mm.
Preparation method of the present invention is:
1) with glass fiber reticular cloth under the traction of automatic winding machine, pass through polymer cement dipping tank and drying box successively, make continuously the dipping rubber cement glass fiber reticular cloth.
2) lay the glass fiber reticular cloth that a layer thickness is the dipping rubber cement of 0.3~1.5mm at mold bottom.
3) respectively apply the one layer of polymeric rubber cement on the upper and lower surface of rock wool heat-preservation plate, and the rock wool heat-preservation plate is placed on the glass fiber reticular cloth of mould dipping rubber cement, the density of rock wool heat-preservation plate is 100~200kg/m
3, thickness is 40~120mm.
4) in mould, lay extrusion forming behind the glass fiber reticular cloth of dipping rubber cement that one deck thickness is 0.3~1.5mm on the rock wool heat-preservation plate, make glass fiber reticular cloth and coat the rock wool composite insulation boards.
5) glass fiber reticular cloth is coated the rock wool composite insulation boards and from mould, eject, and place drying box dry.
The foregoing description only is used to explain the present invention, and wherein the structure of each parts, connected mode etc. can change to some extent, and every equivalent variations of on the basis of technical scheme of the present invention, carrying out and improvement all should not got rid of outside protection scope of the present invention.
Claims (5)
1. a glass fiber reticular cloth coats the rock wool composite insulation boards, and it is characterized in that: it comprises the glass fiber reticular cloth of upper and lower two-layer dipping rubber cement, and one deck rock wool heat-preservation plate is set between the glass fiber reticular cloth of said two-layer dipping rubber cement.
2. a kind of glass fiber reticular cloth as claimed in claim 1 coats the rock wool composite insulation boards, and it is characterized in that: the thickness of the glass fiber reticular cloth of said two-layer dipping rubber cement is 0.3~1.5mm.
3. a kind of glass fiber reticular cloth as claimed in claim 1 coats the rock wool composite insulation boards, it is characterized in that: the slurry that said glass fiber reticular cloth dipping rubber cement uses is polymer cement.
4. a kind of glass fiber reticular cloth as claimed in claim 1 coats the rock wool composite insulation boards, and it is characterized in that: the density of said rock wool heat-preservation plate is 100~200kg/m
3, thickness is 40~120mm.
5. coat the preparation method of rock wool composite insulation boards like each said glass fiber reticular cloth of claim 1~5, it may further comprise the steps:
1) with glass fiber reticular cloth under the traction of automatic winding machine, pass through polymer cement dipping tank and drying box successively, make continuously the dipping rubber cement glass fiber reticular cloth;
2) lay the glass fiber reticular cloth that one deck floods rubber cement at mold bottom;
3) respectively apply the one layer of polymeric rubber cement on the upper and lower surface of rock wool heat-preservation plate, and be placed on the glass fiber reticular cloth of dipping rubber cement in the mould;
4) extrusion forming behind the glass fiber reticular cloth of laying one deck dipping rubber cement on the rock wool heat-preservation plate in mould makes glass fiber reticular cloth and coats the rock wool composite insulation boards;
5) glass fiber reticular cloth is coated the rock wool composite insulation boards and from mould, eject, and place drying box dry.